CN109483171A - A kind of construction method of titanium building materials - Google Patents
A kind of construction method of titanium building materials Download PDFInfo
- Publication number
- CN109483171A CN109483171A CN201811479045.6A CN201811479045A CN109483171A CN 109483171 A CN109483171 A CN 109483171A CN 201811479045 A CN201811479045 A CN 201811479045A CN 109483171 A CN109483171 A CN 109483171A
- Authority
- CN
- China
- Prior art keywords
- titanium
- construction method
- standard
- building materials
- finished product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of construction methods of titanium building materials, and steps are as follows for concrete construction method: step 1: titanium plate being cut into standard titanium mesh, long 1m, wide 50m by numerical control metal cutter；Step 2: the standard titanium mesh grab sample to completion is cut in step 1 carries out nondestructive inspection test and hardness test；Step 3: after test passes, titanium on-gauge plate obtains different surface configurations by the method for shot-peening；Step 4: by treated in step 3, standard titanium mesh uses anodizing, to standard titanium mesh surface coloring；Step 5: the titanium plate material finished product that step 4 is obtained carries out on-site assembly, and is welded between titanium plate material finished product by ultrasonic metal bonding machine, and entirety is linked to be；Step 6: the weld seam that construction surface is completed in welding in step 5 is subjected to polishing colouring processing.The construction method is relatively simple, less energy-consuming, and cost is relatively low for manpower and material resources, and then production efficiency is higher, is suitble to be widely popularized.
Description
Technical field
The invention belongs to the technical field of construction of titanium building materials, and in particular to a kind of construction method of titanium building materials.
Background technique
The corrosion resistance of titanium makes it unlike stainless steel, aluminium building materials, will repair and safeguard by 10 years or so.Although titanium
Processing and installation cost it is higher than stainless steel, but its long service life, from the point of view of standing cost, titanium building materials are most economical
, but existing titanium building materials weld strength after construction is equipped is inadequate, weld seam is not beautiful enough, cannot make building more after installation
Rich intention meets pursuit of the people to artistry, and existing construction technology is more complicated, and construction production efficiency is low.
Summary of the invention
The purpose of the present invention is to provide a kind of construction methods of titanium building materials, mentioned above in the background art existing to solve
Some titanium building materials weld strength after construction is equipped is inadequate, and weld seam is not beautiful enough, and the richer intention of building cannot be made after installation, full
Pursuit of the sufficient people to artistry, and existing construction technology is more complicated, the low problem of construction production efficiency.
To achieve the above object, the invention provides the following technical scheme: a kind of construction method of titanium building materials, Specific construction side
Steps are as follows for method:
Step 1: titanium plate is cut by standard titanium mesh, long 1m, wide 50m by numerical control metal cutter；
Step 2: the standard titanium mesh grab sample to completion is cut in step 1 carries out nondestructive inspection test and hardness is surveyed
Examination；
Step 3: after test passes, titanium on-gauge plate obtains different surface configurations by the method for shot-peening；
Step 4: by treated in step 3, standard titanium mesh uses anodizing, on standard titanium mesh surface
Color；
Step 5: the titanium plate material finished product that step 4 is obtained carries out on-site assembly, and passes through ultrasonic wave between titanium plate material finished product
Metal welding machine is welded, and entirety is linked to be；
Step 6: the weld seam that construction surface is completed in welding in step 5 is subjected to polishing colouring processing.
Further, numerical control metal cutter uses ZLQ-10A small-sized gantry formula numerical control cutting machine in the step 1, horizontal
Beam square tube 1*2m, lateral 2.5m, effectively cutting 2m；Longitudinal precision machined 20KG rail, effective 1.5m.
Further, nondestructive inspection is carried out using X-ray harmless flaw detector in the step 2, hardness test utilizes Richter scale
Hardometer tests hardness number.
Further, in the step 3 its work drum diameter of shot-blasting machine from 850 to 1100mm, highly from 1200 to
2100 mm, standard type have 2-6 ramming head, and maximum bearing capacity is up to 9000 kilograms.
Further, the step 4 Plays titanium plate is clipped on electrode, after immersing in electrolyte solution, in perseverance
Voltage is slowly increased in the case where constant current, in standard titanium plate surface growth protecting layer.
