CN109468854A - A kind of steaming of sweat takes fabric and its preparation process - Google Patents
A kind of steaming of sweat takes fabric and its preparation process Download PDFInfo
- Publication number
- CN109468854A CN109468854A CN201811212445.0A CN201811212445A CN109468854A CN 109468854 A CN109468854 A CN 109468854A CN 201811212445 A CN201811212445 A CN 201811212445A CN 109468854 A CN109468854 A CN 109468854A
- Authority
- CN
- China
- Prior art keywords
- fabric
- sweat
- steams
- parts
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of steaming of sweat and takes fabric and its preparation process, and the fabric successively includes cloth layer, foil layer from top to bottom；The cloth layer is knitting fabric or shuttle-woven fabric, and ingredient is terylene or nylon；The foil layer is that novel PU silver color sweat steams functional membrane.Fabric of the invention generates comprehensive heat radiation, there is heat storing and heat preserving after sweat steaming effect film is compound, weatherability good feature can quickly form the space that heat reflection between body surface recycles, promote body temperature in a short time between fabric and body surface when wearing, sweat gland is activated, sweat discharge is promoted.Internal extra body fat is converted to heat by fabric of the invention, is excreted, is discharged higher caloric energy.Fabric of the invention accelerates human metabolism's speed, and keeps intracorporal thermal balance and water balance, and has to reduce and lose warm effect.
Description
Technical field
The present invention relates to field of textile, it is specifically related to a kind of sweat steaming and takes fabric and its preparation process.
Background technique
Common composite material is generally made of TPU membrane at present, also only single to have wind-shielding function, is worn bored
Heat is also had and is made of hydrophily PU film, has certain waterproof and moisture-permeable function, but film absorbs easy swelling deformation after sweat.And
The fabric of this patent has heat storing and heat preserving, the good feature of weatherability, fabric and body surface when wearing after sweat steaming effect film is compound
Between form the space of heat reflection circulation, promote body temperature in a short time, activate sweat gland, promote sweat discharge；It will be extra in human body
Body fat is converted to heat, excretes, and discharges higher caloric energy；Accelerate human metabolism's speed, and in keeping body
Thermal balance and water balance, and have reduce lose temperature effect.
Current complex technique has been widely used in all kinds of garment materials.But the special silverskin technology in this patent,
One piece not only made has the Fashion of metal quality, even more with the functional health shell fabric of body beautification health efficacy.
Summary of the invention
In view of the above problems, the present invention, which provides a kind of steaming of sweat, takes fabric and its preparation process, by this patent combined processing
Fabric, other than with excellent water-proof function, and have promote body surface heat reflection circulation, activate sweat gland, send out human body
Sweat reaches a health-care slimming fabric that toxin expelling fat reducing is able to maintain body surface constant temperature again.
The technical scheme is that a kind of sweat steaming takes fabric, the fabric successively includes cloth layer, patch from top to bottom
Film layer；The cloth layer is knitting fabric or shuttle-woven fabric, and ingredient is terylene or nylon；The foil layer is novel PU
Silver color sweat steams functional membrane.
As further optimization, the sweat steams function and takes total grammes per square metre of fabric in 45-270g/m2。
As further optimization, the grammes per square metre of the cloth layer is in 30-250g/m2, the fabric of cloth layer is 20D-75D
Terylene or nylon facing material.
As further optimization, the novel PU silver color sweat steams the moisture permeability of functional membrane are as follows:
900g/m2.24H water pressure resistance are as follows: 3500 or more mm H2O。
As further optimization, the novel PU silver color sweat steams the metal film that function film outward appearance is silver color, applies it not
Volatilization is divided into 26-36%, and viscosity is 30-60dpas/25 DEG C, is made of DMF/EtAC, silver-containing rate is in 4-6%.
