CN109464233A - Incontinence of faces ostomy bag and its manufacturing method - Google Patents
Incontinence of faces ostomy bag and its manufacturing method Download PDFInfo
- Publication number
- CN109464233A CN109464233A CN201811510795.5A CN201811510795A CN109464233A CN 109464233 A CN109464233 A CN 109464233A CN 201811510795 A CN201811510795 A CN 201811510795A CN 109464233 A CN109464233 A CN 109464233A
- Authority
- CN
- China
- Prior art keywords
- parts
- hydrocolloid
- incontinence
- faces
- ostomy bag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of incontinence of faces ostomy bag, hydrocolloid formula includes: 20-50 parts of water-soluble high-molecular materials, 10-30 parts of gelling agents, 5-20 parts of viscosity index improvers, 10-35 parts of film forming agents according to mass fraction；The hydrocolloid formula that ostomy bag of the invention uses can thicken lacquer disk(-sc), improve viscosity and imbibition ability, and can create wet environment for wound, enhance skin-friendliness.
Description
Technical field
The present invention relates to ostomy bag field, especially a kind of incontinence of faces ostomy bag and its manufacturing method.
Background technique
Existing hydrocolloid lacquer disk(-sc), the general Water-absorbing high polymer warp using having sticking rubber and with absorbent function
It crosses certain technique to be made, mainly pasting position is abdomen, and adhesive surface is relatively flat, to the tack requirements on stoma chassis
It is not very big.The moderate hydrocolloid lacquer disk(-sc) of this viscosity is not suitable for being pasted onto the more anus area of fold, therefore is badly in need of exploitation
A kind of paste performance is strong, and comfort is preferable, while the preferable stoma chassis of imbibition ability meets this demand, and the present invention solves
Such problems.
Summary of the invention
To solve the deficiencies in the prior art, the purpose of the present invention is to provide a kind of incontinence of faces ostomy bag and its manufacturers
Method, the hydrocolloid formula that ostomy bag uses can thicken lacquer disk(-sc), improve viscosity and imbibition ability, and can create moist ring for wound
Border enhances skin-friendliness.
In order to achieve the above objectives, the present invention adopts the following technical scheme that:
Incontinence of faces ostomy bag, hydrocolloid formula include: 20-50 parts of water-soluble high-molecular materials, 10- according to mass fraction
30 parts of gelling agents, 5-20 parts of viscosity index improvers, 10-35 parts of film forming agents.
Incontinence of faces ostomy bag above-mentioned, hydrocolloid formula include: 40 parts of water-soluble high-molecular materials according to mass fraction,
10 parts of gelling agents, 20 parts of viscosity index improvers, 30 parts of film forming agents.
Incontinence of faces ostomy bag above-mentioned, hydrocolloid formula include: 40 parts of cellulose derivatives according to mass fraction, and 10 parts
Pectin, 20 parts of hydrocarbon oil resins, 30 parts of one isoprene of styrene, one styrene.
The manufacturing method of incontinence of faces ostomy bag, includes the following steps:
Step 1 prepares material according to hydrocolloid formula；Hydrocolloid formula includes: 20-50 parts water-soluble according to mass fraction
Property high molecular material, 10-30 parts of gelling agents, 5-20 parts of viscosity index improvers, 10-35 parts of film forming agents；
Viscosity index improver and film forming agent, stirring melting are added at 120 DEG C -150 DEG C in mixer for step 2
20-40min；
Step 3 is cooled to 100 DEG C -130 DEG C, and water soluble polymer is added, and continuess to mix stirring 20-40min；
Step 4 continues to be cooled to 60 DEG C -90 DEG C, and gelling agent is added and continuess to mix the glue that discharges to obtain after stirring 20-40min
Body；
Step 5 takes the hydrocolloid to be pressed into hydrocolloid thin slice on molding equipment, covers backing film and separated type material, obtains
Stoma lacquer disk(-sc).
