CN109437979A - A kind of rays of sunlight glaze builds water-white pottery burning process - Google Patents
A kind of rays of sunlight glaze builds water-white pottery burning process Download PDFInfo
- Publication number
- CN109437979A CN109437979A CN201811452017.5A CN201811452017A CN109437979A CN 109437979 A CN109437979 A CN 109437979A CN 201811452017 A CN201811452017 A CN 201811452017A CN 109437979 A CN109437979 A CN 109437979A
- Authority
- CN
- China
- Prior art keywords
- glaze
- sunlight
- rays
- kiln
- burning process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of rays of sunlight glaze to build water-white pottery burning process, including selection: the good idiosome of selected shape and condition first is as sample to be fired；Loading of kiln: selected sample is packed into electrical kiln, and is uniformly placed on the surrounding of electrical kiln；Addition glaze: aluminium block is placed at the position for needing the idiosome of upper glaze in the inside of electrical kiln, aluminium powder is placed in the top of aluminium block, and glaze is placed in the top of aluminium powder；It controls stifling position: being covered above glaze with ceramic lid with holes, hole alignment pottery is needed into stifling position；The cover board for covering electrical kiln is fired and controls the temperature of electrical kiln；Stop heating, and is cooled down, kiln discharge.
Description
Technical field
The present invention relates to pottery burning techniques fields, it particularly relates to which a kind of rays of sunlight glaze builds water-white pottery burning process.
Background technique
Rays of sunlight glaze builds water-white pottery, and creation, which combines the Traditional Firing Craft of Red for building water purple pottery and adds glaze, carries out innovation system
Make, so that white pottery works is occurred transmutation in firing, rays of sunlight glaze colours is presented in finished product, similar to build water bavin firing nature transmutation.But it compares
It is burnt in bavin and washes in a pan the uncontrollable randomness of device nature transmutation, rays of sunlight glaze white pottery can be by controlling the additive amount of glaze and the position fumigated
It sets to get a desired effect.
For the problems in the relevant technologies, currently no effective solution has been proposed.
Summary of the invention
For the problems in the relevant technologies, the present invention proposes that a kind of rays of sunlight glaze builds water-white pottery burning process, existing to overcome
Above-mentioned technical problem present in the relevant technologies.
The technical scheme of the present invention is realized as follows:
A kind of rays of sunlight glaze builds water-white pottery burning process, comprising the following steps:
Selection: the good idiosome of selected shape and condition first is as sample to be fired；
Loading of kiln: selected sample is packed into electrical kiln, and is uniformly placed on the surrounding of electrical kiln；
Addition glaze: aluminium block is placed at the position for needing the idiosome of upper glaze in the inside of electrical kiln, the top of aluminium block is placed
Place glaze in the top of aluminium powder, aluminium powder；
It controls stifling position: being covered above glaze with ceramic lid with holes, hole alignment pottery is needed into stifling position；
The cover board for covering electrical kiln is fired and controls the temperature of electrical kiln；
Stop heating, and is cooled down, kiln discharge.
Further, the glaze is Household salt gauge, and the weight of required glaze is 10-30g.
Further, the ceramic lid is the ceramic lid that a side offers gap.
Further, the size of the aluminium block and thickness can need the position of glazing to be selected and adjusted according to ceramics.
Further, firing in 1~12 hour from room temperature to 300 DEG C, then to heat up per hour 30~50 DEG C
Speed rises to 1100 DEG C, is then to slowly warm up to 1215 DEG C.
Beneficial effects of the present invention: the uncontrollable randomness of pottery nature transmutation is burnt compared to bavin, rays of sunlight glaze white pottery can be with
Additive amount and stifling position by controlling glaze can according to need and are adjusted to get a desired effect, so that pottery
Porcelain has gradually changeable, greatly improves the aesthetic feeling for building water purple pottery, avoids the aestheticly tired that tradition builds water pottery art, purple to water is built
Industrial Effects of making pottery are far-reaching, significant, provide important reference and research direction to study the experts and scholars of transmutation, open
Build the new direction of water purple pottery manufacture craft.
