CN109486428A - A kind of adhesion technique of aero seat foaming body and sticky cloth - Google Patents
A kind of adhesion technique of aero seat foaming body and sticky cloth Download PDFInfo
- Publication number
- CN109486428A CN109486428A CN201811517906.5A CN201811517906A CN109486428A CN 109486428 A CN109486428 A CN 109486428A CN 201811517906 A CN201811517906 A CN 201811517906A CN 109486428 A CN109486428 A CN 109486428A
- Authority
- CN
- China
- Prior art keywords
- foaming body
- adhesion
- parts
- sticky cloth
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the adhesion techniques of a kind of aero seat foaming body and sticky cloth, include the following steps: S1: producing heating visbreaking glue, material preparation is carried out first, S2: selection α-cyanoacrylate in parts by weight, curing agent, solvent, self-expanding microballoon foaming agent, chromatic timing powder, prezenta is put into agitator, S3: the foaming body for needing adhesion is surface-treated first, the protrusion on foaming body surface and side is wiped off using scraper, S4: gluing processing is carried out to the foaming body placed, S5: the sticky cloth that dedusting is finished carries out tensioning processing, S6: it will be dried in the adhesion object investment coating oven of foaming body and sticky cloth after sewing, the processing step is clear, implement easy to operate, the preparation for heating visbreaking glue first can guarantee the orderly progress of adhesion technique, it simultaneously can So that adhesion object intensity is high, good toughness.
Description
Technical field
The present invention relates to adhesion technology field more particularly to the adhesion works of a kind of aero seat foaming body and sticky cloth
Skill.
Background technique
Aviation, a kind of mankind's activity that is complicated and having strategic importance.Refer to flying activity of the aircraft in earth atmosphere,
And scientific research and education related to this, industrial manufacture, public transportation, professional operation, air transport, defense military, governability
Etc. various fields.By the utilization for air space and aircraft, aerospace activity can be subdivided into numerous independent industries and
Field, typically such as, aviation, Civil Aviation Industry etc..The production process of aero seat is more in aircraft industry
Important, in this process, need to carry out adhesion to aero seat foaming body and sticky cloth, traditional adhesion technical process is multiple
It is miscellaneous, and the adhesion object intensity of Adhesion formation is inadequate.
Summary of the invention
The invention proposes the adhesion techniques of a kind of aero seat foaming body and sticky cloth, to solve to mention in above-mentioned background technique
Out the problem of.
The invention proposes the adhesion techniques of a kind of aero seat foaming body and sticky cloth, include the following steps:
S1: heating visbreaking glue, first progress material preparation, 25~50 parts of α-cyanoacrylate, curing agent 1 are produced
~10 parts, 30~50 parts of solvent, 5~10 parts of self-expanding microballoon foaming agent, 2~8 parts of chromatic timing powder, 5~10 parts of prezenta, increasing
1~4 part of stick, 1~4 part of stabilizer, 1~3 part of toughener, 1~3 part of polymerization inhibitor.
S2: in parts by weight selection 30~40 parts of α-cyanoacrylate, 2~8 parts of curing agent, 30~40 parts of solvent,
5~10 parts of self-expanding microballoon foaming agent, 3~7 parts of chromatic timing powder in 5~10 parts of investment agitators of prezenta, are with revolving speed
350r/min~800r/min stirring 15min~35min obtains mixed liquor, and mixed liquor is allowed to stand 5min~10min, then
1~4 part of tackifier, 1~4 part of stabilizer, 1~3 part of toughener, 1~3 part of polymerization inhibitor are added, and into mixed liquor with revolving speed
5min~15min is stirred for 200r/min~600r/min and obtains heating visbreaking glue, is finally placed in obtained heating visbreaking glue
Temperature is that 10 DEG C~20 DEG C of interior is saved for future use.
S3: being first surface-treated the foaming body for needing adhesion, using scraper by the convex of foaming body surface and side
It rises and wipes off, while the sticky cloth for needing adhesion is dusted processing using air blower, will be surface-treated followed by shearing knife
Complete foaming body both ends are cut into be needed under foaming body during being cut with the mutually matched inclined surface of sticky cloth
End is laid with steel plate, and the width of steel plate is greater than the width of foaming body.
