CN109439219A - A kind of stretchable removal heat conductive flame-retarding double faced adhesive tape - Google Patents
A kind of stretchable removal heat conductive flame-retarding double faced adhesive tape Download PDFInfo
- Publication number
- CN109439219A CN109439219A CN201811250744.3A CN201811250744A CN109439219A CN 109439219 A CN109439219 A CN 109439219A CN 201811250744 A CN201811250744 A CN 201811250744A CN 109439219 A CN109439219 A CN 109439219A
- Authority
- CN
- China
- Prior art keywords
- layer
- pressure
- adhesive tape
- sensitive adhesive
- double faced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of stretchable removal heat conductive flame-retarding double faced adhesive tapes, belong to tape applications field.The double faced adhesive tape successively includes release material layer, the first pressure-sensitive adhesive layer, substrate layer, the second pressure-sensitive adhesive layer, release material layer;It or successively include the first pressure-sensitive adhesive layer;Substrate layer, the second pressure-sensitive adhesive layer, release material layer;Wherein, the substrate layer and release material layer pass through the first pressure-sensitive adhesive layer respectively and the second pressure-sensitive adhesive layer is pasted.The present invention adds flame-retarded heat-conducting ingredient using substrate modified layer and to adhesive, so that the adhesive tape while guaranteeing original adhesion strength, also improves the fire-retardant and heating conduction of adhesive tape.It is combined releasing the components such as electronic device or battery of mobile phone, when removing 60~90 ° of adhesive tape, also can easily pull out the double faced adhesive tape, and will not be broken between affixed object, provided conveniently for processes such as later rework, maintenances, working efficiency is provided.
Description
Technical field
The present invention relates to a kind of stretchable removal heat conductive flame-retarding double faced adhesive tapes, belong to tape applications field.
Background technique
For the double faced adhesive tape of existing stretchable removal using thermoplastic polyurethane film or rubber as substrate, glue uses third
Olefin(e) acid ester, rubber series, polyurethane series, during removal, when removing angle and being greater than 60 °, when removal is required firmly to be obviously increased,
And it is easily broken off.Electronic device, battery of mobile phone components gap are smaller, and the double faced adhesive tape of existing stretchable removal is being removed
When, some other position parts need to be removed, adhesive tape is removed again.Existing product is almost non-antiflaming simultaneously, and part electronics
Device, battery of mobile phone etc. can generate amount of heat, can not quickly export, and accelerate this kind of components aging.
Summary of the invention
It is required when to reduce product removal firmly to increase and remove angle, reduce risk of breakage;Security performance is promoted, is increased
Flame retardant effect;Extend the service lifes such as electronic device, battery, the present invention provides a kind of stretchable removal heat conductive flame-retarding double-sided adhesives
Band.
Stretchable removal heat conductive flame-retarding double faced adhesive tape of the present invention, successively include release material layer, the first pressure-sensitive adhesive layer,
Substrate layer, the second pressure-sensitive adhesive layer, release material layer;It or successively include the first pressure-sensitive adhesive layer;It is substrate layer, the second pressure-sensitive adhesive layer, release
Material layer;Wherein, the substrate layer and release material layer pass through the first pressure-sensitive adhesive layer respectively and the second pressure-sensitive adhesive layer is pasted.
In one embodiment, the release material layer is the release material of PET, the release material of plain paper, the release material of superpressure paper, ox
One or more of release material of mulberry paper.
In one embodiment, the release material layer with a thickness of 0.012~0.150mm.
In one embodiment, the release material layer is transparent or colourless.
In one embodiment, first pressure-sensitive adhesive layer, the second pressure-sensitive adhesive layer are acrylic ester, silicone-based, rubber
One of glue system or polyurethane series adhesive.
In one embodiment, first pressure-sensitive adhesive layer, the second pressure-sensitive adhesive layer are preferably acrylic ester adhesive
Or rubber series adhesive, wherein heat conductive flame-retarding powder is added in the pressure-sensitive adhesive layer.
In one embodiment, the heat conductive flame-retarding powder is oxide, nitride, phosphide or the arsenide of metal.
In one embodiment, the heat conductive flame-retarding powder is specially aluminium oxide, zinc oxide, potassium oxide, calcium oxide, oxidation
The one or more of magnesium, iron oxide, titanium oxide, aluminium nitride, calcium phosphide or arsenic calcium.
In one embodiment, the specific ingredient of rubber series adhesive is by weight are as follows: and 0-20 parts of SBS rubber,
80-100 parts of SIS rubber, 0-10 parts of IR rubber, 10-40 parts of heat conductive flame-retarding powder, 50-150 parts of solvent.
In one embodiment, the specific ingredient of acrylic ester adhesive is by weight are as follows: acrylic acid 0-20
Part, 80-100 parts of butyl acrylate, 0-10 parts of crosslinking agent, 10-40 parts of heat conductive flame-retarding powder, 50-150 parts of solvent.