A kind of sweat steaming takes the preparation process of fabric, includes the following steps:
(1) various needle tattings the preparation of cloth layer: are prepared by weft machine or tricot machine or loom；
(2) the spill resistant processing of the fabric of cloth layer: waterproofing agent concentration is 40-80g/L, and used waterproofing agent is not fluorine-containing
Element, rolling the band liquid measure expected below by 2 leachings 1 is 40-70%, and the drying temperature of water-proofing treatment is 110-120 DEG C, drying time
For 2-3min；Baking temperature is 160-180 DEG C, drying time 40-60sec, and the spill resistant impact of performance is to 90 points or more；
(3) novel PU silver color sweat steams the preparation of functional membrane: including the following steps: that stirring-deaeration-filtering-release paper is scraped
Painting-drying-separation；Concrete operations are as follows: sequentially adding dimethylamino formamide, nanometer aluminium powder, second in polyurethane solution
Acetoacetic ester is stirred, and mixing speed is that 500-700 turns/min, and composite solution is made in compounding；Solution after compounding carries out vacuum
Deaeration, filtering, then scratches in release paper, and after drying, film and release paper are separated, and novel PU silver color sweat is made and steams function
Film；Wherein, the temperature of drying is 70-160 DEG C, trapezoidal to be successively set to: 70 DEG C -90 DEG C -140 DEG C -160 DEG C, each baking
The dry time is 1.5-2.0min, and the thickness 12-23um of film is made；
(4) laminating process: cloth layer is bonded, specific attaching process is as follows with foil layer: film is passed through into dotted hot melt
Glue is compound with fabric, and pass through dotted hot melt adhesive combination process: a. is transferred on film by the dotted engraved roll glue hot melt adhesive of hot melten type,
Then it is combined with each other with fabric, dotted combined temp is 95-120 DEG C, speed 20-30m/min；B. anti-by 48H moisture
Answer: after compound temperature be 35 DEG C ± 5 DEG C, humidity be 65% ± 5% environment in place 48h, hot melt adhesive is under moisture, sufficiently
Crosslinking, it is compound after film and fabric between peel strength reach 2.5N/cm or more, be formed with fabric and sweat that film is combined
Steaming takes fabric.
As further optimization, the waterproofing agent component is as follows: 10-30g/L resin a, 30-50g/L resin b, 3-
5g/L antistatic agent and for resin liquid pH value to be controlled citric acid between 4.5-6.
It include polysulfonate diimine 20-30 parts by weight, ether compound in the resin a as further optimization
1-5 parts by weight, alcohol compound 5-10 parts by weight, water 60-70 parts by weight.
As further optimization, the resin b includes wax 20-22 parts by weight, ether compound 1-5 parts by weight, water
75-80 parts by weight.
As further optimization, the components by weight percent that the novel PU silver color sweat steams functional membrane is as follows: solvent type fat
Polyurethane 21-26 parts of the same clan, 5-10 parts of nanometer aluminium powder, 20-30 parts of ethyl acetate, 50-60 parts of dimethylformamide.
Compared with prior art, beneficial effects of the present invention:
(1) fabric of the invention generates comprehensive heat radiation, there is heat storing and heat preserving, weatherability is good after sweat steaming effect film is compound
The characteristics of, the space that heat reflection between body surface recycles can be quickly formed when wearing between fabric and body surface, is mentioned in a short time
Body temperature is risen, sweat gland is activated, promotes sweat discharge.
(2) internal extra body fat is converted to heat by fabric of the invention, is excreted, is discharged higher calorie energy
Amount.
(3) fabric of the invention accelerates human metabolism's speed, and keeps intracorporal thermal balance and water balance, and have
Reduce the effect for losing temperature.
Detailed description of the invention
Attached drawing 1 is process flow diagram of the invention；
Attached drawing 2 is that #2450 cloth of the invention pastes common PU film and silver color sweat steaming functional membrane, the accumulation of heat done respectively respectively
Performance test comparison diagram；
Attached drawing 3 is that #1450 cloth of the invention pastes common PU film and silver color sweat steaming functional membrane, the accumulation of heat done respectively respectively
Performance test comparison diagram；
Attached drawing 4 is that #1830 cloth of the invention pastes common PU film and silver color sweat steaming functional membrane, the accumulation of heat done respectively respectively
Performance test comparison diagram.
Specific embodiment
Below in conjunction with drawings and examples, the present invention will be described in further detail.It should be appreciated that described herein
Specific examples are only used to explain the present invention, is not intended to limit the present invention.
Specific embodiment 1
A kind of steaming of sweat takes fabric, and the fabric successively includes cloth layer, foil layer from top to bottom；The cloth layer is
It is knitted fabric or shuttle-woven fabric, ingredient is terylene or nylon；The foil layer is that novel PU silver color sweat steams functional membrane.
