CN109400021A - 一种低收缩低粘度超高强混凝土 - Google Patents

一种低收缩低粘度超高强混凝土 Download PDF

Info

Publication number
CN109400021A
CN109400021A CN201811346244.XA CN201811346244A CN109400021A CN 109400021 A CN109400021 A CN 109400021A CN 201811346244 A CN201811346244 A CN 201811346244A CN 109400021 A CN109400021 A CN 109400021A
Authority
CN
China
Prior art keywords
high strength
super high
water
strength concrete
low viscosity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811346244.XA
Other languages
English (en)
Inventor
高志勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Anjie Geotechnical Engineering Co Ltd
Original Assignee
Jiangsu Anjie Geotechnical Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Anjie Geotechnical Engineering Co Ltd filed Critical Jiangsu Anjie Geotechnical Engineering Co Ltd
Priority to CN201811346244.XA priority Critical patent/CN109400021A/zh
Publication of CN109400021A publication Critical patent/CN109400021A/zh
Pending legal-status Critical Current

Abstract

本发明是一种低收缩低粘度超高强混凝土，配方中的原料按重量百分比组成分别是：水泥1‑5%，微珠1‑5%，矿粉2‑4%，机制砂5‑13%，减水剂15‑20%，碎石8‑10%，水5‑7%，通过本方法制备的产品，可以同时解决超高强混凝土的收缩开裂以及粘性过大导致泵送困难的问题。

Description

一种低收缩低粘度超高强混凝土
技术领域
本发明公开了一种低收缩低粘度超高强混凝土。
背景技术
高强高性能混凝土因具有高强度、高抗腐蚀耐久性，可减小结构尺寸、减轻结构自重、 节约用地、降低能耗、降低结构维修费和重建费等优点，其技术发展成为了建筑行业重点研究并关注的混凝土技术之一，目前多数技术配制超高强混凝土时，胶凝材料种类均在4种及以上，且水泥为52.5硅酸盐水泥，若大规模生产时，商品混凝土搅拌站又将会面临粉料储存罐数量不足的困境，使得混凝土技术难以真正大规模应用于实际工程中，最终脱离实际应用。
发明内容
针对上述现有技术存在的问题，本发明提供一种低收缩低粘度超高强混凝土，可以同时解决超高强混凝土的收缩开裂以及粘性过大导致泵送困难的问题。
为了实现上述目的，本发明通过以下技术方案实现：一种低收缩低粘度超高强混凝土，配方中的原料按重量百分比组成分别是：水泥1-5%，微珠1-5%，矿粉2-4%，机制砂5-13%，减水剂15-20%，碎石8-10%，水5-7%。
有益效果：通过本方法制备的产品，可以同时解决超高强混凝土的收缩开裂以及粘性过大导致泵送困难的问题。
具体实施方式
一种低收缩低粘度超高强混凝土，配方中的原料按重量百分比组成分别是：水泥1-5%，微珠1-5%，矿粉2-4%，机制砂5-13%，减水剂15-20%，碎石8-10%，水5-7%。
实施例1
一种低收缩低粘度超高强混凝土，配方中的原料按重量百分比组成分别是：1%水泥，1%微珠，2%矿粉，5%机制砂，15%减水剂，8%碎石，5%水，此时低收缩低粘度超高强混凝土不能解决收缩开裂的问题。
实施例2
一种低收缩低粘度超高强混凝土，配方中的原料按重量百分比组成分别是：5%水泥，5%微珠，4%矿粉，13%机制砂，20%减水剂，10%碎石，7%水，此时低收缩低粘度超高强混凝土不能解决粘性过大导致泵送困难的问题。
实施例3
一种低收缩低粘度超高强混凝土，配方中的原料按重量百分比组成分别是：3%水泥，3%微珠，3%矿粉，9%机制砂，17%减水剂，9%碎石，6%水，此时低收缩低粘度超高强混凝土可以同时解决超高强混凝土的收缩开裂以及粘性过大导致泵送困难的问题。

Claims (4)

1.一种低收缩低粘度超高强混凝土，其特征在于，配方中的原料按重量百分比组成分别是：水泥1-5%，微珠1-5%，矿粉2-4%，机制砂5-13%，减水剂15-20%，碎石8-10%，水5-7%。
2.根据权利要求1所述的低收缩低粘度超高强混凝土，其特征在于，配方中的原料按重量百分比组成分别是：1%水泥，1%微珠，2%矿粉，5%机制砂，15%减水剂，8%碎石，5%水。
3.根据权利要求1所述的低收缩低粘度超高强混凝土，其特征在于，配方中的原料按重量百分比组成分别是：5%水泥，5%微珠，4%矿粉，13%机制砂，20%减水剂，10%碎石，7%水。
4.根据权利要求1所述的低收缩低粘度超高强混凝土，其特征在于，配方中的原料按重量百分比组成分别是：3%水泥，3%微珠，3%矿粉，9%机制砂，17%减水剂，9%碎石，6%水。
CN201811346244.XA 2018-11-13 2018-11-13 一种低收缩低粘度超高强混凝土 Pending CN109400021A (zh)