CN109517490A - A kind of exterior coating agent of high-adhesion - Google Patents
A kind of exterior coating agent of high-adhesion Download PDFInfo
- Publication number
- CN109517490A CN109517490A CN201811454776.5A CN201811454776A CN109517490A CN 109517490 A CN109517490 A CN 109517490A CN 201811454776 A CN201811454776 A CN 201811454776A CN 109517490 A CN109517490 A CN 109517490A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- exterior coating
- coating agent
- adhesion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of exterior coating agent of high-adhesion of the invention, belongs to technical field of coatings.A kind of exterior coating agent of high-adhesion, the raw material including following parts by weight: epoxy resin, precipitated calcium carbonate, poly-dopamine, antifreezing agent, Chitosan powder, polyvinyl alcohol, SiO 2 powder, polyvinyl butyral, pigments and fillers, crosslinking agent and water；The Chitosan powder is to mix water soluble chitosan and silver ion to make its load silver ion through hydro-thermal method and be made.This exterior coating agent preparation method is simple, and gained exterior coating agent viscosity is high and has mildew resistance, avoids falling off and generating mildew after being applied to wall, influences beauty.
Description
Technical field
The invention belongs to the exterior coating agent of technical field of coatings more particularly to a kind of high-adhesion.
Background technique
With the fast development of building trade, the application field of exterior coating is greatly increased, and traditional exterior coating can be with
Factors are unendurable time, rainy day etc. is adhered on exterior wall, will appear over time fall off, de- flower phenomenon, for exterior wall
Aesthetics produce serious influence.
Summary of the invention
In view of the above problems, the present invention provides a kind of exterior coating agent of high-adhesion, this coating agent preparation
Method is simple and environmentally-friendly, and gained coating agent has good caking property and mildew resistance.
The technical solution adopted by the invention is as follows:
A kind of exterior coating agent of high-adhesion, the raw material including following parts by weight: epoxy resin, gathers precipitated calcium carbonate
Dopamine, antifreezing agent, Chitosan powder, polyvinyl alcohol, SiO 2 powder, polyvinyl butyral, pigments and fillers, crosslinking agent and
Water；The Chitosan powder is to mix water soluble chitosan and silver ion to make its load silver ion through hydro-thermal method and be made.
Further, the exterior coating agent of a kind of high-adhesion, the raw material including following parts by weight: epoxy resin
25~33 parts, it is 10~13 parts of precipitated calcium carbonate, 3~5 parts of poly-dopamine, 1.5~2 parts of antifreezing agent, 1~2 part of Chitosan powder, poly-
2~4 parts of vinyl alcohol, 2~4 parts of SiO 2 powder, 10~12 parts of polyvinyl butyral, 20~28 parts of pigments and fillers, crosslinking agent 4
~6 parts and 64~99 parts of water；The Chitosan powder is to mix water soluble chitosan and silver ion to make its load through hydro-thermal method
Silver ion and be made.
Further, the exterior coating agent of a kind of high-adhesion, the raw material including following parts by weight: epoxy resin
30 parts, 12 parts of precipitated calcium carbonate, 4 parts of poly-dopamine, 1.8 parts of antifreezing agent, 1.5 parts of Chitosan powder, polyvinyl alcohol with low degree of polymerization 3
Part, 3 parts of SiO 2 powder, 11 parts of polyvinyl butyral, 24 parts of pigments and fillers, 5 parts of crosslinking agent and 85 parts of water；The chitosan
Powder is to mix water soluble chitosan and silver ion to make its load silver ion through hydro-thermal method and be made.
Further, the Chitosan powder is by water-soluble chitosan oligomer acid solution and silver chlorate with mass ratio
For 3~5:1 mode carry out room temperature mixing, stirring 30~40min, be then put into reaction kettle carry out 100~120 DEG C 16~
The hydro-thermal reaction of 20h is taken out, is centrifuged, prepared by drying.
Further, the preparation method of the exterior coating agent of a kind of high-adhesion, comprising the following steps:
S1. epoxy resin, precipitated calcium carbonate, SiO 2 powder and pigments and fillers are subjected to ball milling in the ball mill in proportion
3~5h takes out, and the water that formula ratio is added is stirred in quick peeler, obtains slurry；
S2. polyvinyl alcohol with low degree of polymerization, polyvinyl butyral and crosslinking agent are added in quick peeler, 70~
It is stirred 30~50min at 80 DEG C, poly-dopamine is added and stirs 20~30min；Again by slurry obtained by S1 be added stirring 1~
1.5h；
S3. 40~50 DEG C are cooled to, Chitosan powder is added and stirs 10~15min, is down to room temperature, antifreezing agent is added, into
Row stirs 10~20min to get the exterior coating agent of high-adhesion.
