CN109517251A - A kind of High-strength antibacterial type tubing - Google Patents
A kind of High-strength antibacterial type tubing Download PDFInfo
- Publication number
- CN109517251A CN109517251A CN201811449396.2A CN201811449396A CN109517251A CN 109517251 A CN109517251 A CN 109517251A CN 201811449396 A CN201811449396 A CN 201811449396A CN 109517251 A CN109517251 A CN 109517251A
- Authority
- CN
- China
- Prior art keywords
- parts
- bamboo charcoal
- antioxidant
- polyethylene
- pipeline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of High-strength antibacterial type tubing, its pipeline lining and pipeline outer-layer are made up of double-layer coextrusion, pipeline lining formula: 80~90 parts of polyethylene, 5~10 parts of Powdered Activated Carbon, 1~2 part of plasticizer, 1~2 part of antioxidant, 0.5~1 part of vinyltrimethoxysilane coupling agent, 1~2 part of stabilizer, 2~5 parts of glass fibre;Pipeline outer-layer is made by co-extrusion to by mesh cloth and polyethylene material, polyethylene material formula: 75~85 parts of ultra-high molecular weight polyethylene, 10~20 parts of epoxy resin, 1~10 part of bamboo charcoal Subnano-class micro mist, 1~2 part of antioxidant, 0.2~1 part of carbon fiber.The present invention joined active carbon, bamboo charcoal in the feed, pipeline obtained is enabled effectively to inhibit harmful bacteria, fungi and the growth of mould, meet health and health requirements, and pipeline outer-layer is made by co-extrusion to using mesh cloth with polyethylene, the corrosion resistance, impact strength, scratch resistance for strengthening pipeline outer-layer, have a vast market foreground.
Description
Technical field
The present invention relates to tubing technical fields, and in particular to a kind of High-strength antibacterial type tubing.
Background technique
In recent years, polyvinyl piping materials have become after PVC, in the world second largest plastic conduit kind of consumption figure, extensively
The necks such as engineerings and oil field, chemical industry and post and telecommunications such as general water supply, agricultural irrigation, fuel gas transmission, blowdown, the conveying of mine mortar
Domain.Existing polyvinyl piping materials exist following insufficient: one, degradation with aging occurs for tubing, easily becomes fragile, poor mechanical property, shock resistance
Bad, the poor rigidity of property;Two, antibiotic property effect is poor.
Summary of the invention
It is an object of the invention to: the above-mentioned technical problems in the prior art are directed to, a kind of high-intensitive antibacterial is provided
Type tubing.
The present invention is achieved by the following technical solutions:
A kind of High-strength antibacterial type tubing, including pipeline lining and pipeline outer-layer, the pipeline lining and pipeline outer-layer pass through double
Layer be made by co-extrusion to, the pipeline lining use following parts by weight raw material proportioning: 80~90 parts of polyethylene, Powdered Activated Carbon 5~
10 parts, 1~2 part of plasticizer, 1~2 part of antioxidant, 0.5~1 part of vinyltrimethoxysilane coupling agent, 1~2 part of stabilizer,
2~5 parts of glass fibre;The pipeline outer-layer is made by co-extrusion to by mesh cloth and polyethylene material, and polyethylene material uses following parts by weight
Raw material proportioning: 75~85 parts of ultra-high molecular weight polyethylene, 10~20 parts of epoxy resin, 1~10 part of bamboo charcoal Subnano-class micro mist,
1~2 part of antioxidant, 0.2~1 part of carbon fiber, mesh cloth is blended by silver fiber and polyester fiber.
Further, the pipeline lining uses the raw material proportioning of following parts by weight: 85~90 parts of polyethylene, Powdered Activated Carbon
6~8 parts, 1~2 part of plasticizer, 1~2 part of antioxidant, 0.5~0.6 part of vinyltrimethoxysilane coupling agent, stabilizer 2
Part, 2~3 parts of glass fibre;The polyethylene material uses the raw material proportioning of following parts by weight: ultra-high molecular weight polyethylene 78~80
Part, 15~20 parts of epoxy resin, 3~7 parts of bamboo charcoal Subnano-class micro mist, 1~2 part of antioxidant, 1 part of carbon fiber.
