CN109571915A - A kind of processing technology of new energy car battery pallet - Google Patents
A kind of processing technology of new energy car battery pallet Download PDFInfo
- Publication number
- CN109571915A CN109571915A CN201811372462.0A CN201811372462A CN109571915A CN 109571915 A CN109571915 A CN 109571915A CN 201811372462 A CN201811372462 A CN 201811372462A CN 109571915 A CN109571915 A CN 109571915A
- Authority
- CN
- China
- Prior art keywords
- parts
- new energy
- car battery
- processing technology
- energy car
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing technologys of new energy car battery pallet.Processing technology is the following steps are included: (1) makes mold;(2) making material;(3) plastics sucking moulding;(4) it is surface-treated.The present invention uses acrylic resin for primary raw material, the intensity that glass fibre, nano-titanium dioxide and nano silica improve acrylic resin is added, hydrogenated vegetable oil and fatty glyceride reduce the overall weight of raw material, are suitable for new energy car battery pallet.
Description
Technical field
The present invention relates to a kind of processing technologys of new energy car battery pallet, belong to plastic uptake technical field.
Background technique
With the development of technology, new-energy automobile is current development trend.New-energy automobile refers to using unconventional
As a source of power (or using conventional vehicle fuel, using new vehicle-mounted power plant), comprehensive vehicle moves vehicle fuel
The advanced technology of power control and driving aspect, the advanced automobile with new technology, new construction of the technical principle of formation.
The battery of new-energy automobile is very important component, and usual battery is mounted on new-energy automobile by battery tray
Vehicle frame on, the pallet as made of metal, heavier mass, be unfavorable for realize vehicle lightweight, so now beginning to inhale
Pallet is moulded, but existing plastic-sucking tray generally uses conventional plastic-absorbing component processing method, but since pallet is integrally larger, add
Work difficulty is high, and conventional processing method can not be completely adapted to the requirement of new-energy automobile.
Summary of the invention
For overcome the deficiencies in the prior art, the present invention provides a kind of processing technologys of new energy car battery pallet.
The present invention is achieved through the following technical solutions:
A kind of processing technology of new energy car battery pallet, comprising the following steps:
(1) make mold: it is spare to make mold according to the shape of pallet;
(2) making material: glass fibre is placed in smelting furnace, is heated to 200-300 DEG C, and nano-titanium dioxide and nanometer two is added
Silica reacts 30-40min;It is cooled to 60-80 DEG C, it is mixed that acrylic resin, hydrogenated vegetable oil and fatty glyceride is added
It closes, is eventually adding lubricant, is sufficiently mixed and is placed in extruder, obtain base sheet;
(3) plastics sucking moulding: base sheet is placed in Packing Machine, and pallet is prepared;
(4) be surface-treated: spraying one layer of anti-radiation coating in tray surface, by the vacuum formed box after spraying be placed in baking oven drying or
Naturally dry.
A kind of processing technology of new energy car battery pallet, the parts by weight of each raw material of the base sheet
It is respectively as follows: 100-120 parts of acrylic resin, 15-24 parts of glass fibre, 3-9 parts of nano-titanium dioxide, nano silica 3-9
Part, 10-15 parts of hydrogenated vegetable oil, 2-5 parts of fatty glyceride and 3-6 parts of lubricant.
A kind of processing technology of new energy car battery pallet, the lubricant are silicone oil.
A kind of processing technology of new energy car battery pallet, the anti-radiation coating include following raw material: ring
Oxygen resin, antimony oxide, methyl anyl alcohol, dodecyl sodium sulfate and antioxidant.
A kind of processing technology of new energy car battery pallet, the parts by weight of each raw material of the anti-radiation coating
Number is respectively as follows: 100-120 parts of epoxy resin, 3-6 parts of antimony oxide, 20-40 parts of methyl anyl alcohol, 10-16 parts of dodecyl sodium sulfate
With 1-1.5 parts of antioxidant.
A kind of processing technology of new energy car battery pallet, the anti-radiation coating is through the following steps that obtain
: after epoxy resin, antimony oxide and methyl anyl alcohol are sufficiently mixed, dodecyl sodium sulfate and antioxidant is added, mixes again
The anti-radiation coating is obtained after conjunction.
Advantageous effects of the invention:
The present invention uses acrylic resin for primary raw material, and glass fibre, nano-titanium dioxide and nano silica is added and mentions
The high intensity of acrylic resin, hydrogenated vegetable oil and fatty glyceride reduce the overall weight of raw material, suitable for new
Energy automobile battery tray.