Further, the stirring rate of the quick peeler is 500r/min.
By adopting the above-described technical solution, the beneficial effects of the present invention are: the exterior coating of high-adhesion of the invention
Agent preparation method is simple, and gained exterior coating agent viscosity is high and has mildew resistance, avoids falling off and producing after being applied to wall
It mildews change, influences beauty.
Specific embodiment
Below in conjunction with specific embodiment, the present invention will be described in detail:
A kind of exterior coating agent of high-adhesion, the raw material including following parts by weight: epoxy resin, gathers precipitated calcium carbonate
Dopamine, antifreezing agent, Chitosan powder, polyvinyl alcohol, SiO 2 powder, polyvinyl butyral, pigments and fillers, crosslinking agent and
Water；The Chitosan powder is to mix water soluble chitosan and silver ion to make its load silver ion through hydro-thermal method and be made.
Further, the exterior coating agent of a kind of high-adhesion, the raw material including following parts by weight: epoxy resin
25~33 parts, it is 10~13 parts of precipitated calcium carbonate, 3~5 parts of poly-dopamine, 1.5~2 parts of antifreezing agent, 1~2 part of Chitosan powder, poly-
2~4 parts of vinyl alcohol, 2~4 parts of SiO 2 powder, 10~12 parts of polyvinyl butyral, 20~28 parts of pigments and fillers, crosslinking agent 4
~6 parts and 64~99 parts of water；The Chitosan powder is to mix water soluble chitosan and silver ion to make its load through hydro-thermal method
Silver ion and be made.
Further, the exterior coating agent of a kind of high-adhesion, the raw material including following parts by weight: epoxy resin
30 parts, 12 parts of precipitated calcium carbonate, 4 parts of poly-dopamine, 1.8 parts of antifreezing agent, 1.5 parts of Chitosan powder, polyvinyl alcohol with low degree of polymerization 3
Part, 3 parts of SiO 2 powder, 11 parts of polyvinyl butyral, 24 parts of pigments and fillers, 5 parts of crosslinking agent and 85 parts of water；The chitosan
Powder is to mix water soluble chitosan and silver ion to make its load silver ion through hydro-thermal method and be made.
Further, the Chitosan powder is by water-soluble chitosan oligomer acid solution and silver chlorate with mass ratio
For 3~5:1 mode carry out room temperature mixing, stirring 30~40min, be then put into reaction kettle carry out 100~120 DEG C 16~
The hydro-thermal reaction of 20h is taken out, is centrifuged, prepared by drying.
Further, the preparation method of the exterior coating agent of a kind of high-adhesion, comprising the following steps:
S1. epoxy resin, precipitated calcium carbonate, SiO 2 powder and pigments and fillers are subjected to ball milling in the ball mill in proportion
3~5h takes out, and the water that formula ratio is added is stirred in quick peeler, obtains slurry；
S2. polyvinyl alcohol with low degree of polymerization, polyvinyl butyral and crosslinking agent are added in quick peeler, 70~
It is stirred 30~50min at 80 DEG C, poly-dopamine is added and stirs 20~30min；Again by slurry obtained by S1 be added stirring 1~
1.5h；
S3. 40~50 DEG C are cooled to, Chitosan powder is added and stirs 10~15min, is down to room temperature, antifreezing agent is added, into
Row stirs 10~20min to get the exterior coating agent of high-adhesion.
Further, the stirring rate of the quick peeler is 500r/min.
Embodiment of the present invention can be replaced by the difference of particular technique range based on the above technical solution
Change, available numerous embodiment, therefore, several embodiments as described below, be only merely in numerous embodiment compared with
Excellent example, any technology replacement done in above-mentioned technical proposal, all belongs to the scope of protection of the present invention.
Embodiment 1
A kind of exterior coating agent of high-adhesion, the raw material including following parts by weight: 30 parts of epoxy resin, precipitated calcium carbonate
12 parts, 4 parts of poly-dopamine, 1.8 parts of antifreezing agent, 1.5 parts of Chitosan powder, 3 parts of polyvinyl alcohol with low degree of polymerization, SiO 2 powder
3 parts, 11 parts of polyvinyl butyral, 24 parts of pigments and fillers, 5 parts of crosslinking agent and 85 parts of water；The Chitosan powder is will be water-soluble
Chitosan and silver ion mixing make its load silver ion through hydro-thermal method and are made.
The Chitosan powder is the side by water-soluble chitosan oligomer acid solution and silver chlorate with mass ratio for 3:1
Formula carries out room temperature mixing, stirring 30min, is then put into the hydro-thermal reaction that 100 DEG C of 16h are carried out in reaction kettle, takes out, is centrifuged, is dry
Prepared by dry.
