CN109571699A - A kind of no aldehyde moistureproof and mildewproof wood shavings thin plate is mated formation pressure setting and its production method - Google Patents
A kind of no aldehyde moistureproof and mildewproof wood shavings thin plate is mated formation pressure setting and its production method Download PDFInfo
- Publication number
- CN109571699A CN109571699A CN201910052621.7A CN201910052621A CN109571699A CN 109571699 A CN109571699 A CN 109571699A CN 201910052621 A CN201910052621 A CN 201910052621A CN 109571699 A CN109571699 A CN 109571699A
- Authority
- CN
- China
- Prior art keywords
- cabinet
- wall
- raw material
- moistureproof
- aldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Mat formation pressure setting and its production method the invention discloses a kind of no aldehyde moistureproof and mildewproof wood shavings thin plate, its device includes cabinet, the lower wall of cabinet is welded with two supporting legs, the upper side wall of cabinet is fixedly connected with crush box, the lower wall of crush box is welded with horizontally disposed placement plate on the lateral wall of cabinet integrally formed with the discharge port being connected to box house.When the present invention carries out the mixing between moso bamboo raw material by melamine resin, assign raw material the water-fast performance with heatproof, and solidified by melamine cured dose, form tight structure, it avoids and moisture, formaldehyde volatilization is avoided, moisture resistance is increased, addition mould inhibitor increases the mildew resistance of raw material.In products material screening, the fine raw fibre of comparison is filtered out, is used as a raw material for production；And in subsequent process of mating formation, prepressing procedures, there are also the equipment on hot pressing process corresponding adjustment so that the particieboard produced is thinner, can accomplish 4mm, the feature of environmental protection more can be good.
Description
Technical field
Mat formation pressure setting the present invention relates to particieboard technical field more particularly to a kind of no aldehyde moistureproof and mildewproof wood shavings thin plate
And its production method.
Background technique
Bamboo shaving board is one of particieboard kind, which imitates the process flow system of wooden flake board using moso bamboo as raw material
At plate.Current wood shavings thin plate is generally mixed using simple moso bamboo raw material, is easy in the actual use process
The moisture absorption is mouldy, to influence normal use, and the wood shavings plate thickness that current production technology and equipments are produced is general
All over thicker, properties are all unable to get further raising.For this purpose, we have proposed a kind of no aldehyde moistureproof and mildewproof wood shavings thin plates
Pressure setting and its production method mat formation to solve the above problems.
Summary of the invention
The purpose of the present invention is to solve the problems in background techniques, and a kind of no aldehyde moistureproof and mildewproof wood shavings proposed are thin
Plate is mated formation pressure setting and its production method.
To achieve the goals above, present invention employs following technical solutions: a kind of no aldehyde moistureproof and mildewproof wood shavings thin plate paving
Pressure setting is filled, including cabinet, the lower wall of the cabinet are welded with two supporting legs, the upper side wall of the cabinet is fixedly connected
There is crush box, the lower wall of the crush box is integrally formed with the discharge port being connected to box house, the lateral wall of the cabinet
On be welded with horizontally disposed placement plate, the upper side wall of the placement plate is fixedly connected with blower, and the output end of the blower connects
Multiple discharge pipes are connected to, multiple discharge pipe levels are plugged on the outer wall of cabinet, and the upper side wall of the cabinet is flexibly connected
There are multiple sieves, the discharge port is connected with towards sieve and perpendicular setting, the lower end joint activity of multiple sieves
Connecting rod, the cabinet is far from being fixed with vibration excitor, the output end and connecting rod of the vibration excitor on the side inner wall of discharge pipe
One end be fixedly connected, in the cabinet installation there are two the first conveyer belt and the second conveyer belt that are located on the downside of multiple sieves,
The rotation direction of two first conveyer belts and the second conveyer belt is on the contrary, the inner bottom wall of the cabinet is placed with positioned at the first biography
The collecting tank with lower end is sent, the lower wall of the cabinet is equipped with mixing tank, and the lower wall of the cabinet is equipped with mechanism of mating formation, described
Cabinet is equipped with briquetting machine far from the side of blower.
