CN109486307A - A kind of permeable pavement anti-skid surface - Google Patents
A kind of permeable pavement anti-skid surface Download PDFInfo
- Publication number
- CN109486307A CN109486307A CN201811353731.9A CN201811353731A CN109486307A CN 109486307 A CN109486307 A CN 109486307A CN 201811353731 A CN201811353731 A CN 201811353731A CN 109486307 A CN109486307 A CN 109486307A
- Authority
- CN
- China
- Prior art keywords
- agent
- permeable pavement
- protective agent
- quartz sand
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of permeable pavement anti-skid surfaces; the anti-skid surface includes the anti-slip layer set gradually from top to bottom and permeable pavement road surface; the anti-slip layer includes protective agent and quartz sand, and wherein protective agent includes the raw material of following mass fraction: acrylic resin 60~75%, film forming agent 2~5%; flocculation aid 2~4%; polyurethane 12~18%, propylene glycol 1~2%, pigment 6~10%; polyurethane curing agent 1~2%, defoaming agent 0.5~1.5%.The road surface not only ensure that protective agent to the dust-proof stabilization of porous pavement, but also enhanced the coefficient of sliding resistance on road surface, reduce the security risk of rainy day man-powered vehicle row.
Description
Technical field
The present invention relates to technical field of road construction, and in particular to a kind of permeable pavement anti-skid surface.
Background technique
With the increasingly popularization in China sponge city, permeable pavement area constantly expands, and is prepared by single graded aggregate
High pervious concrete appears in daily life, brings all various aspects.But traditional permeable pavement road surface connects with sole
The phenomenon that contacting surface product is small, and rainy day pedestrian falls down happens occasionally, and the skid resistance on road surface is affected.Common permeable pavement road surface
Skid resistance is only only solved by laying road surface material, single effect and can not be ensured.
Summary of the invention
In order to overcome the above technical defects, anti-skidding in the road surface the present invention provides a kind of permeable pavement anti-skid surface
In layer in such a way that protective agent is in conjunction with quartz sand, it not only ensure that protective agent to the dust-proof stabilization of porous pavement, but also enhanced road
The coefficient of sliding resistance in face reduces the security risk of rainy day man-powered vehicle row.
In order to reach above-mentioned technical effect, the present invention provides a kind of permeable pavement anti-skid surface, described includes being arrived from above
Under the anti-slip layer that sets gradually and permeable pavement road surface, the anti-slip layer includes protective agent and quartz sand, and wherein protective agent includes
The raw material of following mass fraction: acrylic resin 60~75%, film forming agent 2~5%, flocculation aid 2~4%, polyurethane 12~
18%, propylene glycol 1~2%, pigment 6~10%, polyurethane curing agent 1~2%, defoaming agent 0.5~1.5%.
Further technical solution is that the protective agent includes the raw material of following mass fraction: acrylic resin 63~
73%, film forming agent 3~5%, flocculation aid 2~3%, polyurethane 14~17%, propylene glycol 1~2%, pigment 8~10%, polyurethane
Curing agent 1.5~2%, defoaming agent 0.5~1%.
Further technical solution is, the anti-slip layer with a thickness of 2~4mm.
Further, the anti-slip layer with a thickness of 3mm.
Further technical solution is that the partial size of quartz sand is 70~90 mesh in the anti-slip layer, described protectant to add
Dosage 0.55~0.60kg/ ㎡, the additive amount of quartz sand are the 5% of protective agent additive amount.
Further, the partial size of quartz sand is 80 mesh, protectant additive amount 0.58kg/m in the anti-slip layer2。
Further technical solution is the method for paving on the permeable pavement road surface specifically: porous pavement pours compacting
Later, external coating a layer thickness is the protective agent of 0.2mm, and quartz sand uniformly sprays to one layer from spraying machine, to be protected dose,
After quartz sand stable solidification, then in one layer of protective agent of external coating.
Compared with prior art, the present invention having the following beneficial effects: that quartz sand is a kind of hard, wear-resisting, chemical property
Stable silicate mineral, anti-skidding using the difference progress between quartz sand size, antiskid effect is prominent, and good appearance, is not easy
Abrasion, can promote the anti-skid factor of porous pavement, combine quartz sand to form anti-slip layer with protective agent, both ensure that protective agent
To the dust-proof stabilization of porous pavement, and the coefficient of sliding resistance on road surface is enhanced, reduces the security risk of rainy day man-powered vehicle row, while more
Color protective agent can make the pattern of color multiplicity, beautify surrounding enviroment.Meanwhile the permeable pavement road surface of lower layer is more gaps knot
Structure can also solve the problems, such as urban waterlogging.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of permeable pavement anti-skid surface of the invention.
