CN109535980A - A kind of environment-friendly type paint formulation - Google Patents
A kind of environment-friendly type paint formulation Download PDFInfo
- Publication number
- CN109535980A CN109535980A CN201811468168.XA CN201811468168A CN109535980A CN 109535980 A CN109535980 A CN 109535980A CN 201811468168 A CN201811468168 A CN 201811468168A CN 109535980 A CN109535980 A CN 109535980A
- Authority
- CN
- China
- Prior art keywords
- parts
- alcohol
- resin
- butyl acetate
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly type paint formulations, by following parts by weight at being grouped as: organic epoxy resin 12-19 parts, 5-7 parts of dimethyl sulfoxide, 11-15 parts of trbasic zinc phosphate, 3-7 parts of barium chromate, 11-16 parts of polyacrylate, 12-15 parts of diacetone alcohol, 13-16 parts of zinc oxide, 0.5-2.5 parts of ethyl alcohol, 11-15 parts of alcohol-soluble resin, 10-13 parts of toluene di-isocyanate(TDI), 4-7 parts of butyl acetate, 15-18 parts of celluosic resin, 6-9 parts of levelling agent, 11-15 parts of epoxy modified silicone resin liquid, 15-17 parts of glycol monoethyl ether, 1-3 parts of defoaming agent, 5-7 parts of talcum powder, 11-18 parts of cyanate, 15-18 parts of butyl acetate, 22-25 parts of benzophenone, triethanolamine 11-17 Part, 4-8 parts of diphenylpolysiloxane, environment protecting of the present invention is good;Coating rate of drying is fast, and unharmful substance, taste is small, and without penetrating odor after having brushed, convenient for construction, insulation performance is superior, moisture resistance waterproof, Rustproof cold-resistant, ozone and aging resistance.
Description
Technical field
The present invention relates to a kind of paint formulation, specifically a kind of environment-friendly type paint formulation belongs to chemical technology field.
Background technique
The comprehensive performances such as sun-proof, heat-resisting, the resistance to migration of traditional paint are relatively poor.Benzene has been used in process of production
Class, ketone and esters equal solvent, these solvent highly volatiles, can cause environmental pollution in the production and use process.
Summary of the invention
In view of the above existing problems in the prior art, the present invention provides a kind of environment-friendly type paint formulations, and environment protecting is good, nothing
Harmful substance, taste are small.
To achieve the goals above, the technical solution adopted by the present invention is that: a kind of environment-friendly type paint formulation, by following weight
Part at being grouped as: organic epoxy resin 12-19 parts, 5-7 parts of dimethyl sulfoxide, 11-15 parts of trbasic zinc phosphate, 3-7 parts of barium chromate,
11-16 parts of polyacrylate, 12-15 parts of diacetone alcohol, 13-16 parts of zinc oxide, 0.5-2.5 parts of ethyl alcohol, alcohol-soluble resin 11-15
It is part, 10-13 parts of toluene di-isocyanate(TDI), 4-7 parts of butyl acetate, 15-18 parts of celluosic resin, 6-9 parts of levelling agent, epoxy-modified
11-15 parts of organic siliconresin liquid, 15-17 parts of glycol monoethyl ether, 1-3 parts of defoaming agent, 5-7 parts of talcum powder, cyanate 11-18
Part, 15-18 parts of butyl acetate, 22-25 parts of benzophenone, 11-17 parts of triethanolamine, 4-8 parts of diphenylpolysiloxane.
As a further improvement of the present invention, by following parts by weight at being grouped as: 12 parts of organic epoxy resin, diformazan
5 parts of base sulfoxide, 11 parts of trbasic zinc phosphate, 3 parts of barium chromate, 11 parts of polyacrylate, 12 parts of diacetone alcohol, 13 parts of zinc oxide, ethyl alcohol 0.5
Part, 11 parts of alcohol-soluble resin, 10 parts of toluene di-isocyanate(TDI), 4 parts of butyl acetate, 15 parts of celluosic resin, 6 parts of levelling agent, ring
11 parts of oxygen modified organic silicone resin liquid, 15 parts of glycol monoethyl ether, 1 part of defoaming agent, 5 parts of talcum powder, 11 parts of cyanate, acetic acid fourth
15 parts of ester, 22 parts of benzophenone, 11 parts of triethanolamine, 4 parts of diphenylpolysiloxane.