In one embodiment, first pressure-sensitive adhesive layer, the second pressure-sensitive adhesive layer with a thickness of 0.025~0.200mm,
Preferably 0.045-0.050mm.
In one embodiment, the substrate layer is that modified polyurethane film, modified rubber film or modified epoxy are thin
One of film.
In one embodiment, the modified polyurethane film is fibroin modified polyurethane film;The modified rubber
Film is blending and modifying rubber film or graft modification rubber film;The modified epoxy film is organic-silicon-modified, polyurethane
Modified, acrylonitrile butadiene rubber modified epoxy film.
In one embodiment, the substrate layer with a thickness of 0.05~0.20mm, preferred thickness 0.050mm.
The advantageous effects that the present invention obtains:
(1) adhesive tape provided by the invention has good elastic property, during stretching can be with the reduction of high degree
Adhesive tape thickness itself, as far as possible contact of the reduction adhesive with affixed object.
(2) present invention adds flame-retarded heat-conducting ingredient using substrate modified layer and to adhesive, so that the adhesive tape is guaranteeing original
While cohesively, the fire-retardant and heating conduction of adhesive tape is also improved.Releasing the components knot such as electronic device or battery of mobile phone
It closes, when removing 60~90 ° of adhesive tape, also can easily pull out the double faced adhesive tape, and will not be broken between affixed object, be returned for the later period
It is convenient that the processes such as work, maintenance provide, and provides working efficiency.
Detailed description of the invention
Fig. 1 is a kind of stretchable removals heat conductive flame-retarding double-faced adhesive tape structure schematic diagram, and in figure: 11 be release material layer;12 are
Release material layer;21 be the first glue pressure-sensitive adhesive layer;22 be the second pressure-sensitive adhesive layer;30 be substrate layer.
Fig. 2 is that a kind of stretchable removals heat conductive flame-retarding double faced adhesive tape removes schematic diagram, and in figure: 40 be affixed object 1;50 be to be somebody's turn to do
Double faced adhesive tape;60 be affixed object 2.
Fig. 3 is partial enlargement diagram at a kind of stretchable removals heat conductive flame-retarding double faced adhesive tape removal, and in figure: 40 be to be pasted
Object 1;50 be the double faced adhesive tape;60 be affixed object 2;70 be heat conductive flame-retarding filler;80 be the gap formed after stretching.
Specific embodiment
Referring to the adhesive tape structure of Fig. 1 (a), heat conductive flame-retarding double faced adhesive tape is can be removed in a kind of stretching of the invention, successively includes
First release material layer 11, the first pressure-sensitive adhesive layer 21, substrate layer 30, the second pressure-sensitive adhesive layer 22 and the second release material layer 12.
Fibroin modified polyurethane film: dry fibroin membrane (4cm × 10cm) is placed on thin polyurethane film surface, surrounding
After being sealed and fixed with paraffin, puts it into rapidly in the prepolymer solution that-NCO base is 2.6 with OH the mass ratio of the material and react 1h.
(upward, polyurethane film is downward for fibroin membrane) after taking-up, is transferred them on polytetrafluoroethylene, certain humidity, temperature are placed in
The reaction was continued in the climatic chamber of degree, generates one silk fibroin composite membrane coating of polyurethane.Then it is not participated in on solvent dissolution composite membrane
The fibroin of reaction is washed with distilled water completely later, spare after vacuum dried.
Embodiment 1:
In the present embodiment, stretchable removal heat conductive flame-retarding double faced adhesive tape successively includes release material layer, the first pressure sensitive adhesive
Layer, substrate layer, the second pressure-sensitive adhesive layer, release material layer, wherein the first release material, which is that 120g is bis-, moulds double silicon white release papers;First
Pressure-sensitive adhesive layer, the second pressure-sensitive adhesive layer be acrylate adhesive, ingredient by weight: 10 parts of acrylic acid, butyl acrylate
80 parts, 5 parts of crosslinking agent, 20 parts of heat conductive flame-retarding ceramic powder, 80 parts of solvent, with a thickness of 0.050mm;Substrate layer is the modified poly- ammonia of fibroin
Ester film, with a thickness of 0.050mm;Second release material is 0.025mm PET release film.
The double faced adhesive tape being prepared is tested for the property, as shown in the table, it is seen then that the addition of heat conductive flame-retarding ceramic powder
So that the excellent flame retardancy for the double-sided adhesive that the present invention is prepared, and using modified substrate the present invention is prepared
Tensile strength, elongation at break and the adhesion strength of double-sided adhesive be remarkably reinforced, can be light and in 45~90 ° of removal adhesive tapes
Pull out the double faced adhesive tape.