Further, eventually by manually painting in the step 6, color selection matches with titanium plate material finished product
Color.
Compared with prior art, the beneficial effects of the present invention are:
1, titanium plate is cut by standard titanium mesh by ZLQ-10A small-sized gantry formula numerical control cutting machine, long 1m is wide
50m, size is moderate, constructs convenient for in-site installation, and the cutting machine cutting efficiency is high, improves production efficiency.
2, nondestructive inspection test and hardness test are used for quickly detecting the dominant item of sheet metal, build the titanium of installation
Material is qualified products, the service life after improving installation.
3, titanium on-gauge plate obtains different surface configurations by the method for shot-peening, makes the richer intention of building, meets people
Pursuit to artistry, titanium is a kind of silver-gray metal, remains tone itself at normal temperature.Monastery is often selected
Titanium does roof, one of them important reason, which is also due to titanium roof, gives simple and unsophisticated, dignified, atmosphere impression.
4, the construction method is relatively simple, less energy-consuming, and cost is relatively low for manpower and material resources, and then production efficiency is higher, is suitble to wide
General popularization.
5, the weld seam that construction surface is completed in welding carries out polishing colouring processing, keeps construction surface weld seam finer, color can be with
The color that selection matches with titanium plate material finished product, effectively improves overall aesthetic degree.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
Embodiment 1
A kind of construction method of titanium building materials, steps are as follows for concrete construction method:
Step 1: titanium plate is cut by standard titanium mesh, long 1m, wide 50m by numerical control metal cutter；
Step 2: the standard titanium mesh grab sample to completion is cut in step 1 carries out nondestructive inspection test and hardness is surveyed
Examination；
Step 3: after test passes, titanium on-gauge plate obtains different surface configurations by the method for shot-peening；
Step 4: by treated in step 3, standard titanium mesh uses anodizing, on standard titanium mesh surface
Color；
Step 5: the titanium plate material finished product that step 4 is obtained carries out on-site assembly, and passes through ultrasonic wave between titanium plate material finished product
Metal welding machine is welded, and entirety is linked to be；
Step 6: the weld seam that construction surface is completed in welding in step 5 is subjected to polishing colouring processing.
Wherein, numerical control metal cutter uses ZLQ-10A small-sized gantry formula numerical control cutting machine, crossbeam side in the step 1
Pipe 1*2m, lateral 2.5m, effectively cutting 2m；Longitudinal precision machined 20KG rail, effective 1.5m can be lengthened arbitrarily.
Wherein, nondestructive inspection is carried out using X-ray harmless flaw detector in the step 2, hardness test utilizes lee ' hardness
Measurement examination hardness number.
Wherein, its work drum diameter of shot-blasting machine is from 850 to 1100mm in the step 3, highly from 1200 to 2100
Mm, standard type have 2-6 ramming head, and maximum bearing capacity is up to 9000 kilograms.
Wherein, the step 4 Plays titanium plate is clipped on electrode, after immersing in electrolyte solution, in constant electricity
Voltage is slowly increased in the case where stream, in standard titanium plate surface growth protecting layer.
Wherein, eventually by manually painting in the step 6, color selects the face to match with titanium plate material finished product
Color.
Embodiment 2
A kind of construction method of titanium building materials, steps are as follows for concrete construction method:
Step 1: titanium plate is cut by standard titanium mesh, long 1m, wide 50m by numerical control metal cutter；
Step 2: the standard titanium mesh grab sample to completion is cut in step 1 carries out nondestructive inspection test and hardness is surveyed
Examination；
Step 3: after test passes, titanium on-gauge plate obtains different surface configurations by the method for shot-peening；
Step 4: by treated in step 3, standard titanium mesh uses anodizing, on standard titanium mesh surface
Color；
Step 5: the titanium plate material finished product that step 4 is obtained carries out on-site assembly, and passes through ultrasonic wave between titanium plate material finished product
Metal welding machine is welded, and entirety is linked to be；
Step 6: the weld seam that construction surface is completed in welding in step 5 is subjected to polishing colouring processing.