The sweat steams function and takes total grammes per square metre of fabric in 45g/m2.The grammes per square metre of the cloth layer is in 30g/m2, cloth layer
Fabric be 20D terylene or nylon facing material.
The novel PU silver color sweat steams the moisture permeability of functional membrane are as follows: 900g/m2.24H, water pressure resistance are as follows: 3500 or more mm
H2O.The novel PU silver color sweat steams the metal film that function film outward appearance is silver color, and applying its non-volatile content is 26%, and viscosity is
It 30dpas/25 DEG C, is made of DMF/EtAC, silver-containing rate is 4%.
As shown in Figure 1, the sweat steams the preparation process for taking fabric, include the following steps:
(1) various needle tattings the preparation of cloth layer: are prepared by weft machine or tricot machine or loom；
(2) the spill resistant processing of the fabric of cloth layer: waterproofing agent concentration is 40g/L, the not fluorine-containing member of used waterproofing agent
Element, rolling the band liquid measure expected below by 2 leachings 1 is 40%, and the drying temperature of water-proofing treatment is 110 DEG C, drying time 2min；Roasting
Drying temperature is 160 DEG C, drying time 40sec, and the spill resistant impact of performance is to 90 points or more；
(3) novel PU silver color sweat steams the preparation of functional membrane: including the following steps: that stirring-deaeration-filtering-release paper is scraped
Painting-drying-separation；Concrete operations are as follows: sequentially adding dimethylamino formamide, nanometer aluminium powder, second in polyurethane solution
Acetoacetic ester is stirred, and mixing speed is 500 turns/min, and composite solution is made in compounding；Solution after compounding carries out vacuum defoamation,
Filtering, then scratches in release paper, and after drying, film and release paper are separated, and novel PU silver color sweat is made and steams functional membrane；Its
In, the temperature of drying is 70-160 DEG C, trapezoidal to be successively set to: 70 DEG C -90 DEG C -140 DEG C -160 DEG C, each drying time
For 1.5min, the thickness 12um of film is made；
(4) laminating process: cloth layer is bonded, specific attaching process is as follows with foil layer: film is passed through into dotted hot melt
Glue is compound with fabric, and pass through dotted hot melt adhesive combination process: a. is transferred on film by the dotted engraved roll glue hot melt adhesive of hot melten type,
Then it is combined with each other with fabric, dotted combined temp is 95 DEG C, speed 20m/min；B. it is reacted by 48H moisture: compound
Afterwards temperature be 30 DEG C, humidity be 60% environment in place 48h, hot melt adhesive is full cross-linked under moisture, it is compound after film with
Peel strength between fabric reaches 2.5N/cm or more, is formed with the sweat steaming that fabric and film are combined and takes fabric.
Wherein, the waterproofing agent component is as follows: 10g/L resin a, 30g/L resin b, 3g/L antistatic agent and being used for
Citric acid by the control of resin liquid pH value 4.5.
It include 20 parts by weight of polysulfonate diimine, 1 parts by weight of ether compound, 5 weight of alcohol compound in the resin a
Measure part, 60 parts by weight of water.
The resin b includes 20 parts by weight of wax, 1 parts by weight of ether compound, 75 parts by weight of water.
The components by weight percent that the novel PU silver color sweat steams functional membrane is as follows: 21 parts of solvent type aliphatic category polyurethane is received
5 parts of aluminium powder, 20 parts of ethyl acetate, 50 parts of dimethylformamide of rice.
Specific embodiment 2
A kind of steaming of sweat takes fabric, and the fabric successively includes cloth layer, foil layer from top to bottom；The cloth layer is
It is knitted fabric or shuttle-woven fabric, ingredient is terylene or nylon；The foil layer is that novel PU silver color sweat steams functional membrane.
The sweat steams function and takes total grammes per square metre of fabric in 270g/m2.The grammes per square metre of the cloth layer is in 250g/m2, face cloth
The fabric of layer is the terylene or nylon facing material of 75D.
The novel PU silver color sweat steams the moisture permeability of functional membrane are as follows: 900g/m2.24H, water pressure resistance are as follows: 3500 or more mm
H2O.The novel PU silver color sweat steams the metal film that function film outward appearance is silver color, and applying its non-volatile content is 36%, and viscosity is
It 60dpas/25 DEG C, is made of DMF/EtAC, silver-containing rate is 6%.