The base sheet good-extensibility that each material combination is prepared, the pallet for being suitble to processing large-scale, using conventional suction
Molding machine can be processed.
Anti-radiation coating is sprayed in tray surface, the capability of resistance to radiation of pallet is improved, suitable for holding battery.
Specific embodiment
The invention will be further described below.Following embodiment is only used for clearly illustrating technical side of the invention
Case, and not intended to limit the protection scope of the present invention.
Embodiment 1
A kind of processing technology of new energy car battery pallet, comprising the following steps:
(1) make mold: it is spare to make mold according to the shape of pallet;
(2) making material: glass fibre is placed in smelting furnace, is heated to 200-300 DEG C, and nano-titanium dioxide and nanometer two is added
Silica reacts 30-40min;It is cooled to 60-80 DEG C, it is mixed that acrylic resin, hydrogenated vegetable oil and fatty glyceride is added
It closes, is eventually adding silicone oil, is sufficiently mixed and is placed in extruder, obtain base sheet;
(3) plastics sucking moulding: base sheet is placed in Packing Machine, and pallet is prepared;
(4) be surface-treated: spraying one layer of anti-radiation coating in tray surface, by the vacuum formed box after spraying be placed in baking oven drying or
Naturally dry.
The parts by weight of each raw material of the base sheet are respectively as follows: 100 parts of acrylic resin, 24 parts of glass fibre, receive
3 parts of titanium dioxide of rice, 3 parts of nano silica, 10 parts of hydrogenated vegetable oil, 5 parts of fatty glyceride and 3 parts of silicone oil.
The anti-radiation coating includes following raw material: epoxy resin, antimony oxide, methyl anyl alcohol, dodecyl sodium sulfate and
Antioxidant.The parts by weight of each raw material of the anti-radiation coating are respectively as follows: 120 parts of epoxy resin, 3 parts of antimony oxide, methylpent
20 parts of alcohol, 10 parts of dodecyl sodium sulfate and 1 part of antioxidant.
The anti-radiation coating is through the following steps that obtain: epoxy resin, antimony oxide and methyl anyl alcohol is sufficiently mixed
After conjunction, dodecyl sodium sulfate and antioxidant is added, obtains the anti-radiation coating after mixing again.
Each raw material cooperative cooperating of the anti-radiation coating is added antimony oxide and antioxidant improves based on epoxy resin
Its anti-radiation and anti-aging ability, is added that methyl anyl alcohol each stock dispersion is uniform, and dodecyl sodium sulfate, which is added, to be improved
The adsorption capacity of epoxy resin, preparation method is simple, and anti-radiation effect is good.
Embodiment 2
A kind of processing technology of new energy car battery pallet, comprising the following steps:
(1) make mold: it is spare to make mold according to the shape of pallet;
(2) making material: glass fibre is placed in smelting furnace, is heated to 200-300 DEG C, and nano-titanium dioxide and nanometer two is added
Silica reacts 30-40min;It is cooled to 60-80 DEG C, it is mixed that acrylic resin, hydrogenated vegetable oil and fatty glyceride is added
It closes, is eventually adding lubricant, is sufficiently mixed and is placed in extruder, obtain base sheet;
(3) plastics sucking moulding: base sheet is placed in Packing Machine, and pallet is prepared;
(4) be surface-treated: spraying one layer of anti-radiation coating in tray surface, by the vacuum formed box after spraying be placed in baking oven drying or
Naturally dry.
The parts by weight of each raw material of the base sheet are respectively as follows: 120 parts of acrylic resin, 15 parts of glass fibre, receive
3 parts of titanium dioxide of rice, 3 parts of nano silica, 15 parts of hydrogenated vegetable oil, 2 parts of fatty glyceride and 3 parts of lubricant.
The anti-radiation coating includes following raw material: epoxy resin, antimony oxide, methyl anyl alcohol, dodecyl sodium sulfate and
Antioxidant.The parts by weight of each raw material of the anti-radiation coating are respectively as follows: 100 parts of epoxy resin, 6 parts of antimony oxide, methylpent
40 parts of alcohol, 16 parts of dodecyl sodium sulfate and 1.5 parts of antioxidant.