Further, the pipeline lining uses the raw material proportioning of following parts by weight: 87.5 parts of polyethylene, Powdered Activated Carbon 6
Part, 1 part of plasticizer, 1 part of antioxidant, 0.5 part of vinyltrimethoxysilane coupling agent, 2 parts of stabilizer, 2 parts of glass fibre;Institute
State the raw material proportioning that polyethylene material uses following parts by weight: 78 parts of ultra-high molecular weight polyethylene, 15 parts of epoxy resin, bamboo charcoal Asia are received
5 parts of meter level micro mist, 1 part of antioxidant, 1 part of carbon fiber.
Further, the antioxidant is the compound of the phenolic antioxidant that mass ratio is 3:2 and phosphite ester antioxidant.
Further, the stabilizer is ultraviolet-resistant absorbent.
Further, the Powdered Activated Carbon is active carbon of the partial size less than 10 μm.
Further, the bamboo charcoal Subnano-class micro mist is the bamboo charcoal for firing high temperature carbonization technology, utilizes normal-pressure radio-frequency cold
Plasma technique is modified bamboo charcoal, so that bamboo charcoal sufficiently etches embrittlement, concrete technology condition are as follows: incident power is
110W, argon flow 10L/min, sulfur hexafluoride flow are 15sccm, and sinking to the bottom temperature is 140 DEG C, and the processing time is 15min,
It may make that bamboo charcoal is sufficiently etched embrittlement, then with planetary ball mill ball milling repeatedly, so that bamboo charcoal micropowder, obtains partial size about
For 0.1-0.2 μm of bamboo carbon powder.
In conclusion by adopting the above-described technical solution, the beneficial effects of the present invention are:
Compared with prior art, the present invention joined active carbon, bamboo charcoal in the feed, and mesh cloth is by silver fiber and polyester fiber
It is blended, so that pipeline obtained has good deodorizing function, harmful bacteria, fungi and the growth of mould are effectively inhibited, is accorded with
Health and health requirements are closed, and pipeline outer-layer is made by co-extrusion to using mesh cloth with polyethylene, and pipeline outer-layer is further enhanced
Corrosion resistance, impact strength, scratch resistance, have a vast market foreground.
Specific embodiment
All features disclosed in this specification or disclosed all methods or in the process the step of, in addition to mutually exclusive
Feature and/or step other than, can combine in any way.
Any feature disclosed in this specification (including any accessory claim, abstract), unless specifically stated,
It is replaced by other equivalent or with similar purpose alternative features.That is, unless specifically stated, each feature is a series of
An example in equivalent or similar characteristics.
Embodiment 1
A kind of High-strength antibacterial type tubing, including pipeline lining and pipeline outer-layer, the pipeline lining and pipeline outer-layer pass through double
Layer is made by co-extrusion to, and the pipeline lining uses the raw material proportioning of following parts by weight: 80 parts of polyethylene, increases 10 parts of Powdered Activated Carbon
Mould 1 part of agent, 2 parts of antioxidant, 1 part of vinyltrimethoxysilane coupling agent, 1 part of stabilizer, 5 parts of glass fibre;The pipeline
Outer layer is made by co-extrusion to by mesh cloth and polyethylene material, and polyethylene material uses the raw material proportioning of following parts by weight: super high molecular weight is poly-
75 parts of ethylene, 20 parts of epoxy resin, 3 parts of bamboo charcoal Subnano-class micro mist, 1 part of antioxidant, 1 part of carbon fiber, mesh cloth is by silver fiber
It is blended with polyester fiber.
Wherein, the antioxidant is the compound of the phenolic antioxidant that mass ratio is 3:2 and phosphite ester antioxidant, surely
Determining agent is ultraviolet-resistant absorbent, and Powdered Activated Carbon is active carbon of the partial size less than 10 μm.
The bamboo charcoal Subnano-class micro mist is the bamboo charcoal for firing high temperature carbonization technology, utilizes normal-pressure radio-frequency cold plasma
Technology is modified bamboo charcoal, so that bamboo charcoal sufficiently etches embrittlement, concrete technology condition are as follows: incident power 110W, argon gas stream
Amount is 10L/min, and sulfur hexafluoride flow is 15sccm, and sinking to the bottom temperature is 140 DEG C, and the processing time is 15min, that is, may make bamboo charcoal
Sufficiently be etched embrittlement, and then with planetary ball mill ball milling repeatedly, so that bamboo charcoal micropowder, obtaining partial size is about 0.1-0.2 μm
Bamboo carbon powder.