S4: carrying out gluing processing to the foaming body placed, need to maintain room temperature 10 DEG C~30 DEG C in gluing processing,
It is ready to produce the heating visbreaking glue finished in step S2, then with the suitable heating visbreaking glue of glue stick absorption is applied, heats visbreaking
Glue must not exceed 5mm~10mm in the thickness applied in glue stick, and then man-hour manually hand-held applies glue stick, and heating visbreaking glue is uniformly smeared
In foaming body, the heating visbreaking glue consistency of thickness on foaming body is kept at this time.
S5: the sticky cloth that dedusting is finished carries out tensioning processing, and heating visbreaking has been smeared in sticky cloth alignment during tensioning
The foaming body of glue then carries out adhesion, is beaten using rubber hammer to sticky cloth upper surface after completing adhesion, so that foaming
Body and sticky cloth complete adhesion, are finally sewed at the both ends of foaming body and sticky cloth.
S6: it will be dried in the adhesion object investment coating oven of foaming body and sticky cloth after sewing, baking temperature
At 100 DEG C~130 DEG C, baking time maintains 3min~10min for setting, and baking takes out the storehouse for being placed on ventilation after finishing
In, while daylight direct irradiation is prevented, the adhesion object being finally completed is in relaxed state 10h~12h in this way.
Preferably, the chromatic timing powder is the mixture of organic toner and inorganic toner, and organic toner and inorganic toner
Mass ratio is 1:2.
Preferably, since shearing knife is too thin in step S3, shearing knife needs that Steel Ruler is cooperated to use.
Preferably, it when being applied to foaming body using heating visbreaking glue in step S4 and need the outer surface of adhesion, needs to utilize
Heating visbreaking glue finishes outer surface covering, and smearing repeats aforesaid operations 3~5 times after finishing once.
Preferably, during rubber hammer beats sticky cloth upper surface in step S5, dynamics needs is beaten and are maintained
0.5Mpa~10Mpa.
The adhesion technique of a kind of aero seat foaming body and sticky cloth proposed by the present invention, beneficial effect are: the aero seat
The adhesion processing step of chair foaming body and sticky cloth is clear, implements easy to operate, and the preparation of heating visbreaking glue first can be protected
The orderly progress of adhesion technique is demonstrate,proved, while enabling to adhesion object intensity high, good toughness, the secondly adhesion of foaming body and sticky cloth
Journey is simple, can obtain the adhesion object of high quality.
Specific embodiment
It is next combined with specific embodiments below that the present invention will be further described.
Embodiment 1
The invention proposes the adhesion techniques of a kind of aero seat foaming body and sticky cloth, include the following steps:
S1: producing heating visbreaking glue, progress material preparation first, 25 parts of α-cyanoacrylate, 1 part of curing agent, molten
30 parts of agent, 5 parts of self-expanding microballoon foaming agent, 2 parts of chromatic timing powder, 5 parts of prezenta, 1 part of tackifier, 1 part of stabilizer, toughener
1 part, 1 part of polymerization inhibitor.
S2: selection 30 parts of α-cyanoacrylate, 2 parts of curing agent, 30 parts of solvent, self-expanding microballoon in parts by weight
5 parts of foaming agent, 3 parts of chromatic timing powder are that 350r/min stirs 15min and mixed with revolving speed in 5 parts of investment agitators of prezenta
Liquid is closed, and mixed liquor is allowed to stand 5min, 1 part of tackifier, 1 part of stabilizer, 1 part of toughener, resistance are then added into mixed liquor
1 part of poly- agent, and be that 200r/min stirring 5min obtains heating visbreaking glue with revolving speed, finally obtained heating visbreaking glue is placed in
Temperature is that 10 DEG C of interior is saved for future use.
S3: being first surface-treated the foaming body for needing adhesion, using scraper by the convex of foaming body surface and side
It rises and wipes off, while the sticky cloth for needing adhesion is dusted processing using air blower, will be surface-treated followed by shearing knife
Complete foaming body both ends are cut into be needed under foaming body during being cut with the mutually matched inclined surface of sticky cloth
End is laid with steel plate, and the width of steel plate is greater than the width of foaming body.
