CN109423204A - 一种薄层保温防腐涂料及其制备方法 - Google Patents

一种薄层保温防腐涂料及其制备方法 Download PDF

Info

Publication number
CN109423204A
CN109423204A CN201710463139.3A CN201710463139A CN109423204A CN 109423204 A CN109423204 A CN 109423204A CN 201710463139 A CN201710463139 A CN 201710463139A CN 109423204 A CN109423204 A CN 109423204A
Authority
CN
China
Prior art keywords
parts
thin
anticorrosive paint
insulation anticorrosive
walled insulation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710463139.3A
Other languages
English (en)
Inventor
陆文兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710463139.3A priority Critical patent/CN109423204A/zh
Publication of CN109423204A publication Critical patent/CN109423204A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种薄层保温防腐涂料，属于涂料技术领域，包括以下重量份数的原料：环氧改性有机硅树脂10～40份、二甲苯25～55份、邻苯二甲酸二丁酯10～20份、陶瓷微球2～3份和高岭土1～3份。本发明的一种薄层保温防腐涂料，以环氧改性有机硅树脂作为成膜物质,并以玻璃体二氧化硅材料、特殊陶瓷材料、磷酸锌、纤维材料为填料,制成保温隔热防腐涂料。该涂料固化后具有耐热、耐油、防潮、绝缘、附着力强、机械性能较好等特点，并具有较好的隔热效果；本发明的另一目的是提供该薄层保温防腐涂料的制备方法。

