CN109554931A - A kind of opaque nylon coating fabric and its production technology - Google Patents
A kind of opaque nylon coating fabric and its production technology Download PDFInfo
- Publication number
- CN109554931A CN109554931A CN201811414904.3A CN201811414904A CN109554931A CN 109554931 A CN109554931 A CN 109554931A CN 201811414904 A CN201811414904 A CN 201811414904A CN 109554931 A CN109554931 A CN 109554931A
- Authority
- CN
- China
- Prior art keywords
- nylon
- opaque
- coating fabric
- machine
- embryo cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of opaque nylon coating fabric and its production technologies, including raw material preparation: preparing staple line and nylon yarn；Warping: two kinds of silk threads are organized into coiled hair, each coiled hair 20 by warping machine respectively by warping machine；Upper machine: prepare 20 coiled hairs be divided into 10 nylon yarns be bottom silk and 10 staple lines be face silk；Weaving: above two silk thread is made into nylon embryo cloth by textile machinery warp knit；It examines: above-mentioned nylon embryo cloth being sent into nylon embryo cloth checking machine and is examined, substandard product is removed.The present invention, there is the opaque polymer emulsion given out light by multiple setting treatment and addition, it improves nylon coating fabric and resists the property lost, the opaqueness of nylon coating fabric is realized simultaneously, it is made suitable for curtain etc., the water imbibition and gas permeability of nylon facing material are enhanced, by the way that nylon yarn is made into nylon coating fabric as bottom silk, staple line as face silk spinning, so that having adsorptivity and bulkiness.
Description
Technical field
The present invention relates to a kind of nylon coating fabric and its production technology, specifically a kind of opaque nylon coating fabric and
Its production technology belongs to fabric technical field.
Background technique
Fabric is exactly the material for making clothes, and as one of clothes three elements, fabric can not only annotate clothes
Style and characteristic, and the expression effect of the color of clothes, moulding is directly controlled, in clothes big world, the fabric of clothes
It is multifarious, make rapid progress.But generally, high-quality, high-grade fabric, mostly have comfortable and easy to wear, sweat-absorbing breathable,
The characteristics of several aspects such as well-pressed, vision is noble, tactile is soft and graceful of dangling.
General nylon coating fabric exists to be there is external force and laminates the case where losing, while nylon because setting treatment is bad
Coating fabric surface lacks light-proof material layer or non-transparency difference and cannot be advantageously applied to corresponding fabric and use neck
Domain, such as curtain, while the single nylon coating fabric gas permeability being woven into nylon yarn is bad and is unfavorable for adsorbing liquid.
Therefore, a kind of opaque nylon coating fabric and its production technology are proposed regarding to the issue above.
Summary of the invention
The object of the invention is that providing a kind of opaque nylon coating fabric and its life to solve the above-mentioned problems
Production. art.