The performance test results of double faced adhesive tape and control group double faced adhesive tape that 1 embodiment 1 of table is prepared
When sample a is no heat conductive flame-retarding ceramic powder, remaining forms product identical with embodiment;Sample b is without thermally conductive resistance
When combustion ceramic powder, substrate are unmodified, remaining composition
Product identical with embodiment.
Embodiment 2:
In the present embodiment, stretchable removal heat conductive flame-retarding double faced adhesive tape successively includes release material layer, the first pressure sensitive adhesive
Layer, substrate layer, the second pressure-sensitive adhesive layer, release material layer, wherein the first release material, which is that 360g is bis-, moulds double silicon white release papers;First
Pressure-sensitive adhesive layer, the second pressure-sensitive adhesive layer be acrylate adhesive, ingredient by weight: 20 parts of acrylic acid, butyl acrylate
100 parts, 10 parts of crosslinking agent, 40 parts of heat conductive flame-retarding ceramic powder, 120 parts of solvent, with a thickness of 0.150mm;Substrate layer is modified for fibroin
Polyurethane film, with a thickness of 0.050mm;Second release material is 0.025mmPET release film.
The double faced adhesive tape being prepared is tested for the property, as shown in the table, it is seen then that the addition of heat conductive flame-retarding ceramic powder
So that the excellent flame retardancy for the double-sided adhesive that the present invention is prepared, and using modified substrate the present invention is prepared
Tensile strength, elongation at break and the adhesion strength of double-sided adhesive be remarkably reinforced, can be light and in 45~90 ° of removal adhesive tapes
Pull out the double faced adhesive tape.
The performance test results of double faced adhesive tape and control group double faced adhesive tape that 2 embodiment 2 of table is prepared
When sample a is no heat conductive flame-retarding ceramic powder, remaining forms product identical with embodiment;Sample b is without thermally conductive resistance
When combustion ceramic powder, substrate are unmodified, remaining composition
Product identical with embodiment.
Embodiment 3:
In the present embodiment, stretchable removal heat conductive flame-retarding double faced adhesive tape successively includes release material layer, the first pressure sensitive adhesive
Layer, substrate layer, the second pressure-sensitive adhesive layer, release material layer, wherein the first release material, which is that 120g is bis-, moulds double silicon white release papers;First
Pressure-sensitive adhesive layer, the second pressure-sensitive adhesive layer be acrylate adhesive, ingredient by weight: 10 parts of SBS rubber, SIS rubber 80
Part, 3 parts of IR rubber, 20 parts of heat conductive flame-retarding ceramic powder, 80 parts of solvent, with a thickness of 0.045mm;The substrate layer is blending and modifying conjunction
At rubber film, with a thickness of 0.060mm;The second release material is 0.025mmPET release film.
The double faced adhesive tape being prepared is tested for the property, as shown in the table, it is seen then that the addition of heat conductive flame-retarding ceramic powder
So that the excellent flame retardancy for the double-sided adhesive that the present invention is prepared, and using modified substrate the present invention is prepared
Tensile strength, elongation at break and the adhesion strength of double-sided adhesive be remarkably reinforced, can be light and in 45~90 ° of removal adhesive tapes
Pull out the double faced adhesive tape.
The performance test results of double faced adhesive tape and control group double faced adhesive tape that 3 embodiment 3 of table is prepared
When sample a is no heat conductive flame-retarding ceramic powder, remaining forms product identical with embodiment;Sample b is without thermally conductive resistance
When combustion ceramic powder, substrate are unmodified, remaining composition
Product identical with embodiment.
Embodiment 4
In the present embodiment, it referring to the adhesive tape structure of Fig. 1 (b), stretches and heat conductive flame-retarding double faced adhesive tape can be removed, successively include
First pressure-sensitive adhesive layer 21, substrate layer 30, the second pressure-sensitive adhesive layer 22 and the first release material layer 11.Wherein, the first release material is 120g
It is double to mould double silicon white release papers;First pressure-sensitive adhesive layer, the second pressure-sensitive adhesive layer are acrylate adhesive, and ingredient is by weight
Meter: 10 parts of SBS rubber, 80 parts of SIS rubber, 3 parts of IR rubber, 20 parts of heat conductive flame-retarding ceramic powder, 80 parts of solvent, with a thickness of
0.045mm;The substrate layer is fibroin modified polyurethane film, with a thickness of 0.060mm.
The double faced adhesive tape being prepared is tested for the property, as shown in the table, it is seen then that the addition of heat conductive flame-retarding ceramic powder
So that the excellent flame retardancy for the double-sided adhesive that the present invention is prepared, and using modified substrate the present invention is prepared
Tensile strength, elongation at break and the adhesion strength of double-sided adhesive be remarkably reinforced, can be light and in 45~90 ° of removal adhesive tapes
Pull out the double faced adhesive tape.