Embodiment 2
A kind of High-strength antibacterial type tubing, including pipeline lining and pipeline outer-layer, the pipeline lining and pipeline outer-layer pass through double
Layer is made by co-extrusion to, and the pipeline lining uses the raw material proportioning of following parts by weight: 89 parts of polyethylene, 5 parts of Powdered Activated Carbon, plasticising
1 part of agent, 1 part of antioxidant, 1 part of vinyltrimethoxysilane coupling agent, 1 part of stabilizer, 2 parts of glass fibre;The polyethylene
Material uses the raw material proportioning of following parts by weight: 85 parts of ultra-high molecular weight polyethylene, 10 parts of epoxy resin, bamboo charcoal Subnano-class micro mist
3 parts, 1 part of antioxidant, 1 part of carbon fiber.
Wherein, the antioxidant is the compound of the phenolic antioxidant that mass ratio is 3:2 and phosphite ester antioxidant, surely
Determining agent is ultraviolet-resistant absorbent, and Powdered Activated Carbon is active carbon of the partial size less than 10 μm.
The bamboo charcoal Subnano-class micro mist is the bamboo charcoal for firing high temperature carbonization technology, utilizes normal-pressure radio-frequency cold plasma
Technology is modified bamboo charcoal, so that bamboo charcoal sufficiently etches embrittlement, concrete technology condition are as follows: incident power 110W, argon gas stream
Amount is 10L/min, and sulfur hexafluoride flow is 15sccm, and sinking to the bottom temperature is 140 DEG C, and the processing time is 15min, that is, may make bamboo charcoal
Sufficiently be etched embrittlement, and then with planetary ball mill ball milling repeatedly, so that bamboo charcoal micropowder, obtaining partial size is about 0.1-0.2 μm
Bamboo carbon powder.
Embodiment 3
A kind of High-strength antibacterial type tubing, including pipeline lining and pipeline outer-layer, the pipeline lining and pipeline outer-layer pass through double
Layer is made by co-extrusion to, and the pipeline lining uses the raw material proportioning of following parts by weight: 87.5 parts of polyethylene, increases 6 parts of Powdered Activated Carbon
Mould 1 part of agent, 1 part of antioxidant, 0.5 part of vinyltrimethoxysilane coupling agent, 2 parts of stabilizer, 2 parts of glass fibre;It is described poly-
Feed ethylene uses the raw material proportioning of following parts by weight: 78 parts of ultra-high molecular weight polyethylene, 15 parts of epoxy resin, bamboo charcoal Subnano-class
5 parts of micro mist, 1 part of antioxidant, 1 part of carbon fiber.
Wherein, the antioxidant is the compound of the phenolic antioxidant that mass ratio is 3:2 and phosphite ester antioxidant, surely
Determining agent is ultraviolet-resistant absorbent, and Powdered Activated Carbon is active carbon of the partial size less than 10 μm.
The bamboo charcoal Subnano-class micro mist is the bamboo charcoal for firing high temperature carbonization technology, utilizes normal-pressure radio-frequency cold plasma
Technology is modified bamboo charcoal, so that bamboo charcoal sufficiently etches embrittlement, concrete technology condition are as follows: incident power 110W, argon gas stream
Amount is 10L/min, and sulfur hexafluoride flow is 15sccm, and sinking to the bottom temperature is 140 DEG C, and the processing time is 15min, that is, may make bamboo charcoal
Sufficiently be etched embrittlement, and then with planetary ball mill ball milling repeatedly, so that bamboo charcoal micropowder, obtaining partial size is about 0.1-0.2 μm
Bamboo carbon powder.
Through detecting, the comparison of pipeline made from the raw material in the present embodiment 1-3: pipeline antibacterial effect made from embodiment 1 is most
Good, tensile strength, corrosion resistance are general, and pipeline tensile strength, corrosion resistance and antibacterial effect made from embodiment 2 are uniform
As, the comprehensive performance of pipeline tensile strength, shock resistance and antibacterial effect made from embodiment 3 is better than embodiment 1, embodiment
2。
Particular embodiments described above has carried out further in detail the purpose of the present invention, technical scheme and beneficial effects
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to restrict the invention.This
Invention expands to any new feature disclosed in the present specification or any new combination, and any new method for disclosing or
The step of process or any new combination.
