CN102659385A - Refractory wall plate material and production method thereof - Google Patents
Refractory wall plate material and production method thereof Download PDFInfo
- Publication number
- CN102659385A CN102659385A CN2012101574080A CN201210157408A CN102659385A CN 102659385 A CN102659385 A CN 102659385A CN 2012101574080 A CN2012101574080 A CN 2012101574080A CN 201210157408 A CN201210157408 A CN 201210157408A CN 102659385 A CN102659385 A CN 102659385A
- Authority
- CN
- China
- Prior art keywords
- component
- bamboo
- fire
- parts
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a refractory wall plate material and a production method thereof. The refractory wall plate material comprises component A, component B and component C, wherein the component A is a mixed solution of magnesium chloride, bamboo root water, ferrous sulfate and thickening agent, the component B is magnesium oxide, and the component C is a mixed material of plant straws, pulverized coal ash, cinder and foam particles; the component A, the component B and the component C are mixed in a ratio of 1:(1-1.5):(1-2.0), and bamboo stickers are added to produce the material; and the bamboo stickers are soaked with insect-proofing mould-proofing liquid, the radial size of each bamboo sticker is between 6 and 10mm, the length of each bamboo sticker is the same as that of the plate, and the bamboo stickers are arranged in the plate at an interval of between 8 and 12cm. The refractory wall plate material and the wall plate have good fire-proofing, water-proofing and anti-corrosion performance, no anti-brine phenomenon, safety and environmental friendliness, no toxic or odor, can be mixed with conventional decoration materials, has high integration degree, good compatibility and lower cost.
Description
Technical field
The present invention relates to a kind of fire-proof wall panel material, mainly be used as body of wall.The working method that relates to this fire-proof wall panel material simultaneously.
Background technology
At present; China's wall board material 90% is a solid clay brick; Compare with external similar wall board material, about its production energy consumption on average doubled, exterior-wall heat insulation and heat-proof quality but differed 4～5 times; Defectives such as the heating energy consumption of unit floor area of building is about 3 times of developed country under the equal conditions, and various body of wall ubiquity sealing properties are weak simultaneously, heat-insulating property is poor, resource consumption is high, the resource regeneration rate is low.China is an energy consumption big country, also is poor with the short relatively country of an energy, and serious waste of resources, a little less than the resource regeneration ability relative thin.We can say that energy shortage is restricting the long term growth of China's economic construction.Accelerating materials for wall innovation and building energy conservation, is an instant major issue.Research and develop novel energy-saving, the environment-friendly type quality matetrial is imperative.Chinese patent CN200410022356.1 environment-friendly fireproof wallboard and method of manufacture thereof; Disclose and used agricultural crop straw, industrial residue, nonmetal breeze and ordinary Portland cement environment-friendly fireproof wallboard and the method for manufacture thereof as main ingredient, main base-material mainly is to select industry wastes such as worker, farming for use, belongs to the utilization of three wastes; Also belong to the agricultural byproducts deep processing; Itself does not fire wallboard, anticorrosion protection against the tide simultaneously, nontoxic, environmental protection.The CN02134043.9 composite environment-protection fire-retardant wall plate; Its component comprises 50～80 parts of magnalium composite gelled materials by weight, 0～20 part of hollow float bead, 2～20 parts of expanded vermiculites; In agricultural crop straw, sawdust and the rice wheat litter shell powder at least a 8～32 parts; 5～20 parts in flyash, 2～8 parts of flame-proofing agents, 1～10 part of composite modifier.This wallboard has fire-resistant, sound insulation property, intensity height, halogenation, frost mist free, water-fast, can saw, can follow closely, the comprehensive utilization industrial and agricultural waste is produced no three wastes generation, is mainly used in non-load bearing partition.CN1621390 inorganic fire plate, its manufacturing materials mainly comprises silicate calcium binder and inorganic oxide particles, wherein, the weight percent of silicate calcium binder in the PLASTIC LAMINATED manufacturing materials is 10-15%.The sub product cinder that the coal-burning power plant produces can be used as the silicate calcium binder.Inorganic fire plate of the present invention is difficult for expanding and is broken, and intensity increases.The CN101781113A inorganic fire-resistant foam filling material for door core board is mainly formed through the whipping agent foaming by slip, and the composition of said slip and the quality of each composition are: Magnesium Chloride Anhydrous 15-25 part; Sal epsom 5-15 part, thomel 0.5-0.8 part, fire prevention bamboo let 0.2-0.3 part; Kaolin 5-10 part; Coal ash 3-6 part, light magnesium oxide 45-55 part, closed perlite 1.5-2.5 part, water 25-35 part; The raw material of said whipping agent and the mass fraction of each composition are: animal protein foaming agent 1.5-2.5 part, K12 whipping agent 1-2 part, water 25-30 part.Framework material uniform distribution in the foam material of the present invention, foaming effect is high, and foaming structure is stable, Kong Mi, soundproof effect are good, and the fire-protection rating of foam material is high, and fire resistance property is strong.Foregoing invention all is the achievement that aspect fire-retardant material, obtains in recent years.
