CN109373062A - A kind of glass winding composite polypropylene and preparation method thereof - Google Patents
A kind of glass winding composite polypropylene and preparation method thereof Download PDFInfo
- Publication number
- CN109373062A CN109373062A CN201811241043.3A CN201811241043A CN109373062A CN 109373062 A CN109373062 A CN 109373062A CN 201811241043 A CN201811241043 A CN 201811241043A CN 109373062 A CN109373062 A CN 109373062A
- Authority
- CN
- China
- Prior art keywords
- parts
- polypropylene
- glass
- composite
- composite polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of glass winding composite polypropylene and preparation method thereof, which is to be obtained using composite polypropylene as liner by Glass Fiber Reinforcement is wound after tube surfaces coating surface inorganic agent.Preparation method is first to carry out sandblasting polishing to polypropylene composite materials pipe surface, and then by composite polypropylene on wrapping machine, surface treating agent is coated in its surface, dosage 100-200g/m by starting rotation2, then the glass fibre belt for being soaked with surface treating agent is wrapped in polypropylene composite materials pipe surface, removes multiple tube after 5-10 layer of winding, progress curing process to get.The present invention substantially increases heat-resisting, the stress levels of PP pipe, and thermal coefficient is small, is a kind of pressure-resistant, heat-resisting, corrosion resistant pipeline material.
Description
Technical field
The invention belongs to engineering plastics technical fields, and in particular to a kind of glass winding composite polypropylene and its preparation side
Method.
Background technique
Polypropylene (PP) is a kind of thermoplastic resin as prepared by propylene polymerization.It is divided into isotactic by methyl arrangement position
Polypropylene (isotactic polypropylene), random polypropylene (atactic polypropylene) and syndiotactic polypropylene
Three kinds of (syndiotactic polypropylene).Usually translucent colorless solid is odorless nontoxic.Due to compound with regular structure
Highly crystallized, therefore fusing point may be up to 167 DEG C.Heat-resisting, corrosion-resistant, product can be its outstanding advantages with moise-heat sterilization.Density is small,
It is most light general-purpose plastics.The disadvantage is that low-temperature impact resistance is poor, it is more easy to aging, but can be overcome respectively by modification.
Polypropylene pipe have the advantages that it is multiple, first, PP manage nontoxic, non-corroding, non-scaling, meet QB1929-93 water supply
Standard and HG20539-92 standard;2nd PP pipe high temperature resistant, the water temperature of pipeline reach as high as 90-100 DEG C;Third, PP pipe
Using hot-melt adhesive paste technology, tubing and pipe fitting congruent melting are integrated, and without dismountable cutting ferrule or pressure type connector, safely may be used
It leans on, Never-leakage;4th, PP pipe are light-weight, and specific gravity is only 1/8th of steel pipe, are easily installed, carry and connect, and save labor
Power cost;5th, PP manage corrosion-resistant, the inside and outside corrosiveness of ion pair pipeline that can be effectively prevent in water or chemical substance;The
Six, PP inside pipe wall are smooth, and system pressure loss is small, and water velocity is fast;7th, PP pipe product color are soft, and color multiplicity can expire
The demand of the various occasions of foot.Therefore, PP pipe is widely used in multi-field, for example, urban water supply, food, chemical field, ore in sand form,
Slurry transportation, displacement pipe of cement, cast iron pipe and steel pipe etc..
Although PP pipe itself has good corrosion resistance, it is used for a long time or corrodes vulnerable to external environment, thus shadow
Ring its service life.
Summary of the invention
There is provided present invention aim to address above-mentioned the deficiencies in the prior art a kind of glass winding composite polypropylene and
Preparation method substantially increases heat-resisting, the stress levels of P P pipe, and thermal coefficient is small, is a kind of pressure-resistant, heat-resisting, corrosion resistant
The pipeline material of erosion.
A kind of glass winding composite polypropylene, is using composite polypropylene as liner, by tube surfaces coating surface
Glass Fiber Reinforcement is wound after inorganic agent to obtain.
Preferably, the raw material of the composite polypropylene includes: 80-100 parts of polypropylene in parts by weight, polyurethane 10-
20 parts, 3-7 parts of bismaleimide, 1-3 parts of calcium carbonate crystal whisker, 4-8 parts of anti-impact modifier, 0.6-1.2 parts of antioxidant, nanometer
0.5-1.5 parts of ceramic powder, 0.5-1.2 parts of fire retardant.
Preferably, the fire retardant is bromo- antimony fire retardant.
Preferably, the raw material of the surface treating agent includes: 10-20 parts of acrylic resin in parts by weight, phenolic resin
5-10 parts, 2-4 parts of tributyl phosphate, 1-2 parts of white carbon black, 1-2 parts of demethylation lignin.
