CN109437683A - A kind of indoor moisture-proof is non-burning brick - Google Patents
A kind of indoor moisture-proof is non-burning brick Download PDFInfo
- Publication number
- CN109437683A CN109437683A CN201811410956.3A CN201811410956A CN109437683A CN 109437683 A CN109437683 A CN 109437683A CN 201811410956 A CN201811410956 A CN 201811410956A CN 109437683 A CN109437683 A CN 109437683A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- proof
- burning brick
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of indoor moisture-proof is non-burning brick, including flyash, cement, riverway sludge, river sand, conch meal, sodium tetraborate, zeolite powder, sepiolite particle, phenolic resin, tricresyl phosphate, rosin resin, polyethylene wax, stearic acid, silver nitrate solution.Non-burning brick made of the present invention, durable, moistureproof and mildewproof is easy to use.
Description
Technical field
The present invention relates to a kind of indoor moisture-proof is non-burning brick, belong to building material technical field.
Background technique
Currently, the brick generally used in building trade can be divided into baking red bricks and non-burning brick.Baking red bricks are with general
Gangue and the slag ash high temperature in kiln is equipped with all over clay to fire；Non-burning brick is to utilize flyash, cinder, gangue, tail
Slag, residue of chemical industry or natural sand, tidal land mud etc. (one or several kinds of the above raw material) are used as primary raw material, without high-temperature calcination
And a kind of novel wall material manufactured.The non-burning brick saving energy, economizes the land resource, therefore application is more and more extensive.
And tradition is non-burning brick has a single function, intensity is weaker, is not able to satisfy now complicated use environment, and especially interior makes
It is non-burning brick.Most worried problem is exactly that mouldy, the traditional construction material that gets damp is difficult to solve the problems, such as this in household room.
Summary of the invention
To overcome above-mentioned deficiency, it is non-burning brick that the object of the invention provides a kind of indoor moisture-proof.
The solution of the present invention is as follows: a kind of indoor moisture-proof is non-burning brick, is made of following raw material according to parts by weight: fine coal
Ash 50 ~ 90 parts, 30 ~ 50 parts of cement, 20 ~ 30 parts of riverway sludge, 10 ~ 15 parts of river sand, 5 ~ 10 parts of conch meal, 2 ~ 5 parts of sodium tetraborate,
10 ~ 15 parts of zeolite powder, 10 ~ 15 parts of sepiolite particle, 20 ~ 25 parts of phenolic resin, 15 ~ 25 parts of tricresyl phosphate, rosin resin 5
~ 10 parts, 5 ~ 10 parts of polyethylene wax, 1 ~ 3 part of stearic acid, 1 ~ 5 part of silver nitrate solution.
Further, it is made of following raw material according to parts by weight: 50 parts of flyash, 30 parts of cement, 20 parts of riverway sludge, river
10 parts of sand, 5 parts of conch meal, 2 parts of sodium tetraborate, 10 parts of zeolite powder, 10 parts of sepiolite particle, 20 parts of phenolic resin, tripotassium phosphate
15 parts of phenolic ester, 5 parts of rosin resin, 5 parts of polyethylene wax, 1 part of stearic acid, 1 part of silver nitrate solution.
Further, it is made of following raw material according to parts by weight: 90 parts of flyash, 50 parts of cement, 30 parts of riverway sludge, river
15 parts of sand, 10 parts of conch meal, 5 parts of sodium tetraborate, 15 parts of zeolite powder, 15 parts of sepiolite particle, 25 parts of phenolic resin, tripotassium phosphate
25 parts of phenolic ester, 10 parts of rosin resin, 10 parts of polyethylene wax, 3 parts of stearic acid, 5 parts of silver nitrate solution.
Further, it is made of following raw material according to parts by weight: 70 parts of flyash, 40 parts of cement, 25 parts of riverway sludge, river
13 parts of sand, 7 parts of conch meal, 3 parts of sodium tetraborate, 12 parts of zeolite powder, 12 parts of sepiolite particle, 23 parts of phenolic resin, tripotassium phosphate
20 parts of phenolic ester, 8 parts of rosin resin, 7 parts of polyethylene wax, 2 parts of stearic acid, 3 parts of silver nitrate solution.