Summary of the invention
The object of the present invention is to provide a kind of flame retardant properties good, cost is lower, the fire-proof wall panel material of health environment-friendly.
Second purpose of the present invention is to provide the working method of this fire-proof wall panel material.
The objective of the invention is to realize through following technical scheme, a kind of fire-proof wall panel material, it is processed by A component (high-efficiency activated dose), B component, three kinds of component mixtures of C component (stopping composition) and bamboo let:
Said A component is the mixed solution of magnesium chloride, bamboo root water, ferrous sulfate and thickening material, and the weight ratio of said each composition of mixed solution is: 80～96.5 parts in magnesium chloride, 2～5 parts in bamboo root water, 1～5 part in ferrous sulfate, 0.5～2 part of thickening material; Adding water after four kinds of mixing of materials again, to be mixed with concentration be 20%～38% mixed solution.The B component is a Natural manganese dioxide; The C component is the solid mixture that is made up of the straw of drying and crushing, flyash or slag, foam (referring to polyethylene) particle; Its weight ratio is: 0～70 part of straw, 10～90 parts in flyash or slag, 10～30 parts of foam beads; In the C component, preferred weight part of each composition is: straw is 20～30 parts; 30～40 parts in flyash or slag; Foam beads is 10～20 parts.
The weight ratio of A component, B component, C component is 1:1～1.5:1～2.0; Range upon range of even placement bamboo let in the mixture of A, B, C three components solidifies the back and constitutes solid plate.
Said Natural manganese dioxide is selected heavy-calcined magnesia for use; The arrangement pitches of bamboo let in firewall body board is 8-12cm, and bamboo let will be used Vermins-proof mildew-proof liquid medicine (like phosphoric acid, Natural manganese dioxide mixed solution) immersion treatment 2-5 hour; The bamboo let radial dimension is 6-10mm, and bamboo let length is identical with sheet material length.
Thickening material is meant cement thickening material commonly used (the cement thickening material of for example, being made up of plaster stone, ethoxylated alkyl sodium sulphite, sodium laurylsulfonate, water reducer etc.).
Bamboo root water is meant the moisture content that comes out with the bamboo boiling.
Foam beads is meant the polyethylene particle.
Second purpose of the present invention realizes through following technical scheme: the working method of fire-proof wall panel material comprises that the following step gathers:
(1) raw material of A component, B component, C component is prepared
The A component: the mixed solution preparation of magnesium chloride and bamboo root water, ferrous sulfate and thickening material takes by weighing raw material by following weight proportion: 88～96.5 parts in magnesium chloride, 2～5 parts in bamboo root water, 1～5 part in ferrous sulfate, 0.5～2 part of thickening material; Adding water again, to be mixed with weight concentration be 20%～38% mixed solution.
The B component: Natural manganese dioxide is heavy-calcined magnesia
The C component: take by weighing 0～70 part of straw by following weight proportion, 10～90 parts in flyash or slag, 10～20 parts of foam beads mix;
By weight for the ratio of 1:1～1.5:1～2.0 takes by weighing said A component, B component, C component respectively, place container, subsequent use;
(2) with the material of A component 30～40%, the material of B component 30～50% adds in the stirrer, mixes;
(3) add the C component, mix, more remaining B component materials is added, stir, then remaining A component materials is poured into, stir into slurry;
(4) gathered (3) gained slurry the step and pour in the mould, in pouring the slurry process into, horizontal every interval 8-12cm places a bamboo let, compaction moulding, (or after 5～19 hours) form removal after 2～24 hours of hardening, finishing, check warehouse-in.
Described bamboo let soaked 2 ~ 5 hours with liquid medicine (like phosphoric acid, Natural manganese dioxide mixed solution) earlier.
The present invention's fire-proof wall panel material and existing like product relatively have the following advantages:
1, product of the present invention can not produce anti-halogen phenomenon because of environmental degradation in production process and practical process; 2, have higher fire-retardant, fire prevention, explosion-proof ability, have more safe and practical property.3, unharmful substance or toxic gas discharging; 4, can mix use with present some finishing material on the market, conjugation is high, and consistency is good; 5, cost is low, and construction is simple, improves decoration efficiency.