Wherein, numerical control metal cutter uses ZLQ-10A small-sized gantry formula numerical control cutting machine, crossbeam side in the step 1
Pipe 1*2m, lateral 2.5m, effectively cutting 2m；Longitudinal precision machined 20KG rail, effective 1.5m can be lengthened arbitrarily.
Wherein, nondestructive inspection is carried out using X-ray harmless flaw detector in the step 2, hardness test utilizes lee ' hardness
Measurement examination hardness number.
Wherein, its work drum diameter of shot-blasting machine is from 850 to 1100mm in the step 3, highly from 1200 to 2100
Mm, standard type have 2-6 ramming head, and maximum bearing capacity is up to 9000 kilograms.
Wherein, the step 4 Plays titanium plate is clipped on electrode, after immersing in electrolyte solution, in constant electricity
Voltage is slowly increased in the case where stream, in standard titanium plate surface growth protecting layer.
Wherein, eventually by manually painting in the step 6, color selects the face to match with titanium plate material finished product
Color.
When the invention works: titanium plate is cut by standard titanium by ZLQ-10A small-sized gantry formula numerical control cutting machine
Metal plate, long 1m, wide 50m, size is moderate, constructs convenient for in-site installation, and the cutting machine cutting efficiency is high, improves production effect
Rate；Nondestructive inspection test and hardness test are used for quickly detecting the dominant item of sheet metal, close the titanium building materials of installation
Lattice product, the service life after improving installation；Titanium on-gauge plate obtains different surface configurations by the method for shot-peening, makes to build
The richer intention of object meets pursuit of the people to artistry, and titanium is a kind of silver-gray metal, remains color itself at normal temperature
It adjusts.Monastery often selects titanium to do roof, one of them important reason be also due to titanium roof give it is simple and unsophisticated, dignified,
The impression of atmosphere；The construction method is relatively simple, less energy-consuming, and cost is relatively low for manpower and material resources, and then production efficiency is higher, is suitble to wide
General popularization.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of construction method of titanium building materials, which is characterized in that steps are as follows for concrete construction method:
Step 1: titanium plate is cut by standard titanium mesh, long 1m, wide 50m by numerical control metal cutter；
Step 2: the standard titanium mesh grab sample to completion is cut in step 1 carries out nondestructive inspection test and hardness is surveyed
Examination；
Step 3: after test passes, titanium on-gauge plate obtains different surface configurations by the method for shot-peening；
Step 4: by treated in step 3, standard titanium mesh uses anodizing, on standard titanium mesh surface
Color；
Step 5: the titanium plate material finished product that step 4 is obtained carries out on-site assembly, and passes through ultrasonic wave between titanium plate material finished product
Metal welding machine is welded, and entirety is linked to be；
Step 6: the weld seam that construction surface is completed in welding in step 5 is subjected to polishing colouring processing.
2. a kind of construction method of titanium building materials according to claim 1, it is characterised in that: numerical control metal in the step 1
Cutting machine uses ZLQ-10A small-sized gantry formula numerical control cutting machine, crossbeam square tube 1*2m, lateral 2.5m, effectively cutting 2m；Longitudinal essence
The 20KG rail of close processing, effective 1.5m.
3. a kind of construction method of titanium building materials according to claim 1, it is characterised in that: penetrated in the step 2 using X
Line harmless flaw detector carries out nondestructive inspection, and hardness test tests hardness number using Leeb Hardness Tester.
4. a kind of construction method of titanium building materials according to claim 1, it is characterised in that: in the step 3 shot-blasting machine its
Drum diameter work from 850 to 1100mm, the highly mm from 1200 to 2100, standard type has 2-6 ramming head, and maximum is held
Carrying capacity is up to 9000 kilograms.
5. a kind of construction method of titanium building materials according to claim 1, it is characterised in that: the step 4 Plays titanium
Belong to board clamp on the electrode, after immersing in electrolyte solution, voltage is slowly increased in the case where constant current, in standard titanium
Belong to plate surface growth protecting layer.
6. a kind of construction method of titanium building materials according to claim 1, it is characterised in that: in the step 6 eventually by
Manually paint, the color that color selection matches with titanium plate material finished product.