As a further improvement of the present invention, by following parts by weight at being grouped as: 19 parts of organic epoxy resin, diformazan
7 parts of base sulfoxide, 15 parts of trbasic zinc phosphate, 7 parts of barium chromate, 16 parts of polyacrylate, 15 parts of diacetone alcohol, 16 parts of zinc oxide, ethyl alcohol 2.5
Part, 15 parts of alcohol-soluble resin, 13 parts of toluene di-isocyanate(TDI), 7 parts of butyl acetate, 18 parts of celluosic resin, 9 parts of levelling agent, ring
15 parts of oxygen modified organic silicone resin liquid, 17 parts of glycol monoethyl ether, 3 parts of defoaming agent, 7 parts of talcum powder, 18 parts of cyanate, acetic acid fourth
18 parts of ester, 25 parts of benzophenone, 17 parts of triethanolamine, 8 parts of diphenylpolysiloxane.
Compared with prior art, environment protecting of the present invention is good;Coating rate of drying is fast, and unharmful substance, taste is small, has brushed
Afterwards without penetrating odor, convenient for construction, insulation performance is superior, moisture resistance waterproof, Rustproof cold-resistant, ozone and aging resistance.
Specific embodiment
Embodiment one
The present invention a kind of environment-friendly type paint formulation, by following parts by weight at being grouped as: organic epoxy resin 12-19
Part, 5-7 parts of dimethyl sulfoxide, 11-15 parts of trbasic zinc phosphate, 3-7 parts of barium chromate, 11-16 parts of polyacrylate, diacetone alcohol 12-15
Part, 13-16 parts of zinc oxide, 0.5-2.5 parts of ethyl alcohol, 11-15 parts of alcohol-soluble resin, 10-13 parts of toluene di-isocyanate(TDI), acetic acid fourth
4-7 parts of ester, 15-18 parts of celluosic resin, 6-9 parts of levelling agent, 11-15 parts of epoxy modified silicone resin liquid, ethylene glycol list first
15-17 parts of ether, 1-3 parts of defoaming agent, 5-7 parts of talcum powder, 11-18 parts of cyanate, 15-18 parts of butyl acetate, benzophenone 22-25
Part, 11-17 parts of triethanolamine, 4-8 parts of diphenylpolysiloxane.
Embodiment two
The present invention a kind of environment-friendly type paint formulation, by following parts by weight at being grouped as: 12 parts of organic epoxy resin, two
5 parts of methyl sulfoxide, 11 parts of trbasic zinc phosphate, 3 parts of barium chromate, 11 parts of polyacrylate, 12 parts of diacetone alcohol, 13 parts of zinc oxide, ethyl alcohol
0.5 part, 11 parts of alcohol-soluble resin, 10 parts of toluene di-isocyanate(TDI), 4 parts of butyl acetate, 15 parts of celluosic resin, 6 parts of levelling agent,
11 parts of epoxy modified silicone resin liquid, 15 parts of glycol monoethyl ether, 1 part of defoaming agent, 5 parts of talcum powder, 11 parts of cyanate, acetic acid
15 parts of butyl ester, 22 parts of benzophenone, 11 parts of triethanolamine, 4 parts of diphenylpolysiloxane.