Embodiment 2
A kind of exterior coating agent of high-adhesion, the raw material including following parts by weight: 25 parts of epoxy resin, precipitated calcium carbonate
10 parts, 3 parts of poly-dopamine, 1.5 parts of antifreezing agent, 1 part of Chitosan powder, 2 parts of polyvinyl alcohol, 2 parts of SiO 2 powder, polyethylene
10 parts of butyral, 20 parts of pigments and fillers, 4 parts of crosslinking agent and 64 parts of water；The Chitosan powder is by water soluble chitosan and silver
Ar ion mixing makes its load silver ion through hydro-thermal method and is made.
The Chitosan powder is the side by water-soluble chitosan oligomer acid solution and silver chlorate with mass ratio for 5:1
Formula carries out room temperature mixing, stirring 40min, is then put into the hydro-thermal reaction that 120 DEG C of 20h are carried out in reaction kettle, takes out, is centrifuged, is dry
Prepared by dry.
Embodiment 3
A kind of exterior coating agent of high-adhesion, the raw material including following parts by weight: 33 parts of epoxy resin, precipitated calcium carbonate
13 parts, 5 parts of poly-dopamine, 2 parts of antifreezing agent, 2 parts of Chitosan powder, 4 parts of polyvinyl alcohol, 4 parts of SiO 2 powder, polyvinyl alcohol
12 parts of butyral, 28 parts of pigments and fillers, 6 parts of crosslinking agent and 99 parts of water；The Chitosan powder be by water soluble chitosan and silver from
Son mixing makes its load silver ion through hydro-thermal method and is made.
The Chitosan powder is the side by water-soluble chitosan oligomer acid solution and silver chlorate with mass ratio for 4:1
Formula carries out room temperature mixing, stirring 35min, is then put into the hydro-thermal reaction that 110 DEG C of 18h are carried out in reaction kettle, takes out, is centrifuged, is dry
Prepared by dry.
Embodiment 4
A kind of preparation method of the exterior coating agent of high-adhesion, comprising the following steps:
S1. epoxy resin, precipitated calcium carbonate, SiO 2 powder and pigments and fillers are subjected to ball milling in the ball mill in proportion
3h takes out, and the water that formula ratio is added is stirred in quick peeler, obtains slurry；
S2. polyvinyl alcohol with low degree of polymerization, polyvinyl butyral and crosslinking agent are added in quick peeler, at 70 DEG C
Under be stirred 30min, poly-dopamine is added and stirs 20min；Stirring 1h is added in slurry obtained by S1 again；
S3. 40 DEG C are cooled to, Chitosan powder is added and stirs 10min, is down to room temperature, antifreezing agent is added, is stirred
10min to get high-adhesion exterior coating agent.
Further, the stirring rate of the quick peeler is 500r/min.
Embodiment 5
A kind of preparation method of the exterior coating agent of high-adhesion, comprising the following steps:
S1. epoxy resin, precipitated calcium carbonate, SiO 2 powder and pigments and fillers are subjected to ball milling in the ball mill in proportion
5h takes out, and the water that formula ratio is added is stirred in quick peeler, obtains slurry；
S2. polyvinyl alcohol with low degree of polymerization, polyvinyl butyral and crosslinking agent are added in quick peeler, at 80 DEG C
Under be stirred 50min, poly-dopamine is added and stirs 30min；Stirring 1.5h is added in slurry obtained by S1 again；
S3. 50 DEG C are cooled to, Chitosan powder is added and stirs 15min, is down to room temperature, antifreezing agent is added, is stirred
20min to get high-adhesion exterior coating agent.
Further, the stirring rate of the quick peeler is 500r/min.
Embodiment 6
A kind of preparation method of the exterior coating agent of high-adhesion, comprising the following steps:
S1. epoxy resin, precipitated calcium carbonate, SiO 2 powder and pigments and fillers are subjected to ball milling in the ball mill in proportion
4h takes out, and the water that formula ratio is added is stirred in quick peeler, obtains slurry；
S2. polyvinyl alcohol with low degree of polymerization, polyvinyl butyral and crosslinking agent are added in quick peeler, at 75 DEG C
Under be stirred 40min, poly-dopamine is added and stirs 25min；Stirring 1.2h is added in slurry obtained by S1 again；
S3. 45 DEG C are cooled to, Chitosan powder is added and stirs 12min, is down to room temperature, antifreezing agent is added, is stirred
15min to get high-adhesion exterior coating agent.
Further, the stirring rate of the quick peeler is 500r/min.