Embodiment
Below in conjunction with embodiment the present invention is described further.
Embodiment 1: this fire-proof wall panel material is processed by A component, B component, three kinds of mixtures of C component and bamboo let:
Said A component is the mixed solution of magnesium chloride, bamboo root water, ferrous sulfate and thickening material; Each composition weight proportioning: magnesium chloride 88kg, bamboo root water 5kg, ferrous sulfate 5kg, cement thickening material 2kg; Adding water, to be mixed with weight concentration be 30% mixed solution; The B component is a heavy-calcined magnesia; The C component is a weighting material, is mixed by straw, flyash or the slag of drying and crushing, foam beads to constitute; The C components by weight does; Straw 40kg, flyash 50kg, foam beads 10kg.Bamboo let will be used Vermins-proof mildew-proof liquid medicine (like phosphoric acid, Natural manganese dioxide mixed solution) immersion treatment 2-5 hour; The bamboo let radial dimension is 6-10mm, and bamboo let length is identical with sheet material length.
In said three kinds of component mixtures, the weight ratio of A component, B component, C component is 1:1:1; The mixture of said A, B, three kinds of components of C is evenly placed bamboo let, constitutes solid plate.
Its working method comprises that the following step gathers:
(1) A component, B component, C component raw material are prepared
A component: take by weighing magnesium chloride, bamboo root water, ferrous sulfate, thickening material by the predetermined weight proportioning: adding water again, to be mixed with weight concentration be 30% mixed solution.B component: by the predetermined weight proportioning matter Natural manganese dioxide of weighing; C component: take by weighing straw, flyash or slag, foam beads after the pulverizing by the predetermined weight proportioning, mix;
By weight take by weighing said A, B, C three component materials respectively for the ratio of 1:1:1, place container again, subsequent use;
(2) material of A component 35% and the material of B component 40% are added in the stirrer, mix;
(3) add the C component, mix, the material with remaining B component 60% adds again, stirs, and then remaining A component materials is poured into, stirs into slurry;
(4) gathered (3) gained slurry the step and pour in the mould, in pouring the slurry process into, horizontal every interval 8-12cm places a bamboo let, and compaction moulding hardened after 6 hours, form removal, finishing, check warehouse-in.
Said each starting material specify:
The A component is high-efficiency activated dose, and chemical property is stable.Join and to make product have good acid resistance, resistivity against fire, heat insulating ability and moisture absorption in the product.
The B component is a heavy-calcined magnesia, white powder, and specific density 3.26%～3.43%, water insoluble and pure; Be dissolved in acid and ammonium solution, mix easy gelling sclerosis with A, C component, nontoxic, be prone to absorb carbon dioxide in air and moisture content when being exposed in the air; And generate alkali or magnesiumcarbonate and hardening, the fireproof heat-insulating performance of height is arranged, require Natural manganese dioxide contain>=85%; Loss on ignition≤8% is deposited in dry place, keeps away from moisture.
The C component is organic filler, and the straw end requires inclusion-free, does not have to go rotten, and does not have situation such as rotten.Its water ratio should be less than 25%, and silt content should can be powder such as cogongrass, branch on the wheat head, straw, rice husk, cornstalk, sesame stalk, sunflower stalk, tobacco stalk, the mountain less than 3%.Can put cinder ash 10%.
The present embodiment product is pressed the GB/T5464-1999 prescriptive procedure and is detected, and 3 ℃ of temperature rises in the stove (standard≤30 ℃) the sustained combustion time is 0 second (standard is 0 second), mass loss rate 36.6% (standard≤50%); Press the GB/T14402-2007 prescriptive procedure and detect calorific value 0.2MJ/kg (standard≤2.0); Press the GB/T20285-2006 prescriptive procedure and detect, cigarette poison gas property 100.0ml/L (safe primary standard AQ1>=100,0, laboratory animal 30min in the contamination phase and back three days of contamination not dead, and mean body weight is extensive heavy); Press GB/T8624-2006 and judge that flame retardant properties reaches national fire-proof construction material A1 level specified requirement; Press the GB/T5464-1999 prescriptive procedure and detect, except reaching A1 level flame retardant properties, fire endurance was greater than 2 hours; Cigarette poison gas property is pressed GB/T20285-2006 and is judged, reaches safe one-level (AQ1).
