CN109538080A - High-intensitive closed guard gate - Google Patents
High-intensitive closed guard gate Download PDFInfo
- Publication number
- CN109538080A CN109538080A CN201710607872.8A CN201710607872A CN109538080A CN 109538080 A CN109538080 A CN 109538080A CN 201710607872 A CN201710607872 A CN 201710607872A CN 109538080 A CN109538080 A CN 109538080A
- Authority
- CN
- China
- Prior art keywords
- parts
- copper wire
- stratum reticulare
- wire stratum
- closed guard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high-intensitive closed guard gates, including door body, the door body to be followed successively by corrosion-resistant finishes, outer stereotype, electro-magnetic screen layer, foamed plastic layer, the first copper wire stratum reticulare, reinforced concrete floor, the second copper wire stratum reticulare and interior stereotype from outside to inside;Wherein, the first copper wire stratum reticulare is identical as the thickness of the second copper wire stratum reticulare, and the outer stereotype is identical as the thickness of the interior stereotype.The integral strength of the high intensity closed guard gate is high, can resist high impact wave.
Description
Technical field
The present invention relates to a kind of high-intensitive closed guard gates, belong to defense equipment field.
Background technique
People's air defense is also known as civil defence, and civil defence is international word, English CIVIL DEFENCE, is that government mobilizes and organize group
Crowd takes anti-air strike, measure of fighting calamities and providing relief, and implements rescue action, prevention and the activity for mitigating disaster harm.Closed guard gate is to belong to
Civil defence safeguard, as its name suggests, closed guard gate are exactly the door of people's protection works entrance.
Existing closed guard gate, door body surface is soaked or is being easy jaundice, mouldy and change after moist environment for a long time
Color, and its integral strength is not good enough, it is difficult to resist high-intensitive shock wave.
It is therefore desirable to design a kind of high-intensitive closed guard gate, to overcome the above problem.
Summary of the invention
It is an object of the invention to overcome the defect of the prior art, provide that a kind of integral strength is high, can resist high intensity
The high-intensitive closed guard gate of shock wave.
The present invention is implemented as follows:
The present invention provides a kind of high-intensitive closed guard gate, including door body, the door body are followed successively by corrosion-resistant finishes, outer lead from outside to inside
Plate, electro-magnetic screen layer, foamed plastic layer, the first copper wire stratum reticulare, reinforced concrete floor, the second copper wire stratum reticulare and interior stereotype;
The corrosion-resistant finishes is made of the raw material of following parts by weight: 20-25 parts of epoxy resin, 18-20 parts of organobentonite,
2-8 parts of clay, 2-3 parts of SiO 2 hollow microsphere, 2-3 parts of silane coupling agent, 2-3 parts of anti-flash rusting agent, is prevented 25-50 parts of borax
Heavy agent 2-3 parts, 1-3 parts of curing agent fiber, 2-3 parts of opacifiers, 1-3 parts of adhesive agent;
The electro-magnetic screen layer is made of the raw material of following parts by weight: 32-40 parts of acryl-modified silicone resin resin, aqueous poly-
22-28 parts of urethane resin, 20-25 parts of epoxy resin, 18-25 parts of electrically conductive polyaniline, 12-15 parts of chemical silvering carbon fiber, nickel powder
5-9 parts, 5-8 parts of carbon black, 4-6 parts of copper powder, 18-20 parts of organobentonite, 18-20 parts of organic silicon modified by polyether, ethyl acetate 5-
10 parts, 3-4 parts of glycerine, 12-20 parts of sodium carboxymethylcellulose, 9-14 parts of polyvinyl alcohol, 9-12 parts of dispersing agent;
Wherein, the first copper wire stratum reticulare is identical as the thickness of the second copper wire stratum reticulare, the outer stereotype and the interior stereotype
Thickness it is identical.
Further, the first copper wire stratum reticulare is identical as the structure of the second copper wire stratum reticulare.
Further, the first copper wire stratum reticulare is all made of proof copper-wire braided with the second copper wire stratum reticulare and forms.
Further, the foamed plastic layer is polystyrene plastics layer.