S4: gluing processing is carried out to the foaming body placed, needs to maintain room temperature into 10 DEG C in gluing processing, be ready to
The heating visbreaking glue finished is produced in step S2, then with the suitable heating visbreaking glue of glue stick absorption is applied, heating visbreaking glue is being applied
Thickness in glue stick must not exceed 5mm, and then man-hour manually hand-held applies glue stick, and heating visbreaking glue is uniformly applied to foaming body, this
When to keep heating visbreaking glue consistency of thickness on foaming body.
S5: the sticky cloth that dedusting is finished carries out tensioning processing, and heating visbreaking has been smeared in sticky cloth alignment during tensioning
The foaming body of glue then carries out adhesion, is beaten using rubber hammer to sticky cloth upper surface after completing adhesion, so that foaming
Body and sticky cloth complete adhesion, are finally sewed at the both ends of foaming body and sticky cloth.
S6: it will be dried in the adhesion object investment coating oven of foaming body and sticky cloth after sewing, baking temperature
Setting is at 100 DEG C, and baking time maintains 3min, and baking is taken out after finishing and is placed in the storehouse of ventilation, while to prevent
The adhesion object being finally completed is in relaxed state 10h in this way by daylight direct irradiation.
The chromatic timing powder is the mixture of organic toner and inorganic toner, and the mass ratio of organic toner and inorganic toner is
1:2。
Since shearing knife is too thin in step S3, shearing knife needs that Steel Ruler is cooperated to use.
When being applied to foaming body using heating visbreaking glue in step S4 and need the outer surface of adhesion, need to utilize heating visbreaking
Glue finishes outer surface covering, and smearing finishes primary repetition aforesaid operations 3 times later.
During rubber hammer beats sticky cloth upper surface in step S5, the dynamics of beating needs to maintain 0.5Mpa.
Embodiment 2
The invention proposes the adhesion techniques of a kind of aero seat foaming body and sticky cloth, include the following steps:
S1: produce heating visbreaking glue, first progress material preparation, 50 parts of α-cyanoacrylate, 10 parts of curing agent,
50 parts of solvent, 8 parts of chromatic timing powder, 10 parts of prezenta, 4 parts of tackifier, 4 parts of stabilizer, increases 10 parts of self-expanding microballoon foaming agent
Tough dose 3 parts, 3 parts of polymerization inhibitor.
S2: selection 40 parts of α-cyanoacrylate, 8 parts of curing agent, 40 parts of solvent, self-expanding microballoon in parts by weight
10 parts of foaming agent, 7 parts of chromatic timing powder are that 800r/min stirs 35min and obtains with revolving speed in 10 parts of investment agitators of prezenta
Mixed liquor, and allow mixed liquor stand 10min, then into mixed liquor addition 4 parts of tackifier, 4 parts of stabilizer, 3 parts of toughener,
3 parts of polymerization inhibitor, and be that 600r/min stirring 15min obtains heating visbreaking glue, the heating visbreaking glue that will finally obtain with revolving speed
The interior that temperature is 20 DEG C is placed in be saved for future use.
S3: being first surface-treated the foaming body for needing adhesion, using scraper by the convex of foaming body surface and side
It rises and wipes off, while the sticky cloth for needing adhesion is dusted processing using air blower, will be surface-treated followed by shearing knife
Complete foaming body both ends are cut into be needed under foaming body during being cut with the mutually matched inclined surface of sticky cloth
End is laid with steel plate, and the width of steel plate is greater than the width of foaming body.
S4: gluing processing is carried out to the foaming body placed, needs to maintain room temperature into 30 DEG C in gluing processing, be ready to
The heating visbreaking glue finished is produced in step S2, then with the suitable heating visbreaking glue of glue stick absorption is applied, heating visbreaking glue is being applied
Thickness in glue stick must not exceed 10mm, and then man-hour manually hand-held applies glue stick, and heating visbreaking glue is uniformly applied to foaming body, this
When to keep heating visbreaking glue consistency of thickness on foaming body.
S5: the sticky cloth that dedusting is finished carries out tensioning processing, and heating visbreaking has been smeared in sticky cloth alignment during tensioning
The foaming body of glue then carries out adhesion, is beaten using rubber hammer to sticky cloth upper surface after completing adhesion, so that foaming
Body and sticky cloth complete adhesion, are finally sewed at the both ends of foaming body and sticky cloth.