As shown in Figure 1, the sweat steams the preparation process for taking fabric, include the following steps:
(1) various needle tattings the preparation of cloth layer: are prepared by weft machine or tricot machine or loom；
(2) the spill resistant processing of the fabric of cloth layer: waterproofing agent concentration is 80g/L, the not fluorine-containing member of used waterproofing agent
Element, rolling the band liquid measure expected below by 2 leachings 1 is 70%, and the drying temperature of water-proofing treatment is 120 DEG C, drying time 3min；Roasting
Drying temperature is 180 DEG C, drying time 60sec, and the spill resistant impact of performance is to 90 points or more；
(3) novel PU silver color sweat steams the preparation of functional membrane: including the following steps: that stirring-deaeration-filtering-release paper is scraped
Painting-drying-separation；Concrete operations are as follows: sequentially adding dimethylamino formamide, nanometer aluminium powder, second in polyurethane solution
Acetoacetic ester is stirred, and mixing speed is 700 turns/min, and composite solution is made in compounding；Solution after compounding carries out vacuum defoamation,
Filtering, then scratches in release paper, and after drying, film and release paper are separated, and novel PU silver color sweat is made and steams functional membrane；Its
In, the temperature of drying is 70-160 DEG C, trapezoidal to be successively set to: 70 DEG C -90 DEG C -140 DEG C -160 DEG C, each drying time
For 2.0min, the thickness 23um of film is made；
(4) laminating process: cloth layer is bonded, specific attaching process is as follows with foil layer: film is passed through into dotted hot melt
Glue is compound with fabric, and pass through dotted hot melt adhesive combination process: a. is transferred on film by the dotted engraved roll glue hot melt adhesive of hot melten type,
Then it is combined with each other with fabric, dotted combined temp is 120 DEG C, speed 30m/min；B. it is reacted by 48H moisture: compound
Afterwards temperature be 40 DEG C, humidity be 70% environment in place 48h, hot melt adhesive is full cross-linked under moisture, it is compound after film with
Peel strength between fabric reaches 2.5N/cm or more, is formed with the sweat steaming that fabric and film are combined and takes fabric.
Wherein, the waterproofing agent component is as follows: 30g/L resin a, 50g/L resin b, 5g/L antistatic agent and being used for
Citric acid by the control of resin liquid pH value 6.
It include 30 parts by weight of polysulfonate diimine, 5 parts by weight of ether compound, alcohol compound 10 in the resin a
Parts by weight, 70 parts by weight of water.
The resin b includes 22 parts by weight of wax, 5 parts by weight of ether compound, 80 parts by weight of water.
The components by weight percent that the novel PU silver color sweat steams functional membrane is as follows: 26 parts of solvent type aliphatic category polyurethane is received
10 parts of aluminium powder, 30 parts of ethyl acetate, 60 parts of dimethylformamide of rice.
Specific embodiment 3
A kind of steaming of sweat takes fabric, and the fabric successively includes cloth layer, foil layer from top to bottom；The cloth layer is
It is knitted fabric or shuttle-woven fabric, ingredient is terylene or nylon；The foil layer is that novel PU silver color sweat steams functional membrane.
The sweat steams function and takes total grammes per square metre of fabric in 160g/m2.The grammes per square metre of the cloth layer is in 140g/m2, face cloth
The fabric of layer is the terylene or nylon facing material of 55D.
The novel PU silver color sweat steams the moisture permeability of functional membrane are as follows: 900g/m2.24H, water pressure resistance are as follows: 3500 or more mm
H2O.The novel PU silver color sweat steams the metal film that function film outward appearance is silver color, and applying its non-volatile content is 29%, and viscosity is
It 50dpas/25 DEG C, is made of DMF/EtAC, silver-containing rate is 5%.