The invention has the following advantages:
The high intensity closed guard gate is by setting corrosion-resistant finishes, so that its moisture resistance ability is strong, it is not only wear-resisting, and but also it is not afraid of water immersion,
It can be soaked with effective solution door body surface or it is easy jaundice, mouldy and discoloration etc. after moist environment in long-time asks
Topic;Barrier nuclear radiation ability can be enhanced by the way that outer stereotype and interior stereotype is arranged;Foamed plastic layer is set, foreign impacts can be absorbed
The energy of wave reduces door body and is hit, and improves the shock wave resistance performance of high-intensitive closed guard gate;By the way that electro-magnetic screen layer energy is arranged
Effective shielding electromagnetic interference.
Detailed description of the invention
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below
There is attached drawing needed in technical description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this
Some embodiments of invention for those of ordinary skill in the art without creative efforts, can be with
Other attached drawings are obtained according to these attached drawings.
Fig. 1 is the structural schematic diagram of high-intensitive closed guard gate provided in an embodiment of the present invention.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art without making creative work it is obtained it is all its
Its embodiment, shall fall within the protection scope of the present invention.
Such as Fig. 1, the embodiment of the present invention provides a kind of high-intensitive closed guard gate, including door body, and the door body is from outside to inside successively
For corrosion-resistant finishes 1, outer stereotype 2, electro-magnetic screen layer 3, foamed plastic layer 4, the first copper wire stratum reticulare 5, reinforced concrete floor 6,
Two copper wire stratum reticulares 7 and interior stereotype 8.
The corrosion-resistant finishes 1 is made of the raw material of following parts by weight: 20-25 parts of epoxy resin, organobentonite 18-
20 parts, 2-8 parts of clay, 25-50 parts of borax, 2-3 parts of SiO 2 hollow microsphere, 2-3 parts of silane coupling agent, anti-flash rusting agent 2-3
Part, 2-3 parts of anti-settling agent, 1-3 parts of curing agent fiber, 2-3 parts of opacifiers, 1-3 parts of adhesive agent.Wherein, the opacifiers be fluorite,
One or more of zirconium dioxide, titanium oxide, tin oxide.
In the preferred embodiment, the corrosion-resistant finishes 1 is made of the raw material of following parts by weight: epoxy resin 25
Part, 18 parts of organobentonite, 4 parts of clay, 30 parts of borax, 2 parts of SiO 2 hollow microsphere, 2 parts of silane coupling agent, anti-flash rusting agent
2- parts, 2 parts of anti-settling agent, 3 parts of curing agent fiber, 3 parts of opacifiers, 2 parts of adhesive agent.Above-mentioned raw materials are mixed according to a certain percentage,
It is coated on outer stereotype 2 after being prepared into mixing slurry, the moisture resistance ability of the corrosion-resistant finishes 1 is strong, not only wear-resisting but also not afraid of water
It impregnates, it can or in long-time in moist environment after easy jaundice, mouldy and discoloration soaked with effective solution door body surface
The problems such as.
The electro-magnetic screen layer 3 is made of the raw material of following parts by weight: 32-40 parts of acryl-modified silicone resin resin,
22-28 parts of waterborne polyurethane resin, 20-25 parts of epoxy resin, 18-25 parts of electrically conductive polyaniline, chemical silvering carbon fiber 12-15
Part, 5-9 parts of nickel powder, 5-8 parts of carbon black, 4-6 parts of copper powder, 18-20 parts of organobentonite, 18-20 parts of organic silicon modified by polyether, acetic acid
5-10 parts of ethyl ester, 3-4 parts of glycerine, 12-20 parts of sodium carboxymethylcellulose, 9-14 parts of polyvinyl alcohol, 9-12 parts of dispersing agent.
The specific preparation process of the electro-magnetic screen layer 3 are as follows: according to above-mentioned parts by weight, by acryl-modified silicone resin tree
Rouge, waterborne polyurethane resin, epoxy resin and polyvinyl alcohol stir to obtain mixed solution, at high speeds will
Electrically conductive polyaniline, chemical silvering carbon fiber, nickel powder, carbon black, copper powder, organobentonite, organic silicon modified by polyether are dispersed to fineness
Less than 60um, above-mentioned crushing raw material is successively put under stiring;By dispersing agent and ethyl acetate, glycerine, carboxymethyl cellulose
Sodium, polyvinyl alcohol are added in above-mentioned solution and are uniformly dispersed using ultrasonic wave, and the electro-magnetic screen layer 3 is made.The electromagnetic shielding
Layer 3 has excellent shielding action, can effectively shield electromagnetic wave.
