CN109537354A - A kind of bamboo fibre and wood pulp spun lacing composite cleaning cloth and preparation method thereof - Google Patents
A kind of bamboo fibre and wood pulp spun lacing composite cleaning cloth and preparation method thereof Download PDFInfo
- Publication number
- CN109537354A CN109537354A CN201811429664.4A CN201811429664A CN109537354A CN 109537354 A CN109537354 A CN 109537354A CN 201811429664 A CN201811429664 A CN 201811429664A CN 109537354 A CN109537354 A CN 109537354A
- Authority
- CN
- China
- Prior art keywords
- spun lacing
- bamboo fibre
- wood pulp
- cleaning cloth
- bamboo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of bamboo fibres and wood pulp spun lacing composite cleaning cloth and preparation method thereof, are formed by following weight parts raw material proportioning: wood pulp 40%-50% and bamboo fibre 50%-60%；The present invention passes sequentially through, pre- shredding, cylinder is discongested, wet web, thorn spun lacing, vacuum suction are dry, obtained by drying in advance.The beneficial effects of the present invention are: cost of the invention is lower than full bamboo fibre, got well than full properties of bamboo, pulling force, thickness, moisture content, the uniformity and flexibility are superior.Bamboo fibre natural bacteriostatic does not add any industrial chemicals, so that cleaning cloth is healthier, hygienic, is all biomass, complete environment-friendly degradable is harmless.By vacuum suction dehydration in bamboo fibre wooden oar wet tissue preparation process of the invention, avoid causing the thickness of wet tissue not reach requirement using the dewatering type of physical squeezing；The usage amount of heat drying steam is greatly saved, and has saved energy consumption.
Description
Technical field
The invention belongs to cleaning cloth manufacturing technology fields, and in particular to a kind of bamboo fibre and wood pulp spun lacing composite clean
Cloth and preparation method thereof.
Background technique
In the prior art, as the progress people in epoch increasingly focus on environmental protection and health, wet tissue has become people
Indispensable thing in daily life, the wet tissue overwhelming majority currently on the market are had pure using terylene as main raw material(s)
Terylene, there is terylene to add viscose rayon, also have bamboo fibre etc..
Because terylene material itself be it is not hydrophilic, the wet tissue of pure polyester is all added to hydrophilic agent in the market,
And the wet tissue better quality of pure viscose rayon or pure bamboo fibre, but cost is too high, and non-degradable.
Therefore, how to produce a kind of new product to mix bamboo fibre and wood pulp, by the natural bacteriostatic of bamboo fibre, not only
Complete environment-friendly degradable can be reached, can also be more much lower than pure bamboo fibre wet tissue in cost, and then improve market competition
Power.
Summary of the invention
Present invention aim to address above-mentioned technical problem of the existing technology, a kind of bamboo fibre and wood pulp spun lacing are provided
Composite cleaning cloth and preparation method thereof, with overcome the deficiencies in the prior art.
To achieve the goals above, a kind of bamboo fibre of the present invention and wood pulp spun lacing composite cleaning cloth and preparation method thereof, by
Following weight parts raw material proportioning forms:
Wood pulp 40%-50% and bamboo fibre 50%-60%；
The present invention is made by the steps:
Step 1: bamboo fibre is carried out pre- shredding by bale opener, enters back into carding machine and carry out smart shredding；
Step 2: the good bamboo fibre of shredding is reached air pressure cotton box by conveying fan, discongest, is formed into cylinder by weighing
Cotton net by pre- thorn circle drum spun lacing, the pressure of spun lacing is 20kg-50kg, obtains some strength, it is multiple that cotton net follows trawlnet to reach
It closes；
It is discongested Step 3: pulpboard first passes through mashing the pre- of pot, concentration control passes through the sub-wire broom of mill in 3%-6%, subsequent wood pulp
Change, reach the beating degree of 16-17 ° of SR, the wood pulp of milled forms wet web by paper machine, and it is multiple that wet web follows inclined wire to reach
It closes, cotton net and wet web are combined with each other by extruding and suction；
Step 4: the product after compound is by pre- thorn spun lacing together, the pressure of spun lacing is 10-30kg, enters platform through trawlnet
Spun lacing successively passes through five platform spun lacings later, and spun lacing pressure is 30-70kg, and bamboo fibre wood pulp Compound Fabric passes through high-pressure water-jet
It is closely combined together, obtains high-intensitive；
Step 5: also to pass through one of plain net after platform spun lacing, plain net is equipped with vacuum tank below, in order to keep rising for wet tissue
Bao Du and pliability cannot use squeezing, need as far as possible to come out moisture absorption by vacuum suction, reduce dry difficulty
Degree；
It is dried Step 6: the product after spun lacing enters drying cylinder, totally three groups of drying cylinders, every group 10, drying cylinder wall temperature is in 80-
140 degrees Celsius, the product after drying is wound up after tested to obtain the final product.
The beneficial effects of the present invention are:
1, cost of the invention is lower than full bamboo fibre, gets well than full properties of bamboo, pulling force, thickness, moisture content, the uniformity and
Flexibility is superior.