Further, the preparation method is as follows: (1) is by flyash, cement, riverway sludge, river sand, conch meal, sodium tetraborate, boiling
Mountain flour, sepiolite particle are sufficiently mixed after crushing；(2) raw material obtained by step (1) is put into blender and is stirred, in whipping process
Phenolic resin, tricresyl phosphate, rosin resin, polyethylene wax, stearic acid, silver nitrate solution is added, mixing time is one small
When；(3) raw material obtained by step (2) is put into brick machine machine and adobe is made；(4) adobe obtained by step (3) is put into vaporium
Interior maintenance, curing time are six hours；(5) gained adobe in step (4) is cooled to room temperature, then lay flat after mulching straw from
So maintenance 25 ~ 30 days.
Beneficial effects of the present invention: non-burning brick, durable, moistureproof and mildewproof made of the present invention, it is easy to use.
Specific embodiment
Embodiment 1
A kind of indoor moisture-proof is non-burning brick, is made of following raw material according to parts by weight: 50 parts of flyash, 30 parts of cement, river
20 parts of mud, 10 parts of river sand, 5 parts of conch meal, 2 parts of sodium tetraborate, 10 parts of zeolite powder, 10 parts of sepiolite particle, phenolic resin 20
Part, 15 parts of tricresyl phosphate, 5 parts of rosin resin, 5 parts of polyethylene wax, 1 part of stearic acid, 1 part of silver nitrate solution, preparation method
It is as follows: (1) to be filled after crushing flyash, cement, riverway sludge, river sand, conch meal, sodium tetraborate, zeolite powder, sepiolite particle
Divide mixing；(2) raw material obtained by step (1) is put into blender and is stirred, phenolic resin, tricresol phosphate are added in whipping process
Ester, rosin resin, polyethylene wax, stearic acid, silver nitrate solution, mixing time are one hour；(3) by raw material obtained by step (2)
It is put into brick machine machine and adobe is made；(4) adobe obtained by step (3) is put into maintenance in vaporium, curing time is six hours；
(5) gained adobe in step (4) is cooled to room temperature, is then laid flat after mulching straw natural curing 25 ~ 30 days.
Embodiment 2
A kind of indoor moisture-proof is non-burning brick, is made of following raw material according to parts by weight: 90 parts of flyash, 50 parts of cement, river
30 parts of mud, 15 parts of river sand, 10 parts of conch meal, 5 parts of sodium tetraborate, 15 parts of zeolite powder, 15 parts of sepiolite particle, phenolic resin 25
Part, 25 parts of tricresyl phosphate, 10 parts of rosin resin, 10 parts of polyethylene wax, 3 parts of stearic acid, 5 parts of silver nitrate solution, preparation side
Method is as follows: (1) after crushing flyash, cement, riverway sludge, river sand, conch meal, sodium tetraborate, zeolite powder, sepiolite particle
It is sufficiently mixed；(2) raw material obtained by step (1) is put into blender and is stirred, phenolic resin, tripotassium phosphate are added in whipping process
Phenolic ester, rosin resin, polyethylene wax, stearic acid, silver nitrate solution, mixing time are one hour；It (3) will be former obtained by step (2)
Material, which is put into brick machine machine, is made adobe；(4) adobe obtained by step (3) is put into maintenance in vaporium, curing time is six small
When；(5) gained adobe in step (4) is cooled to room temperature, is then laid flat after mulching straw natural curing 25 ~ 30 days.
Embodiment 3
A kind of indoor moisture-proof is non-burning brick, is made of following raw material according to parts by weight: 70 parts of flyash, 40 parts of cement, river
25 parts of mud, 13 parts of river sand, 7 parts of conch meal, 3 parts of sodium tetraborate, 12 parts of zeolite powder, 12 parts of sepiolite particle, phenolic resin 23
Part, 20 parts of tricresyl phosphate, 8 parts of rosin resin, 7 parts of polyethylene wax, 2 parts of stearic acid, 3 parts of silver nitrate solution, preparation method
It is as follows: (1) to be filled after crushing flyash, cement, riverway sludge, river sand, conch meal, sodium tetraborate, zeolite powder, sepiolite particle
Divide mixing；(2) raw material obtained by step (1) is put into blender and is stirred, phenolic resin, tricresol phosphate are added in whipping process
Ester, rosin resin, polyethylene wax, stearic acid, silver nitrate solution, mixing time are one hour；(3) by raw material obtained by step (2)
It is put into brick machine machine and adobe is made；(4) adobe obtained by step (3) is put into maintenance in vaporium, curing time is six hours；
(5) gained adobe in step (4) is cooled to room temperature, is then laid flat after mulching straw natural curing 25 ~ 30 days.
