CN109517466A - A kind of composite heat insulatant thermal insulation material that thermal coefficient low cost is low - Google Patents
A kind of composite heat insulatant thermal insulation material that thermal coefficient low cost is low Download PDFInfo
- Publication number
- CN109517466A CN109517466A CN201710850608.7A CN201710850608A CN109517466A CN 109517466 A CN109517466 A CN 109517466A CN 201710850608 A CN201710850608 A CN 201710850608A CN 109517466 A CN109517466 A CN 109517466A
- Authority
- CN
- China
- Prior art keywords
- low
- thermal
- composite heat
- thermal coefficient
- insulation material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of composite heat insulatant thermal insulation material that thermal coefficient low cost is low, it is characterized in that, it is grouped as by the group of following parts by weight percentage: acrylic emulsion 26%, styrene-acrylic emulsion 18%, fluorine silicone rubber 5%, calcium carbonate 15%, glass fibre 9%, fire retardant 2%, talcum powder 1.6%, film forming agent 1%, dispersing agent 0.02%, water 22.38%.Thermal-insulation coating effect of the present invention is good, thermal coefficient is low, coating is thin, construction cost is low.
Description
Technical field
The invention belongs to building material technical field, especially a kind of composite, insulating material that thermal coefficient low cost is low
Material.
Background technique
Building energy conservation increasingly payes attention to by country in this year, and building heat-insulation and heat-preservation is energy saving, improvement inhabitation
Environment and an importance for using function.Traditional heat insulating coating material for wall, big, easy to aging, volume change that there are water imbibitions
Greatly, cause product later strength low, be easy cracking, be unable to satisfy and build the demands such as water-fast to coating, weather-proof.Due to one-component
Heat insulating coatings weatherability, the performances such as anti-aging it is unsatisfactory, finding several composite heat insulation coatings can have
Effect makes up each defect, to reach the better thermal insulation coatings of performance.
Summary of the invention
The purpose of the present invention is to provide a kind of composite heat insulatant thermal insulation materials that thermal coefficient low cost is low.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of composite heat insulatant thermal insulation material that thermal coefficient low cost is low, which is characterized in that it is by following parts by weight percentage
Group is grouped as: acrylic emulsion 26%, styrene-acrylic emulsion 18%, fluorine silicone rubber 5%, calcium carbonate 15%, glass fibre 9%, fire retardant 2%,
Talcum powder 1.6%, film forming agent 1%, dispersing agent 0.02%, water 22.38%.
Beneficial effects of the present invention: thermal-insulation coating effect of the present invention is good, thermal coefficient is low, coating is thin, construction cost is low.
Specific embodiment
The invention will be further described combined with specific embodiments below.
A kind of composite heat insulatant thermal insulation material that thermal coefficient low cost is low, which is characterized in that it is by following parts by weight percentage
The group of ratio is grouped as: acrylic emulsion 26%, styrene-acrylic emulsion 18%, fluorine silicone rubber 5%, calcium carbonate 15%, glass fibre 9%, fire retardant
2%, talcum powder 1.6%, film forming agent 1%, dispersing agent 0.02%, water 22.38%.
Preparation method: the acrylic emulsion 26%, styrene-acrylic emulsion 18%, fluorine silicone rubber 5% of weight percent is taken to be mixed
It is even, water 22.38%, calcium carbonate 15%, glass fibre 9%, fire retardant 2%, talcum powder 1.6%, dispersing agent 0.02% are sequentially added, it is high
Speed stirs evenly, and is eventually adding film forming agent 1%, stands 2 hours and obtains coating of the present invention.
Claims (1)
1. a kind of composite heat insulatant thermal insulation material that thermal coefficient low cost is low, which is characterized in that it is by following parts by weight percentage
Group be grouped as: acrylic emulsion 26%, styrene-acrylic emulsion 18%, fluorine silicone rubber 5%, calcium carbonate 15%, glass fibre 9%, fire retardant
2%, talcum powder 1.6%, film forming agent 1%, dispersing agent 0.02%, water 22.38%.