The present invention is achieved through the following technical solutions above-mentioned purpose, a kind of opaque nylon coating fabric and its production work
Skill, the nylon facing material are woven by staple line and nylon yarn by textile machinery, and nylon facing material two sides is smeared and determined
The light non-transmittable layers that type has opaque polymer emulsion to be formed, comprising the following steps:
1) raw material preparation: prepare staple line and nylon yarn；
2) warping: two kinds of silk threads are organized into coiled hair, each coiled hair 20 by warping machine respectively by warping machine；
3) machine on: prepare 20 coiled hairs be divided into 10 nylon yarns be bottom silk and 10 staple lines be face silk；
4) it weaves: above two silk thread is made into nylon embryo cloth by textile machinery warp knit；
5) it examines: above-mentioned nylon embryo cloth being sent into nylon embryo cloth checking machine and is examined, substandard product is removed；
6) high-temperature shaping: qualified nylon embryo cloth is sent into forming machine, the temperature of forming machine is 220-240 DEG C, speed 18-20
Code/minute；
7) hot light is handled before: the above-mentioned nylon embryo cloth cooling through sizing being sent into natural lustre finishing machine and auxiliary agent is added, which includes first
Aldehyde and ethanol solution 1:6 in mass ratio, the temperature of the natural lustre finishing machine are 170 DEG C, and speed is 20 yards/minute；
8) pre-setting is handled: the processed nylon embryo cloth of hot light being sent into forming machine and is formed again, the temperature of the forming machine is 200
DEG C, speed is 40 yards/minute；
9) dyeing is handled: above-mentioned processed nylon embryo cloth being sent into high temperature overflow dye vat, dyeing temperature is 130 DEG C, when dyeing
Between be 30 minutes；
10) dehydration: the nylon embryo cloth dyed is sent into high speed dewatering machine, the speed of the high speed dewatering machine is 500-700
Rev/min；
11) shaping and drying: sending dehydrated nylon embryo cloth into shaping drying and be added softening agent, smooth agent, leavening agent and
Antistatic agent, temperature are 180 DEG C, and speed is 30 yards/minute；
12) hot light is handled afterwards: the nylon embryo cloth that drying and processing is crossed being sent into natural lustre finishing machine and auxiliary agent is added, the temperature of the natural lustre finishing machine is
170 DEG C, speed: 20 yards/minute；
13) finished product is formed: the processed nylon embryo cloth of rear hot light being sent into forming machine, the temperature of the forming machine is 180 DEG C, vehicle
Speed is 30 yards/minute, has been handled and finished product nylon cloth is made；
14) compound: to be blended with helping the opaque polymer emulsion of photo etching to be uniformly coated in finished product Buddhist nun in a manner of a kind of scraper
On imperial cloth, then will be coated with opaque polymer emulsion nylon cloth be sent into compounding machine, compound 100G/ ㎡ fibre suede, then using
The fixation of oven temperature makes to form one layer of light non-transmittable layers of uniform fold in web surface, after the completion of compound, finally examine and beats
Coil packing；
15) manufacturing of opaque nylon coating fabric is completed.
Preferably, 10 nylon yarns and 10 staple lines are separately mounted to weave in step 4) in the step 3)
On machine on corresponding silk thread drawing export structure.
Preferably, formalin 10kg and ethanol solution 60kg is distinguished in the step 7) in proportion, is then blended in appearance
In the middle part of device, and uniform stirring, then mixed liquor is soaked on nylon cloth.
Preferably, the step 9) dye vat sequentially adds disperse dyes while dyestuff is added, the dye of positive ion, divides
Dissipate levelling agent, cationic levelling agent, degreaser, chelating agent and glacial acetic acid.
Preferably, nylon cloth expansion after dehydration and corrugationless cool to 20 minutes are being subjected to step in the step 10)
11) shaping and drying in.
Preferably, the step 10) high speed dewatering time is 20-30 minutes.
Preferably, the auxiliary agent in the step 12) includes hot light powder, oil sense agent, formaldehyde and ethanol solution and by quality
It is used in mixed way than 1:1:3:8.
Preferably, the nylon embryo cloth edge of weaving is subjected to shear treatment in the step 4), keeps nylon embryo cloth edge whole
Together without the end of a thread.
Preferably, finished product nylon facing material surface is subjected to dustless cleaning in the step 13), and folded spare.
Preferably, oven interior temperature is controlled at 30-60 DEG C in the step 14).
The beneficial effects of the present invention are:
1, this kind of opaque nylon coating fabric and its production technology, it is impermeable with giving out light by multiple setting treatment and addition
Photopolymer lotion improves nylon coating fabric and resists the property lost, while realizing the opaqueness of nylon coating fabric, is applicable in
It is made in curtain etc..
, this kind of opaque nylon coating fabric and its production technology, enhance the water imbibition and gas permeability of nylon facing material, lead to
It crosses and nylon yarn is made into nylon coating fabric as bottom silk, staple line as face silk spinning, so that having adsorptivity and bulkiness.
Detailed description of the invention
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below
There is attached drawing needed in technical description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this
Some embodiments of invention without any creative labor, may be used also for those of ordinary skill in the art
To obtain other attached drawings according to these attached drawings.