Although the detailed description and description of the specific embodiments of the present invention are given above, it should be noted that
We can carry out various equivalent changes and modification to above embodiment according to the concept of the present invention, and generated function is made
It, should all be within protection scope of the present invention when with the spirit still covered without departing from specification.
Claims (5)
1. a kind of indoor moisture-proof is non-burning brick, which is characterized in that be made of following raw material according to parts by weight: flyash 50 ~ 90
Part, 30 ~ 50 parts of cement, 20 ~ 30 parts of riverway sludge, 10 ~ 15 parts of river sand, 5 ~ 10 parts of conch meal, 2 ~ 5 parts of sodium tetraborate, zeolite powder
10 ~ 15 parts, 10 ~ 15 parts of sepiolite particle, 20 ~ 25 parts of phenolic resin, 15 ~ 25 parts of tricresyl phosphate, 5 ~ 10 parts of rosin resin,
5 ~ 10 parts of polyethylene wax, 1 ~ 3 part of stearic acid, 1 ~ 5 part of silver nitrate solution.
2. a kind of indoor moisture-proof is non-burning brick according to claim 1, which is characterized in that according to parts by weight by following raw material
Composition: 50 parts of flyash, 30 parts of cement, 20 parts of riverway sludge, 10 parts of river sand, 5 parts of conch meal, 2 parts of sodium tetraborate, zeolite powder 10
Part, 10 parts of sepiolite particle, 20 parts of phenolic resin, 15 parts of tricresyl phosphate, 5 parts of rosin resin, 5 parts of polyethylene wax, tristearin
1 part, 1 part of silver nitrate solution of acid.
3. a kind of indoor moisture-proof is non-burning brick according to claim 1, which is characterized in that according to parts by weight by following raw material
Composition: 90 parts of flyash, 50 parts of cement, 30 parts of riverway sludge, 15 parts of river sand, 10 parts of conch meal, 5 parts of sodium tetraborate, zeolite powder
15 parts, 15 parts of sepiolite particle, 25 parts of phenolic resin, 25 parts of tricresyl phosphate, 10 parts of rosin resin, 10 parts of polyethylene wax,
3 parts of stearic acid, 5 parts of silver nitrate solution.
4. a kind of indoor moisture-proof is non-burning brick according to claim 1, which is characterized in that according to parts by weight by following raw material
Composition: 70 parts of flyash, 40 parts of cement, 25 parts of riverway sludge, 13 parts of river sand, 7 parts of conch meal, 3 parts of sodium tetraborate, zeolite powder 12
Part, 12 parts of sepiolite particle, 23 parts of phenolic resin, 20 parts of tricresyl phosphate, 8 parts of rosin resin, 7 parts of polyethylene wax, tristearin
2 parts, 3 parts of silver nitrate solution of acid.
5. a kind of indoor moisture-proof is non-burning brick according to claim 1, which is characterized in that the preparation method is as follows: (1) is by fine coal
Ash, cement, riverway sludge, river sand, conch meal, sodium tetraborate, zeolite powder, sepiolite particle are sufficiently mixed after crushing；It (2) will step
Suddenly raw material obtained by (1), which is put into blender, stirs, and phenolic resin is added in whipping process, tricresyl phosphate, rosin resin, gathers
Ethylene waxes, stearic acid, silver nitrate solution, mixing time are one hour；(3) raw material obtained by step (2) is put into brick machine machine
Adobe is made；(4) adobe obtained by step (3) is put into maintenance in vaporium, curing time is six hours；It (5) will be in step (4)
Gained adobe is cooled to room temperature, and is then laid flat after mulching straw natural curing 25 ~ 30 days.