2, bamboo fibre natural bacteriostatic does not add any industrial chemicals, so that cleaning cloth is healthier, hygienic, is all biology
Matter, complete environment-friendly degradable are harmless.
3, it is avoided by vacuum suction dehydration using physical squeezing in bamboo fibre wooden oar wet tissue preparation process of the invention
Dewatering type causes the thickness of wet tissue not reach requirement；The usage amount of heat drying steam is greatly saved, and has saved energy
Consumption.
Detailed description of the invention
Fig. 1 is production technological process of the invention.
Specific embodiment
Referring to Fig.1, a kind of bamboo fibre of the present invention and wood pulp spun lacing composite cleaning cloth and preparation method thereof, by following weight parts
Raw material proportioning forms:
Wood pulp 40%-50% and bamboo fibre 50%-60%；
The present invention is made by the steps:
Step 1: bamboo fibre is carried out pre- shredding by bale opener, enters back into carding machine and carry out smart shredding；
Step 2: the good bamboo fibre of shredding is reached air pressure cotton box by conveying fan, discongest, is formed into cylinder by weighing
Cotton net by pre- thorn circle drum spun lacing, the pressure of spun lacing is 20kg-50kg, obtains some strength, it is multiple that cotton net follows trawlnet to reach
It closes；
It is discongested Step 3: pulpboard first passes through mashing the pre- of pot, concentration control passes through the sub-wire broom of mill in 3%-6%, subsequent wood pulp
Change, reach the beating degree of 16-17 ° of SR, the wood pulp of milled forms wet web by paper machine, and it is multiple that wet web follows inclined wire to reach
It closes, cotton net and wet web are combined with each other by extruding and suction；
Step 4: the product after compound is by pre- thorn spun lacing together, the pressure of spun lacing is 10-30kg, enters platform through trawlnet
Spun lacing successively passes through five platform spun lacings later, and spun lacing pressure is 30-70kg, and bamboo fibre wood pulp Compound Fabric passes through high-pressure water-jet
It is closely combined together, obtains high-intensitive；
Step 5: also to pass through one of plain net after platform spun lacing, plain net is equipped with vacuum tank below, in order to keep rising for wet tissue
Bao Du and pliability cannot use squeezing, need as far as possible to come out moisture absorption by vacuum suction, reduce dry difficulty
Degree；
It is dried Step 6: the product after spun lacing enters drying cylinder, totally three groups of drying cylinders, every group 10, drying cylinder wall temperature is in 80-
140 degrees Celsius, the product after drying is wound up after tested to obtain the final product.
The beneficial effects of the present invention are:
1, cost of the invention is lower than full bamboo fibre, gets well than full properties of bamboo, pulling force, thickness, moisture content, the uniformity and
Flexibility is superior.
2, bamboo fibre natural bacteriostatic does not add any industrial chemicals, so that cleaning cloth is healthier, hygienic, is all biology
Matter, complete environment-friendly degradable are harmless.
3, it is avoided by vacuum suction dehydration using physical squeezing in bamboo fibre wooden oar wet tissue preparation process of the invention
Dewatering type causes the thickness of wet tissue not reach requirement；The usage amount of heat drying steam is greatly saved, and has saved energy
Consumption.
Claims (1)
1. a kind of bamboo fibre and wood pulp spun lacing composite cleaning cloth and preparation method thereof, are formed by following weight parts raw material proportioning:
Wood pulp 40%-50% and bamboo fibre 50%-60%；
The present invention is made by the steps:
Step 1: bamboo fibre is carried out pre- shredding by bale opener, enters back into carding machine and carry out smart shredding；
Step 2: the good bamboo fibre of shredding is reached air pressure cotton box by conveying fan, discongest, is formed into cylinder by weighing
Cotton net by pre- thorn circle drum spun lacing, the pressure of spun lacing is 20kg-50kg, obtains some strength, it is multiple that cotton net follows trawlnet to reach
It closes；
It is discongested Step 3: pulpboard first passes through mashing the pre- of pot, concentration control passes through the sub-wire broom of mill in 3%-6%, subsequent wood pulp
Change, reach the beating degree of 16-17 ° of SR, the wood pulp of milled forms wet web by paper machine, and it is multiple that wet web follows inclined wire to reach
It closes, cotton net and wet web are combined with each other by extruding and suction；
Step 4: the product after compound is by pre- thorn spun lacing together, the pressure of spun lacing is 10-30kg, enters platform through trawlnet
Spun lacing successively passes through five platform spun lacings later, and spun lacing pressure is 30-70kg, and bamboo fibre wood pulp Compound Fabric passes through high-pressure water-jet
It is closely combined together, obtains high-intensitive；
Step 5: also to pass through one of plain net after platform spun lacing, plain net is equipped with vacuum tank below, in order to keep rising for wet tissue
Bao Du and pliability cannot use squeezing, need as far as possible to come out moisture absorption by vacuum suction, reduce dry difficulty
Degree；
It is dried Step 6: the product after spun lacing enters drying cylinder, totally three groups of drying cylinders, every group 10, drying cylinder wall temperature is in 80-
140 degrees Celsius, the product after drying is wound up after tested to obtain the final product.