Fig. 1 is process flow chart of the invention；
Fig. 2 is nylon coating fabric structure schematic diagram of the present invention.
In figure: 1, nylon coating fabric, 101, nylon yarn, 102, staple line, 103, light non-transmittable layers.
Specific embodiment
In order to make the invention's purpose, features and advantages of the invention more obvious and easy to understand, below in conjunction with the present invention
Attached drawing in embodiment, technical scheme in the embodiment of the invention is clearly and completely described, it is clear that disclosed below
Embodiment be only a part of the embodiment of the present invention, and not all embodiment.Based on the embodiments of the present invention, this field
Those of ordinary skill's all other embodiment obtained without making creative work, belongs to protection of the present invention
Range.
To further illustrate the technical scheme of the present invention below with reference to the accompanying drawings and specific embodiments.
In the description of the present invention, it is to be understood that, term " on ", "lower", "top", "bottom", "inner", "outside" etc. indicate
Orientation or positional relationship be based on the orientation or positional relationship shown in the drawings, be merely for convenience of description the present invention and simplification retouch
It states, rather than the device or element of indication or suggestion meaning must have a particular orientation, be constructed and operated in a specific orientation,
Therefore it is not considered as limiting the invention.
It please refers to shown in Fig. 1-2, a kind of opaque nylon coating fabric and its production technology, the nylon facing material is by staple
Line and nylon yarn are woven by textile machinery, and nylon facing material two sides smear sizing have opaque polymer emulsion shape
At light non-transmittable layers, comprising the following steps:
1) raw material preparation: prepare staple line and nylon yarn；
2) warping: two kinds of silk threads are organized into coiled hair, each coiled hair 20 by warping machine respectively by warping machine；
3) machine on: prepare 20 coiled hairs be divided into 10 nylon yarns be bottom silk and 10 staple lines be face silk；
4) it weaves: above two silk thread is made into nylon embryo cloth by textile machinery warp knit；
5) it examines: above-mentioned nylon embryo cloth being sent into nylon embryo cloth checking machine and is examined, substandard product is removed；
6) high-temperature shaping: qualified nylon embryo cloth is sent into forming machine, the temperature of forming machine is 220-240 DEG C, speed 18-20
Code/minute；
7) hot light is handled before: the above-mentioned nylon embryo cloth cooling through sizing being sent into natural lustre finishing machine and auxiliary agent is added, which includes first
Aldehyde and ethanol solution 1:6 in mass ratio, the temperature of the natural lustre finishing machine are 170 DEG C, and speed is 20 yards/minute；
8) pre-setting is handled: the processed nylon embryo cloth of hot light being sent into forming machine and is formed again, the temperature of the forming machine is 200
DEG C, speed is 40 yards/minute；
9) dyeing is handled: above-mentioned processed nylon embryo cloth being sent into high temperature overflow dye vat, dyeing temperature is 130 DEG C, when dyeing
Between be 30 minutes；
10) dehydration: the nylon embryo cloth dyed is sent into high speed dewatering machine, the speed of the high speed dewatering machine is 500-700
Rev/min；
11) shaping and drying: sending dehydrated nylon embryo cloth into shaping drying and be added softening agent, smooth agent, leavening agent and
Antistatic agent, temperature are 180 DEG C, and speed is 30 yards/minute；
12) hot light is handled afterwards: the nylon embryo cloth that drying and processing is crossed being sent into natural lustre finishing machine and auxiliary agent is added, the temperature of the natural lustre finishing machine is
170 DEG C, speed: 20 yards/minute；
13) finished product is formed: the processed nylon embryo cloth of rear hot light being sent into forming machine, the temperature of the forming machine is 180 DEG C, vehicle
Speed is 30 yards/minute, has been handled and finished product nylon cloth is made；
14) compound: to be blended with helping the opaque polymer emulsion of photo etching to be uniformly coated in finished product Buddhist nun in a manner of a kind of scraper
On imperial cloth, then will be coated with opaque polymer emulsion nylon cloth be sent into compounding machine, compound 100G/ ㎡ fibre suede, then using
The fixation of oven temperature makes to form one layer of light non-transmittable layers of uniform fold in web surface, after the completion of compound, finally examine and beats
Coil packing；
15) manufacturing of opaque nylon coating fabric is completed.
