CN109487567A - A kind of manufacturing method of multicoat waterproof cloth - Google Patents
A kind of manufacturing method of multicoat waterproof cloth Download PDFInfo
- Publication number
- CN109487567A CN109487567A CN201811170206.3A CN201811170206A CN109487567A CN 109487567 A CN109487567 A CN 109487567A CN 201811170206 A CN201811170206 A CN 201811170206A CN 109487567 A CN109487567 A CN 109487567A
- Authority
- CN
- China
- Prior art keywords
- coating
- waterproof
- multicoat
- drying
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of multicoat waterproof cloths, including base cloth layer, the top base of the base cloth layer is bonded with the first waterproof coating, and first waterproof coating is bonded with the second waterproof coating far from the side of base cloth layer, second waterproof coating is bonded matcoveredn far from the first waterproof coating, structure of the invention is compact, by the way that multilayer flashing layer is arranged, increase the waterproof effect of protection water cloth, multiple coating is carried out at different temperatures, can when the smooth flaw of waterproof cloth surface compact it is few, and have waterproof, fungus-resistant, environmental protection and other effects, increase the inoxidizability of waterproof cloth, extend its service life.
Description
Technical field:
The present invention relates to waterproof cloth technical field, in particular to a kind of manufacturing method of multicoat waterproof cloth.
Background technique:
Waterproof cloth is relatively conventional in the market, and waterproof cloth damp proof insulation needs in the manufacturing process of some waterproof cloths
Waterproof coating is added to it, the preparation of existing waterproof cloth can not increase the waterproof effect of protection water cloth, can not be in not equality of temperature
Degree is lower to carry out multiple coating, can not when the smooth flaw of waterproof cloth surface compact it is few, and do not have waterproof, fungus-resistant, ring
Protect and other effects, the inoxidizability of waterproof cloth can not be increased, its service life can not be extended.
Summary of the invention:
The object of the invention is that a kind of manufacturing method of multicoat waterproof cloth is provided to solve the above-mentioned problems,
It solves the problems, such as of the existing technology.
To solve the above-mentioned problems, the present invention provides a kind of technical solutions:
A kind of multicoat waterproof cloth, including base cloth layer, the top base of the base cloth layer are bonded with the painting of the first waterproof
Layer, and first waterproof coating is bonded with the second waterproof coating far from the side of base cloth layer, second waterproof coating is separate
First waterproof coating is bonded matcoveredn.
A kind of manufacturing method of multicoat waterproof cloth, described steps are as follows:
A, base fabric is weaved: base fabric is raw material by high-strength polyester fibers, and fiber number is 1300D~1500D；
B, prepared by coating agent: coating agent includes following mass parts composition: polyethylene pastes resin 20-60 parts, 50 parts of plasticizer-
100 parts, 1 part -2.5 parts of calcium zinc stabilizer, 10-50 parts of ultrafine aluminium hydroxide, 1 part -5 parts of ultraviolet absorbing agent, barium zinc stabilizer 1
- 5 parts, 1 part -50 parts of coarse whiting of part；
C, primary coating: taking above-mentioned b to obtain coating, and suitable crosslinking agent is added, and is sufficiently mixed uniformly prepares coating agent；
Coating agent is evenly applied to the front of base fabric first with coating machine and through vertical drying oven drying and processing, then existed using coating machine
The back side is coated with one layer of coating agent and drying and processing, when smearing, controls the movement velocity of coating machine, and control drying temperature and
Drying time；
D, coating agent secondary coating: is coated on the positive and anti-of the terylene base fabric after primary coating first with coating machine
Face and drying processing: when secondary smearing, the movement velocity of coating machine, and control drying temperature and drying time are controlled；
E, it is surface-treated: carrying out plasticizing forming after drying and processing after two secondary coatings, be then surface-treated；
F, clot after processing is completed is packed, storage.
Preferably, the density of base fabric is between per inch 10 × 10 to 20 × 20 in a.
Preferably, coarse whiting is 3000 mesh coarse whitings in the b.
Preferably, 240 to 340 nanometers of absorption region of ultraviolet light of the b middle-ultraviolet lamp absorbent.
Preferably, in the c coating machine movement velocity control be 6m/min, and drying temperature control 170 DEG C-
180℃。
Preferably, the coated weight control in the c is 130 square metres every gram.
