CN109453676A - Two-sided hydrophilic film - Google Patents
Two-sided hydrophilic film Download PDFInfo
- Publication number
- CN109453676A CN109453676A CN201811560100.4A CN201811560100A CN109453676A CN 109453676 A CN109453676 A CN 109453676A CN 201811560100 A CN201811560100 A CN 201811560100A CN 109453676 A CN109453676 A CN 109453676A
- Authority
- CN
- China
- Prior art keywords
- hydrophilic film
- film
- substrate
- hydrophilic
- lower layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of two-sided hydrophilic films, including substrate, it is coated with upper layer hydrophilic film in the upper surface of substrate, is coated with lower layer's hydrophilic film in the lower surface of substrate, it is compounded with upper layer PE film in the upper layer hydrophilic film, lower layer's PE film is compounded in lower layer's hydrophilic film.Two-sided hydrophilic film of the invention can greatly improve the blood diffusion of blood sugar test paper hydrophilic film, in favor of further increasing the detection accuracy of blood glucose target.The hydrophilic coating solvent of the invention spirit solvent easily dry using low temperature avoids the destruction to PE film this makes it possible to using cold drying drying.
Description
Technical field
The present invention relates to a kind of two-sided hydrophilic films.
Background technique
In the detection of blood glucose quick diagnosis, blood sugar test paper has been widely used.In blood sugar test paper, detection accuracy is influenced
Other than oxidoreducing enzyme, conducting medium, there are also be exactly hydrophilic film.When tested blood sample drop is on blood sugar test paper, hydrophilic film energy
It is enough that drop of blood is quickly spread to and sucked electrode working zone, to ensure the progress of blood sugar test.
It, can only in the case where oxidoreducing enzyme, conducting medium have determined in order to improve the detection accuracy of blood sugar test paper
Improve the diffusion of hydrophilic film.The performance for how improving blood sugar test paper hydrophilic film, puts in face of those skilled in the art
One important topic.
Summary of the invention
The object of the present invention is to provide a kind of two-sided hydrophilic films, can greatly improve the blood diffusion of blood sugar test paper hydrophilic film
Performance, in favor of further increasing the detection accuracy of blood glucose target.
To achieve the above object, the present invention adopts the following technical scheme:
A kind of two-sided hydrophilic film, including substrate are coated with upper layer hydrophilic film in the upper surface of substrate, are coated in the lower surface of substrate
There is lower layer's hydrophilic film, upper layer PE film is compounded in the upper layer hydrophilic film, is compounded with lower layer PE in lower layer's hydrophilic film
Film.
The upper and lower layer hydrophilic film is to be dissolved in ethanol solution by fatty alcohol polyoxyethylene ether to be coated on the substrate table
The film formed behind face through low temperature drying.
The substrate is made of PET material.
Compared with prior art the beneficial effects of the present invention are: the present invention to change the prior art hydrophilic in substrate one side coating
The structure of film is coated with hydrophilic film in the upper and lower faces of substrate for the first time, and this structure can spread blood sample from upper and lower surface
To detection zone, substantially increase the blood diffusion of blood sugar test paper hydrophilic film, thus improve blood diffusion reliability and
Validity is conducive to the detection accuracy for improving blood glucose target.
Existing blood sugar test paper is a surface (i.e. single side) the coating hydrophilic substance in substrate, passes through and be coated with drying tunnel
Dry, hydrophilic substance adheres to substrate surface and constitutes hydrophilic film, then the compound PE film in hydrophilic film.Of the invention is two-sided
Hydrophilic film, after substrate upper surface completes coating and compound PE film, when in substrate lower surface, coating hydrophilic film enters drying tunnel drying,
Because drying tunnel drying temperature is higher, it can deform, blister, delamination after the PE film of upper surface is heated, in order to solve this problem, the present invention
Hydrophilic coating solvent using the easily dry spirit solvent of low temperature, this makes it possible to dry using cold drying, avoid pair
The destruction of PE film.
Detailed description of the invention
Fig. 1 is structural schematic diagram of the invention;
Fig. 2 is the structural schematic diagram for manufacturing coating system used in the two-sided hydrophilic film of Fig. 1.
Specific embodiment
In order to be more clear technical solution of the present invention, below in conjunction with attached Fig. 1 and 2, the present invention is described in detail.
It should be understood that specific embodiment described in this specification is not intended to limit just for the sake of explaining the present invention
Protection scope of the present invention.
The present invention is a kind of two-sided hydrophilic film, including substrate 1, is coated with upper layer hydrophilic film 2 in the upper surface of substrate 1,
The lower surface of substrate 1 is coated with lower layer's hydrophilic film 3, upper layer PE film 4 is compounded in the upper layer hydrophilic film 2, in the lower layer
Lower layer's PE film 5 is compounded in hydrophilic film 3.