The anti-radiation coating is through the following steps that obtain: epoxy resin, antimony oxide and methyl anyl alcohol is sufficiently mixed
After conjunction, dodecyl sodium sulfate and antioxidant is added, obtains the anti-radiation coating after mixing again.
Embodiment 3
A kind of processing technology of new energy car battery pallet, comprising the following steps:
(1) make mold: it is spare to make mold according to the shape of pallet;
(2) making material: glass fibre is placed in smelting furnace, is heated to 200-300 DEG C, and nano-titanium dioxide and nanometer two is added
Silica reacts 30-40min;It is cooled to 60-80 DEG C, it is mixed that acrylic resin, hydrogenated vegetable oil and fatty glyceride is added
It closes, is eventually adding silicone oil, is sufficiently mixed and is placed in extruder, obtain base sheet;
(3) plastics sucking moulding: base sheet is placed in Packing Machine, and pallet is prepared;
(4) be surface-treated: spraying one layer of anti-radiation coating in tray surface, by the vacuum formed box after spraying be placed in baking oven drying or
Naturally dry.
The parts by weight of each raw material of the base sheet are respectively as follows: 110 parts of acrylic resin, 20 parts of glass fibre, receive
6 parts of titanium dioxide of rice, 6 parts of nano silica, 13 parts of hydrogenated vegetable oil, 3 parts of fatty glyceride and 5 parts of silicone oil.
The anti-radiation coating includes following raw material: epoxy resin, antimony oxide, methyl anyl alcohol, dodecyl sodium sulfate and
Anti-oxidant DLTP.The parts by weight of each raw material of the anti-radiation coating are respectively as follows: 120 parts of epoxy resin, 5 parts of antimony oxide, first
30 parts of base amylalcohol, 12 parts of dodecyl sodium sulfate and 1 part of anti-oxidant DLTP.
The anti-radiation coating is through the following steps that obtain: epoxy resin, antimony oxide and methyl anyl alcohol is sufficiently mixed
After conjunction, dodecyl sodium sulfate and antioxidant is added, obtains the anti-radiation coating after mixing again.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvement and deformations can also be made, these improvement and deformations
Also it should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of processing technology of new energy car battery pallet, characterized in that the following steps are included:
(1) make mold: it is spare to make mold according to the shape of pallet;
(2) making material: glass fibre is placed in smelting furnace, is heated to 200-300 DEG C, and nano-titanium dioxide and nanometer two is added
Silica reacts 30-40min;It is cooled to 60-80 DEG C, it is mixed that acrylic resin, hydrogenated vegetable oil and fatty glyceride is added
It closes, is eventually adding lubricant, is sufficiently mixed and is placed in extruder, obtain base sheet;
(3) plastics sucking moulding: base sheet is placed in Packing Machine, and pallet is prepared;
(4) be surface-treated: spraying one layer of anti-radiation coating in tray surface, by the vacuum formed box after spraying be placed in baking oven drying or
Naturally dry.
2. a kind of processing technology of new energy car battery pallet according to claim 1, characterized in that the basis piece
The parts by weight of each raw material of material are respectively as follows: 100-120 parts of acrylic resin, 15-24 parts of glass fibre, nano-titanium dioxide 3-
9 parts, 3-9 parts of nano silica, 10-15 parts of hydrogenated vegetable oil, 2-5 parts of fatty glyceride and 3-6 parts of lubricant.
3. a kind of processing technology of new energy car battery pallet according to claim 1 or 2, characterized in that the profit
Lubrication prescription is silicone oil.
4. a kind of processing technology of new energy car battery pallet according to claim 1, characterized in that described anti-radiation
Coating includes following raw material: epoxy resin, antimony oxide, methyl anyl alcohol, dodecyl sodium sulfate and antioxidant.
5. a kind of processing technology of new energy car battery pallet according to claim 4, characterized in that described anti-radiation
The parts by weight of each raw material of coating are respectively as follows: 100-120 parts of epoxy resin, 3-6 parts of antimony oxide, 20-40 parts of methyl anyl alcohol, ten
10-16 parts and antioxidant 1-1.5 parts of dialkyl sulfonates.
6. a kind of processing technology of new energy car battery pallet according to claim 4 or 5, characterized in that described anti-
Radiation paint through the following steps that obtain: after epoxy resin, antimony oxide and methyl anyl alcohol are sufficiently mixed, be added dodecane
Base sodium sulfonate and antioxidant obtain the anti-radiation coating after mixing again.