CN1094334C - 一种防弹头盔制造方法 - Google Patents

一种防弹头盔制造方法 Download PDF

Info

Publication number
CN1094334C
CN1094334C CN 97115106 CN97115106A CN1094334C CN 1094334 C CN1094334 C CN 1094334C CN 97115106 CN97115106 CN 97115106 CN 97115106 A CN97115106 A CN 97115106A CN 1094334 C CN1094334 C CN 1094334C
Authority
CN
China
Prior art keywords
aramid fiber
helmet
bullletproof
rubber fabric
resin glue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 97115106
Other languages
English (en)
Other versions
CN1205852A (zh
Inventor
周国泰
杨廷欣
刘善晖
刘水林
张建春
吴铿敏
胡汝能
周宏�
杨琪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Technique Development Dept Military Supplies And Equipments Inst General
Original Assignee
Technique Development Dept Military Supplies And Equipments Inst General
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Technique Development Dept Military Supplies And Equipments Inst General filed Critical Technique Development Dept Military Supplies And Equipments Inst General
Priority to CN 97115106 priority Critical patent/CN1094334C/zh
Publication of CN1205852A publication Critical patent/CN1205852A/zh
Application granted granted Critical
Publication of CN1094334C publication Critical patent/CN1094334C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种防弹头盔制造方法,其工艺过程是,有一个循环运行的涂胶带,该胶带运行的一端设有树脂胶胶池,运行的中部设有加热板,运行的另一端设有冷却板,芳纶布带一端卷在生料辊上另一端卷在熟料辊上,并由生料辊向熟料辊上卷绕,涂胶带挂胶后与芳纶布带合并在一起,共同经加热板加热,将树脂胶转移到芳纶布表面上,将带有树脂胶的芳纶布用模具冲裁成多瓣花形坯料,将该坯料依次多层叠放在一起,再放入成型模具中加压、加热成型。

Description

一种防弹头盔制造方法
本发明涉及一种防弹头盔制造方法,该头盔是采用多层芳纶布压制而成的高性能防护制品,它适用于军人作战训练及保安人员执行任务时佩戴。
现有的防弹头盔有金属头盔和芳纶布头盔,芳纶布头盔的盔体,由多层芳纶布叠加并经树脂胶粘合,并热压而成,其工艺过程是先将芳纶布浸胶后再叠加,由于树脂胶浸入布的组织内,使芳纶布变脆,导致防弹能力下降。
本发明的目的是提供一种防弹头盔制造方法,该方法可将树脂胶涂在芳纶布的表面,不会浸入芳纶布的组织内,可提高本发明的防弹能力。
本发明的目的是由下述的技术方案实现的,一种防弹头盔制造方法,其盔体采用多层芳纶布压制而成,其工艺过程是,有一个循环运行的涂胶带,该胶带运行的一端设有树脂胶胶池,运行的中部设有加热板,运行的另一端设有冷却板,芳纶布带一端卷在生料辊上另一端卷在熟料辊上,并由生料辊向熟料辊上卷绕,涂胶带的线速度与芳纶布带的线速度相同,涂胶带经过胶池时挂胶,经过加热板加热到60-80℃,并通风干燥,经干燥后的涂胶带与芳纶布带合并在一起,共同经加热板加热到50-60℃,将树脂胶转移到芳纶布表面上,再经冷却板冷却处理,然后带有胶膜的芳纶布带与涂胶带分离,卷制到熟料辊上,将带有树脂胶的芳纶布用模具冲裁成多瓣花形坯料,将该坯料依次多层叠放在一起,层与层之间相对错开相同的角度,将叠加后的坯料放入模具加热预成型,用裁边机裁去毛边,再放入成型模具中加压、加热成型。
用本发明制造的头盔具有抗弹性能好,抗钝击能力强,能适应恶劣环境的优点。
以下结合附图及实施例对本发明作进一步说明:
图1  用本发明制造的防弹头盔示意图
图2  涂胶流程及设备示意图
图3  多瓣花形坯料示意图
参见附图,用本发明制造的防弹头盔由盔体1、帽顶带组件2、迷彩罩3、帽口组件4、风带组件5及下颌带组件6组成,其盔体采用多层芳纶布压制而成,其工艺过程是:参见附图2、附图3,有一个循环运行的涂胶带8,该胶带运行的一端设有树脂胶胶池9,运行的中部设有加热板10,运行的另一端设有冷却板12,芳纶布带14一端卷在生料辊15上另一端卷在熟料辊16上,并由生料辊向熟料辊上卷绕,涂胶带的线速度与芳纶布带的线速度相同,涂胶带经过胶池时挂胶,经过加热板加热到60-80℃,并经通风道7通风干燥,经干燥后的涂胶带与芳纶布带合并在一起,共同经加热板加热到50-60℃,将树脂胶转移到芳纶布表面上,形成0.08-0.09毫米厚的胶膜,该胶膜将不会浸入布纹,因而不会影响到芳纶布的防弹能力,然后再经冷却板冷却处理,冷却处理后,带有胶膜的芳纶布带与涂胶带分离,卷制到熟料辊上,将带有树脂胶的芳纶布用模具裁成多瓣花形坯料18,将该坯料依次多层叠放在一起,层与层之间相对错开相同的角度,并保证叠加厚度均匀,将叠加后的坯料放入模具加热预成型,用裁边机裁去毛边,再放入成型模具中加压、加热成型。所述涂胶带的线速度是1-3米/分,最佳线速度是2米/分。所述的树脂胶由酚醛树脂及聚乙烯醇缩丁醛组成,其重量比为1比1,并由酒精调配而成。所述的预成型压力为5Mpa,温度为60℃,保持4-5分钟,成型压力为7Mpa,温度为160℃,保持15-20分钟。然后是盔体钻孔→盔面处理→贴胶条→喷底漆→装配悬挂附件→喷面漆→成品包装。
用本发明制造的防弹头盔的盔体有效防护及积为1266cm2,盔体重心低,佩截稳定性好,护耳突出,听力效果好。本发明抗弹性能优良,在五四式手枪,五一式标准弹。5米射距、弹速在420-450米/秒的射击条件下,抗弹率为100%;抗钝击能力符合国家安全帽GB2811-89的标准测试要求,而且其抗纯击能力优于现行GK80钢盔。成品盔总重量平均不超过1450克。头盔无论在-40℃低温下和50℃高温环境条件下不影响盔体抗弹效果,该盔体耐淋雨抗冲击性能,防盐雾腐蚀和抗霉菌能力均符合国家标准要求。

