CN109397790A - Chinese herbaceous peony the gear multi-functional composite glass structure of lifting and its manufacturing method - Google Patents
Chinese herbaceous peony the gear multi-functional composite glass structure of lifting and its manufacturing method Download PDFInfo
- Publication number
- CN109397790A CN109397790A CN201811427345.XA CN201811427345A CN109397790A CN 109397790 A CN109397790 A CN 109397790A CN 201811427345 A CN201811427345 A CN 201811427345A CN 109397790 A CN109397790 A CN 109397790A
- Authority
- CN
- China
- Prior art keywords
- glass
- lifter plate
- tin oxide
- plate
- compound glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Keeping off the invention discloses a kind of Chinese herbaceous peony with the multi-functional composite glass structure of lifting and its manufacturing method, the compound glass lifter plate includes the glass matrix set gradually, conductive indium-tin oxide layer, ink screen structure, thermally conductive layer, conductive indium-tin oxide layer, glass matrix；Side heat-conducting plate is provided in compound glass lifter plate two sides corresponding with vehicle A column；Conductive indium-tin oxide layer passes through light current winding displacement and DC circuit system communication；Microcapsules containing mass density 10% in ink screen structure, microcapsules include positively charged black particle and negatively charged white particle.Compound glass lifter plate of the invention have the shade function from main regulation, simple amusement function, vehicle body change it is small, widely used, cost performance is high, long service life.
Description
Technical field
The present invention relates to Automobile Products field more particularly to a kind of Chinese herbaceous peony gear with go up and down multi-functional composite glass structure and its
Manufacturing method.
Background technique
Automotive light-shading board in routine techniques is divided into two kinds, and one is the equipment of Universal automobile, what is referred to is just mounted in department
Be used to above machine to prevent the plank that the eyes are affected by the sunlight, with when can turn down and can roll up when not in use；It is for second
Preceding sun shield, its kind is not too much more, generally there is aluminium foil and non-woven fabrics two kinds.General point of common " tabula rasa " type of aluminium foil
With pattern type, size generally is 60*130cm, is suitble to most of compact cars, and hot weather then can be outside by aluminium foil, with true
Protect reflection sunlight.
But the first does not have complete shading function, is not for second the device of automobile standard configuration, user oneself is needed to buy,
And due to being activity, not only inconvenient to carry and keeping but also it is inconvenient to use, be not durable also, and be not provided with second of screening
The automobile of tabula rasa, interior temperature rise is exceedingly fast in open-air atmosphere, can heat up in one hour nearly 15 DEG C under the sunlight of summer sweltering heat,
Therefore interior plastics relatively inferior even can release toxic gas, usage experience is very poor.As people want automobile experience
Higher and higher today is asked, simple, low cost a eternal-fixing-type for not changing existing body construction substantially is easy to use
Complete shading plate can for automobile bonus point it is many, application prospect is extremely wide after popularization.
And at present in the related patents applied at home, not about vehicle light screen and its compound glass lifter plate
The prior art, thus need in the market it is a kind of have the shade function from main regulation, simple amusement function, vehicle body change it is small, use
Way is extensive, cost performance is high, front structure with long service life.
Summary of the invention
The present invention is intended to provide having, the shade function from main regulation, simple amusement function, vehicle body change is small, purposes is wide
It is general, cost performance is high, compound glass lifter plate with long service life and its manufacturing method.