As shown in Figure 1, the sweat steams the preparation process for taking fabric, include the following steps:
(1) various needle tattings the preparation of cloth layer: are prepared by weft machine or tricot machine or loom；
(2) the spill resistant processing of the fabric of cloth layer: waterproofing agent concentration is 60g/L, the not fluorine-containing member of used waterproofing agent
Element, rolling the band liquid measure expected below by 2 leachings 1 is 50%, and the drying temperature of water-proofing treatment is 113 DEG C, drying time 2.5min；
Baking temperature is 170 DEG C, drying time 50sec, and the spill resistant impact of performance is to 90 points or more；
(3) novel PU silver color sweat steams the preparation of functional membrane: including the following steps: that stirring-deaeration-filtering-release paper is scraped
Painting-drying-separation；Concrete operations are as follows: sequentially adding dimethylamino formamide, nanometer aluminium powder, second in polyurethane solution
Acetoacetic ester is stirred, and mixing speed is 600 turns/min, and composite solution is made in compounding；Solution after compounding carries out vacuum defoamation,
Filtering, then scratches in release paper, and after drying, film and release paper are separated, and novel PU silver color sweat is made and steams functional membrane；Its
In, the temperature of drying is 70-160 DEG C, trapezoidal to be successively set to: 70 DEG C -90 DEG C -140 DEG C -160 DEG C, each drying time
For 1.7min, the thickness 17um of film is made；
(4) laminating process: cloth layer is bonded, specific attaching process is as follows with foil layer: film is passed through into dotted hot melt
Glue is compound with fabric, and pass through dotted hot melt adhesive combination process: a. is transferred on film by the dotted engraved roll glue hot melt adhesive of hot melten type,
Then it is combined with each other with fabric, dotted combined temp is 112 DEG C, speed 24m/min；B. it is reacted by 48H moisture: compound
Afterwards temperature be 35 DEG C, humidity be 65% environment in place 48h, hot melt adhesive is full cross-linked under moisture, it is compound after film with
Peel strength between fabric reaches 2.5N/cm or more, is formed with the sweat steaming that fabric and film are combined and takes fabric.
Wherein, the waterproofing agent component is as follows: 20g/L resin a, 40g/L resin b, 4g/L antistatic agent and being used for
Citric acid by the control of resin liquid pH value 5.
It include 24 parts by weight of polysulfonate diimine, 3 parts by weight of ether compound, 7 weight of alcohol compound in the resin a
Measure part, 64 parts by weight of water.
The resin b includes 21 parts by weight of wax, 3 parts by weight of ether compound, 77 parts by weight of water.
The components by weight percent that the novel PU silver color sweat steams functional membrane is as follows: 24 parts of solvent type aliphatic category polyurethane is received
7 parts of aluminium powder, 26 parts of ethyl acetate, 53 parts of dimethylformamide of rice.
As in Figure 2-4, in the present invention, same fabric pastes common PU film and silver color sweat respectively and steams functional membrane, does respectively
Heat storage performance test, experimental condition: fabric damping: 20 DEG C of * 65%RH*12h or more；Irradiation distance: 30cm；Test: temperature passes
Sensor is placed among two pieces of samples, reflective light irradiation fabric surface, records 10min；Power of lamp tube: 500W.Lamp-type number:
PRF500W/D.The difference of comparison temperature.As a result as follows: silver color sweat steams the recovery electric heating system of functional membrane fabric obviously higher than normal film
Composite material.
Fabric of the invention generates comprehensive heat radiation, there is heat storing and heat preserving, the good spy of weatherability after sweat steaming effect film is compound
Point can quickly form the space that heat reflection between body surface recycles, in a short time lifting body between fabric and body surface when wearing
Temperature activates sweat gland, promotes sweat discharge.Internal extra body fat is converted to heat by fabric of the invention, is excreted, and release is more
High caloric energy.Fabric of the invention accelerates human metabolism's speed, and keeps intracorporal thermal balance and water balance,
And has to reduce and lose warm effect.
This practical preferred embodiment has shown and described in above description, as previously described, it should be understood that this practical not office
Be limited to form disclosed herein, should not be regarded as an exclusion of other examples, and can be used for various other combinations, modification and
Environment, and can be changed in practical contemplated scope described herein by the above teachings or related fields of technology or knowledge
It is dynamic.And changes and modifications made by those skilled in the art do not depart from this practical spirit and scope, then it all should be practical appended at this
In claims.
Claims (10)
1. a kind of sweat steaming takes fabric, it is characterised in that: the fabric successively includes cloth layer, foil layer from top to bottom；It is described
Cloth layer be knitting fabric or shuttle-woven fabric, ingredient is terylene or nylon；The foil layer is the steaming of novel PU silver color sweat
Functional membrane.