Claims (10)
1. a kind of High-strength antibacterial type tubing, which is characterized in that including pipeline lining and pipeline outer-layer, the pipeline lining and pipe
Road outer layer is made up of double-layer coextrusion, and the pipeline lining uses the raw material proportioning of following parts by weight: 80~90 parts of polyethylene, powder
It is 5~10 parts of last active carbon, 1~2 part of plasticizer, 1~2 part of antioxidant, 0.5~1 part of vinyltrimethoxysilane coupling agent, steady
Determine 1~2 part of agent, 2~5 parts of glass fibre;The pipeline outer-layer is made by co-extrusion to by mesh cloth and polyethylene material, and polyethylene material uses
The raw material proportioning of following parts by weight: 75~85 parts of ultra-high molecular weight polyethylene, 10~20 parts of epoxy resin, bamboo charcoal Subnano-class are micro-
1~10 part of powder, 1~2 part of antioxidant, 0.2~1 part of carbon fiber, mesh cloth is blended by silver fiber and polyester fiber.
2. a kind of High-strength antibacterial type tubing as described in claim 1, which is characterized in that the pipeline lining is using following heavy
Measure the raw material proportioning of part: 85~90 parts of polyethylene, 6~8 parts of Powdered Activated Carbon, 1~2 part of plasticizer, 1~2 part of antioxidant, ethylene
0.5~0.6 part of base trimethoxysilane coupling agent, 2 parts of stabilizer, 2~3 parts of glass fibre;The polyethylene material is using following
The raw material proportioning of parts by weight: 78~80 parts of ultra-high molecular weight polyethylene, 15~20 parts of epoxy resin, bamboo charcoal Subnano-class micro mist 3
~7 parts, 1~2 part of antioxidant, 1 part of carbon fiber.
3. a kind of High-strength antibacterial type tubing as claimed in claim 1 or 2, which is characterized in that the pipeline lining use with
The raw material proportioning of lower parts by weight: 87.5 parts of polyethylene, 6 parts of Powdered Activated Carbon, 1 part of plasticizer, 1 part of antioxidant, vinyl front three
0.5 part of oxysilane coupling agent, 2 parts of stabilizer, 2 parts of glass fibre;The polyethylene material is matched using the raw material of following parts by weight
Than: 78 parts of ultra-high molecular weight polyethylene, 15 parts of epoxy resin, 5 parts of bamboo charcoal Subnano-class micro mist, 1 part of antioxidant, 1 part of carbon fiber.
4. a kind of High-strength antibacterial type tubing as claimed in claim 1 or 2, which is characterized in that the antioxidant is mass ratio
For the phenolic antioxidant of 3:2 and the compound of phosphite ester antioxidant.
5. a kind of High-strength antibacterial type tubing as claimed in claim 3, which is characterized in that the antioxidant is that mass ratio is 3:
2 phenolic antioxidant and the compound of phosphite ester antioxidant.
6. a kind of High-strength antibacterial type tubing as claimed in claim 1 or 2, which is characterized in that the stabilizer is uvioresistant
Light absorbers.
7. a kind of High-strength antibacterial type tubing as claimed in claim 3, which is characterized in that the stabilizer is uvioresistant suction
Receive agent.
8. a kind of High-strength antibacterial type tubing as claimed in claim 1 or 2, which is characterized in that the Powdered Activated Carbon is grain
Active carbon of the diameter less than 10 μm.
9. a kind of High-strength antibacterial type tubing as claimed in claim 1 or 2, which is characterized in that the bamboo charcoal Subnano-class is micro-
Powder is the bamboo charcoal for firing high temperature carbonization technology, is modified using normal-pressure radio-frequency cold plasma technology to bamboo charcoal, so that bamboo
Charcoal sufficiently etches embrittlement, concrete technology condition are as follows: incident power 110W, argon flow 10L/min, sulfur hexafluoride flow are
15sccm, sinking to the bottom temperature is 140 DEG C, and the processing time is 15min, that is, may make that bamboo charcoal is sufficiently etched embrittlement, then uses planet
Ball mill ball milling repeatedly, so that bamboo charcoal micropowder, obtains the bamboo carbon powder that partial size is about 0.1-0.2 μm.
10. a kind of High-strength antibacterial type tubing as claimed in claim 3, which is characterized in that the bamboo charcoal Subnano-class micro mist
It is the bamboo charcoal for firing high temperature carbonization technology, bamboo charcoal is modified using normal-pressure radio-frequency cold plasma technology, so that bamboo charcoal
Sufficiently etching embrittlement, concrete technology condition are as follows: incident power 110W, argon flow 10L/min, sulfur hexafluoride flow are
15sccm, sinking to the bottom temperature is 140 DEG C, and the processing time is 15min, that is, may make that bamboo charcoal is sufficiently etched embrittlement, then uses planet
Ball mill ball milling repeatedly, so that bamboo charcoal micropowder, obtains the bamboo carbon powder that partial size is about 0.1-0.2 μm.