Specific embodiment
Embodiment 1
A kind of permeable pavement anti-skid surface, it is anti-skidding including the anti-slip layer set gradually from top to bottom and permeable pavement road surface
Layer includes protective agent and quartz sand, and wherein protective agent includes the raw material of following mass fraction: acrylic resin 70%, film forming agent
2%, flocculation aid 2%, polyurethane 12%, propylene glycol 2%, pigment 10%, polyurethane curing agent 1.5%, defoaming agent 0.5%.It is anti-
Slip layer with a thickness of 3mm.Protectant additive amount 0.55kg/m2, the additive amount of quartz sand is the 5% of protective agent additive amount, is prevented
The partial size of quartz sand is 70 mesh in slip layer, and permeable pavement road surface is multiple-void structure.The method for paving on the permeable pavement road surface
After pouring compacting for porous pavement, external coating a layer thickness is the protective agent of 0.2mm, from spraying machine uniformly by quartz sand
One layer of sprinkling, to be protected dose, after quartz sand stable solidification, then in one layer of protective agent of external coating.
Embodiment 2
A kind of permeable pavement anti-skid surface, it is anti-skidding including the anti-slip layer set gradually from top to bottom and permeable pavement road surface
Layer includes protective agent and quartz sand, and wherein protective agent includes the raw material of following mass fraction: acrylic resin 66%, film forming agent
3%, flocculation aid 4%, polyurethane 15%, propylene glycol 2%, pigment 7%, polyurethane curing agent 2%, defoaming agent 1%.Anti-slip layer
With a thickness of 2mm.Protectant additive amount 0.58kg/m2, the additive amount of quartz sand is the 5% of protective agent additive amount, in anti-slip layer
The partial size of quartz sand is 80 mesh, and permeable pavement road surface is multiple-void structure.The method for paving on the permeable pavement road surface is permeable
After road surface pours compacting, external coating a layer thickness is the protective agent of 0.2mm, and quartz sand is uniformly sprayed one from spraying machine
Layer, to be protected dose, after quartz sand stable solidification, then in one layer of protective agent of external coating.
Embodiment 3
A kind of permeable pavement anti-skid surface, it is anti-skidding including the anti-slip layer set gradually from top to bottom and permeable pavement road surface
Layer includes protective agent and quartz sand, and wherein protective agent includes the raw material of following mass fraction: acrylic resin 66%, film forming agent
4%, flocculation aid 2%, polyurethane 17%, propylene glycol 1%, pigment 8%, polyurethane curing agent 1.5%, defoaming agent 0.5%.It is anti-skidding
Layer with a thickness of 4mm.Protectant additive amount 0.60kg/m2, the additive amount of quartz sand is the 5% of protective agent additive amount, anti-skidding
The partial size of quartz sand is 90 mesh in layer, and permeable pavement road surface is multiple-void structure.The method for paving on the permeable pavement road surface is
After porous pavement pours compacting, external coating a layer thickness is the protective agent of 0.2mm, and quartz sand is uniformly sprayed from spraying machine
Spill one layer, to be protected dose, after quartz sand stable solidification, then in one layer of protective agent of external coating.
Although reference be made herein to invention has been described for explanatory embodiment of the invention, and above-described embodiment is only this hair
Bright preferable embodiment, embodiment of the present invention are not limited by the above embodiments, it should be appreciated that those skilled in the art
Member can be designed that a lot of other modification and implementations, these modifications and implementations will fall in principle disclosed in the present application
Within scope and spirit.
Claims (5)
1. a kind of permeable pavement anti-skid surface, which is characterized in that the anti-skid surface include set gradually from top to bottom it is anti-skidding
Layer and permeable pavement road surface, the anti-slip layer includes protective agent and quartz sand, and wherein protective agent includes the original of following mass fraction
Material: acrylic resin 60~75%, film forming agent 2~5%, flocculation aid 2~4%, polyurethane 12~18%, propylene glycol 1~2%,
Pigment 6~10%, polyurethane curing agent 1~2%, defoaming agent 0.5~1.5%.
2. permeable pavement anti-skid surface according to claim 1, which is characterized in that the protective agent includes following quality point
Several raw material: acrylic resin 63~73%, film forming agent 3~5%, flocculation aid 2~3%, polyurethane 14~17%, propylene glycol 1
~2%, pigment 8~10%, polyurethane curing agent 1.5~2%, defoaming agent 0.5~1%.
3. permeable pavement anti-skid surface according to claim 1, which is characterized in that the anti-slip layer with a thickness of 2~
4mm。
4. permeable pavement anti-skid surface according to claim 1, which is characterized in that the partial size of quartz sand in the anti-slip layer
For 70~90 mesh, protectant 0.55~0.60kg/kg/m of additive amount2, the additive amount of quartz sand is protective agent additive amount
5%.
5. permeable pavement anti-skid surface according to claim 1, which is characterized in that the method for paving of the anti-skid surface has
Body are as follows: after porous pavement pours compacting, external coating a layer thickness is the protective agent of 0.2mm, by quartz sand from spraying machine
Uniformly one layer of sprinkling, to be protected dose, after quartz sand stable solidification, then in one layer of protective agent of external coating.