Preferably, being added with crosslinking agent when the c is processed, and isocyanate content is 3% in the crosslinking agent.
Beneficial effects of the present invention: structure of the invention is compact, by the way that multilayer flashing layer is arranged, increases the anti-of protection water cloth
Water effect carries out multiple coating at different temperatures, can when the smooth flaw of waterproof cloth surface compact it is few, and have it is waterproof,
Fungus-resistant, environmental protection and other effects increase the inoxidizability of waterproof cloth, extend its service life.
Detailed description of the invention:
Detailed description will be given by the following detailed implementation and drawings by the present invention for ease of explanation,.
Fig. 1 is the structural diagram of the present invention.
In figure: 1- base cloth layer, the first waterproof coating of 2-, the second waterproof coating of 3-, 4- protective layer.
Specific embodiment:
As shown in Figure 1, present embodiment uses following technical scheme: a kind of multicoat waterproof cloth, including base fabric
Layer 1, the top base of the base cloth layer 1 is bonded with the first waterproof coating 2, and first waterproof coating 2 is far from base cloth layer 1
Side be bonded with the second waterproof coating 3, second waterproof coating 3 is bonded matcoveredn 4 far from the first waterproof coating 2.
A kind of manufacturing method of multicoat waterproof cloth, described steps are as follows:
A, base fabric is weaved: base fabric is raw material by high-strength polyester fibers, and fiber number is 1300D~1500D；
B, prepared by coating agent: coating agent includes following mass parts composition: polyethylene pastes resin 20-60 parts, 50 parts of plasticizer-
100 parts, 1 part -2.5 parts of calcium zinc stabilizer, 10-50 parts of ultrafine aluminium hydroxide, 1 part -5 parts of ultraviolet absorbing agent, barium zinc stabilizer 1
- 5 parts, 1 part -50 parts of coarse whiting of part；
C, primary coating: taking above-mentioned b to obtain coating, and suitable crosslinking agent is added, and is sufficiently mixed uniformly prepares coating agent；
Coating agent is evenly applied to the front of base fabric first with coating machine and through vertical drying oven drying and processing, then existed using coating machine
The back side is coated with one layer of coating agent and drying and processing, when smearing, controls the movement velocity of coating machine, and control drying temperature and
Drying time；
D, coating agent secondary coating: is coated on the positive and anti-of the terylene base fabric after primary coating first with coating machine
Face and drying processing: when secondary smearing, the movement velocity of coating machine, and control drying temperature and drying time are controlled；
E, it is surface-treated: carrying out plasticizing forming after drying and processing after two secondary coatings, be then surface-treated；
F, clot after processing is completed is packed, storage.
Wherein, in a density of base fabric between per inch 10 × 10 to 20 × 20.
Wherein, coarse whiting is 3000 mesh coarse whitings in the b.
Wherein, 240 to 340 nanometers of absorption region of ultraviolet light of the b middle-ultraviolet lamp absorbent.
Wherein, the movement velocity control of coating machine is 6m/min in the c, and drying temperature control is at 170 DEG C -180 DEG C.
Wherein, the coated weight control in the c is 130 square metres every gram.
Wherein, it is added with crosslinking agent when the c is processed, and isocyanate content is 3% in the crosslinking agent.
Embodiment 1, choosing base fabric density is 10 × 10, by coating by number including such as the following group；Component polyethylene pastes resin 30
Part, 50 parts of plasticizer, 1 part of calcium zinc stabilizer, ultrafine aluminium hydroxide 10,3 parts of ultraviolet absorbing agent, 4 parts of barium zinc stabilizer, coarse whiting
2 parts；
C, primary coating: suitable crosslinking agent is added in the coating after obtaining above-mentioned raw materials hybrid process, is sufficiently mixed
It is even, prepares coating agent；Coating agent is evenly applied to the front of base fabric first with coating machine and through vertical drying oven drying and processing, so
One layer of coating agent and drying and processing are overleaf coated with using coating machine afterwards, when smearing, control the movement velocity control of coating machine
For 7m/min, and drying temperature control is at 170 DEG C；
D, coating agent secondary coating: is coated on the positive and anti-of the terylene base fabric after primary coating first with coating machine
Face and drying processing: when secondary smearing, the movement velocity for controlling coating machine is 9m/min, and control drying temperature is 180
℃；
E, it is surface-treated: carrying out plasticizing forming after drying and processing after two secondary coatings, be then surface-treated；
F, clot after processing is completed is packed, storage.