The upper layer hydrophilic film 2, lower layer's hydrophilic film 3 are to be dissolved in ethanol solution, then by fatty alcohol polyoxyethylene ether
The film for being coated on 1 surface of substrate, being formed again through low temperature drying.In the ethanol solution of the fatty alcohol polyoxyethylene ether,
The weight percent content of fatty alcohol polyoxyethylene ether is 1-3%.The substrate 1 is made of PET material.
A kind of manufacturing method of above-mentioned two-sided hydrophilic film, includes the following steps:
Step 1: first it is coated with lower layer's hydrophilic film.Substrate 1 is released from substrate coiled strip emptying roller 01, is become through guide roller guiding
Horizontal transmission and its following table is face-up, lower layer's hydrophilic film coating die head 07 is above coated the lower surface of substrate 1;
Step 2: compound lower layer PE film after drying.The substrate 1 for being coated with lower layer's hydrophilic film 3 is dried into dry baking tunnel 08,
Lower layer's hydrophilic film 3 by after drying, release from lower layer's hydrophilic film coiled strip emptying roller 03 by lower layer's PE film 5, passes through the first compound rolling
It is compound to wheel 04 and the substrate 1 that is coated with lower layer's hydrophilic film 3;
Step 3: it is coated upper layer hydrophilic film.It is coated with lower layer's hydrophilic film 3 and is compounded with the substrate 1 of lower layer's hydrophilic film 3 through first
Compound rolling is oriented to wheel 04, becomes horizontal transmission and its upper surface upward, upper layer hydrophilic film coating die head 06 is above to base
The upper surface of material 1 is coated;
Step 4: compound upper layer PE film after low temperature drying.The substrate 1 for being coated with upper layer hydrophilic film 2 enters low temperature drying channel 09
Low temperature drying is carried out, upper layer hydrophilic film 2 by after drying, release from upper layer PE film roll material emptying roller 02 by upper layer PE film 4, by the
Two compound rolling are compound to wheel 05 and the substrate 1 that is coated with upper layer hydrophilic film 2;
Step 5: it cuts.The two-sided hydrophilic film 6 of finished product is sent to cutter 011 to wheel 05 by the second compound rolling and cuts.
The coating system of above-mentioned two-sided hydrophilic film, including substrate coiled strip emptying roller 01,02 He of upper layer PE film roll material emptying roller
Lower layer's hydrophilic film coiled strip emptying roller 03, and play the first compound rolling rolling pair compound to wheel 04 and second of constant tension stretch
Wheel 05, for the upper layer hydrophilic film coating die head 06 and lower layer's hydrophilic film coating die head 07 of coating, dry baking tunnel 08 and low temperature are dry
Dry channel 09, substrate 1 are released from substrate coiled strip emptying roller 01, successively through guide roller, lower layer's hydrophilic film coating die head 07, dry
The compound rolling of dry drying tunnel 08, first is to wheel 04, upper layer hydrophilic film coating die head 06, low temperature drying channel 09, the second compound rolling
To wheel 05, it is transmitted in cutter 011, lower layer's PE film 5 is released from lower layer's hydrophilic film coiled strip emptying roller 03, passes through the first compound rolling
To press compound with the substrate 1 that is coated with lower layer's hydrophilic film 3 to wheel 04, upper layer PE film 4 is released from upper layer PE film roll material emptying roller 02,
It is compound to wheel 05 and the substrate 1 that is coated with upper layer hydrophilic film 2 by the second compound rolling.Preferably, the substrate 1 is through being oriented to
Idler wheel is directed to horizontal transmission and its following table is face-up, and lower layer's hydrophilic film coating die head 07 is located at the upper of 1 lower surface of substrate
Side;The substrate 1 is directed to horizontal transmission and its upper surface upward to wheel 04 through the first compound rolling, and the upper layer hydrophilic film applies
Cloth die head 06 is located at the top of 1 upper surface of substrate.
Claims (3)
1. a kind of two-sided hydrophilic film, including substrate (1), it is characterised in that: be coated with upper layer hydrophilic film in the upper surface of substrate (1)
(2), lower layer's hydrophilic film (3) are coated in the lower surface of substrate (1), are compounded with upper layer PE film on the upper layer hydrophilic film (2)
(4), lower layer's PE film (5) is compounded on lower layer's hydrophilic film (3).
2. two-sided hydrophilic film according to claim 1, it is characterised in that: the upper and lower layer hydrophilic film (2,3) is for by rouge
Fat alcohol polyoxyethylene ether is dissolved in ethanol solution and is coated on the film formed behind the substrate (1) surface through low temperature drying.
3. two-sided hydrophilic film according to claim 1, it is characterised in that: the substrate (1) is made of PET material.