Preferably, the Glass Fiber Reinforcement includes: 10 parts of glass fibre in parts by weight, 0.5-1 parts of silicon carbide, even
Agent 0.1-0.3 parts, 2-3 parts of chopped carbon fiber of connection.
The preparation method of above-mentioned glass winding composite polypropylene, comprising the following steps:
Step 1, polypropylene, polyurethane, bismaleimide, calcium carbonate crystal whisker, anti-impact modifier, antioxidant, nanometer are made pottery
Porcelain powder, fire retardant are placed in 90-120 DEG C of dry 1h, import double screw extruder, and melting extrusion is made through vacuum sizing, molding
Composite polypropylene;
Step 2, glass fibre, silicon carbide, coupling agent, chopped carbon fiber are mixed, glass fibre belt is made after melting extrusion;
Step 3, acrylic resin, phenolic resin, tributyl phosphate, white carbon black, demethylation lignin are mixed, in 100-
120 DEG C of heat preservation 30-40min, grinding, obtain surface treating agent;
Step 4, sandblasting polishing is carried out to polypropylene composite materials pipe surface, then by composite polypropylene on wrapping machine, starting
Surface treating agent is coated in its surface, dosage 100-200g/m by rotation2, then the glass fibre belt for being soaked with surface treating agent twined
Be wound on polypropylene composite materials pipe surface, remove multiple tube after 5-10 layer of winding, progress curing process to get.
The present invention uses the PA tube of high comprehensive performance for liner, winds glass after specially treated is made on surface, makes
Be securely joined with integral, form unique PP/ gf Winding Composite Pipes.The multiple tube both maintained PP it is light, it is anti-corrosion,
Heat-resisting, nontoxic, free of contamination superperformance, and the high advantage of glass hardness of steel has been played, substantially increase the heat-resisting, resistance to of PP pipe
Grade is pressed, and thermal coefficient is small, and pipeline need not be kept the temperature, and is a kind of not only economy, structure is again reasonably pressure-resistant, heat-resisting, corrosion resistant
Pipeline material.
Specific embodiment
Embodiment 1
A kind of glass winding composite polypropylene, is to be handled tube surfaces coating surface using composite polypropylene as liner
Glass Fiber Reinforcement is wound after agent to obtain.
The raw material of the composite polypropylene includes: 80 parts of polypropylene in parts by weight, and 10 parts of polyurethane, bismaleimide
3 parts of amine, 1 part of calcium carbonate crystal whisker, 4 parts of anti-impact modifier, 0.6 part of antioxidant, 0.5 part of nano-ceramic powder, 0.5 part of fire retardant.
The fire retardant is bromo- antimony fire retardant.
The raw material of the surface treating agent includes: 10 parts of acrylic resin in parts by weight, and 5 parts of phenolic resin, tricresyl phosphate
2 parts of butyl ester, 1 part of white carbon black, 1 part of demethylation lignin.
The Glass Fiber Reinforcement includes: 10 parts of glass fibre in parts by weight, and 0.5 part of silicon carbide, coupling agent 0.1
Part, 2 parts of chopped carbon fiber.
The preparation method of above-mentioned glass winding composite polypropylene, comprising the following steps:
Step 1, polypropylene, polyurethane, bismaleimide, calcium carbonate crystal whisker, anti-impact modifier, antioxidant, nanometer are made pottery
Porcelain powder, fire retardant are placed in 90-120 DEG C of dry 1h, import double screw extruder, and melting extrusion is made through vacuum sizing, molding
Composite polypropylene;
Step 2, glass fibre, silicon carbide, coupling agent, chopped carbon fiber are mixed, glass fibre belt is made after melting extrusion;
Step 3, acrylic resin, phenolic resin, tributyl phosphate, white carbon black, demethylation lignin are mixed, in 100-
120 DEG C of heat preservation 30-40min, grinding, obtain surface treating agent;
Step 4, sandblasting polishing is carried out to polypropylene composite materials pipe surface, then by composite polypropylene on wrapping machine, starting
Surface treating agent is coated in its surface, dosage 100-200g/m by rotation2, then the glass fibre belt for being soaked with surface treating agent twined
Be wound on polypropylene composite materials pipe surface, remove multiple tube after 5-10 layer of winding, progress curing process to get.
After tested, obtained 50mm multiple tube, density 1.19g/cm3, PP is with glass reinforced plastic interface shear strength
10MPa, axial tensile strength 140MPa, axial compression strength are 160 MPa.
Embodiment 2
A kind of glass winding composite polypropylene, is to be handled tube surfaces coating surface using composite polypropylene as liner
Glass Fiber Reinforcement is wound after agent to obtain.