Claims (4)

1、一种防弹头盔制造方法,其盔体(1)采用多层芳纶布压制而成,其特征在于:有一个循环运行的涂胶带(8),该胶带运行的一端设有树脂胶胶池(9),运行的中部设有加热板(10),运行的另一端设有冷却板(12),芳纶布带(14)一端卷在生料辊(15)上另一端卷在熟料辊(16)上,并由生料辊向熟料辊上卷绕,涂胶带的线速度与芳纶布带的线速度相同,涂胶带经过胶池时挂胶,经过加热板加热到60-80℃,并通风干燥,经干燥后的涂胶带与芳纶布带合并在一起,共同经加热板加热到50-60℃,将树脂胶转移到芳纶布表面上,形成0.08-0.09毫米厚的胶膜,再经冷却板冷却处理,然后带有胶膜的芳纶布带与涂胶带分离,卷制到熟料辊上,将带有树脂胶的芳纶布用模具冲裁成多瓣花形坯料(18),将该坯料依次多层叠放在一起,层与层之间相对错开相同的角度,将叠加后的坯料放入模具加热预成型,用裁边机裁去毛边,再放入成型模具中加压、加热成型。
2、根据权利要求1所述的防弹头盔制造方法,其特征在于:所述的树脂胶由酚醛树脂及聚乙烯醇缩丁醛组成,其重量比为1比1,并由酒精调配而成。
3、根据权利要求2所述的防弹头盔制造方法,其特征在于:所述的预成型压力为5Mpa,温度为60℃,保持5分钟,成型压力为7Mpa,温度为160℃,保持15-20分钟。
4、根据权利要求3所述的防弹头盔制造方法,其特征在于:所述涂胶带的线速度是1-3米/分,最佳线速度是2米/分。
CN 97115106 1997-07-21 1997-07-21 一种防弹头盔制造方法 Expired - Fee Related CN1094334C (zh)