CN109440451A - A kind of multifunctional fabric, processing technology and its application - Google Patents
A kind of multifunctional fabric, processing technology and its application Download PDFInfo
- Publication number
- CN109440451A CN109440451A CN201810961031.1A CN201810961031A CN109440451A CN 109440451 A CN109440451 A CN 109440451A CN 201810961031 A CN201810961031 A CN 201810961031A CN 109440451 A CN109440451 A CN 109440451A
- Authority
- CN
- China
- Prior art keywords
- fabric
- finishing agent
- multifunctional fabric
- processing technology
- multifunctional
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of multifunctional fabric, processing technology and its application.The processing technology of the multifunctional fabric, include the following steps: for manufactured fabric to be straightened it is open and flat be put into impregnated 5~15 minutes in composite finishing agent after drying to get to multifunctional fabric.Multifunctional fabric proposed by the present invention meets wearer in the function intensified property for the dress ornament for dressing various different demands functions, meets the needs of people are for health and health.
Description
Technical field:
The invention belongs to fabric technical fields, and in particular to a kind of multifunctional fabric, processing technology and its application.
Background technique:
With the development of society, living standard generally improves, the requirement of people's quality of life is higher and higher, and people start to infuse
The quality worn the clothes again, and the quality requirements of fabric are higher and higher.Although existing dress ornament raw material update, function and
It constantly brings forth new ideas on style, but can not meet people for the demand of health and health preserving.
Summary of the invention:
The object of the present invention is to provide a kind of multifunctional fabric, processing technology and its applications, meet wearer and are wearing
The function intensified property for wearing the dress ornament of various different demands functions meets the needs of people are for health and health.
The present invention is achieved by the following technical programs:
A kind of composite finishing agent, consists of the following mass percentage components, atom carbon 6%~9%, fastness promotor
2%~5%, anionic finishing agent 4%~7%, surplus is water.
Atom carbon exists as the single substance of single substance or 4~5 atoms, be partial size is 1nm or less (166 angstroms)
Ultramicron.Since atomic carbon tool is there are four arm, and in the state that each carbon atom is not in conjunction with other atoms, particle
In the presence of so its ion adsorption capacity is especially strong.Fastness promotor improves the dry and wet crock fastness of fabric, improves the resistance to of fabric
Scourability.
Anionic finishing agent can release anion, and anion is referred to as " air vitamin ", it is believed that it is such as food
Object vitamin is the same, has highly important influence to the vital movement of human body and other biological, and closely with the longevity of the mankind
Correlation, it is referred to as " long-lived element ".Anion can activating cell, improve lung function, improve myocardial function, improve sleep, promote new
Old metabolism enhances human resistance to disease, and has excellent purification air and dispelling abnormal flavor performance, therefore have good health care
Effect.
The skin contact of anionic and people in the present invention utilizes rubbing for the thermal energy of human body and human motion and skin
The transmitting for accelerating anion is wiped, forms an anion air layer between skin and textile fabric, eliminates peculiar smell, purifies air,
And the permanent electrode of anion material generates micro-electrical stimulation effect to skin, adjusts automatic nervous system, and anti-inflammatory analgesic improves
Immunity plays preferable adjuvant treatment effect to a variety of chronic diseases.
It is preferred that the atom carbon is made by the steps to obtain: in a nitrogen atmosphere, timber or bamboo being existed
After heating 70~90 minutes under conditions of 300 DEG C~500 DEG C, 450 DEG C of discharge nitrogen are raised the temperature to, importing low temperature nitrogen makes
The temperature of system is down to 50 DEG C~100 DEG C to get atom carbon is arrived.
It is preferred that the fastness promotor is XB FIX-ET, the anionic finishing agent is nano-scaled electric mountain flour.
A kind of processing technology of multifunctional fabric, include the following steps: for manufactured fabric to be straightened it is open and flat be put into it is above-mentioned
It is dried after being impregnated 5~15 minutes in composite finishing agent to get multifunctional fabric is arrived.
Atom carbon is directly added from polymerization end, and copolymerization is synthesized with fastness promotor or anion finishing or is merged into fabric
Among, atom carbon can export 100 times of dose of radiation higher than long charcoal, high 400 times of the dose of radiation of specific activity charcoal.Atomic carbon
Element, fastness promotor and anionic finishing agent three's coupling, improve the washing resistance performance of fabric, improve its dry and wet friction
Fastness；The dress ornament that atom carbon cooperation anionic finishing agent can be such that processed cloth is made into generates the anion of high power amount and remote
Infrared ray (being 4 times or more caused by its is single of amount), anion can antibacterial, deodorization and purification air；Atom carbon simultaneously
It is small in size, so that web surface is formed lotus leaf effect, there is the effect of waterproof and oilproof.
