CN109500933A - A kind of high-strength composite board manufacture craft - Google Patents
A kind of high-strength composite board manufacture craft Download PDFInfo
- Publication number
- CN109500933A CN109500933A CN201811542724.3A CN201811542724A CN109500933A CN 109500933 A CN109500933 A CN 109500933A CN 201811542724 A CN201811542724 A CN 201811542724A CN 109500933 A CN109500933 A CN 109500933A
- Authority
- CN
- China
- Prior art keywords
- proof
- moisture
- composite board
- strength composite
- material layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-strength composite board manufacture crafts, add water to mix sawdust, carpenter's rubber powder, being mixed into knead is advisable;The mixture that clamp mould bottom is half-soled to step (1) puts metal mesh, then a remaining semifused is laid on metal mesh, and starting press is pressed into synthesized wood material layer;The synthesized wood material layer suppressed is taken out to dry 3-5 days;Synthesized wood material layer upper layer and lower layer are pasted into moisture-proof bottom plate and moisture-proof upper plate using carpenter's glue, places into press to suppress 24 hours and be formed, further take out and dry;By the upper surface spraying abrasion-proof panel of moisture-proof upper plate.Compared with prior art, the present invention forms lumber layer using metal mesh and sawdust compacting, and not only waste utilization is more environmentally friendly, but also enhances intensity, moisture resistance, wearability and the toughness that plate is further increased in conjunction with two-sided moist-proof board and wearing plate, have the value of popularization and application.
Description
Technical field
The present invention relates to field of material technology more particularly to a kind of high-strength composite board manufacture crafts.
Background technique
Plate be earliest carpenter solid wood board, be used as and make furniture or other living facilities, in showing for development in science and technology
The definition of modern plate is very extensive, has the plate of unlike material in Furniture manufacture, construction industry, processing industry etc..In the prior art, greatly
Most wood planks are all using made of wooden unit and plank, and this material advantages are natural timbers, but the disadvantage is that toughness is lower, separately
Outside, there is the plate using sawdust compression moulding, this timber intensity is lower, and advantage is environmental protection, and accordingly, there exist rooms for improvement.
Summary of the invention
The object of the invention is that providing a kind of high-strength composite board manufacture craft to solve the above-mentioned problems.
The present invention through the following technical solutions to achieve the above objectives:
The present invention the following steps are included:
(1) water is added to mix sawdust, carpenter's rubber powder, being mixed into knead is advisable;
(2) mixture that clamp mould bottom is half-soled to step (1), puts metal mesh, then by a remaining meromict
Object is laid on metal mesh, and starting press is pressed into synthesized wood material layer;
(3) the synthesized wood material layer suppressed is taken out to dry 3-5 days;
(4) synthesized wood material layer upper layer and lower layer are pasted into moisture-proof bottom plate and moisture-proof upper plate using carpenter's glue, places into compacting
It suppresses 24 hours and is formed in machine, further take out and dry;
(5) by the upper surface spraying abrasion-proof panel of moisture-proof upper plate.
Preferably, the sawdust in the step (1) accounts for 85%, carpenter's rubber powder and accounts for 15%.
Preferably, the pressure of the step (2) is 2-2.5 tons, and pressure hold time is 10-15 minutes.
Preferably, the moisture-proof bottom plate is formed using silica gel material hot spraying cooling and shaping.
Preferably, the wear-resisting panel uses 25% polyamic acid resin, 5% carbon fiber, 5% white fused alumina, 8% aluminium oxide
Ultramicro-powder, 4% dimethylbenzene, 6% quartz sand, 6% zirconium oxide, 41% corrosion-resistant resin are sprayed by electrostatic painting process.
The beneficial effects of the present invention are:
The present invention is a kind of high-strength composite board manufacture craft, compared with prior art, the present invention using metal mesh with
Sawdust compacting forms lumber layer, and not only waste utilization is more environmentally friendly, but also enhances intensity, in conjunction with two-sided moist-proof board and wear-resisting
Plate further increases moisture resistance, wearability and the toughness of plate, has the value of popularization and application.
Detailed description of the invention
Fig. 1 is structural schematic diagram of the invention.
In figure: the moisture-proof bottom plate of 1-, 2- synthesized wood material layer, the moisture-proof upper plate of 3-, the wear-resisting panel of 4-.
Specific embodiment
The present invention will be further explained below with reference to the attached drawings:
As shown in Figure 1: the present invention the following steps are included:
(1) water is added to mix sawdust, carpenter's rubber powder, being mixed into knead is advisable;
(2) mixture that clamp mould bottom is half-soled to step (1), puts metal mesh, then by a remaining meromict
Object is laid on metal mesh, and starting press is pressed into synthesized wood material layer 2;
(3) the synthesized wood material layer suppressed is taken out to dry 3-5 days;
(4) synthesized wood material layer upper layer and lower layer are pasted into moisture-proof bottom plate 1 and moisture-proof upper plate 3 using carpenter's glue, places into pressure
It suppresses 24 hours and is formed in machine processed, further take out and dry;
(5) by the upper surface spraying abrasion-proof panel 4 of moisture-proof upper plate.
Preferably, the sawdust in the step (1) accounts for 85%, carpenter's rubber powder and accounts for 15%.
Preferably, the pressure of the step (2) is 2-2.5 tons, and pressure hold time is 10-15 minutes.
Preferably, the moisture-proof bottom plate is formed using silica gel material hot spraying cooling and shaping.
Preferably, the wear-resisting panel uses 25% polyamic acid resin, 5% carbon fiber, 5% white fused alumina, 8% aluminium oxide
Ultramicro-powder, 4% dimethylbenzene, 6% quartz sand, 6% zirconium oxide, 41% corrosion-resistant resin are sprayed by electrostatic painting process.
Basic principles and main features and advantages of the present invention of the invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (5)
1. a kind of high-strength composite board manufacture craft, it is characterised in that: the following steps are included:
(1) water is added to mix sawdust, carpenter's rubber powder, being mixed into knead is advisable;
(2) mixture that clamp mould bottom is half-soled to step (1) puts metal mesh, then a remaining semifused is spread
In on metal mesh, starting press is pressed into synthesized wood material layer;
(3) the synthesized wood material layer suppressed is taken out to dry 3-5 days;
(4) synthesized wood material layer upper layer and lower layer are pasted into moisture-proof bottom plate and moisture-proof upper plate using carpenter's glue, placed into press
It suppresses 24 hours and is formed, further take out and dry;
(5) by the upper surface spraying abrasion-proof panel of moisture-proof upper plate.
2. high-strength composite board manufacture craft according to claim 1, it is characterised in that: the wood in the step (1)
Bits account for 85%, carpenter's rubber powder and account for 15%.
3. high-strength composite board manufacture craft according to claim 1, it is characterised in that: the pressure of the step (2)
It is 2-2.5 tons, pressure hold time is 10-15 minutes.
4. high-strength composite board manufacture craft according to claim 1, it is characterised in that: the moisture-proof bottom plate uses silicon
Glue material hot spraying cooling and shaping forms.
5. high-strength composite board manufacture craft according to claim 1, it is characterised in that: the wear-resisting panel uses
25% polyamic acid resin, 5% carbon fiber, 5% white fused alumina, 8% aluminium oxide Ultramicro-powder, 4% dimethylbenzene, 6% quartz sand, 6%
Zirconium oxide, 41% corrosion-resistant resin are sprayed by electrostatic painting process.