S6: it will be dried in the adhesion object investment coating oven of foaming body and sticky cloth after sewing, baking temperature
Setting is at 130 DEG C, and baking time maintains 10min, and baking is taken out after finishing and is placed in the storehouse of ventilation, while to prevent
The adhesion object being finally completed is in relaxed state 12h in this way by daylight direct irradiation.
The chromatic timing powder is the mixture of organic toner and inorganic toner, and the mass ratio of organic toner and inorganic toner is
1:2。
Since shearing knife is too thin in step S3, shearing knife needs that Steel Ruler is cooperated to use.
When being applied to foaming body using heating visbreaking glue in step S4 and need the outer surface of adhesion, need to utilize heating visbreaking
Glue finishes outer surface covering, and smearing finishes primary repetition aforesaid operations 5 times later.
During rubber hammer beats sticky cloth upper surface in step S5, the dynamics of beating needs to maintain 10Mpa.
Embodiment 3
The invention proposes the adhesion techniques of a kind of aero seat foaming body and sticky cloth, include the following steps:
S1: producing heating visbreaking glue, progress material preparation first, 40 parts of α-cyanoacrylate, 9 parts of curing agent, molten
40 parts of agent, 9 parts of self-expanding microballoon foaming agent, 7 parts of chromatic timing powder, 6 parts of prezenta, 2 parts of tackifier, 2 parts of stabilizer, toughener
2 parts, 2 parts of polymerization inhibitor.
S2: selection 20 parts of α-cyanoacrylate, 6 parts of curing agent, 35 parts of solvent, self-expanding microballoon in parts by weight
7 parts of foaming agent, 5 parts of chromatic timing powder are that 500r/min stirs 20min and mixed with revolving speed in 8 parts of investment agitators of prezenta
Liquid is closed, and mixed liquor is allowed to stand 6min, 2 parts of tackifier, 2 parts of stabilizer, 2 parts of toughener, resistance are then added into mixed liquor
2 parts of poly- agent, and be that 500r/min stirring 10min obtains heating visbreaking glue with revolving speed, finally obtained heating visbreaking glue is set
It is saved for future use in the interior that temperature is 15 DEG C.
S3: being first surface-treated the foaming body for needing adhesion, using scraper by the convex of foaming body surface and side
It rises and wipes off, while the sticky cloth for needing adhesion is dusted processing using air blower, will be surface-treated followed by shearing knife
Complete foaming body both ends are cut into be needed under foaming body during being cut with the mutually matched inclined surface of sticky cloth
End is laid with steel plate, and the width of steel plate is greater than the width of foaming body.
S4: gluing processing is carried out to the foaming body placed, needs to maintain room temperature into 20 DEG C in gluing processing, be ready to
The heating visbreaking glue finished is produced in step S2, then with the suitable heating visbreaking glue of glue stick absorption is applied, heating visbreaking glue is being applied
Thickness in glue stick must not exceed 6mm, and then man-hour manually hand-held applies glue stick, and heating visbreaking glue is uniformly applied to foaming body, this
When to keep heating visbreaking glue consistency of thickness on foaming body.
S5: the sticky cloth that dedusting is finished carries out tensioning processing, and heating visbreaking has been smeared in sticky cloth alignment during tensioning
The foaming body of glue then carries out adhesion, is beaten using rubber hammer to sticky cloth upper surface after completing adhesion, so that foaming
Body and sticky cloth complete adhesion, are finally sewed at the both ends of foaming body and sticky cloth.
S6: it will be dried in the adhesion object investment coating oven of foaming body and sticky cloth after sewing, baking temperature
Setting is at 120 DEG C, and baking time maintains 5min, and baking is taken out after finishing and is placed in the storehouse of ventilation, while to prevent
The adhesion object being finally completed is in relaxed state 11h in this way by daylight direct irradiation.
The chromatic timing powder is the mixture of organic toner and inorganic toner, and the mass ratio of organic toner and inorganic toner is
1:2。
Since shearing knife is too thin in step S3, shearing knife needs that Steel Ruler is cooperated to use.
When being applied to foaming body using heating visbreaking glue in step S4 and need the outer surface of adhesion, need to utilize heating visbreaking
Glue finishes outer surface covering, and smearing finishes primary repetition aforesaid operations 4 times later.