Embodiment 7
With embodiment 4, the dosage of the raw material is the same as embodiment 1.
Embodiment 8
With embodiment 4, the dosage of the raw material is the same as embodiment 2.
Embodiment 9
With embodiment 4, the dosage of the raw material is the same as embodiment 3.
Embodiment 10
With embodiment 5, the dosage of the raw material is the same as embodiment 1.
Embodiment 11
With embodiment 5, the dosage of the raw material is the same as embodiment 2.
Embodiment 12
With embodiment 5, the dosage of the raw material is the same as embodiment 3.
Embodiment 13
With embodiment 6, the dosage of the raw material is the same as embodiment 1.
Embodiment 14
With embodiment 6, the dosage of the raw material is the same as embodiment 2.
Embodiment 15
With embodiment 6, the dosage of the raw material is the same as embodiment 3.
As being detected to obtain table 1 to exterior coating obtained by embodiment 7~15, execution standard is the People's Republic of China (PRC)
Building material industry coating examination criteria GB/T9755-2001.
It provides to carry out fungus-proof test by GB/T1741, mould proof grade is up to 0 grade.
1 exterior coating performance of table
Exterior coating agent performance of the invention meets professional standard, and viscosity is good, and 450 hours are greater than in aging test not
It falls off, is not blistering, is flawless；Adhesive force grade is up to 1 grade.
Claims (6)
1. a kind of exterior coating agent of high-adhesion, which is characterized in that the raw material including following parts by weight: epoxy resin, lightweight
Calcium carbonate, poly-dopamine, antifreezing agent, Chitosan powder, polyvinyl alcohol, SiO 2 powder, polyvinyl butyral, face are filled out
Material, crosslinking agent and water；The Chitosan powder be water soluble chitosan and silver ion are mixed through hydro-thermal method make its load silver from
Son and be made.
2. a kind of exterior coating agent of high-adhesion as described in claim 1, which is characterized in that the original including following parts by weight
Material: 25~33 parts of epoxy resin, 10~13 parts of precipitated calcium carbonate, 3~5 parts of poly-dopamine, 1.5~2 parts of antifreezing agent, chitosan powder
1~2 part last, 2~4 parts of polyvinyl alcohol, 2~4 parts of SiO 2 powder, 10~12 parts of polyvinyl butyral, pigments and fillers 20~
28 parts, 4~6 parts of crosslinking agent and 64~99 parts of water；The Chitosan powder is to mix water soluble chitosan and silver ion through water
Thermal method makes its load silver ion and is made.
3. a kind of exterior coating agent of high-adhesion as described in claim 1, which is characterized in that the original including following parts by weight
Material: 30 parts of epoxy resin, 12 parts of precipitated calcium carbonate, 4 parts of poly-dopamine, 1.8 parts of antifreezing agent, 1.5 parts of Chitosan powder, oligomerization
Spend 3 parts of polyvinyl alcohol, 3 parts of SiO 2 powder, 11 parts of polyvinyl butyral, 24 parts of pigments and fillers, 5 parts of crosslinking agent and water 85
Part；The Chitosan powder is to mix water soluble chitosan and silver ion to make its load silver ion through hydro-thermal method and be made.
4. a kind of exterior coating agent of high-adhesion according to any one of claims 1 to 3, which is characterized in that the shell
Glycan powder is that water-soluble chitosan oligomer acid solution and silver chlorate are carried out room temperature in such a way that mass ratio is 3~5:1
Mixing, 30~40min of stirring, are then put into the hydro-thermal reaction that 100~120 DEG C of 16~20h are carried out in reaction kettle, take out, be centrifuged,
Prepared by drying.
5. a kind of preparation method of the exterior coating agent of high-adhesion according to any one of claims 1 to 3, feature exist
In, comprising the following steps:
S1. by epoxy resin, precipitated calcium carbonate, SiO 2 powder and pigments and fillers in proportion in the ball mill carry out ball milling 3~
5h takes out, and the water that formula ratio is added is stirred in quick peeler, obtains slurry；
S2. polyvinyl alcohol with low degree of polymerization, polyvinyl butyral and crosslinking agent are added in quick peeler, at 70~80 DEG C
Under be stirred 30~50min, poly-dopamine is added and stirs 20~30min；1~1.5h of stirring is added in slurry obtained by S1 again；
S3. 40~50 DEG C are cooled to, Chitosan powder is added and stirs 10~15min, is down to room temperature, antifreezing agent is added, is stirred
10~20min is mixed to get the exterior coating agent of high-adhesion.
6. a kind of preparation method of the exterior coating agent of high-adhesion as claimed in claim 5, which is characterized in that the high speed
The stirring rate of whirler is 500r/min.