Preferably, multiple sieves are sequentially reduced in aperture from left to right.
Preferably, second conveyer belt is located at the downside of the sieve of right end, and the upper side wall of the mixing tank offers
Feed inlet, the feed inlet are located on the downside of the right end of the second conveyer belt, and the upper side wall of the mixing tank is fixedly connected with stirring motor,
The output end of the stirring motor extends to the inside of mixing tank and is connected with agitating shaft, the lower wall of mixing tank one at
Type, which has, extends to external outlet, offers installing port on the outer wall of the mixing tank, is equipped with transparent screen in the installing port,
The feed pipe for being inserted on the outer wall of the cabinet and being connected to inside mixing tank, the upper end of the feed pipe are communicated with volumetric flask,
It is carved on the volumetric flask and transparent screen and is equipped with graduation mark, be mounted on valve on the discharge port, outlet and feed pipe.
Preferably, the mechanism of mating formation includes placement plate, and the lower wall of the placement plate is described integrally formed with support rod
The lower end of support rod is equipped with idler wheel, and the upper side wall of the placement plate offers placing groove, is placed with template in the placing groove,
The lower wall of the cabinet is welded with two fixed plates being vertically arranged, and two fixed plates are fixed with telescopic rod jointly, institute
The driving end for stating telescopic rod is fixedly connected with the outer wall of placement plate.
Preferably, the lower wall of the cabinet is fixedly connected with spreading machine, the output end of the spreading machine by connecting tube
It is in contact with the upper side wall of placement plate.
Preferably, the briquetting machine includes the continuous hot press fixed with cabinet exterior, and the continuous hot press includes
Body, pressboard and the heating pole composition being mounted on inside pressboard.
Above-mentioned no aldehyde moistureproof and mildewproof wood shavings thin plate is mated formation the production method of pressure setting, comprising the following steps:
S1: the moso bamboo of chopping is put into crush box and crushes by crushing and screening, opens the valve and blower of discharge port, crushes
Raw material afterwards is dropped out from discharge port, is blown raw material by the air-flow of discharge pipe and is shed, by the filtering of sieve, tiny original
Material is dropped out by the sieve of right end to the second conveyer belt；
S2: being stirred, and the second conveyer belt will drop down onto mixing tank at tiny feedstock transportation to feed inlet, is passed through suitable raw material
The melamine resin of proportion, mould inhibitor, melamine cured dose, defoaming agent and release agent start stirring motor, are mixed
It closes；
S3: uniformly mating formation, and opens the valve in outlet, mixed raw material is exported, and starts telescopic rod, drives placement plate or so
Mobile, spreading machine is contacted with the upper surface of template, paves the raw material in template uniformly；
S4: heating compacting, starting heating pole pressboard is heated, telescopic rod push template movement to pressboard just under
Side, body driving pressboard is moved down to be contacted with the raw material in template, is pressed to separate；
S5: cutting and polishing takes out the wood shavings thin plate after compression moulding, carries out corner and cuts sanding and polishing.
The present invention mainly in products material screening, filters out the fine raw fibre of comparison, makes as a raw material for production
With；And in subsequent process of mating formation, prepressing procedures, there are also the equipment on hot pressing process corresponding adjustment so that giving birth to
The particieboard that output is come is thinner, and the feature of environmental protection more can be good.
Compared with prior art, the present invention has the advantages that
1, the sieve that multiple apertures directly reduce is arranged to screen raw material, the raw material for meeting aperture passes through the second conveyer belt
Conveying drops down onto mixing tank, and the raw material for not meeting aperture is delivered in collecting tank by the first conveyer belt to be collected, by rear
Continuous secondary operation obtains more fine fibrous raw material and carries out using making wood shavings plate thickness after molding to composite demand
Thinner, the particieboard produced at present can accomplish that thickness only has 4mm, be most thin in industry.