The composite finishing agent is for processing the film that multifunctional fabric surface made from fabric is capable of forming one layer of nano thickness
Layer, can maximumlly reduce the dust and dirt for being adhered to surface, and contact angle of the water on this surface is greater than 160 ° (close to ball
Shape), multifunctional fabric can reach antifouling and self-cleaning effect in the case where rainwater or tap water rinse.
It is preferred that above-mentioned processing technology, specifically comprises the following steps: for manufactured fabric to be straightened and open and flat be put into above-mentioned answer
Close finishing agent in 25 DEG C~30 DEG C impregnate 5~15 minutes after, 80 DEG C~120 DEG C drying to get arrive multifunctional fabric.
It is preferred that the fabric is by cotton, polyester-cotton blend, linen-cotton or terylene through weaving.
According to the multifunctional fabric that the processing technology of above-mentioned multifunctional fabric obtains, in clothes, home textile articles, health care
On application.
There is quick-drying, fast clean, antibacterial, deodorization, absorbing sweat, environmental protection, cumulative with the dress ornament that above-mentioned multifunctional fabric manufactures, change
Traditional washing methods, shaken slightly in clear water can decontamination easily, reduce washing powder (liquid) chemical contamination, allow washing clothing
Object is simpler, it is more environmentally friendly not liquid, waterproof and oilproof, it is non-sticky dirty the features such as；It can promote velocity of blood flow, improve that body is micro- to follow
Ring improves locomotive organ function, increases total balance of the body, delaying cell aging, restores cell elasticity, and promotion muscle is compact, draws
Human body thermogenetic effect is sent out, raw, alleviation joint pain in vivo is excluded, improves the quality of living, the quantum higher-order of oscillation, remove cell toxicant
Dirt increases velocity of blood flow, excretes toxin, repairs disorder cell magnetic field, improves cells survival environment, promotes cell again
Raw, cutting ultraviolet light；It prevents electrostatic and offsets external electromagnetic wave, enhancing physical efficiency relatively, reduce disease, malicious, bacterium infection and invade
Enter, activating human body function, purification blood, resistance building, calm the nerves, help for sleep, repairing human immune system, improves immune
Power promotes the functions such as physical efficiency.
Unless otherwise indicated, nominal definition of the present invention, which has, is generally understood identical contain with those skilled in the art
Justice.
Compared with prior art, the invention has the following advantages that
1, the atom carbon in composite finishing agent proposed by the present invention, fastness promotor and anionic finishing agent three coupling
Effect, improves the washing resistance performance of fabric, improves its dry and wet crock fastness；Atom carbon cooperation anionic finishing agent can make to locate
The dress ornament that the cloth managed is made into generates the negative anion of high power amount and far infrared (is 4 times or more caused by its is single
Amount)；Atomic carbon pixel volume is small simultaneously, so that web surface is formed lotus leaf effect, there is the effect of waterproof and oilproof.
2, multifunctional fabric proposed by the present invention meets wearer in the function for the dress ornament for dressing various different demands functions
Can the property strengthened, such as there is snow defence, waterproof, the cutting of moisture-penetrable ventilated, anti-pollution, easy to clean, ultraviolet light, bacteriostasis, and deodorization taste, antistatic；
Improve erythrocyte deformability, oxygen carrying content simultaneously；Vivotoxin rubbish is cleaned, metabolism is improved, human activin function repairs people
Body immune system improves immunity, enhances physical efficiency, promotes soldier's energy, vigor and fighting capacity and is conducive to human health.
Detailed description of the invention:
Fig. 1 is the 1000 power microscope enlarged drawings by the web surface of the processing of embodiment 2 front and back, wherein Fig. 1 a is base
Cloth is undressed preceding 1000 power microscope enlarged drawing of lines, Fig. 1 b are undressed preceding 1000 power microscope enlarged drawing of fabric section, figure
1c is the 1000 power microscope enlarged drawing of fabric section after processing.
Specific embodiment:
The following examples are further illustrations of the invention, rather than limiting the invention.Except special instruction, this hair
Experimental material and reagent in bright are the art regular market purchase product.
Embodiment 1:
A kind of processing technology of multifunctional fabric specifically comprises the following steps: that open and flat be put into again for manufactured fabric is straightened
Close finishing agent liquid pool in 25 DEG C impregnate 15 minutes after, 120 DEG C drying to get arrive multifunctional fabric.Fabric by cotton through weaving and
At.
Composite finishing agent consists of the following mass percentage components, atom carbon 6%, fastness promotor 5%, bear from
Sub- finishing agent 4%, water 85%.
Atom carbon is made by the steps to obtain: in a nitrogen atmosphere, green wood being heated under conditions of 300 DEG C
After 70 minutes, 450 DEG C of discharge nitrogen are raised the temperature to, importing low temperature nitrogen makes the temperature of system be down to 50 DEG C to get original is arrived
Sub- carbon.
