CN109486059A - A kind of manufacturing method of sandals soles - Google Patents

A kind of manufacturing method of sandals soles Download PDF

Info

Publication number
CN109486059A
CN109486059A CN201811321418.7A CN201811321418A CN109486059A CN 109486059 A CN109486059 A CN 109486059A CN 201811321418 A CN201811321418 A CN 201811321418A CN 109486059 A CN109486059 A CN 109486059A
Authority
CN
China
Prior art keywords
raw material
completion
injection molding
sandals soles
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811321418.7A
Other languages
Chinese (zh)
Inventor
王九田
王九松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Gaoyou Qiangjie Plastic Products Co Ltd
Original Assignee
Gaoyou Qiangjie Plastic Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Gaoyou Qiangjie Plastic Products Co Ltd filed Critical Gaoyou Qiangjie Plastic Products Co Ltd
Priority to CN201811321418.7A priority Critical patent/CN109486059A/en
Publication of CN109486059A publication Critical patent/CN109486059A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of manufacturing methods of sandals soles, the following steps are included: pretreatment of raw material: carrying out ingredient according to the manufacture formula of sandals soles, suitable carbon dust is added in the raw material prepared after the completion of ingredient, and it is sufficiently mixed each raw material with carbon dust, cooling treatment is carried out to raw material after the completion of remixing and discharges;It is granulated: pretreated raw material being put into extruder, particle is made in raw material by extruder;Injection molding: being put into particle in injection molding machine, makes particle plasticizing, foaming, and demoulding processing is carried out shaping after the completion of foaming, forms sole blank;Moditied processing: modifying sole blank, after the completion of modification, carries out spray painting processing to sole blank, obtains finished product sandals soles.This method after Sole moulding by spray painting by way of formulate the color of sole, sandals soles are produced in enormous quantities in advance, to substantially increase delivery speed.

Description

A kind of manufacturing method of sandals soles
Technical field
The present invention relates to manufacture method of sole technical field, in particular to a kind of manufacturing method of sandals soles.
Background technique
With the raising of people's levels of substance, the change of aesthetic consciousness, the production type and scale of sandals have very big Variation, the competition in market is also more and more fierce, and colorant is added in ingredient for sandals soles color in the prior art, directly raw The sole of fixed color is produced into, but this method needs could be produced quantitatively after being connected to order, delivery rate is slower, thus Affect customer experience degree.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of manufacturing methods of sandals soles, cool in the prior art to solve Shoes sole cannot produce in advance, the slow technical problem of delivery rate.
To achieve the above object, the present invention provides a kind of manufacturing method of sandals soles, comprising the following steps:
S1, pretreatment of raw material: ingredient: 98 parts of PVC, dibasic lead phosphite 1, adjacent benzene is carried out according to following parts by weight 23 parts of dioctyl phthalate dibutyl ester, 23 parts of dibutyl phthalate, 10 parts of calcium carbonate, 0.3 part of hard acid rouge, 3 parts of three formula lead sulfate, Suitable carbon dust is added in the raw material prepared after the completion of ingredient, and make in 100 DEG C -120 DEG C of environment each raw material with Carbon dust is sufficiently mixed, and is carried out cooling treatment to the raw material after the completion of remixing and is discharged;
S2, granulation: the pretreated raw material is put into extruder, particle is made in the raw material by the extruder;
S3, injection molding: being put into the particle in injection molding machine, makes the particle plasticizing, foaming, and after the completion of foaming Demoulding processing is carried out shaping, sole blank is formed;
S4, moditied processing: modifying the sole blank, after the completion of modification, sprays to the sole blank Paint processing, obtains finished product sandals soles.
Further, the formula is composed of the following parts by weight in step sl: 98 parts of PVC, two alkali formulas are sub- Lead phosphate 1,23 parts of o-phthalic acid dibutyl ester, 23 parts of dibutyl phthalate, 10 parts of calcium carbonate, 0.3 part of hard acid rouge, three formulas 3 parts of lead sulfate.
Further, the raw material and the carbon dust are mixed in 110 DEG C of mixing machine in step sl, it is laggard Enter cooling mixing machine to discharge, the temperature of the cooling mixing machine is not higher than 40 DEG C.
Further, the extruder is successively made of feeding device, compression set and plasticizing apparatus in step s 2.
Further, the temperature of the feeding device is not less than 150 DEG C, and the temperature of the compression set is not less than 130 DEG C, The temperature of the plasticizing apparatus is not less than 100 DEG C.
Further, the injection molding machine is rotating disc type injection molding machine, the molding temperature of the rotating disc type injection molding machine in step s3 Degree is not less than 150 DEG C.
Further, the setting time is 1-2min in step s3.
Compared with prior art, present invention produces it is following the utility model has the advantages that a kind of sandals soles of the invention manufacturer Method, this method after Sole moulding by spray painting by way of formulate the color of sole so that sandals soles can be with Produce in enormous quantities in advance, painted after being connected to order according to order requirements, to substantially increase delivery speed.
Detailed description of the invention
Fig. 1 is flow chart of the invention;
Specific embodiment
Specific embodiments of the present invention will be further explained with reference to the accompanying drawing.It should be noted that for The explanation of these embodiments is used to help understand the present invention, but and does not constitute a limitation of the invention.In addition, disclosed below The each embodiment of the present invention involved in technical characteristic can be combined with each other as long as they do not conflict with each other.
Referring to Fig. 1, the preferred embodiment of the present invention one provides a kind of manufacturing method of sandals soles, including following step It is rapid:
S1, pretreatment of raw material: ingredient is carried out according to the manufacture formula of sandals soles, the formula is by following parts by weight Group is grouped as: 98 parts of PVC, dibasic lead phosphite 1,23 parts of o-phthalic acid dibutyl ester, 23 parts of dibutyl phthalate, 10 parts of calcium carbonate, 0.3 part of hard acid rouge, 3 parts of three formula lead sulfate are added in the raw material prepared suitable after the completion of ingredient Carbon dust is added in carbon dust in the feed, so that made sole is conductive, can play the role of antistatic, and 100 Each raw material is sufficiently mixed with carbon dust in DEG C -120 DEG C of environment, and cooling treatment is carried out to the raw material after the completion of remixing and is gone out Material, the raw material and carbon dust are sufficiently mixed in 110 DEG C of mixing machine, are entered cooling mixing machine later and are discharged, institute The temperature of cooling mixing machine is stated not higher than 40 DEG C;
The pretreated raw material: being put into extruder by S2, granulation, and particle is made in the raw material by the extruder, The extruder is successively made of feeding device, compression set and plasticizing apparatus.The temperature of the feeding device is not less than 150 DEG C, the temperature of the compression set is not less than 130 DEG C, and the temperature of the plasticizing apparatus is not less than 100 DEG C;In pelletization stage particle It generally does not require to be plasticized completely, avoids the generation of particle foamed phenomenon in production.
S3, injection molding: being put into the particle in rotating disc type injection molding machine, and rotating disc type injection molding machine has the spy of one machine with multi-mode Point, can greatly improve working efficiency, and the forming temperature of the rotating disc type injection molding machine is not less than 150 DEG C, and temperature when injection molding is No control is appropriate, directly affects the expansion ratio of foaming shoe, makes the particle plasticizing, foaming, and the gas release of larger sole should be controlled System is in 5-6mm, and the gas release of medium size should be controlled in 4-5mm, and the gas release of handle should be controlled in 3-4mm;And after the completion of foaming Demoulding processing is carried out shaping, setting time 1-2min, the specific time should determine according to shoes size, form sole blank;
S4, moditied processing: modifying the sole blank, after the completion of modification, sprays to the sole blank Paint processing, obtains finished product sandals soles, formulates the color of sole by way of spray painting after Sole moulding, so that cool Shoes sole can be produced in enormous quantities in advance, be painted after being connected to order according to order requirements, to substantially increase delivery Speed.
It can be seen from the above description that the above embodiments of the present invention realized the following chievements: this method is logical It crosses after Sole moulding and formulates the color of sole by way of spray painting, so that sandals soles can high-volume life in advance It produces, is painted after being connected to order according to order requirements, to substantially increase delivery speed.
In conjunction with attached drawing, the embodiments of the present invention are described in detail above, but the present invention is not limited to described implementations Mode.For a person skilled in the art, in the case where not departing from the principle of the invention and spirit, to these embodiments A variety of change, modification, replacement and modification are carried out, are still fallen in protection scope of the present invention.