2, after leading to raw material in mixing tank, melamine resin, mould inhibitor, melamine cured dose, defoaming agent are imported
It is mixed with release agent, is exported by outlet to template, drive placement plate to move left and right by telescopic rod, spreading machine and original
Material contact, raw material is paved in template, and carries out precompressed to fibrous raw material.
3, the downside of pressboard is moved to placement plate by telescopic rod, starting heating tube heats pressboard, the
Two telescopic rods drive pressboard to move down with template to far from contacting, and carry out extrusion forming to raw material, carry out continuous hot-press work, make
Fibrous raw material after precompressed carries out shaping.
When the present invention carries out the mixing between moso bamboo raw material by melamine resin, assign raw material the water-fast property with heatproof
Can, and solidified by melamine cured dose, form tight structure, avoided and moisture, avoided formaldehyde volatilization, increase
Add moisture resistance, addition mould inhibitor increases the mildew resistance of raw material, makes molding raw material with no aldehyde moistureproof and mildewproof by compacting of mating formation
Performance, and carried out simultaneously by spreading machine precompressed, continuous hot press heating with compacting, reduction material and energy consumption, Forming Quality
More preferably, production process is more environmentally-friendly.
Detailed description of the invention
Fig. 1 is to mat formation the structural schematic diagram of pressure setting in embodiment without aldehyde moistureproof and mildewproof wood shavings thin plate.
Fig. 2 is the enlarged drawing of part A in Fig. 1.
Fig. 3 is to mat formation the top view of placement plate in pressure setting in embodiment without aldehyde moistureproof and mildewproof wood shavings thin plate.
In figure: 1-cabinet, 2-supporting legs, 3-crush boxes, 4-discharge ports, 5-placement plates, 6-blowers, 7-outlet air
Pipe, 8-sieves, 9-vibration excitors, 10-connecting rods, the 11-the first conveyer belt, the 12-the second conveyer belt, 13-collecting tanks, 14-
Mixing tank, 15-stirring motors, 16-transparent screens, 17-placement plates, 18-templates, 19-idler wheels, 20-fixed plates, 21-are stretched
Contracting bar, 22-spreading machines, 23-volumetric flasks, 24-feed pipes, 25-valves, 26-bodies, 27-pressboards, 28-heating
Bar, 29-placing grooves.
Specific embodiment
In order to describe the technical content, the structural feature, the achieved object and the effect of this invention in detail, below in conjunction with embodiment
And attached drawing is cooperated to be explained in detail.
As shown in Figure 1 to Figure 3, no aldehyde moistureproof and mildewproof wood shavings thin plate of the invention pressure setting of mating formation includes cabinet 1, cabinet
1 lower wall is welded with two supporting legs 2, and the upper side wall of cabinet 1 is fixedly connected with crush box 3, the lower wall one of crush box 3
The discharge port 4 being connected to inside cabinet 1 is formed, by the moso bamboo investment crush box 3 of chopping, is directed at after crushing by discharge port
In cabinet 1, horizontally disposed placement plate 5 is welded on the lateral wall of cabinet 1, the upper side wall of placement plate 5 is fixedly connected with blower
6, the output end of blower 6 is connected with multiple discharge pipes 7, and multiple 7 levels of discharge pipe are plugged on the outer wall of cabinet 1, cabinet 1 it is upper
Side wall is connected with multiple sieves 8, and multiple sieves 8 are sequentially reduced in aperture from left to right, and blower 6 works, and passes through outlet air
Pipe 7 exports air-flow and is contacted with the raw material fallen, blow raw material do the sieve 8 of the biggish raw material of projectile motion and left end into
Row contact, lesser raw material are contacted with the sieve 8 of right end.