Description

一种薄层保温防腐涂料及其制备方法
技术领域
本发明属于涂料技术领域，具体涉及一种薄层保温防腐涂料及其制备方法。
背景技术
近年来，中国涂料行业在高速成长的房地产、汽车、船舶、等下游行业的推动下，以高于GDP5％-10％的速度增长，成为世界涂料生产和消费第二大国。
2006年1-12月，中国涂料、油墨、颜料及类似产品制造业实现累计工业总产值191,934,746千元，比上年同期增长26.19％；全年实现累计产品销售收入185,825,254千元，比上年同期增长25.94％；全年实现累计利润总额12,513,338千元，比上年同期增长25.7％。
2007年1-11月，全国1985家涂料企业累计的现价工业总产值为11909344万元，同比增长27.5％，其中新产品产值1-11月累计为528843万元，同比增长39.2％，同期涂料销量也保持快速增长的势头。涂料行业连续多年都保持较快增长，从2006年1月1日起取消相关产品出口关税，涂料行业的发展进一步提速。
涂料产品品种越来越多，应用范围也不断扩大，涂料工业已成为化学工业中一个重要的独立生产工业部门。我国目前涂料产量约为200万吨以上，其中工业涂料占60％，近年来需求量以3.4％的平均速度增长。
2008年我国涂料市场供需大体平衡，但结构尚需优化。2008年我国家装及建筑用涂料消费量将呈增加趋势，涂料需求量将超过255万吨。其中，工业涂料约90万吨，建筑涂料115万吨，特种涂料及其他功能性涂料50万吨。品种结构大体按工业涂料35％～40％、建筑涂料45％～50％、特种涂料10％～15％分布。2007年全国涂料供给量约260万吨，与需求量大体相近，基本平衡。
2009年中国涂料产量达755万吨，其中汽车涂料占6％，约为45万吨，木器涂料占10％，约为74万吨，船舶涂料占5％，约为40万吨，粉末涂料占11％，约为80万吨，其它工业涂料占33％，约为253万吨，建筑涂料占35％，约为264万吨。按年产量来算，我国涂料行业己挤身世界最前列。但人均涂料用量仍非常少，我们认为在庞大并正迅速增长的市场需求面前，提升涂料品质迫在眉睫！
发明内容
发明目的：本发明的目的在于提供一种薄层保温防腐涂料，本发明的另一目的是提供该薄层保温防腐涂料的制备方法。
技术方案：为实现上述发明目的，本发明采用如下技术方案：
一种薄层保温防腐涂料，包括以下重量份数的原料：环氧改性有机硅树脂10～40份、二甲苯25～55份、邻苯二甲酸二丁酯10～20份、陶瓷微球2～3份和高岭土1～3份。
所述的原料还包括重量份数为5～10份的玻璃粉。
所述的原料还包括重量份数为2～3份的石棉绒。
所述的原料还包括重量份数为5～10份的玻璃体的二氧化硅。
一种薄层保温防腐涂料的制备方法，包括以下步骤：
1)按照比例将环氧改性有机硅树脂、二甲苯、邻苯二甲酸二丁酯、陶瓷微球和高岭土混合搅拌均匀，得到混合物；
2)取混合物，向其中依次添加其他配料得到薄层保温防腐涂料。
有益效果：与现有技术相比，本发明的一种薄层保温防腐涂料，以环氧改性有机硅树脂作为成膜物质,并以玻璃体二氧化硅材料、特殊陶瓷材料、磷酸锌、纤维材料为填料,制成保温隔热防腐涂料。该涂料固化后具有耐热、耐油、防潮、绝缘、附着力强、机械性能较好等特点，并具有较好的隔热效果；本发明的另一目的是提供该薄层保温防腐涂料的制备方法。
具体实施方式
下面结合具体实施方式对本发明做进一步的说明。
实施例1
一种薄层保温防腐涂料，包括以下重量份数的原料：环氧改性有机硅树脂10份、二甲苯25份、邻苯二甲酸二丁酯10份、陶瓷微球2份和高岭土1份。
原料还包括重量份数为5份的玻璃粉、2份的石棉绒、5份的玻璃体的二氧化硅。
一种薄层保温防腐涂料的制备方法，包括以下步骤：
1)按照比例将环氧改性有机硅树脂、二甲苯、邻苯二甲酸二丁酯、陶瓷微球和高岭土混合搅拌均匀，得到混合物；
2)取混合物5g，用250ml开水冲泡后，放置10分钟，滤出杂质后即得薄层保温防腐涂料。
实施例2
一种薄层保温防腐涂料，包括以下重量份数的原料：环氧改性有机硅树脂40份、二甲苯55份、邻苯二甲酸二丁酯20份、陶瓷微球3份和高岭土3份。
原料还包括重量份数为10份的玻璃粉、3份的石棉绒、10份的玻璃体的二氧化硅。
一种薄层保温防腐涂料的制备方法，包括以下步骤：
1)按照比例将环氧改性有机硅树脂、二甲苯、邻苯二甲酸二丁酯、陶瓷微球和高岭土混合搅拌均匀，得到混合物；
2)取混合物，向其中依次添加其他配料得到薄层保温防腐涂料。
实施例3
一种薄层保温防腐涂料，包括以下重量份数的原料：环氧改性有机硅树脂15份、二甲苯30份、邻苯二甲酸二丁酯12份、陶瓷微球2.2份和高岭土1.5份。
原料还包括重量份数为6份的玻璃粉、2.5份的石棉绒、7份的玻璃体的二氧化硅。
一种薄层保温防腐涂料的制备方法，包括以下步骤：
1)按照比例将环氧改性有机硅树脂、二甲苯、邻苯二甲酸二丁酯、陶瓷微球和高岭土混合搅拌均匀，得到混合物；
2)取混合物，向其中依次添加其他配料得到薄层保温防腐涂料。
实施例4
一种薄层保温防腐涂料，包括以下重量份数的原料：环氧改性有机硅树脂30份、二甲苯25份、邻苯二甲酸二丁酯20份、陶瓷微球3份和高岭土1份。
原料还包括重量份数为10份的玻璃粉、3份的石棉绒、8份的玻璃体的二氧化硅。
一种薄层保温防腐涂料的制备方法，包括以下步骤：
1)按照比例将环氧改性有机硅树脂、二甲苯、邻苯二甲酸二丁酯、陶瓷微球和高岭土混合搅拌均匀，得到混合物；
2)取混合物，向其中依次添加其他配料得到薄层保温防腐涂料。
实施例5
一种薄层保温防腐涂料，包括以下重量份数的原料：环氧改性有机硅树脂40份、二甲苯55份、邻苯二甲酸二丁酯20份、陶瓷微球3份和高岭土1份。
原料还包括重量份数为10份的玻璃粉、3份的石棉绒、8份的玻璃体的二氧化硅。
一种薄层保温防腐涂料的制备方法，包括以下步骤：
1)按照比例将环氧改性有机硅树脂、二甲苯、邻苯二甲酸二丁酯、陶瓷微球和高岭土混合搅拌均匀，得到混合物；
2)取混合物，向其中依次添加其他配料得到薄层保温防腐涂料。
在219管道外进行测试,管道外部涂覆了115mm厚该涂料,隔热测试结果如下表所示。
测试结果
管内温度/℃ 外表点1/℃ 外表点2/℃ 外表平均温度/℃ 隔热能力/℃
60 34 32 33 27
100 51 52 5115 4815
150 59 60 5915 4015
200 78 76 77 123
250 94 92 93 157

Claims (5)

1.一种薄层保温防腐涂料，其特征在于：包括以下重量份数的原料：环氧改性有机硅树脂10～40份、二甲苯25～55份、邻苯二甲酸二丁酯10～20份、陶瓷微球2～3份和高岭土1～3份。
2.根据权利要求1所述的一种薄层保温防腐涂料，其特征在于：所述的原料还包括重量份数为5～10份的玻璃粉。
3.根据权利要求1所述的一种薄层保温防腐涂料，其特征在于：所述的原料还包括重量份数为2～3份的石棉绒。
4.根据权利要求1所述的一种薄层保温防腐涂料，其特征在于：所述的原料还包括重量份数为5～10份的玻璃体的二氧化硅。
5.权利要求1～4中任意一项所述的一种薄层保温防腐涂料的制备方法，其特征在于：包括以下步骤：
1)按照比例将环氧改性有机硅树脂、二甲苯、邻苯二甲酸二丁酯、陶瓷微球和高岭土混合搅拌均匀，得到混合物；
2)取混合物，向其中依次添加其他配料得到薄层保温防腐涂料。
CN201710463139.3A 2017-06-19 2017-06-19 一种薄层保温防腐涂料及其制备方法 Pending CN109423204A (zh)