This product is Administration of Quality and Technology Supervision's check through the Hunan Province, and check data is following, confirms as quality products:
(1) aspect the bad load check of anti-folding, surpasses national building standard 1526 (state-set standard lower limit 2000, this examination and test of products data are 3526);
(2) aspect the drying shrinkage value check, be strict in national building standard 0.33 (be limited to 0.6 on the state-set standard, this examination and test of products data are 0.27);
(3) aspect the water ratio check, be strict in national standard (be limited to 15 on the state-set standard, this examination and test of products data are 26);
(4) aspect radioassay, be strict in national standard 0.9 (national regulation is up to the standards and is limited to 1 on the designation number, and this product internal radiation exponential sum external radiation exposure exponential check data is 0.1);
(5) aspect the shock resistance check, surpass national inspecting standard, (be limited to 5 under the state-set standard, this examination and test of products data are 7).
(6) be qualified or surpass national inspecting standard at aspect check conclusions such as air-dry density, hanging force, air sonic bang power sound insulation power oise insulation factors.In addition through the Hunan Province Administration of Quality and Technology Supervision " four disasters " assay of product is confirmed as qualified.
Embodiment 2:A component: each composition weight proportion: magnesium chloride 96.5kg, bamboo root water 2kg, ferrous sulfate 1kg, cement thickening material 0.5kg; Adding water, to be mixed with weight concentration be 30% mixed solution;
B component: industrial magnesium oxide;
C component: slag 90kg, foam beads 10kg.
In three kinds of component mixtures, the weight ratio of A component, B component, C component is 1:1.5:2; In the mixture of three kinds of components, evenly place bamboo let, constitute solid plate.
Setting time 10 hours.Surplus with implementing 1.
To various starting material specific requirements also with embodiment 1.
The present embodiment product is pressed the GB/T5464-1999 prescriptive procedure and is detected, and 5 ℃ of temperature rises in the stove (standard≤30 ℃) the sustained combustion time is 0 second (standard is 0 second), mass loss rate 40.2% (standard≤50%); Press the GB/T14402-2007 prescriptive procedure and detect calorific value 0.5MJ/kg (standard≤2.0); Press the GB/T20285-2006 prescriptive procedure and detect, cigarette poison gas property 100.0ml/L (safe primary standard AQ1>=100, laboratory animal 30min in the contamination phase and back three days of contamination not dead, and mean body weight is extensive heavy); Press GB/T8624-2006 and judge that flame retardant properties reaches national fire-proof construction material A1 level specified requirement; Press the GB/T5464-1999 prescriptive procedure and detect, except reaching A1 level flame retardant properties, fire endurance was greater than 2 hours; Cigarette poison gas property is pressed GB/T20285-2006 and is judged, also reaches safe one-level (AQ1)
Quality products is confirmed as in Administration of Quality and Technology Supervision's check through the Hunan Province
(1) surpassing national building standard 1526 (state-set standard lower limit 2000, and check data is 3526) aspect the bad load check of anti-folding;
(2) be strict in national building standard 0.33 (be limited to 0.6 on the state-set standard, and check data being 0.27) aspect the drying shrinkage value check;
(3) be strict in national standard (be limited to 15 on the state-set standard, and check data being 2.6) aspect the water ratio check;
(4) be strict in national standard 0.9 (national regulation is up to the standards and is limited to 1 on the designation number, and product internal radiation exponential sum external radiation exposure exponential check data is 0.1) aspect the radioassay;
(5) surpassing national inspecting standard 2 (be limited to 5 under the state-set standard, and check data being 7) aspect the shock resistance check;
(6) be qualified or surpass national inspecting standard at aspect check conclusions such as air-dry density, hanging force, air sonic bang power sound insulation power oise insulation factors.In addition through the Hunan Province Administration of Quality and Technology Supervision " four disasters " assay of product is confirmed as qualified.
Embodiment 3:
A component: its each composition weight proportion, magnesium chloride 92kg, bamboo root water 3.5kg, ferrous sulfate 3kg, cement thickening material 1.5kg; Adding water, to be mixed with weight concentration be 40% mixed solution;
B component: industrial magnesium oxide;
C component: straw 70kg, flyash 10kg, foam beads 20kg;
In three kinds of component mixtures, the weight ratio of A component, B component, C component is 1:1.3:1.5; Evenly place bamboo let in three kinds of component mixtures, constitute solid plate.
Setting time 20 hours.Surplus with implementing 1.
To various starting material specific requirements also with embodiment 1.
Anti-halogen phenomenon does not all take place in embodiment 1,2,3 products in process of production.
Embodiment 1,2,3 products in use all do not produce anti-halogen phenomenon because of environmental degradation.
