CN109576046A - Dedicated drawing powder of spring steel wire and preparation method thereof - Google Patents
Dedicated drawing powder of spring steel wire and preparation method thereof Download PDFInfo
- Publication number
- CN109576046A CN109576046A CN201811633934.3A CN201811633934A CN109576046A CN 109576046 A CN109576046 A CN 109576046A CN 201811633934 A CN201811633934 A CN 201811633934A CN 109576046 A CN109576046 A CN 109576046A
- Authority
- CN
- China
- Prior art keywords
- steel wire
- spring steel
- drawing powder
- preparation
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of dedicated drawing powder of spring steel wire, its each raw material component and its content are stearic acid 50%~80%, sodium hydroxide 8%~20%, sodium nitrite 1%~10%, molybdenum disulfide 1%~4%, water 5%~20%, it can be in the iron phosphate membrane of steel tube surface formation layer, this layer of ferric phosphate film layer has preferable ductility, ensure steel pipe in alternative process not by plucking, along with the oil base lubricant layer on surface, and meet the lubrication and the requirement of the antirust in later period of drawing completion.
Description
[technical field]
The present invention relates to chemical field, specially a kind of dedicated drawing powder of spring steel wire and preparation method thereof.
[background technique]
Spring steel wire generally requires have higher intensity, and preferable anti-fatigue performance, this requires spring steel wires to make
Biggish deflection again in the process.The preparation of spring steel wire generally uses medium and high carbon steel, and steel wire compression ratio is drawn 90% or more
It pulls out rear surface and is unable to Fil-Lumiere.This undoubtedly proposes very high requirement to the lubrication in spring steel wire drawing process.This wire drawing powder
It is specific to the wire drawing powder of spring steel wire exploitation, he has preferable greasy property, and the grain of our strict control wire drawing powder
Diameter distribution, greatly reduces the lift of wire drawing powder in use, will not influence the health of operator.
[summary of the invention]
The present invention is able to satisfy high pressure in view of the above-mentioned problems, provide a kind of dedicated drawing powder of spring steel wire and preparation method thereof
The drawing requirement of shrinkage.
To solve the above-mentioned problems, the present invention provides a kind of dedicated drawing powder of spring steel wire and preparation method thereof, Qi Geyuan
Expect component and its content is stearic acid 50%~80%, sodium hydroxide 8%~20%, sodium nitrite 1%~10%, molybdenum disulfide
1%~4%, water 5%~20%.
Further, each raw material component and its content are stearic acid 50%~70%, sodium hydroxide 15%~20%, Asia
Sodium nitrate 1%~5%, molybdenum disulfide 1%~4%, water 5%~10%.
Further, each raw material component and its content are stearic acid 70%, sodium hydroxide 15%, sodium nitrite 5%, two
Molybdenum sulfide 2%, water 8%.
To solve the above-mentioned problems, the present invention also provides the preparation method for preparing the dedicated drawing powder of the spring steel wire, packets
Include following steps:
(1) sodium hydroxide and water are poured into container, opens stirring and heating, set 150~200 DEG C of oil temperature, material temperature 100
It~120 DEG C, stirs 5-10 minutes;
(2) stearic acid is added to be sufficiently stirred;
(3) sodium nitrite then is added and molybdenum disulfide is being heated and stirred 6~7 hours;
(4) heating is closed, it is cooling.
Further, reaction 1-1.5 hours in step (2).
Further, 120 DEG C -150 DEG C of temperature of material temperature in step (3).
Further, the preparation method of the dedicated drawing powder of the spring steel wire,
(1) sodium hydroxide and water are poured into container, opens stirring and heating, set 200 DEG C of oil temperature, 120 DEG C of material temperature, stir
It mixes 5 minutes;
(2) stearic acid is added and reaction 1 hour is sufficiently stirred;
(3) sodium nitrite then is added and molybdenum disulfide stirs 6 hours at 120 DEG C again, close heating, it is cooling.
Compared with prior art, the present invention has the advantage that
1. by the steel wire after this drawing powder drawing, 95% or more 5.5mm steel wire compression ratio, the steel wire black after drawing is equal
Even no Fil-Lumiere;
2. being able to satisfy the drawing requirement of high compression rate;
3. drawing speed can reach 7m/s or more;
4. the granularity of 20~40 mesh of drawing powder accounts for 80%, dust is greatly reduced.
[Detailed description of the invention]
Nothing
[specific embodiment]
The dedicated drawing powder each raw material component of spring steel wire and its content in the present invention are stearic acid 50%~80%, hydrogen-oxygen
Change sodium 8%~20%, sodium nitrite 1%~10%, molybdenum disulfide 1%~15%, water 5%~20%, preparation method: by hydrogen-oxygen
Change sodium and water pours into kneader, open stirring and heating, sets 150~200 DEG C of oil temperature, 100~120 DEG C of material temperature.Stir 5-
10 minutes, be added stearic acid be sufficiently stirred reaction 1-1.5 hour, then addition sodium nitrite and molybdenum disulfide again 120 DEG C~
150 lower stirrings 6~7 hours, close heating, cooling takes the dish out of the pot.