Discharge port 4 is vertically arranged the effect energy vertical screen for guaranteeing raw material contact air-flow towards sieve 8 and perpendicular setting
On net 8, the lower end joint activity of multiple sieves 8 is connected with connecting rod 10, and cabinet 1 is far from fixed on the side inner wall of discharge pipe 7
There is vibration excitor 9, the output end of vibration excitor 9 is fixedly connected with one end of connecting rod 10, drives connecting rod 10 and sieve by vibration excitor 9
Net 8 shakes, and avoids sieve 8 from blocking, guarantees the orderly progress of screening operation.
Installation is there are two the first conveyer belt 11 and the second conveyer belt 12 that are located at multiple 8 downsides of sieves in cabinet 1, and two the
The rotation direction of one conveyer belt 11 and the second conveyer belt 12 is on the contrary, the inner bottom wall of cabinet 1 is placed under the first conveyer belt 11
The collecting tank 13 at end, biggish raw material are fallen on the first conveyer belt 11, are extremely collected feedstock transportation by the first conveyer belt 11
In slot 13, the lower wall of cabinet 1 is equipped with mixing tank 14, and the second conveyer belt 12 is located at the downside of the sieve 8 of right end, mixing tank 14
Upper side wall offer feed inlet, feed inlet is located on the downside of the right end of the second conveyer belt 12, lesser to be used for mixed original
Material drops down on the second conveyer belt 12, will be in feedstock transportation to mixing tank 14 by the second conveyer belt 12.
The upper side wall of mixing tank 14 is fixedly connected with stirring motor 15, and the output end of stirring motor 15 extends to mixing tank 14
Inside is simultaneously connected with agitating shaft, and the lower wall of mixing tank 14 is integrally formed with the outlet for extending to outside, the outer wall of mixing tank 14
On offer installing port, transparent screen 16 is installed, raw material drops down onto mixing tank 14, passes through the scale on transparent screen 16 in installing port
Line puts into melamine resin, mould inhibitor, melamine cured dose, defoaming agent accordingly matched convenient for observation material quantity
And release agent, the feed pipe 24 being connected to inside mixing tank 14 is inserted on the outer wall of cabinet 1, and the upper end of feed pipe 24 is communicated with
Volumetric flask 23 stores melamine resin, mould inhibitor, melamine cured dose, defoaming agent and release agent in volumetric flask 23
Mixed liquor, and matching is 40-50 parts, 0.1-0.2 parts, 0.2-0.5 parts, 0.02-0.08 parts and 0.03-0.06 parts, and be should ensure that
The proportion of raw material and mixed liquor is 3:1, carves on volumetric flask 23 and transparent screen 16 and is equipped with graduation mark, discharge port 4, outlet and charging
Valve 25 is mounted on pipe 24, the valve 25 opened on discharge port 4 drains into mixed liquor in mixing tank 14, passes through stirring motor
15 drive raw materials are mixed with mixed liquor, and when carrying out the mixing between moso bamboo raw material by melamine resin, it is water-fast to assign raw material
With the performance of heatproof, and solidified by melamine cured dose, form tight structure, avoided and moisture, is avoided
Formaldehyde volatilization, increases moisture resistance, and addition mould inhibitor increases the mildew resistance of raw material.
The lower wall of cabinet 1, which is equipped with, mats formation mechanism, and mechanism of mating formation includes placement plate 17, the lower wall one of placement plate 17 at
Type has a support rod, and the lower end of support rod is equipped with idler wheel 19, and the upper side wall of placement plate 17 offers placing groove 29, in placing groove 29
It is placed with template 18, the lower wall of cabinet 1 is welded with two fixed plates being vertically arranged 20, and two fixed plates 20 are fixed with jointly
The driving end of telescopic rod 21, telescopic rod 21 is fixedly connected with the outer wall of placement plate 17, and the lower wall of cabinet 1 is fixed by connecting tube
It is connected with spreading machine 22, the output end of spreading machine 22 is in contact with the upper side wall of placement plate 17.
Cabinet 1 is equipped with briquetting machine far from the side of blower 6, and briquetting machine includes the Continuous Heat fixed with 1 outer wall of cabinet
Press, continuous hot press include that body 26, pressboard 27 and the heating pole 28 being mounted on inside pressboard 27 form.