10 nylon yarns and 10 staple lines are separately mounted in step 4) phase on textile machinery in the step 3)
On the silk thread drawing export structure answered；Formalin 10kg and ethanol solution 60kg is distinguished in the step 7) in proportion, then
It is blended in the middle part of container, and uniform stirring, then mixed liquor is soaked on nylon cloth；Dyestuff is being added in the step 9) dye vat
Disperse dyes, the dye of positive ion, Disperse Leveler, cationic levelling agent, degreaser, chelating agent and ice vinegar are sequentially added simultaneously
Acid；By nylon cloth expansion after dehydration and corrugationless cool to 20 minutes in the step 10), dried carrying out the sizing in step 11)
It is dry；The step 10) high speed dewatering time is 20-30 minutes；Auxiliary agent in the step 12) includes hot light powder, oil sense
Agent, formaldehyde and ethanol solution and 1:1:3:8 is used in mixed way in mass ratio；By the nylon embryo cloth side of weaving in the step 4)
Edge carries out shear treatment, makes nylon embryo cloth neat in edge without the end of a thread；Finished product nylon facing material surface is subjected to nothing in the step 13)
Dirt cleaning, and fold spare；The control of oven interior temperature is at 30-60 DEG C in the step 14).
In the use of the present invention, by smearing opaque polymer emulsion and impermeable photopolymerization on nylon coating fabric 1
Object lotion is attached to formation light non-transmittable layers 103 on nylon coating fabric 1 in soft condition, is total to according to by styrene and acrylate
The opaque polymer emulsion that copolymer dispersion system is constituted changes when light penetrates the light non-transmittable layers 103 on nylon coating fabric 1
The refraction angle of incident light is become, to generate refraction effect, has improved refractive index, increase the opacity of nylon coating fabric；
By the way that nylon yarn 101 is made into nylon coating fabric 1 as face silk spinning as bottom silk, staple line 102, so that having adsorptivity
And bulkiness, to enhance the water imbibition and gas permeability of nylon facing material.
It is related to circuit and electronic component and module is the prior art, those skilled in the art may be implemented completely,
Without superfluous words, the content that the present invention protects is not related to the improvement for software and method yet.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that by fall in claim with all in the meaning and scope of important document
Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.
The above, the above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although referring to before
Stating embodiment, invention is explained in detail, those skilled in the art should understand that: it still can be to preceding
Technical solution documented by each embodiment is stated to modify or equivalent replacement of some of the technical features；And these
It modifies or replaces, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (10)
1. a kind of opaque nylon coating fabric and its production technology, it is characterised in that: the nylon facing material is by staple line and Buddhist nun
Nylon yarn line is woven by textile machinery, and nylon facing material two sides smears sizing and has opaque polymer emulsion to be formed not
Photic zone, comprising the following steps:
1) raw material preparation: prepare staple line and nylon yarn；
2) warping: two kinds of silk threads are organized into coiled hair, each coiled hair 20 by warping machine respectively by warping machine；
3) machine on: prepare 20 coiled hairs be divided into 10 nylon yarns be bottom silk and 10 staple lines be face silk；
4) it weaves: above two silk thread is made into nylon embryo cloth by textile machinery warp knit；
5) it examines: above-mentioned nylon embryo cloth being sent into nylon embryo cloth checking machine and is examined, substandard product is removed；
6) high-temperature shaping: qualified nylon embryo cloth is sent into forming machine, the temperature of forming machine is 220-240 DEG C, speed 18-20
Code/minute；
7) hot light is handled before: the above-mentioned nylon embryo cloth cooling through sizing being sent into natural lustre finishing machine and auxiliary agent is added, which includes first