Step 2: the manufacturing method of incontinence of faces ostomy bag above-mentioned viscosity index (VI) is added in mixer and changes at 140 DEG C
Into agent and film forming agent, stirring melting 20-40min.
The manufacturing method of incontinence of faces ostomy bag above-mentioned, step 3 are cooled to 120 DEG C, and water soluble polymer is added, after
It is continuous that 30min is mixed.
The manufacturing method of incontinence of faces ostomy bag above-mentioned, step 4 continue to be cooled to 80 DEG C, and gelling agent is added and continues to mix
Close the hydrocolloid that discharges to obtain after stirring 30min.
The manufacturing method of incontinence of faces ostomy bag above-mentioned, the thickness range of hydrocolloid thin slice are as follows: 1.0mm-1.8mm.
The manufacturing method of incontinence of faces ostomy bag above-mentioned, the water imbibition range of hydrocolloid thin slice are as follows: 5645-5903g/
m2/24h。
The peel strength range of the manufacturing method of incontinence of faces ostomy bag above-mentioned, hydrocolloid thin slice and stainless steel plate is
17.2-19.3N/2.5cm。
The invention has the beneficial effects that:
The hydrocolloid formula that ostomy bag of the invention uses can thicken lacquer disk(-sc), the hydrocolloid thin slice after thickening with a thickness of
1.0mm-1.8mm；
The peel strength range of hydrocolloid formula raising viscosity, hydrocolloid thin slice and stainless steel plate is 17.2-19.3N/
2.5cm；
Hydrocolloid formula improves imbibition ability, the water imbibition range of hydrocolloid thin slice are as follows: 5645-5903g/m2/ for 24 hours, energy
Wet environment is created for wound, enhances skin-friendliness；
Total physical efficiency provides closed Moist healing environment for affected part.
Specific embodiment
Below in conjunction with detailed description of the invention by specific embodiments.
Incontinence of faces ostomy bag, hydrocolloid formula include: 20-50 parts of water-soluble high-molecular materials, 10- according to mass fraction
30 parts of gelling agents, 5-20 parts of viscosity index improvers, 10-35 parts of film forming agents.
As one embodiment, water soluble polymer can be cellulose and cellulose derivative, such as carboxymethyl cellulose
Sodium, carboxymethyl cellulose, cross-linked carboxymethyl cellulose, hydroxyethyl cellulose etc.；It is also possible to starch, such as primary or denaturation is formed sediment
Powder is also possible to the polymer such as sodium acrylate, polyvinyl alcohol.
As one embodiment, gelling agent can be biopolymer, such as xanthan gum；It is also possible to vegetable seeds powder, such as
Guar gum；It is also possible to plant extract, such as Arabic gum；It is also possible to animal class hydrophilic colloid, such as gelatin；It is also possible to
Pectin etc..
As one embodiment, viscosity index improver can be polyisobutene, Petropols, hydrogenated petroleum resin, terpene
Olefine resin, rosin resin etc..
As one embodiment, film forming agent can be one isoprene of styrene, one styrene (SIS), ethylene, propylene rubber
Glue, butadiene-styrene rubber (SBS) etc..
The manufacturing method of incontinence of faces ostomy bag, includes the following steps:
Step 1 prepares material according to hydrocolloid formula；Hydrocolloid formula includes: 20-50 parts water-soluble according to mass fraction
Property high molecular material, 10-30 parts of gelling agents, 5-20 parts of viscosity index improvers, 10-35 parts of film forming agents；
Viscosity index improver and film forming agent, stirring melting are added at 120 DEG C -150 DEG C in mixer for step 2
20-40min；As a preference, preferably 140 DEG C of temperature, the stirring melting time selects 30min.
Step 3 is cooled to 100 DEG C -130 DEG C, and water soluble polymer is added, and continuess to mix stirring 20-40min；As one
Preferably, preferably 120 DEG C of temperature, the stirring melting time selects 30min to kind.