After more fine limit raw material is laid with, precompressed is carried out after mating formation by spreading machine, makes its basic forming, then pass through
It crosses subsequent continuous hot press and carries out continuous hot-press, continuous hot-press production process serialization reduces the production time, moreover, continuously
Hot pressing heating is synchronous with pressurization, reduces material loss, reduces energy consumption, and production process is more environmentally-friendly.
Above-mentioned no aldehyde moistureproof and mildewproof wood shavings thin plate is mated formation the production method of pressure setting, comprising the following steps:
S1: the moso bamboo of chopping is put into crush box and crushes by crushing and screening, opens the valve and blower of discharge port, crushes
Raw material afterwards is dropped out from discharge port, is blown raw material by the air-flow of discharge pipe and is shed, by the filtering of sieve, tiny original
Material is dropped out by the sieve of right end to the second conveyer belt；
S2: being stirred, and the second conveyer belt will drop down onto mixing tank at tiny feedstock transportation to feed inlet, is passed through suitable raw material
The melamine resin of proportion, mould inhibitor, melamine cured dose, defoaming agent and release agent start stirring motor, are mixed
It closes；
S3: uniformly mating formation, and opens the valve in outlet, mixed raw material is exported, and starts telescopic rod, drives placement plate or so
Mobile, spreading machine is contacted with the upper surface of template, paves the raw material in template uniformly；
S4: heating compacting, starting heating pole pressboard is heated, telescopic rod push template movement to pressboard just under
Side, body driving pressboard is moved down to be contacted with the raw material in template, is pressed to separate；
S5: cutting and polishing takes out the wood shavings thin plate after compression moulding, carries out corner and cuts sanding and polishing.
It further illustrates, it is above-mentioned to be fixedly connected unless specifically defined or limited otherwise, otherwise to shall be understood in a broad sense, example
Such as, it can be welding, be also possible to gluing, or be integrally formed the customary means well known to those skilled in the art such as setting.
Although cabinet 1, supporting leg 2, crush box 3, discharge port 4, placement plate 5, blower 6, outlet air is used more herein
Pipe 7, sieve 8, vibration excitor 9, connecting rod 10, the first conveyer belt 11, the second conveyer belt 12, collecting tank 13, mixing tank 14, stirring electricity
Machine 15, transparent screen 16, placement plate 17, template 18, idler wheel 19, fixed plate 20, telescopic rod 21, spreading machine 22, volumetric flask 23, charging
The terms such as pipe 24, valve 25, body 26, pressboard 27, heating pole 28, placing groove 29, but be not precluded using other terms
Possibility.The use of these items is only for be more convenient to describe and explain essence of the invention；It is construed as any
It is a kind of it is additional limitation be all to be disagreed with spirit of that invention.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright specification and accompanying drawing content is applied directly or indirectly in other relevant skills
Art field is included in scope of patent protection of the invention.
Claims (7)
- Pressure setting, including cabinet 1. a kind of no aldehyde moistureproof and mildewproof wood shavings thin plate is mated formation, which is characterized in that the downside of the cabinet Wall is welded with two supporting legs, and the upper side wall of the cabinet is fixedly connected with crush box, the lower wall one of the crush box at Type has the discharge port being connected to box house, and horizontally disposed placement plate, the placement are welded on the lateral wall of the cabinet The upper side wall of plate is fixedly connected with blower, and the output end of the blower is connected with multiple discharge pipes, and multiple discharge pipes are horizontal Be plugged on the outer wall of cabinet, the upper side wall of the cabinet is connected with multiple sieves, the discharge port towards sieve and with It is vertically arranged, and the lower end joint activity of multiple sieves is connected with connecting rod, and the cabinet is far from the side of discharge pipe Vibration excitor is fixed on wall, the output end of the vibration excitor is fixedly connected with one end of connecting rod, is equipped with two in the cabinet A the first conveyer belt and the second conveyer belt on the downside of multiple sieves, two first conveyer belts and the second conveyer belt turn Move contrary, the inner bottom wall of the cabinet is placed with the collecting tank positioned at the first conveyer belt lower end, the lower wall of the cabinet Equipped with mixing tank, the lower wall of the cabinet is equipped with mechanism of mating formation, and the cabinet is equipped with briquetting machine far from the side of blower.