Aldehyde and ethanol solution 1:6 in mass ratio, the temperature of the natural lustre finishing machine are 170 DEG C, and speed is 20 yards/minute；
8) pre-setting is handled: the processed nylon embryo cloth of hot light being sent into forming machine and is formed again, the temperature of the forming machine is 200
DEG C, speed is 40 yards/minute；
9) dyeing is handled: above-mentioned processed nylon embryo cloth being sent into high temperature overflow dye vat, dyeing temperature is 130 DEG C, when dyeing
Between be 30 minutes；
10) dehydration: the nylon embryo cloth dyed is sent into high speed dewatering machine, the speed of the high speed dewatering machine is 500-700
Rev/min；
11) shaping and drying: sending dehydrated nylon embryo cloth into shaping drying and be added softening agent, smooth agent, leavening agent and
Antistatic agent, temperature are 180 DEG C, and speed is 30 yards/minute；
12) hot light is handled afterwards: the nylon embryo cloth that drying and processing is crossed being sent into natural lustre finishing machine and auxiliary agent is added, the temperature of the natural lustre finishing machine is
170 DEG C, speed: 20 yards/minute；
13) finished product is formed: the processed nylon embryo cloth of rear hot light being sent into forming machine, the temperature of the forming machine is 180 DEG C, vehicle
Speed is 30 yards/minute, has been handled and finished product nylon cloth is made；
14) compound: to be blended with helping the opaque polymer emulsion of photo etching to be uniformly coated in finished product Buddhist nun in a manner of a kind of scraper
On imperial cloth, then will be coated with opaque polymer emulsion nylon cloth be sent into compounding machine, compound 100G/ ㎡ fibre suede, then using
The fixation of oven temperature makes to form one layer of light non-transmittable layers of uniform fold in web surface, after the completion of compound, finally examine and beats
Coil packing；
15) manufacturing of opaque nylon coating fabric is completed.
2. a kind of opaque nylon coating fabric according to claim 1 and its production technology, it is characterised in that: the step
It is rapid 3) in that 10 nylon yarns and 10 staple lines are separately mounted in step 4) on textile machinery corresponding silk thread drawing is defeated
Out in structure.
3. a kind of opaque nylon coating fabric according to claim 1 and its production technology, it is characterised in that: the step
It is rapid 7) in distinguish formalin 10kg and ethanol solution 60kg in proportion, be then blended in the middle part of container, and uniform stirring, then will
Mixed liquor soaks on nylon cloth.
4. a kind of opaque nylon coating fabric according to claim 1 and its production technology, it is characterised in that: the step
Rapid 9) dye vat sequentially added while dyestuff is added disperse dyes, the dye of positive ion, Disperse Leveler, cationic levelling agent,
Degreaser, chelating agent and glacial acetic acid.
5. a kind of opaque nylon coating fabric according to claim 1 and its production technology, it is characterised in that: the step
It is rapid 10) in will dehydration after nylon cloth expansion and corrugationless cool to 20 minutes, carry out step 11) in shaping and drying.
6. a kind of opaque nylon coating fabric according to claim 1 and its production technology, it is characterised in that: the step
Rapid 10) high speed dewatering time is 20-30 minutes.
7. a kind of opaque nylon coating fabric according to claim 1 and its production technology, it is characterised in that: the step
It is rapid 12) in auxiliary agent include hot light powder, oil sense agent, formaldehyde and ethanol solution and 1:1:3:8 is used in mixed way in mass ratio.
8. a kind of opaque nylon coating fabric according to claim 1 and its production technology, it is characterised in that: the step
It is rapid 4) in the nylon embryo cloth edge of weaving is subjected to shear treatment, make nylon embryo cloth neat in edge without the end of a thread.
9. a kind of opaque nylon coating fabric according to claim 1 and its production technology, it is characterised in that: the step
It is rapid 13) in finished product nylon facing material surface is subjected to dustless cleaning, and fold spare.
10. a kind of opaque nylon coating fabric according to claim 1 and its production technology, it is characterised in that: described
The control of oven interior temperature is at 30-60 DEG C in step 14).