As a further improvement of the present invention, by following parts by weight at being grouped as: 19 parts of organic epoxy resin, diformazan
7 parts of base sulfoxide, 15 parts of trbasic zinc phosphate, 7 parts of barium chromate, 16 parts of polyacrylate, 15 parts of diacetone alcohol, 16 parts of zinc oxide, ethyl alcohol 2.5
Part, 15 parts of alcohol-soluble resin, 13 parts of toluene di-isocyanate(TDI), 7 parts of butyl acetate, 18 parts of celluosic resin, 9 parts of levelling agent, ring
15 parts of oxygen modified organic silicone resin liquid, 17 parts of glycol monoethyl ether, 3 parts of defoaming agent, 7 parts of talcum powder, 18 parts of cyanate, acetic acid fourth
18 parts of ester, 25 parts of benzophenone, 17 parts of triethanolamine, 8 parts of diphenylpolysiloxane.
Environment protecting of the present invention is good;Coating rate of drying is fast, and unharmful substance, taste is small, does not have irritation gas after having brushed
Taste, convenient for construction, insulation performance is superior, moisture resistance waterproof, Rustproof cold-resistant, ozone and aging resistance.
Claims (3)
1. a kind of environment-friendly type paint formulation, which is characterized in that by following parts by weight at being grouped as: organic epoxy resin 12-
19 parts, 5-7 parts of dimethyl sulfoxide, 11-15 parts of trbasic zinc phosphate, 3-7 parts of barium chromate, 11-16 parts of polyacrylate, diacetone alcohol 12-
15 parts, 13-16 parts of zinc oxide, 0.5-2.5 parts of ethyl alcohol, 11-15 parts of alcohol-soluble resin, 10-13 parts of toluene di-isocyanate(TDI), acetic acid
4-7 parts of butyl ester, 15-18 parts of celluosic resin, 6-9 parts of levelling agent, 11-15 parts of epoxy modified silicone resin liquid, ethylene glycol list
15-17 parts of methyl ether, 1-3 parts of defoaming agent, 5-7 parts of talcum powder, 11-18 parts of cyanate, 15-18 parts of butyl acetate, benzophenone 22-
25 parts, 11-17 parts of triethanolamine, 4-8 parts of diphenylpolysiloxane.
2. a kind of environment-friendly type paint formulation according to claim 1, which is characterized in that by following parts by weight at grouping
At: 12 parts of organic epoxy resin, 5 parts of dimethyl sulfoxide, 11 parts of trbasic zinc phosphate, 3 parts of barium chromate, 11 parts of polyacrylate, dipropyl
12 parts of keto-alcohol, 13 parts of zinc oxide, 0.5 part of ethyl alcohol, 11 parts of alcohol-soluble resin, 10 parts of toluene di-isocyanate(TDI), 4 parts of butyl acetate,
15 parts of celluosic resin, 6 parts of levelling agent, 11 parts of epoxy modified silicone resin liquid, 15 parts of glycol monoethyl ether, 1 part of defoaming agent,
5 parts of talcum powder, 11 parts of cyanate, 15 parts of butyl acetate, 22 parts of benzophenone, 11 parts of triethanolamine, diphenylpolysiloxane 4
Part.
3. a kind of environment-friendly type paint formulation according to claim 1 or 2, which is characterized in that by the ingredient of following parts by weight
Composition: 19 parts of organic epoxy resin, 7 parts of dimethyl sulfoxide, 15 parts of trbasic zinc phosphate, 7 parts of barium chromate, 16 parts of polyacrylate, two
15 parts of pyruvic alcohol, 16 parts of zinc oxide, 2.5 parts of ethyl alcohol, 15 parts of alcohol-soluble resin, 13 parts of toluene di-isocyanate(TDI), butyl acetate 7
Part, 18 parts of celluosic resin, 9 parts of levelling agent, 15 parts of epoxy modified silicone resin liquid, 17 parts of glycol monoethyl ether, defoaming agent 3
Part, 7 parts of talcum powder, 18 parts of cyanate, 18 parts of butyl acetate, 25 parts of benzophenone, 17 parts of triethanolamine, diphenylpolysiloxane
8 parts.