During rubber hammer beats sticky cloth upper surface in step S5, the dynamics of beating needs to maintain 5Mpa.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (5)
1. the adhesion technique of a kind of aero seat foaming body and sticky cloth, which comprises the following steps:
S1: heating visbreaking glue, first progress material preparation, 25~50 parts of α-cyanoacrylate, curing agent 1~10 are produced
Part, 30~50 parts of solvent, 5~10 parts of self-expanding microballoon foaming agent, 2~8 parts of chromatic timing powder, 5~10 parts of prezenta, tackifier
1~4 part, 1~4 part of stabilizer, 1~3 part of toughener, 1~3 part of polymerization inhibitor.
S2: in parts by weight 30~40 parts of α-cyanoacrylate of selection, 2~8 parts of curing agent, 30~40 parts of solvent, from swollen
5~10 parts of swollen microballoon foaming agent, 3~7 parts of chromatic timing powder are 350r/ with revolving speed in 5~10 parts of investment agitators of prezenta
Min~800r/min stirring 15min~35min obtains mixed liquor, and mixed liquor is allowed to stand 5min~10min, then toward mixed
It closes and 1~4 part of tackifier, 1~4 part of stabilizer, 1~3 part of toughener, 1~3 part of polymerization inhibitor is added in liquid, and be with revolving speed
200r/min~600r/min stirring 5min~15min obtains heating visbreaking glue, and obtained heating visbreaking glue is finally placed in temperature
Degree is saved for future use for 10 DEG C~20 DEG C of interior.
S3: being first surface-treated the foaming body for needing adhesion, is scraped the protrusion on foaming body surface and side using scraper
Fall, while the sticky cloth for needing adhesion is dusted processing using air blower, finishes surface treatment followed by shearing knife
Foaming body both ends are cut into be needed to spread in foaming body lower end with the mutually matched inclined surface of sticky cloth during being cut
If steel plate, and the width of steel plate is greater than the width of foaming body.
S4: gluing processing is carried out to the foaming body placed, needs to maintain room temperature 10 DEG C~30 DEG C in gluing processing, prepares
The heating visbreaking glue finished is produced in good step S2, then with the suitable heating visbreaking glue of glue stick absorption is applied, heating visbreaking glue exists
The thickness applied in glue stick must not exceed 5mm~10mm, and then man-hour manually hand-held applies glue stick, and heating visbreaking glue is uniformly applied to hair
Foam will keep the heating visbreaking glue consistency of thickness on foaming body at this time.
S5: the sticky cloth that dedusting is finished carries out tensioning processing, and heating visbreaking glue has been smeared in sticky cloth alignment during tensioning
Foaming body then carries out adhesion, is beaten using rubber hammer to sticky cloth upper surface after completing adhesion so that foaming body with
Sticky cloth completes adhesion, is finally sewed at the both ends of foaming body and sticky cloth.
S6: it will be dried in the adhesion object investment coating oven of foaming body and sticky cloth after sewing, baking temperature setting
At 100 DEG C~130 DEG C, baking time maintains 3min~10min, and baking is taken out after finishing and is placed in the storehouse of ventilation,
Daylight direct irradiation is prevented simultaneously, the adhesion object being finally completed is in relaxed state 10h~12h in this way.
2. the adhesion technique of a kind of aero seat foaming body and sticky cloth according to claim 1, it is characterised in that: the tune
Toner is the mixture of organic toner and inorganic toner, and the mass ratio of organic toner and inorganic toner is 1:2.
3. the adhesion technique of a kind of aero seat foaming body and sticky cloth according to claim 1, it is characterised in that: step S3
In due to shearing knife it is too thin, shearing knife needs that Steel Ruler is cooperated to use.
4. the adhesion technique of a kind of aero seat foaming body and sticky cloth according to claim 1, it is characterised in that: step S4
It is middle when being applied to foaming body using heating visbreaking glue and need the outer surface of adhesion, it needs to cover outer surface using heating visbreaking glue
It finishes, smearing finishes primary repetition aforesaid operations 3~5 times later.
5. the adhesion technique of a kind of aero seat foaming body and sticky cloth according to claim 1, it is characterised in that: step S5
During middle rubber hammer beats sticky cloth upper surface, the dynamics of beating needs to maintain 0.5Mpa~10Mpa.