Embodiment 2, choosing base fabric density is 20 × 20, by coating by number including such as the following group；Component polyethylene pastes resin 40
Part, 40 parts of plasticizer, 1 part of calcium zinc stabilizer, ultrafine aluminium hydroxide 5,3 parts of ultraviolet absorbing agent, 9 parts of barium zinc stabilizer, coarse whiting 2
Part；
C, primary coating: suitable crosslinking agent is added in the coating after obtaining above-mentioned raw materials hybrid process, is sufficiently mixed
It is even, prepares coating agent；Coating agent is evenly applied to the front of base fabric first with coating machine and through vertical drying oven drying and processing, so
One layer of coating agent and drying and processing are overleaf coated with using coating machine afterwards, when smearing, control the movement velocity control of coating machine
For 8m/min, and drying temperature control is at 190 DEG C；
D, coating agent secondary coating: is coated on the positive and anti-of the terylene base fabric after primary coating first with coating machine
Face and drying processing: when secondary smearing, the movement velocity for controlling coating machine is 6m/min, and control drying temperature is 160
℃；
E, it is surface-treated: carrying out plasticizing forming after drying and processing after two secondary coatings, be then surface-treated；
F, clot after processing is completed is packed, storage
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, the technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention, the claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (8)
1. a kind of multicoat waterproof cloth, including base cloth layer (1), which is characterized in that the top base of the base cloth layer (1) is viscous
It is connected to the first waterproof coating (2), and first waterproof coating (2) is bonded with the painting of the second waterproof far from the side of base cloth layer (1)
Layer (3), second waterproof coating (3) is far from the first waterproof coating (2) bonding matcoveredn (4).
2. a kind of manufacturing method of multicoat waterproof cloth, it is characterised in that: described steps are as follows:
A, base fabric is weaved: base fabric is raw material by high-strength polyester fibers, and fiber number is 1300D~1500D；
B, prepared by coating agent: coating agent includes following mass parts composition: polyethylene pastes resin 20-60 parts, 50 part -100 of plasticizer
Part, 1 part -2.5 parts of calcium zinc stabilizer, 10-50 parts of ultrafine aluminium hydroxide, 1 part -5 parts of ultraviolet absorbing agent, 1 part of barium zinc stabilizer -
5 parts, 1 part -50 parts of coarse whiting；
C, primary coating: taking above-mentioned b to obtain coating, and suitable crosslinking agent is added, and is sufficiently mixed uniformly prepares coating agent；First benefit
Coating agent is evenly applied to the front of base fabric with coating machine and through vertical drying oven drying and processing, then overleaf using coating machine
It is coated with one layer of coating agent and drying and processing, when smearing, controls the movement velocity of coating machine, and control drying temperature and drying
Time；
D, coating agent secondary coating: is coated on the obverse and reverse of the terylene base fabric after primary coating simultaneously first with coating machine
Drying processing: when secondary smearing, the movement velocity of coating machine, and control drying temperature and drying time are controlled；
E, it is surface-treated: carrying out plasticizing forming after drying and processing after two secondary coatings, be then surface-treated；
F, clot after processing is completed is packed, storage.
3. a kind of manufacturing method of multicoat waterproof cloth according to claim 1, it is characterised in that: base fabric in a
Density between per inch 10 × 10 to 20 × 20.
4. a kind of manufacturing method of multicoat waterproof cloth according to claim 1, it is characterised in that: coarse whiting in the b
It is 3000 mesh coarse whitings.
5. a kind of manufacturing method of multicoat waterproof cloth according to claim 1, it is characterised in that: ultraviolet in the b
240 to 340 nanometers of absorption region of ultraviolet light of light absorbers.
6. a kind of manufacturing method of multicoat waterproof cloth according to claim 1, it is characterised in that: be coated in the c
The movement velocity control of machine is 6m/min, and drying temperature control is at 170 DEG C -180 DEG C.
7. a kind of manufacturing method of multicoat waterproof cloth according to claim 2, it is characterised in that: the painting in the c
The amount of covering control is 130 square metres every gram.
8. a kind of manufacturing method of multicoat waterproof cloth according to claim 2, it is characterised in that: when the c is processed
Added with crosslinking agent, and in the crosslinking agent, isocyanate content is 3%.