Such as Fig. 1, the outer stereotype 2 is identical as the thickness of the interior stereotype 8, is used as door body by outer stereotype 2 and interior stereotype 8
Main support structure, integral strength not only can be enhanced, but can be enhanced barrier nuclear radiation ability.
Such as Fig. 1, wherein the first copper wire stratum reticulare 5 is identical as the thickness of the second copper wire stratum reticulare 7, further, institute
It is identical as the structure of the second copper wire stratum reticulare 7 to state the first copper wire stratum reticulare 5.In the preferred embodiment, first copper mesh
Layer 5 is all made of proof copper-wire braided with the second copper wire stratum reticulare 7 and forms.The first copper wire stratum reticulare 5, the reinforced concrete floor 6
And the second copper wire stratum reticulare 7 can not only reinforce the integral strength of closed guard gate, but also the shielding properties of closed guard gate can be enhanced, and make
It has stronger tempest performance.
The foamed plastic layer 4 is polystyrene plastics layer, can absorb the energy of foreign impacts wave, reduces the suffered punching of door body
It hits, improves the shock wave resistance performance of the high-intensitive closed guard gate.
The high intensity closed guard gate is by setting corrosion-resistant finishes, so that its moisture resistance ability is strong, it is not only wear-resisting, and but also it is not afraid of water logging
Bubble, can or in long-time in moist environment after easy jaundice, mouldy and discoloration etc. soaked with effective solution door body surface
Problem;Barrier nuclear radiation ability can be enhanced by the way that outer stereotype and interior stereotype is arranged;Foamed plastic layer is set, extraneous punching can be absorbed
The energy of wave is hit, door body is reduced and is hit, improves the shock wave resistance performance of high-intensitive closed guard gate;By the way that electro-magnetic screen layer is arranged
Electromagnetic interference can effectively be shielded.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (4)
1. it is a kind of high intensity closed guard gate, which is characterized in that including door body, the door body be followed successively by from outside to inside corrosion-resistant finishes,
Outer stereotype, electro-magnetic screen layer, foamed plastic layer, the first copper wire stratum reticulare, reinforced concrete floor, the second copper wire stratum reticulare and interior lead
Plate;
The corrosion-resistant finishes is made of the raw material of following parts by weight: 20-25 parts of epoxy resin, 18-20 parts of organobentonite,
2-8 parts of clay, 2-3 parts of SiO 2 hollow microsphere, 2-3 parts of silane coupling agent, 2-3 parts of anti-flash rusting agent, is prevented 25-50 parts of borax
Heavy agent 2-3 parts, 1-3 parts of curing agent fiber, 2-3 parts of opacifiers, 1-3 parts of adhesive agent;
The electro-magnetic screen layer is made of the raw material of following parts by weight: 32-40 parts of acryl-modified silicone resin resin, aqueous poly-
22-28 parts of urethane resin, 20-25 parts of epoxy resin, 18-25 parts of electrically conductive polyaniline, 12-15 parts of chemical silvering carbon fiber, nickel powder
5-9 parts, 5-8 parts of carbon black, 4-6 parts of copper powder, 18-20 parts of organobentonite, 18-20 parts of organic silicon modified by polyether, ethyl acetate 5-
10 parts, 3-4 parts of glycerine, 12-20 parts of sodium carboxymethylcellulose, 9-14 parts of polyvinyl alcohol, 9-12 parts of dispersing agent;
Wherein, the first copper wire stratum reticulare is identical as the thickness of the second copper wire stratum reticulare, the outer stereotype and the interior stereotype
Thickness it is identical.
2. high intensity closed guard gate as described in claim 1, it is characterised in that: the first copper wire stratum reticulare and second copper wire
The structure of stratum reticulare is identical.
3. high intensity closed guard gate as described in claim 1, it is characterised in that: the first copper wire stratum reticulare and second copper wire
Stratum reticulare is all made of proof copper-wire braided and forms.
4. high intensity closed guard gate as described in claim 1, it is characterised in that: the foamed plastic layer is polystyrene plastics
Layer.