Embodiment 1:
The dedicated drawing powder each raw material component of spring steel wire and its content in the present invention are stearic acid 50%, sodium hydroxide
20%, sodium nitrite 9%, molybdenum disulfide 1%, water 20%, preparation method: sodium hydroxide and water are poured into kneader, are opened
Stirring and heating, set 180 DEG C of oil temperature, 112 DEG C of material temperature.Stirring 8 minutes is added stearic acid and reaction 1 hour is sufficiently stirred, then
Sodium nitrite is added and molybdenum disulfide stirs 7 hours at 120 DEG C again, closes heating, cooling takes the dish out of the pot.The steel wire drawing of 5.5mm is arrived
1.3mm, drawing speed 6m/s.
Embodiment 2:
The dedicated drawing powder each raw material component of spring steel wire and its content in the present invention are stearic acid 80%, sodium hydroxide
8%, sodium nitrite 10%, molybdenum disulfide 2%, water 5%, preparation method: sodium hydroxide and water are poured into kneader, and opening is stirred
Heating is mixed and stirred, sets 150 DEG C of oil temperature, 100 DEG C of material temperature.Stirring 5 minutes is added stearic acid and reaction 1.3 hours is sufficiently stirred, then
Sodium nitrite is added and molybdenum disulfide stirs 6.5 hours at 130 DEG C again, closes heating, cooling takes the dish out of the pot.The steel wire of 5.5mm is drawn
To 1.3mm, drawing speed 7m/s.
Embodiment 3:
The dedicated drawing powder each raw material component of spring steel wire and its content in the present invention are stearic acid 70%, sodium hydroxide
15%, sodium nitrite 5%, molybdenum disulfide 15%, water 8%, preparation method: sodium hydroxide and water are poured into kneader, are opened
Stirring and heating, set 200 DEG C of oil temperature, 120 DEG C of material temperature.Stirring 10 minutes is added stearic acid and reaction 1.5 hours is sufficiently stirred,
Then sodium nitrite is added and molybdenum disulfide stirs 7 hours at 150 DEG C again, close heating, cooling takes the dish out of the pot.The steel wire of 5.5mm
Draw 1.3mm, drawing speed 7.5m/s.
Embodiment 4:
The dedicated drawing powder each raw material component of spring steel wire and its content in the present invention are stearic acid 65%, sodium oxide molybdena
15%, sodium nitrite 1%, molybdenum disulfide 4%, water 10%, preparation method: sodium hydroxide and water are poured into kneader, are opened
Stirring and heating, set 150 DEG C of oil temperature, 120 DEG C of material temperature.Stirring 5 minutes is added stearic acid and reaction 1.5 hours is sufficiently stirred, so
Sodium nitrite is added afterwards and molybdenum disulfide stirs 6 hours at 140 DEG C again, closes heating, cooling takes the dish out of the pot.The steel wire of 5.5mm is drawn
To 1.3mm, drawing speed 6.8m/s.
Use technique:
Drawing powder is poured into drawing mould box, drawing powder additional amount is 2/3rds of mold box.
The advantages of the invention:
1. by the steel wire after this drawing powder drawing, 95% or more 5.5mm steel wire compression ratio, the steel wire black after drawing is equal
Even no Fil-Lumiere;
2. being able to satisfy the drawing requirement of high compression rate;
3. drawing speed can reach 7m/s or more;
4. the granularity of 20~40 mesh of drawing powder accounts for 80%, dust is greatly reduced.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (7)
1. a kind of dedicated drawing powder of spring steel wire, which is characterized in that its each raw material component and its content be stearic acid 50%~
80%, sodium hydroxide 8%~20%, sodium nitrite 1%~10%, molybdenum disulfide 1%~4%, water 5%~20%.
2. the dedicated drawing powder of spring steel wire according to claim 1, which is characterized in that its each raw material component and its content are hard
Resin acid 50%~70%, sodium hydroxide 15%~20%, sodium nitrite 1%~5%, molybdenum disulfide 1%~4%, water 5%~
10%.
3. the dedicated drawing powder of spring steel wire according to claim 1 or claim 2, which is characterized in that its each raw material component and its content
For stearic acid 70%, sodium hydroxide 15%, sodium nitrite 5%, molybdenum disulfide 2%, water 8%.
4. a kind of preparation method of the dedicated drawing powder of the spring steel wire as described in any one of claims 1 to 3, which is characterized in that packet
Include following steps:
(1) sodium hydroxide and water are poured into container, open stirring and heated, 150~200 DEG C of oil temperature of setting, material temperature 100~
It 120 DEG C, stirs 5-10 minutes;
(2) stearic acid is added to be sufficiently stirred;
(3) sodium nitrite then is added and molybdenum disulfide is being heated and stirred 6~7 hours;
(4) heating is closed, it is cooling.
5. the preparation method of the dedicated drawing powder of spring steel wire according to claim 4, which is characterized in that reaction in step (2)
1-1.5 hour.
6. the preparation method of the dedicated drawing powder of spring steel wire according to claim 4, which is characterized in that material temperature in step (3)
120 DEG C -150 DEG C of temperature.
7. the preparation method of the dedicated drawing powder of spring steel wire according to claim 4, which is characterized in that
(1) sodium hydroxide and water are poured into container, opens stirring and heating, set 200 DEG C of oil temperature, 120 DEG C of material temperature, stir 5
Minute;
(2) stearic acid is added and reaction 1 hour is sufficiently stirred;
(3) sodium nitrite then is added and molybdenum disulfide stirs 6 hours at 120 DEG C again, close heating, it is cooling.