The present embodiment product is pressed the GB/T5464-1999 prescriptive procedure and is detected, and 6 ℃ of temperature rises in the stove (standard≤30 ℃) the sustained combustion time is 0 second (standard is 0 second), mass loss rate 36.6% (standard≤50%); Press the GB/T14402-2007 prescriptive procedure and detect calorific value 0.6MJ/kg (standard≤2.0); Press the GB/T20285-2006 prescriptive procedure and detect, cigarette poison gas property 100.0ml/L (safe primary standard AQ1>=100, laboratory animal 30min in the contamination phase and back three days of contamination not dead, and mean body weight is extensive heavy); Press GB/T8624-2006 and judge that flame retardant properties reaches national fire-proof construction material A1 level specified requirement; Press the GB/T5464-1999 prescriptive procedure and detect, except reaching A1 level flame retardant properties, fire endurance was greater than 2 hours; Cigarette poison gas property is pressed GB/T20285-2006 and is judged, also reaches safe one-level (AQ1).
Product is Administration of Quality and Technology Supervision's check through the Hunan Province, regards as quality products.
(1) surpassing national building standard 1526 (state-set standard lower limit 2000, this examination and test of products data are 3526) aspect the bad load check of anti-folding;
(2) be strict in national building standard 0.33 (be limited to 0.6 on the state-set standard, this examination and test of products data are 0.27) aspect the drying shrinkage value check;
(3) be strict in national standard (be limited to 15 on the state-set standard, this examination and test of products data are 2.6) aspect the water ratio check;
(4) be strict in national standard 0.9 (national regulation is up to the standards and is limited to 1 on the designation number, and this product internal radiation exponential sum external radiation exposure exponential check data is 0.1) aspect the radioassay;
(5) surpassing national inspecting standard 2 (be limited to 5 under the state-set standard, this examination and test of products data are 7) aspect the shock resistance check;
(6) be qualified or surpass national inspecting standard at aspect check conclusions such as air-dry density, hanging force, air sonic bang power sound insulation power oise insulation factors.In addition through the Hunan Province Administration of Quality and Technology Supervision " four disasters " assay of product is confirmed as qualified.
Claims (5)
1. a fire-proof wall panel material is characterized in that, is processed by A component, B component, three kinds of mixtures of C component and bamboo let:
Said A component is the mixed solution of magnesium chloride, bamboo root water, ferrous sulfate and thickening material, and the weight ratio of each composition is in the said mixed solution: 80～96.5 parts in magnesium chloride, 2～5 parts in bamboo root water, 1～5 part in ferrous sulfate, 0.5～2 part of thickening material; Adding water after four kinds of mixing of materials again, to be mixed with concentration be 20%～38% mixed solution;
Said B component is a Natural manganese dioxide;
Said C component is a solid mixture, and the weight part of each raw material is: 0～70 part of straw, 10～90 parts in flyash or slag, 10～30 parts of foam beads;
The weight ratio of A, B, C three components is 1:1～1.5:1～2.0; In the mixture of A, B, C three components, evenly place bamboo let, compaction moulding solidifies the back and constitutes solid plate.
2. fire-proof wall material according to claim 1 is characterized in that: said Natural manganese dioxide is industrial heavy-calcined magnesia; The arrangement pitches of bamboo let in firewall body board is 8-12cm, and bamboo let length is identical with sheet material length.
3. fire-proof wall material according to claim 1 and 2 is characterized in that: in the C component, the weight part of each raw material is: straw is 20～30 parts; 30～40 parts in flyash or slag; Foam beads is 10～20 parts.
4. the working method of fire-proof wall panel material is characterized in that: may further comprise the steps:
(1) raw material is prepared
A component mixed solution preparation takes by weighing each raw material by above-mentioned weight part, and adding water again, to be mixed with weight concentration be 20%～38% mixed solution;
B component: Natural manganese dioxide;
C component: take by weighing straw, flyash or slag, foam beads after the drying and crushing by above-mentioned weight part, mix;
Ratio in A, B, C three components by weight 1:1～1.5:1～2.0 takes by weighing said material respectively, places container, and is subsequent use;
(2) A component materials 30～40% and B component materials 30～50% are added in the stirrer, mix;
(3) add the C component, mix, remaining B component materials is added stir again, then remaining A component materials is poured into, stir into slurry;
(4) gathered (3) gained slurry the step and pour in the mould, in pouring the slurry process into, horizontal every interval 8-12cm places a bamboo let, and compaction moulding hardened after 5～19 hours, form removal, finishing, check warehouse-in.
5. according to the working method of the said fire-proof wall material of claim 4, it is characterized in that described bamboo let will be used Vermins-proof mildew-proof liquid medicine immersion treatment 2-5 hour; The bamboo let radial dimension is 6-10mm, and bamboo let length is identical with sheet material length.