To achieve the goals above, the invention adopts the following technical scheme: a kind of Chinese herbaceous peony gear multi-functional compound glass of lifting
Glass structure, the compound glass lifter plate are arranged between engine bin cover and roof cover, which includes successively
Glass matrix, conductive indium-tin oxide layer, ink screen structure, thermally conductive layer, the conductive indium-tin oxide layer, glass matrix of setting；
Side heat-conducting plate is provided in compound glass lifter plate two sides corresponding with vehicle A column；Conductive indium-tin oxide layer is arranged by light current
Line and DC circuit system communication；Microcapsules containing mass density 10% in ink screen structure, microcapsules include partial size and are
0.02mm-0.04mm positively charged black particle and partial size is the negatively charged white particle of 0.02mm-0.04mm；Compound glass
Glass lifter plate side is fixed using the sealing of glass insulation glue, and glass insulation is used between conductive indium-tin oxide layer and side heat-conducting plate
Glue isolation is fixed；This composite glass structure is additionally provided with lifting motor, which is arranged in roof over body case, with compound glass
The matching of glass lifter plate and control compound glass the lifter plate activity between engine bin cover and roof cover；
Wherein compound glass lifter plate manufacturing process the following steps are included:
1) prepare before production
1. vitreum raw material prepare: preparation 85 parts -90 parts of silica, 10 parts -15 parts of potassium oxide by weight；
2. ink screen material prepares: preparing the metal strip being adapted with vehicle two sides A column, prepare enough built-in mass densityes
Transparent oil-based liquid, the enough oxidations of preparation of 10% negatively charged black particle and oppositely charged white particle microcapsules
Indium, enough tin oxide, graphene film；
3. technological preparation: preparation asbestos board, enough pure oxygens, silicon nitride ceramics container, furnace chamber top are integrated with recirculated water cooling
But the protective atmosphere heating furnace, enough hydrofluoric acid of system；
2) glass body firing, tempering and molding
1. by with 1) in after the step silica, the potassium oxide that 1. prepare be uniformly mixed and melt, poured in vacuum environment
Casting obtains vitreum fluid into the mold being adapted with automobile front windshield radian；
2. 1. vitreum fluid that step obtains is gas-cooled under the nitrogen of 3bar-4bar, i.e. acquisition tempering rear vitreous body；
3) the compound glass lifter plate of ink electrical screen built in
1. prepare two pieces of stages 2) obtain tempering rear vitreous body, a vitreum convex surface fits closely graphene wherein
Film is set as the first glass plate and is fixed with the second glass plate of graphene film；
2. using indium oxide: the mixture of the ratio mixture of tin oxide 20:1 in mass ratio is recessed in the first glass plate as raw material
High permeability ito film is deposited in side surface；Using indium oxide: the mixture of the ratio mixture of tin oxide 9:1 in mass ratio is raw material,
Harmonious ito film is deposited in the convex side surface of two glass plates；Two ito films are provided with light current row close to panel bottom side and top side region
Line；Two pieces of glass plates are immersed and contain the stage 1) in the transparent oil-based liquid containing microcapsules that 2. prepares of step, by two pieces of glass plates
Be placed in parallel, two sides ito film close to and control room septal space 0.3mm-0.5mm after, gap side place the stage 1) step is 2.
The metal strip of preparation, it is interspersed in two metal strips to be provided with light current winding displacement, then using insulating cement by two pieces of glass plate surroundings
Gap closing simultaneously separates metal strip and ito film, exposes four light current winding displacements, that is, built-in ink electrical screen answers needed for obtaining
Combined glass glass lifter plate；
3. the compound glass lifter plate of 2. built-in ink electrical screen that step obtains is placed in hydrofluoric acid vapor environment, until
Mirror status is presented in two surfaces of convex-concave of crude compound glass lifter plate, that is, compound glass lifter plate needed for obtaining.
The compound glass lifter plate, the light transmittance in full frame inkization is 10%-15%, and in full frame permeabilization, light transmittance is
70%-75% is not more than 8 DEG C by its temperature rise as confined space 2h under 50 DEG C of air environments of unique external material, work
Make -40 DEG C -200 DEG C of adaptive temperature, stability is good, and service life is not less than 5 years.