Step 4 continues to be cooled to 60 DEG C -90 DEG C, and gelling agent is added and continuess to mix the glue that discharges to obtain after stirring 20-40min
Body；As a preference, preferably 80 DEG C of temperature, the stirring melting time selects 30min.
Step 5 takes the hydrocolloid to be pressed into hydrocolloid thin slice on molding equipment, covers backing film and separated type material, must make
Chewing-gum disk.
The thickness range of obtained hydrocolloid thin slice is manufactured in this way are as follows: 1.0mm-1.8mm.The water imbibition model of hydrocolloid thin slice
It encloses are as follows: 5645-5903g/m2/24h.The peel strength range of hydrocolloid thin slice and stainless steel plate is 17.2-19.3N/2.5cm.
Experimental verification part:
Embodiment 1: hydrocolloid formula includes: 200g water-soluble high-molecular material according to mass fraction, 100g gelling agent,
50g viscosity index improver, 100g film forming agent；The film forming agent of selection is the SIS product D1163 of Kraton, and viscosity index (VI) is improved
Agent is domestic C5 hydrocarbon oil resin, and water soluble polymer is the sodium carboxymethylcellulose CMC of U.S. Ashland company, gelling
Agent is import pectin.
Embodiment 2: hydrocolloid formula includes: 400g water-soluble high-molecular material according to mass fraction, 100 parts of gelling agents,
200g viscosity index improver, 300g film forming agent；The film forming agent of selection is the SIS product D1163 of Kraton, and viscosity index (VI) is improved
Agent is domestic C5 hydrocarbon oil resin, and water soluble polymer is the sodium carboxymethylcellulose CMC of U.S. Ashland company, gelling
Agent is import pectin.
Embodiment 3: hydrocolloid formula includes: 500g water-soluble high-molecular material according to mass fraction, 300g gelling agent,
200g viscosity index improver, 350g film forming agent；The film forming agent of selection is the SIS product D1163 of Kraton, and viscosity index (VI) is improved
Agent is domestic C5 hydrocarbon oil resin, and water soluble polymer is the sodium carboxymethylcellulose CMC of U.S. Ashland company, gelling
Agent is import pectin.
Hydrocolloid, the glue piece that hydrocolloid is made with a thickness of 1.0mm on molding machine, covering is made according to methodology above
PE film and release paper sheets obtain sample 1, sample 2, sample 3；
Experiment one: imbibition ability experiment
Water absorbing capacity test: 047 1.1-2004 contact Wound dressing test method part 1 of use < < Y Y/T: liquid
Absorbability > > in method carry out the test of hydrocolloid lacquer disk(-sc) water imbibition, specific data are as follows:
The result of sample 1:
The result of sample 2:
The result of sample 3:
Interpretation of result:
By experimental result as above it is found that the universal water absorbing properties of lacquer disk(-sc) produced with formula of the invention are good, with sample 2
Water absorbing properties it is best.
Experiment two: peel strength test:
Taking width is the batten of 25mm, and sample is pasted on to the centre of stainless steel plate, the both sides of sample is made to be parallel to steel plate
Two long sides, with roller to sample adhesive portion apply pressure, with the speed of about 60cm/min along specimen length direction roll
Four times, it is made to park 10min at normal atmospheric pressure.It is suitable between the 15%-85% of full scale with force value range of readings
Dynamometry instrument, measurement is from power required for steel sheet peeling off sample, and peel angle is 180 °, peeling rate 300mm/min.It sees
Survey the active force applied at first 25mm length.Every 30mm observes direct action power, takes the average value of six readings.To in addition
4 samples repeat above-mentioned test, take 5 sample means.Peel strength result is as follows:
The result of sample 1:
The result of sample 2:
The result of sample 3:
Interpretation of result:
By experimental result as above it is found that the lacquer disk(-sc) peel strength produced with formula of the invention is larger, with sample 2
Peel strength it is maximum.