- The pressure setting 2. no aldehyde moistureproof and mildewproof wood shavings thin plate according to claim 1 is mated formation, which is characterized in that multiple described Aperture is sequentially reduced sieve from left to right.
- The pressure setting 3. no aldehyde moistureproof and mildewproof wood shavings thin plate according to claim 1 is mated formation, which is characterized in that described second Conveyer belt is located at the downside of the sieve of right end, and the upper side wall of the mixing tank offers feed inlet, and the feed inlet is located at the On the downside of the right end of two conveyer belts, the upper side wall of the mixing tank is fixedly connected with stirring motor, and the output end of the stirring motor prolongs Extend to the inside of mixing tank and be connected with agitating shaft, the lower wall of the mixing tank integrally formed with extending to external outlet, Installing port is offered on the outer wall of the mixing tank, and transparent screen is installed in the installing port, is plugged on the outer wall of the cabinet Have and mixing tank inside the feed pipe that is connected to, the upper end of the feed pipe is communicated with volumetric flask, on the volumetric flask and transparent screen It carves and is equipped with graduation mark, be mounted on valve on the discharge port, outlet and feed pipe.
- The pressure setting 4. no aldehyde moistureproof and mildewproof wood shavings thin plate according to claim 1 is mated formation, which is characterized in that described to mat formation Mechanism includes placement plate, and for the lower wall of the placement plate integrally formed with support rod, the lower end of the support rod is equipped with idler wheel, The upper side wall of the placement plate offers placing groove, and template is placed in the placing groove, and the lower wall of the cabinet is welded with Two fixed plates being vertically arranged, two fixed plates are fixed with telescopic rod, the driving end of the telescopic rod and placement jointly The outer wall of plate is fixedly connected.
- The pressure setting 5. no aldehyde moistureproof and mildewproof wood shavings thin plate according to claim 4 is mated formation, which is characterized in that the cabinet Lower wall spreading machine is fixedly connected with by connecting tube, the output end of the spreading machine is in contact with the upper side wall of placement plate.
- The pressure setting 6. no aldehyde moistureproof and mildewproof wood shavings thin plate according to claim 1 is mated formation, which is characterized in that the compacting Mechanism includes the continuous hot press fixed with cabinet exterior, and the continuous hot press includes body, pressboard and is mounted on compacting The heating pole of intralamellar part forms.
- 7. a kind of mat formation the producer of pressure setting as described in any one of claims 1 to 6 without aldehyde moistureproof and mildewproof wood shavings thin plate Method, which comprises the following steps:S1: the moso bamboo of chopping is put into crush box and crushes by crushing and screening, opens the valve and blower of discharge port, crushes Raw material afterwards is dropped out from discharge port, is blown raw material by the air-flow of discharge pipe and is shed, by the filtering of sieve, tiny original Material is dropped out by the sieve of right end to the second conveyer belt；S2: being stirred, and the second conveyer belt will drop down onto mixing tank at tiny feedstock transportation to feed inlet, is passed through suitable raw material The melamine resin of proportion, mould inhibitor, melamine cured dose, defoaming agent and release agent start stirring motor, are mixed It closes；S3: uniformly mating formation, and opens the valve in outlet, mixed raw material is exported, and starts telescopic rod, drives placement plate or so Mobile, spreading machine is contacted with the upper surface of template, paves the raw material in template uniformly；S4: heating compacting, starting heating pole pressboard is heated, telescopic rod push template movement to pressboard just under Side, body driving pressboard is moved down to be contacted with the raw material in template, is pressed to separate；S5: cutting and polishing takes out the wood shavings thin plate after compression moulding, carries out corner and cuts sanding and polishing.