Claims (6)

1. a kind of manufacturing method of sandals soles, which comprises the following steps:
S1, pretreatment of raw material: ingredient: 98 parts of PVC, dibasic lead phosphite 1, O-phthalic is carried out according to following parts by weight 23 parts of sour dibutyl ester, 23 parts of dibutyl phthalate, 10 parts of calcium carbonate, 0.3 part of hard acid rouge, 3 parts of three formula lead sulfate, in ingredient Suitable carbon dust is added in the raw material prepared after the completion, and makes each raw material and carbon dust in 100 DEG C -120 DEG C of environment It is sufficiently mixed, cooling treatment is carried out to the raw material after the completion of remixing and discharges;
S2, granulation: the pretreated raw material is put into extruder, particle is made in the raw material by the extruder;
S3, injection molding: being put into the particle in injection molding machine, makes the particle plasticizing, foaming, and carry out after the completion of foaming Demoulding of being formed is handled, and forms sole blank;
S4, moditied processing: modifying the sole blank, after the completion of modification, carries out at spray painting to the sole blank Reason, obtains finished product sandals soles.
2. a kind of manufacturing method of sandals soles according to claim 1, it is characterised in that: the raw material in step sl It is mixed in 110 DEG C of mixing machine with the carbon dust, enters cooling mixing machine later and discharge, the cooling mixing machine Temperature be not higher than 40 DEG C.
3. a kind of manufacturing method of sandals soles according to claim 1, it is characterised in that: the extrusion in step s 2 Machine is successively made of feeding device, compression set and plasticizing apparatus.
4. a kind of manufacturing method of sandals soles according to claim 3, it is characterised in that: the temperature of the feeding device Not less than 150 DEG C, the temperature of the compression set is not less than 130 DEG C, and the temperature of the plasticizing apparatus is not less than 100 DEG C.
5. a kind of manufacturing method of sandals soles according to claim 1, it is characterised in that: the injection molding in step s3 Machine is rotating disc type injection molding machine, and the forming temperature of the rotating disc type injection molding machine is not less than 150 DEG C.
6. a kind of manufacturing method of sandals soles according to claim 1, it is characterised in that: the sizing in step s3 Time is 1-2min.
CN201811321418.7A 2018-11-07 2018-11-07 A kind of manufacturing method of sandals soles Pending CN109486059A (en)