Most highly preferred embodiment of the invention are as follows: hydrocolloid formula includes: 40 parts of cellulose derivatives according to mass fraction, and 10 parts
Pectin, 20 parts of hydrocarbon oil resins, 30 parts of one isoprene of styrene, one styrene.
The present invention provides a kind of incontinence of faces ostomy bag and its manufacturing method, and the hydrocolloid formula that ostomy bag uses can add
Thick lacquer disk(-sc) improves viscosity and imbibition ability, and can create wet environment for wound, enhances skin-friendliness.
The basic principles, main features and advantages of the invention have been shown and described above.The technical staff of the industry should
Understand, the above embodiments do not limit the invention in any form, all obtained by the way of equivalent substitution or equivalent transformation
Technical solution is fallen within the scope of protection of the present invention.
Claims (10)
1. incontinence of faces ostomy bag, which is characterized in that hydrocolloid formula includes: 20-50 parts of water-soluble high scores according to mass fraction
Sub- material, 10-30 parts of gelling agents, 5-20 parts of viscosity index improvers, 10-35 parts of film forming agents.
2. incontinence of faces ostomy bag according to claim 1, which is characterized in that hydrocolloid formula is according to mass fraction packet
It includes: 40 parts of water-soluble high-molecular materials, 10 parts of gelling agents, 20 parts of viscosity index improvers, 30 parts of film forming agents.
3. incontinence of faces ostomy bag according to claim 2, which is characterized in that hydrocolloid formula is according to mass fraction packet
It includes: 40 parts of cellulose derivatives, 10 parts of pectin, 20 parts of hydrocarbon oil resins, 30 parts of one isoprene of styrene, one styrene.
4. the manufacturing method of incontinence of faces ostomy bag, which comprises the steps of:
Step 1 prepares material according to hydrocolloid formula；Hydrocolloid formula includes: 20-50 parts of high water solubilities according to mass fraction
Molecular material, 10-30 parts of gelling agents, 5-20 parts of viscosity index improvers, 10-35 parts of film forming agents；
Viscosity index improver and film forming agent, stirring melting 20- are added at 120 DEG C -150 DEG C in mixer for step 2
40min；
Step 3 is cooled to 100 DEG C -130 DEG C, and water soluble polymer is added, and continuess to mix stirring 20-40min；
Step 4 continues to be cooled to 60 DEG C -90 DEG C, and gelling agent is added and continuess to mix the hydrocolloid that discharges to obtain after stirring 20-40min；
Step 5 takes the hydrocolloid to be pressed into hydrocolloid thin slice on molding equipment, covers backing film and separated type material, obtains stoma
Lacquer disk(-sc).
5. the manufacturing method of incontinence of faces ostomy bag according to claim 4, which is characterized in that step 2: at 140 DEG C
Viscosity index improver and film forming agent, stirring melting 30min are added in mixer.
6. the manufacturing method of incontinence of faces ostomy bag according to claim 4, which is characterized in that step 3 is cooled to 120
DEG C, water soluble polymer is added, continuess to mix stirring 30min.
7. the manufacturing method of incontinence of faces ostomy bag according to claim 4, which is characterized in that step 4 continues to cool down
To 80 DEG C, it is added after gelling agent continuess to mix stirring 30min and discharges to obtain hydrocolloid.
8. the manufacturing method of incontinence of faces ostomy bag according to claim 4, which is characterized in that the hydrocolloid thin slice
Thickness range are as follows: 1.0mm-1.8mm.
9. the manufacturing method of incontinence of faces ostomy bag according to claim 4, which is characterized in that the hydrocolloid thin slice
Water imbibition range are as follows: 5645-5903g/m2/24h。
10. the manufacturing method of incontinence of faces ostomy bag according to claim 4, which is characterized in that the hydrocolloid thin slice
Peel strength range with stainless steel plate is 17.2-19.3N/2.5cm.