The performance test results of double faced adhesive tape and control group double faced adhesive tape that 4 embodiment 4 of table is prepared
When sample a is no heat conductive flame-retarding ceramic powder, remaining forms product identical with embodiment;Sample b is without thermally conductive resistance
When combustion ceramic powder, substrate are unmodified, remaining composition
Product identical with embodiment.
Comparative example 1:
First pressure-sensitive adhesive layer in this comparative example, the butyl acrylate in the second pressure-sensitive adhesive layer are 50 parts, remaining each component with
Embodiment 1 is identical, and adhesive tape is bonded SUS respectively, and different angle removes test after placing 20min, and the removal force at 80 ° can
Up to 5200g/25mm, when removing angle greater than 80 °, adhesive tape is broken.
Comparative example 2:
First pressure-sensitive adhesive layer in this comparative example, the heat conductive flame-retarding ceramic powder in the second pressure-sensitive adhesive layer are 5 parts, remaining each component
It is same as Example 1, adhesive tape is bonded SUS respectively, different angle removes test after placing 20min, can be in 90 ° of time shifts
It removes, but its thermal coefficient only has 0.35, flame retardant rating is lower.
Comparative example 3:
First pressure-sensitive adhesive layer in this comparative example, the heat conductive flame-retarding ceramic powder in the second pressure-sensitive adhesive layer are 50 parts, remaining each group
Point same as Example 1, adhesive tape is bonded SUS up to 0.82 by thermal coefficient respectively, places different angle after 20min
Test is removed, when removing angle is 80 °, adhesive tape breaking.
Although the present invention has been described by way of example and in terms of the preferred embodiments, it is not intended to limit the invention, any to be familiar with this skill
The people of art can do various change and modification, therefore protection model of the invention without departing from the spirit and scope of the present invention
Enclosing subject to the definition of the claims.
Claims (10)
1. a kind of stretchable removal heat conductive flame-retarding double faced adhesive tape, which is characterized in that successively include release material layer, the first pressure sensitive adhesive
Layer, substrate layer, the second pressure-sensitive adhesive layer, release material layer;Or successively include the first pressure-sensitive adhesive layer, substrate layer, the second pressure-sensitive adhesive layer, from
Profile layer;Wherein, the substrate layer and release material layer pass through the first pressure-sensitive adhesive layer respectively and the second pressure-sensitive adhesive layer is pasted;Described
One pressure-sensitive adhesive layer and the second pressure-sensitive adhesive layer are one of acrylic ester, silicone-based, rubber series or polyurethane series adhesive, and
Add heat conductive flame-retarding powder.
2. the stretchable removal heat conductive flame-retarding double faced adhesive tape of one kind according to claim 1, which is characterized in that the thermally conductive resistance
Fire oxide, nitride, phosphide or the arsenide that powder is metal.
3. the stretchable removal heat conductive flame-retarding double faced adhesive tape of one kind according to claim 1 or 2, which is characterized in that described to lead
Hot fireproof powder is aluminium oxide, zinc oxide, potassium oxide, calcium oxide, magnesia, iron oxide, titanium oxide, aluminium nitride, calcium phosphide or arsenic
Change the one or more of calcium.
4. the stretchable removal heat conductive flame-retarding double faced adhesive tape of one kind according to claim 1 to 3, which is characterized in that described
Release material layer is one or more of the release material of PET, the release material of plain paper, the release material of superpressure paper, the release material of brown paper.
5. the stretchable removal heat conductive flame-retarding double faced adhesive tape of one kind according to claim 1 to 4, which is characterized in that described
Release material layer with a thickness of 0.012~0.150mm.
6. -5 any stretchable removal heat conductive flame-retarding double faced adhesive tape of one kind according to claim 1, which is characterized in that described
Substrate layer is one of modified polyurethane film, modified rubber film or modified epoxy film.
7. the stretchable removal heat conductive flame-retarding double faced adhesive tape of one kind according to claim 6, which is characterized in that the modification is poly-
Urethane film is fibroin modified polyurethane film;The modified rubber film is blending and modifying rubber film or graft modification rubber
Film;The modified epoxy film is organic-silicon-modified, polyurethane-modified, acrylonitrile butadiene rubber modified epoxy film.
8. -7 any stretchable removal heat conductive flame-retarding double faced adhesive tape of one kind according to claim 1, which is characterized in that described
First pressure-sensitive adhesive layer, the second pressure-sensitive adhesive layer thickness be respectively 0.025~0.200mm.
9. -8 any stretchable removal heat conductive flame-retarding double faced adhesive tape of one kind according to claim 1, which is characterized in that described
Substrate layer with a thickness of 0.05~0.20mm.
10. any stretchable removal heat conductive flame-retarding double faced adhesive tape of one kind of claim 1-9 is in electronics, machinery, chemical industry neck
The application in domain.