2. sweat steaming as described in claim 1 takes fabric, it is characterised in that: total grammes per square metre that the sweat steaming function takes fabric exists
45-270g/m2。
3. sweat steaming as described in claim 1 takes fabric, it is characterised in that: the grammes per square metre of the cloth layer is in 30-250g/m2, face
The fabric of layer of cloth is the terylene or nylon facing material of 20D-75D.
4. sweat steaming as described in claim 1 takes fabric, it is characterised in that: the novel PU silver color sweat steams the moisture-inhibiting of functional membrane
Degree are as follows: 900g/m2.24H, water pressure resistance are as follows: 3500 or more mm H2O。
5. sweat steaming as described in claim 1 takes fabric, it is characterised in that: the novel PU silver color sweat steams function film outward appearance and is
The metal film of silver color, applying its non-volatile content is 26-36%, and viscosity is 30-60dpas/25 DEG C, is made of DMF/EtAC, argentiferous
Rate is in 4-6%.
6. a kind of sweat as described in claim 1 steams the preparation process for taking fabric, characterized by the following steps:
(1) various needle tattings the preparation of cloth layer: are prepared by weft machine or tricot machine or loom；
(2) the spill resistant processing of the fabric of cloth layer: waterproofing agent concentration is 40-80g/L, the not fluorine-containing member of used waterproofing agent
Element, rolling the band liquid measure expected below by 2 leachings 1 is 40-70%, and the drying temperature of water-proofing treatment is 110-120 DEG C, and drying time is
2-3min；Baking temperature is 160-180 DEG C, drying time 40-60sec, and the spill resistant impact of performance is to 90 points or more；
(3) novel PU silver color sweat steams the preparation of functional membrane: including the following steps: stirring-deaeration-filtering-release paper blade coating-
Drying-separation；Concrete operations are as follows: sequentially adding dimethylamino formamide, nanometer aluminium powder, acetic acid second in polyurethane solution
Ester is stirred, and mixing speed is that 500-700 turns/min, and composite solution is made in compounding；Solution after compounding carries out vacuum defoamation,
Filtering, then scratches in release paper, and after drying, film and release paper are separated, and novel PU silver color sweat is made and steams functional membrane；Its
In, the temperature of drying is 70-160 DEG C, trapezoidal to be successively set to: 70 DEG C -90 DEG C -140 DEG C -160 DEG C, each drying time
For 1.5-2.0min, the thickness 12-23um of film is made；
(4) laminating process: cloth layer is bonded with foil layer, specific attaching process is as follows: by film by dotted hot melt adhesive with
Fabric is compound, and pass through dotted hot melt adhesive combination process: a. is transferred on film by the dotted engraved roll glue hot melt adhesive of hot melten type, then
It is combined with each other with fabric, dotted combined temp is 95-120 DEG C, speed 20-30m/min；B. it is reacted by 48H moisture: multiple
After conjunction temperature be 35 DEG C ± 5 DEG C, humidity be 65% ± 5% environment in place 48h, hot melt adhesive is full cross-linked under moisture,
The peel strength between film and fabric after compound reaches 2.5N/cm or more, is formed with the sweat that fabric and film are combined and steams clothes
Fabric.
7. sweat as claimed in claim 6 steams the preparation process for taking fabric, it is characterised in that: the waterproofing agent component is as follows:
10-30g/L resin a, 30-50g/L resin b, 3-5g/L antistatic agent and for by resin liquid pH value control between 4.5-6
Citric acid.
8. sweat as claimed in claim 7 steams the preparation process for taking fabric, it is characterised in that: include polysulfonate in the resin a
Change diimine 20-30 parts by weight, ether compound 1-5 parts by weight, alcohol compound 5-10 parts by weight, water 60-70 parts by weight.
9. sweat as claimed in claim 7 steams the preparation process for taking fabric, it is characterised in that: the resin b includes wax 20-22
Parts by weight, ether compound 1-5 parts by weight, water 75-80 parts by weight.
10. sweat as claimed in claim 7 steams the preparation process for taking fabric, it is characterised in that: the novel PU silver color sweat steams
The components by weight percent of functional membrane is as follows: 21-26 parts of solvent type aliphatic category polyurethane, and 5-10 parts of nanometer aluminium powder, ethyl acetate 20-30
Part, 50-60 parts of dimethylformamide.