Compared with prior art, the invention has the following advantages that (1) present invention can be according to car owner by middle control computer
It needs, when realizing parking, occurs by lifting motor control compound glass lifter plate or hidden, it is complete in compound glass lifter plate
When stretching, output signal and electrode are controlled by the two sides ito film that computer board controls, image is formed in ink screen, completes letter
The forming of single electron book reads or generates simple and elegant ink and wash, while realizing light-blocking and heat insulating function, makes us happy；It is opening
Compound glass lifter plate is risen when vehicle, and enough traveling sights are obtained by windshield light transmission.(2) it is not provided with tool shading function
Can baffle automobile, interior temperature rise is exceedingly fast in open-air atmosphere, can heat up nearly 15 in one hour under the sunlight of summer sweltering heat
DEG C, therefore interior plastics relatively inferior even can release toxic gas, usage experience is very poor.Applicant considers with people
It is higher and higher to automobile experience requirements, provide one through the invention and simple, low cost do not change existing vehicle substantially
The eternal-fixing-type of body structure, ink screen convenient to use replace common windshield, can realize light-blocking function or letter in parking
Single amusement function, and can realize anti-glare function and perspectiveization function when driving realizing, can it is effective, lasting, be neatly realized
Consumer, every the great demand such as light peep-proof, heat-insulated, has biggish realistic meaning and practicability to front barn door.(3) this hair
Bright specific all material is from a wealth of sources, it is low in cost, be easily achieved, and tolerable 200 DEG C or so of high temperature；All materials
The raw material of material can be used non-harmful mode and be produced, also not using any poisonous and hazardous auxiliary in process of the invention
Material is a kind of environmental-friendly invention.Therefore compound glass lifter plate of the invention have the shade function from main regulation,
Simple amusement function, vehicle body change is small, widely used, cost performance is high, characteristic with long service life.
Detailed description of the invention
Fig. 1 is structural schematic diagram of the invention；
Fig. 2 is compound glass lifter plate schematic diagram of the invention；
Fig. 3 is compound glass lifter plate schematic cross-section of the invention；
In figure: engine bin cover 1, compound glass lifter plate 2, roof cover 3, glass matrix 4, conductive indium-tin oxide layer 5, ink
Water screen structure 6, thermally conductive layer 7, DC circuit system 8, glass insulation glue 9, side heat-conducting plate 10, light current winding displacement 11, micro- glue
Capsule 12, lifting motor 13.
Specific embodiment
Embodiment 1:
A kind of Chinese herbaceous peony gear multi-functional composite glass structure of lifting, the compound glass lifter plate 2 are arranged in engine bin cover 1
Between roof cover 3, which includes glass matrix 4, the conductive indium-tin oxide layer 5, ink screen set gradually
Structure 6, thermally conductive layer 7, conductive indium-tin oxide layer 5, glass matrix 4；In compound glass lifter plate 2 corresponding with vehicle A column two
Side is provided with side heat-conducting plate 10；Conductive indium-tin oxide layer 5 passes through light current winding displacement 11 and 8 connection of DC circuit system；Ink
Shield the microcapsules 12 containing mass density 10% in structure 6, it is that 0.02mm-0.04mm is positively charged that microcapsules 12, which include partial size,
Black particle and partial size are the negatively charged white particle of 0.02mm-0.04mm；2 side of compound glass lifter plate is exhausted using glass
The sealing of edge glue is fixed, and is fixed between conductive indium-tin oxide layer 5 and side heat-conducting plate 10 using the isolation of glass insulation glue；This compound glass
Glass structure is additionally provided with lifting motor 13, which is arranged in 3 shell of roof cover, matches with compound glass lifter plate 2
And control compound glass lifter plate 2 is movable between engine bin cover 1 and roof cover 3；
Wherein compound glass lifter plate 2 manufacturing process the following steps are included:
1) prepare before production