Embodiment 2:
A kind of processing technology of multifunctional fabric specifically comprises the following steps: that open and flat be put into again for manufactured fabric is straightened
It closes in the liquid pool of finishing agent and impregnates after ten minutes for 28 DEG C, 100 DEG C dry to get multifunctional fabric is arrived.Fabric is by polyester-cotton blend through weaving
It forms.
Composite finishing agent consists of the following mass percentage components, atom carbon 8%, fastness promotor 4%, bear from
Sub- finishing agent 5%, water 83%.
Atom carbon is made by the steps to obtain: in a nitrogen atmosphere, raw bamboo being heated under conditions of 400 DEG C
After 80 minutes, 450 DEG C of discharge nitrogen are raised the temperature to, importing low temperature nitrogen makes the temperature of system be down to 80 DEG C to get original is arrived
Sub- carbon.
As shown in Figure 1, without the fabric of processing, its surface texture is compact, in the hollow structure of the fabric after processing
Between form air bag and can keep body temperature here, enhancing air permeability reaches heat insulation effect, and screen resilience is good, durable and be unlikely to deform, light and soft comfortable, no
Regular concavo-convex surface texture, possesses more space surfaces, and air permeability is high, water absorbing capacity than it is undressed when it is 2.5 times high.
Embodiment 3:
A kind of processing technology of multifunctional fabric specifically comprises the following steps: that open and flat be put into again for manufactured fabric is straightened
It closes in the liquid pool of finishing agent and impregnates after five minutes for 30 DEG C, 80 DEG C dry to get multifunctional fabric is arrived.Fabric is by cotton through weaving.
Composite finishing agent consists of the following mass percentage components, atom carbon 9%, fastness promotor 2%, bear from
Sub- finishing agent 7%, water 82%.
Atom carbon is made by the steps to obtain: in a nitrogen atmosphere, green wood being heated under conditions of 500 DEG C
After 90 minutes, 450 DEG C of discharge nitrogen are raised the temperature to, importing low temperature nitrogen makes the temperature of system be down to 100 DEG C to get original is arrived
Sub- carbon.
Comparative example 1:
It is same as Example 2, the difference is that: atom carbon is fullerene.
Comparative example 2:
It is same as Example 2, the difference is that: atom carbon is carbon nanotube.
Test case 1:
The multifunctional fabric that Examples 1 to 3 and comparative example 1~2 are obtained and commercially available textile carry out uvioresistant/red
Outside line IR thermal reflection test obtains that the results are shown in Table 1.
Table 1
Test case 2:
Wind coat jacket is made in the multifunctional fabric (test specimens) that embodiment 2 obtains, the wind coat jacket with certain commercially available brand
(comparative sample) does antiallergic sense and microcirculation performance test, and test method and test result are as shown in table 2.
Table 2
It is obtained by table 2, wind coat jacket is made in the multifunctional fabric after the processing of embodiment 2, and it improves blood circulation, flesh
Skin comfort level is higher.
The above embodiment is a preferred embodiment of the present invention, but embodiments of the present invention are not by above-described embodiment
Limitation, other any changes, modifications, substitutions, combinations, simplifications made without departing from the spirit and principles of the present invention etc.
It should be equivalent substitute mode, be included within the scope of the present invention.
Claims (8)
1. a kind of composite finishing agent, which is characterized in that consist of the following mass percentage components, atom carbon 6%~9%,
Fastness promotor 2%~5%, anionic finishing agent 4%~7%, surplus are water.
2. composite finishing agent according to claim 1, which is characterized in that the atom carbon is made by the steps
It obtains: in a nitrogen atmosphere, after timber or bamboo are heated 70~90 minutes under conditions of 300 DEG C~500 DEG C, by temperature liter
Up to 450 DEG C discharge nitrogen, importing low temperature nitrogen makes the temperature of system be down to 50 DEG C~100 DEG C to get atom carbon is arrived.
3. composite finishing agent according to claim 1, which is characterized in that the fastness promotor is XB FIX-ET, institute
The anionic finishing agent stated is nano-scaled electric mountain flour.
4. a kind of processing technology of multifunctional fabric, which comprises the steps of: open and flat put is straightened in manufactured fabric
Enter and is dried after being impregnated 5~15 minutes in composite finishing agent described in claim 1 to get multifunctional fabric is arrived.
5. the processing technology of multifunctional fabric according to claim 4, which is characterized in that specifically comprise the following steps: by
Manufactured fabric be straightened it is open and flat be put into composite finishing agent described in claim 1 25 DEG C~30 DEG C impregnate 5~15 minutes after, 80
DEG C~120 DEG C drying to get arrive multifunctional fabric.
6. the processing technology of multifunctional fabric according to claim 4, which is characterized in that the fabric by cotton, polyester-cotton blend,
Linen-cotton or terylene are through weaving.
7. a kind of multifunctional fabric that the processing technology of multifunctional fabric as claimed in claim 4 obtains.
8. application of the multifunctional fabric as claimed in claim 7 in clothes, home textile articles, health care.