Detailed description of the invention
It in order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, below will be to institute in embodiment
Attached drawing to be used is needed to be briefly described, it should be apparent that, the accompanying drawings in the following description is only some implementations of the invention
Example, for those of ordinary skill in the art, without creative efforts, can also obtain according to these attached drawings
Obtain other attached drawings.
Fig. 1 is the step flow chart that a kind of rays of sunlight glaze according to an embodiment of the present invention builds water-white pottery burning process.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art's every other embodiment obtained belong to what the present invention protected
Range.
According to an embodiment of the invention, providing a kind of rays of sunlight glaze builds water-white pottery burning process.
As shown in Figure 1, a kind of preparation method of STEVIA REBAUDIANA lozenge according to an embodiment of the present invention, comprising the following steps:
S101: selection: the good idiosome of selected shape and condition first is as sample to be fired；
S103: loading of kiln: selected sample is packed into electrical kiln, and is uniformly placed on the surrounding of electrical kiln；
S105: aluminium block, the top of aluminium block addition glaze: are placed at the position for needing the idiosome of upper glaze in the inside of electrical kiln
Aluminium powder is placed, glaze is placed in the top of aluminium powder；
S107: controlling stifling position: being covered above glaze with ceramic lid with holes, and hole alignment pottery is needed to fumigate
Position；
S109: the cover board for covering electrical kiln is fired and controls the temperature of electrical kiln；
S111: stop heating, and cooled down, kiln discharge.
In one embodiment, the glaze is Household salt gauge, and the weight of required glaze is 10-30g.
In one embodiment, the ceramic lid is the ceramic lid that a side offers gap, is equipped with by side
Gap, can be adjusted angle according to the ceramics to be fumigated, the control of more convenient people and achieve the effect that desired.
In one embodiment, the size of the aluminium block and thickness can need the position of glazing to be selected according to ceramics
And adjusting.
In one embodiment, firing in 1~12 hour from room temperature to 300 DEG C, then with heat up 30 per hour~
50 DEG C of speed rises to 1100 DEG C, is then to slowly warm up to 1215 DEG C.
In conclusion, by being fired in electrical kiln, temperature can be convenient by means of above-mentioned technical proposal of the invention
Control, while using aluminium block and aluminium powder, since aluminium block and aluminium powder have high temperature resistance, glaze is placed on aluminium powder can be to prevent
Only directly melt the inside for staying in electrical kiln when high temperature, electrical kiln is caused to damage, the steam of glaze smokes idiosome
It steams, is more favorable for the aesthetic feeling of ceramics.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (5)
1. a kind of rays of sunlight glaze builds water-white pottery burning process, which comprises the following steps:
Selection: the good idiosome of selected shape and condition first is as sample to be fired；
Loading of kiln: selected sample is packed into electrical kiln, and is uniformly placed on the surrounding of electrical kiln；
Addition glaze: placing aluminium block at the position for needing the idiosome of upper glaze in the inside of electrical kiln, and aluminium powder is placed in the top of aluminium block,
Place glaze in the top of aluminium powder；
It controls stifling position: being covered above glaze with ceramic lid with holes, hole alignment pottery is needed into stifling position；
The cover board for covering electrical kiln is fired and controls the temperature of electrical kiln；
Stop heating, and is cooled down, kiln discharge.
2. a kind of rays of sunlight glaze according to claim 1 builds water-white pottery burning process, which is characterized in that the glaze is household
Salt, the weight of required glaze are 10-30g.
3. a kind of rays of sunlight glaze according to claim 1 builds water-white pottery burning process, which is characterized in that the ceramic lid is
A side offers the ceramic lid of gap.
4. a kind of rays of sunlight glaze according to claim 1 builds water-white pottery burning process, which is characterized in that the size of the aluminium block
The position of glazing can be needed to be selected and adjusted according to ceramics with thickness.
5. a kind of rays of sunlight glaze according to claim 1 builds water-white pottery burning process, which is characterized in that firing is small 1~12
When it is interior from room temperature to 300 DEG C, then rise to 1100 DEG C with 30~50 DEG C of the speed of heating up per hour, be then to slowly warm up to
1215℃。