1. vitreum raw material prepare: preparation silica 90Kg, potassium oxide 10Kg by weight；
2. ink screen material prepares: preparing the metal strip being adapted with vehicle two sides A column, prepare enough built-in mass densityes
Transparent oil-based liquid, the enough oxidations of preparation of 10% negatively charged black particle and oppositely charged white particle microcapsules
Indium, enough tin oxide, graphene film；
3. technological preparation: preparation asbestos board, enough pure oxygens, silicon nitride ceramics container, furnace chamber top are integrated with recirculated water cooling
But the protective atmosphere heating furnace, enough hydrofluoric acid of system；
2) glass body firing, tempering and molding
1. by with 1) in after the step silica, the potassium oxide that 1. prepare be uniformly mixed and melt, poured in vacuum environment
Casting obtains vitreum fluid into the mold being adapted with automobile front windshield radian；
2. 1. vitreum fluid that step obtains is gas-cooled under the nitrogen of 3bar-4bar, i.e. acquisition tempering rear vitreous body；
3) the compound glass lifter plate 2 of ink electrical screen built in
1. prepare two pieces of stages 2) obtain tempering rear vitreous body, a vitreum convex surface fits closely graphene wherein
Film is set as the first glass plate and is fixed with the second glass plate of graphene film；
2. using indium oxide: the mixture of the ratio mixture of tin oxide 20:1 in mass ratio is recessed in the first glass plate as raw material
High permeability ito film is deposited in side surface；Using indium oxide: the mixture of the ratio mixture of tin oxide 9:1 in mass ratio is raw material,
Harmonious ito film is deposited in the convex side surface of two glass plates；Two ito films are provided with light current row close to panel bottom side and top side region
Line 11；Two pieces of glass plates are immersed and contain the stage 1) in the transparent oil-based liquid containing microcapsules that 2. prepares of step, by two blocks of glass
Plate is placed in parallel, two sides ito film close to and control room septal space 0.3mm-0.5mm after, gap side place the stage 1) step
2. the metal strip prepared, interspersed in two metal strips to be provided with light current winding displacement 11, then using insulating cement by two pieces of glass plates
The closing of surrounding gap simultaneously separates metal strip and ito film, exposes four light current winding displacements 11, that is, built-in ink electronics needed for obtaining
The compound glass lifter plate of screen；
3. the compound glass lifter plate of 2. built-in ink electrical screen that step obtains is placed in hydrofluoric acid vapor environment, until
Mirror status is presented in two surfaces of convex-concave of crude compound glass lifter plate, that is, compound glass lifter plate 2 needed for obtaining.
The compound glass lifter plate produced through this embodiment, the light transmittance in full frame inkization is 15%, full frame
Light transmittance is 75% when change, by its 8 DEG C of temperature rise as uniquely confined space 2h under 50 DEG C of air environments of external material, work
Make -40 DEG C -200 DEG C of adaptive temperature, stability is good, and service life is not less than 5 years.
Embodiment 2:
It is whole consistent with embodiment 1, it is in place of difference:
Wherein compound glass lifter plate 2 manufacturing process the following steps are included:
1) prepare before production
1. vitreum raw material prepare: preparation silica 85Kg, potassium oxide 15Kg by weight；
The compound glass lifter plate produced through this embodiment, the light transmittance in full frame inkization is 10%, full frame
Light transmittance is 70% when change, by its 7 DEG C of temperature rise as uniquely confined space 2h under 50 DEG C of air environments of external material, work
Make -40 DEG C -200 DEG C of adaptive temperature, stability is good, and service life is not less than 5 years.
The foregoing description of the disclosed embodiments, only for can be realized professional and technical personnel in the field or use this
Invention.Various modifications to these embodiments will be readily apparent to those skilled in the art, institute herein
The General Principle of definition can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore,
The present invention will not be limited to the embodiments shown herein, and is to fit to special with principles disclosed herein and novelty
The consistent widest scope of point.
