CN109467823A - A kind of soft flame retardant automotive sheath - Google Patents
A kind of soft flame retardant automotive sheath Download PDFInfo
- Publication number
- CN109467823A CN109467823A CN201811138146.7A CN201811138146A CN109467823A CN 109467823 A CN109467823 A CN 109467823A CN 201811138146 A CN201811138146 A CN 201811138146A CN 109467823 A CN109467823 A CN 109467823A
- Authority
- CN
- China
- Prior art keywords
- parts
- soft
- flame retardant
- sheath
- sulphur
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The object of the present invention is to provide a kind of soft flame retardant automotive sheaths, it can have the fire-retardant function of soft by using the combination of ethylene propylene diene rubber, zinc oxide, stearic acid, N330 carbon black, paraffin oil, fire retardant, talcum powder, sulphur, promotor, and also add heat resistance accessory, anti-aging agent further promotes heat resistance and prevents old performance, entire formula soft halogen-free flameproof, meets the needs of automobile sheath well.
Description
Technical field
The present invention relates to rubber sheath field more particularly to a kind of soft flame retardant automotive sheaths.
Background technique
With the continuous development of society, the use of automobile is more and more important, and people increasingly pay attention to the safety of automobile.
It is needed on automobile using various harness, has various sheaths on harness, the use of sheath is particularly significant for the work of automobile, needs
Sheath has the function of that soft is fire-retardant.But the performance of current automobile sheath is bad, it is desirable to provide a kind of jacket formula.Cause
This solves the problems, such as that this is just seemed very necessary.
Summary of the invention
To solve the above problems, the present invention provides a kind of soft flame retardant automotive sheath, by using ethylene propylene diene rubber,
The combination of zinc oxide, stearic acid, N330 carbon black, paraffin oil, fire retardant, talcum powder, sulphur, promotor can have soft resistance
The function of combustion, and also addition heat resistance accessory, anti-aging agent further promote heat resistance and prevent old performance, solve background technique
The middle problem.
The object of the present invention is to provide a kind of soft flame retardant automotive sheaths, include the component material of following mass fraction:
90-110 parts of ethylene propylene diene rubber, 3-8 parts of zinc oxide, 1-3 parts of stearic acid, 15-25 parts of N330 carbon black, paraffin oil 55-65
Part, 55-65 parts of fire retardant, 55-65 parts of talcum powder, 1.0-1.5 parts of sulphur, 2.70-2.80 parts of promotor.
Further improvement lies in that: it further include having 2-5 parts of heat resistance accessory, 1-3 parts of anti-aging agent.
Further improvement lies in that: 100 parts of the ethylene propylene diene rubber, 5 parts of zinc oxide, 1 part of stearic acid, N330 carbon black 20
Part, 60 parts of paraffin oil, 60 parts of fire retardant, 60 parts of talcum powder, 1.2 parts of sulphur, 2.75 parts of promotor.
Beneficial effects of the present invention: the present invention is by using ethylene propylene diene rubber, zinc oxide, stearic acid, N330 carbon black, stone
The combination of wax oil, fire retardant, talcum powder, sulphur, promotor can have the fire-retardant function of soft, and also add heat-resisting help
Agent, anti-aging agent further promote heat resistance and prevent old performance, entire to be formulated soft halogen-free flameproof, meet vehicle protection well
The demand of set.
Specific embodiment
In order to deepen the understanding of the present invention, the present invention will be described in further detail with reference to the examples below, the embodiment
For explaining only the invention, it is not intended to limit the scope of the present invention..
Embodiment one:
The present embodiment provides a kind of soft flame retardant automotive sheaths, include the component material of following mass fraction: ethylene-propylene-diene monomer
90 parts of glue, 3 parts of zinc oxide, 2 parts of stearic acid, 15 parts of N330 carbon black, 55 parts of paraffin oil, 55 parts of fire retardant, 55 parts of talcum powder, sulphur
1.0 parts of sulphur, 2.70 parts of promotor.It further include having 2 parts of heat resistance accessory, 2 parts of anti-aging agent.
Embodiment two:
The present embodiment provides a kind of soft flame retardant automotive sheaths, include the component material of following mass fraction: ethylene-propylene-diene monomer
100 parts of glue, 5 parts of zinc oxide, 1 part of stearic acid, 20 parts of N330 carbon black, 60 parts of paraffin oil, 60 parts of fire retardant, 60 parts of talcum powder, sulphur
1.2 parts of sulphur, 2.75 parts of promotor.It further include having 3 parts of heat resistance accessory, 1 part of anti-aging agent.
Embodiment three:
The present embodiment provides a kind of soft flame retardant automotive sheaths, include the component material of following mass fraction:
110 parts of ethylene propylene diene rubber, 8 parts of zinc oxide, 3 parts of stearic acid, 25 parts of N330 carbon black, 65 parts of paraffin oil, fire retardant 65
Part, 65 parts of talcum powder, 1.5 parts of sulphur, 2.80 parts of promotor.It further include having 5 parts of heat resistance accessory, 3 parts of anti-aging agent.
By using ethylene propylene diene rubber, zinc oxide, stearic acid, N330 carbon black, paraffin oil, fire retardant, talcum powder, sulphur
The combination of sulphur, promotor can have the fire-retardant function of soft, and also add heat resistance accessory, anti-aging agent further promoted it is resistance to
Hot property and prevent old performance, it is entire to be formulated soft halogen-free flameproof, meet the needs of automobile sheath well.
Claims (3)
1. a kind of soft flame retardant automotive sheath, it is characterised in that: include the component material of following mass fraction:
90-110 parts of ethylene propylene diene rubber, 3-8 parts of zinc oxide, 1-3 parts of stearic acid, 15-25 parts of N330 carbon black, paraffin oil 55-65
Part, 55-65 parts of fire retardant, 55-65 parts of talcum powder, 1.0-1.5 parts of sulphur, 2.70-2.80 parts of promotor.
2. a kind of soft flame retardant automotive sheath as described in claim 1, it is characterised in that: further include have 2-5 parts of heat resistance accessory,
1-3 parts of anti-aging agent.
3. a kind of soft flame retardant automotive sheath as described in claim 1, it is characterised in that: the ethylene propylene diene rubber 100
Part, 5 parts of zinc oxide, 1 part of stearic acid, 20 parts of N330 carbon black, 60 parts of paraffin oil, 60 parts of fire retardant, 60 parts of talcum powder, sulphur 1.2
Part, 2.75 parts of promotor.