Claims (1)
1. a kind of Chinese herbaceous peony gear multi-functional composite glass structure of lifting, it is characterised in that: compound glass lifter plate (2) setting is being sent out
Motivation storehouse is covered between (1) and roof cover (3), which includes the glass matrix (4) set gradually, oxidation
Indium tin conductive layer (5), ink screen structure (6), thermally conductive layer (7), conductive indium-tin oxide layer (5), glass matrix (4)；Multiple
Combined glass glass lifter plate (2) two sides corresponding with vehicle A column are provided with side heat-conducting plate (10)；Conductive indium-tin oxide layer (5) passes through
Light current winding displacement (11) and DC circuit system (8) connection；Microcapsules containing mass density 10% in ink screen structure (6)
(12), microcapsules (12) include that partial size is the positively charged black particle of 0.02mm-0.04mm and partial size is 0.02mm-0.04mm
Negatively charged white particle；Compound glass lifter plate (2) side is fixed using the sealing of glass insulation glue, conductive indium-tin oxide layer
(5) it is fixed between side heat-conducting plate (10) using the isolation of glass insulation glue；This composite glass structure is additionally provided with lifting motor
(13), it in the lifting motor (13) setting roof cover (3) shell, is matched with compound glass lifter plate (2) and controls compound glass
Lifter plate (2) is movable between engine bin cover (1) and roof cover (3)；
Wherein compound glass lifter plate (2) manufacturing process the following steps are included:
1) prepare before production
1. vitreum raw material prepare: preparation 85 parts -90 parts of silica, 10 parts -15 parts of potassium oxide by weight；
2. ink screen material prepares: preparing the metal strip being adapted with vehicle two sides A column, prepare enough built-in mass densityes 10%
The transparent oil-based liquid of negatively charged black particle and oppositely charged white particle microcapsules prepares enough indium oxides, is enough
Tin oxide, graphene film；
3. technological preparation: preparation asbestos board, enough pure oxygens, silicon nitride ceramics container, furnace chamber top are integrated with circulating water system
Protective atmosphere heating furnace, the enough hydrofluoric acid of system；
2) glass body firing, tempering and molding
1. by with 1) in after the step silica, the potassium oxide that 1. prepare be uniformly mixed and melt, cast in vacuum environment to
In the mold being adapted with automobile front windshield radian, vitreum fluid is obtained；
2. 1. vitreum fluid that step obtains is gas-cooled under the nitrogen of 3bar-4bar, i.e. acquisition tempering rear vitreous body；
3) the compound glass lifter plate (2) of ink electrical screen built in
1. prepare two pieces of stages 2) obtain tempering rear vitreous body, it is thin to fit closely graphene for a vitreum convex surface wherein
Film is set as the first glass plate and is fixed with the second glass plate of graphene film；
2. using indium oxide: the mixture of the ratio mixture of tin oxide 20:1 in mass ratio is raw material, in the first glass plate concave side table
High permeability ito film is deposited in face；Using indium oxide: the mixture of the ratio mixture of tin oxide 9:1 in mass ratio is raw material, in the second glass
Harmonious ito film is deposited in the convex side surface of glass plate；Two ito films are provided with light current winding displacement close to panel bottom side and top side region
(11)；Two pieces of glass plates are immersed and contain the stage 1) in the transparent oil-based liquid containing microcapsules that 2. prepares of step, by two blocks of glass
Plate is placed in parallel, two sides ito film close to and control room septal space 0.3mm-0.5mm after, gap side place the stage 1) step
2. the metal strip prepared, interspersed in two metal strips to be provided with light current winding displacement (11), then using insulating cement by two blocks of glass
The closing of plate surrounding gap simultaneously separates metal strip and ito film, exposes four light current winding displacements (11), that is, built-in ink needed for obtaining
The compound glass lifter plate of electrical screen；
3. the compound glass lifter plate of 2. built-in ink electrical screen that step obtains is placed in hydrofluoric acid vapor environment, until crude
Mirror status is presented in two surfaces of convex-concave of compound glass lifter plate, that is, compound glass lifter plate (2) needed for obtaining.