The raw material of the composite polypropylene includes: 90 parts of polypropylene in parts by weight, and 15 parts of polyurethane, bismaleimide
5 parts of amine, 2 parts of calcium carbonate crystal whisker, 6 parts of anti-impact modifier, 0.9 part of antioxidant, 1.1 parts of nano-ceramic powder, 0.9 part of fire retardant.
The fire retardant is bromo- antimony fire retardant.
The raw material of the surface treating agent includes: 14 parts of acrylic resin in parts by weight, and 7 parts of phenolic resin, tricresyl phosphate
3 parts of butyl ester, 1 part of white carbon black, 2 parts of demethylation lignin.
The Glass Fiber Reinforcement includes: 10 parts of glass fibre in parts by weight, and 0.7 part of silicon carbide, coupling agent 0.2
Part, 2 parts of chopped carbon fiber.
The preparation method of above-mentioned glass winding composite polypropylene, comprising the following steps:
Step 1, polypropylene, polyurethane, bismaleimide, calcium carbonate crystal whisker, anti-impact modifier, antioxidant, nanometer are made pottery
Porcelain powder, fire retardant are placed in 90-120 DEG C of dry 1h, import double screw extruder, and melting extrusion is made through vacuum sizing, molding
Composite polypropylene;
Step 2, glass fibre, silicon carbide, coupling agent, chopped carbon fiber are mixed, glass fibre belt is made after melting extrusion;
Step 3, acrylic resin, phenolic resin, tributyl phosphate, white carbon black, demethylation lignin are mixed, in 100-
120 DEG C of heat preservation 30-40min, grinding, obtain surface treating agent;
Step 4, sandblasting polishing is carried out to polypropylene composite materials pipe surface, then by composite polypropylene on wrapping machine, starting
Surface treating agent is coated in its surface, dosage 100-200g/m2, then the glass fibre belt for being soaked with surface treating agent is twined by rotation
Be wound on polypropylene composite materials pipe surface, remove multiple tube after 5-10 layer of winding, progress curing process to get.
After tested, obtained 50mm multiple tube, density 1.23g/cm3, PP is with glass reinforced plastic interface shear strength
12MPa, axial tensile strength 135MPa, axial compression strength 158MPa.
Embodiment 3
A kind of glass winding composite polypropylene, is to be handled tube surfaces coating surface using composite polypropylene as liner
Glass Fiber Reinforcement is wound after agent to obtain.
The raw material of the composite polypropylene includes: 100 parts of polypropylene in parts by weight, and 20 parts of polyurethane, span carrys out acyl
7 parts of imines, 3 parts of calcium carbonate crystal whisker, 8 parts of anti-impact modifier, 1.2 parts of antioxidant, 1.5 parts of nano-ceramic powder, fire retardant 1.2
Part.The fire retardant is bromo- antimony fire retardant.
The raw material of the surface treating agent includes: 20 parts of acrylic resin in parts by weight, and 10 parts of phenolic resin, tricresyl phosphate
4 parts of butyl ester, 2 parts of white carbon black, 2 parts of demethylation lignin.
The Glass Fiber Reinforcement includes: 10 parts of glass fibre in parts by weight, and 1 part of silicon carbide, 0.3 part of coupling agent,
3 parts of chopped carbon fiber.
The preparation method of above-mentioned glass winding composite polypropylene, comprising the following steps:
Step 1, polypropylene, polyurethane, bismaleimide, calcium carbonate crystal whisker, anti-impact modifier, antioxidant, nanometer are made pottery
Porcelain powder, fire retardant are placed in 90-120 DEG C of dry 1h, import double screw extruder, and melting extrusion is made through vacuum sizing, molding
Composite polypropylene;
Step 2, glass fibre, silicon carbide, coupling agent, chopped carbon fiber are mixed, glass fibre belt is made after melting extrusion;
Step 3, acrylic resin, phenolic resin, tributyl phosphate, white carbon black, demethylation lignin are mixed, in 100-
120 DEG C of heat preservation 30-40min, grinding, obtain surface treating agent;
Step 4, sandblasting polishing is carried out to polypropylene composite materials pipe surface, then by composite polypropylene on wrapping machine, starting
Surface treating agent is coated in its surface, dosage 100-200g/m2, then the glass fibre belt for being soaked with surface treating agent is twined by rotation
Be wound on polypropylene composite materials pipe surface, remove multiple tube after 5-10 layer of winding, progress curing process to get.
After tested, obtained 50mm multiple tube, density 1.19g/cm3, PP is with glass reinforced plastic interface shear strength
10MPa, axial tensile strength 140MPa, axial compression strength are 160 MPa.
After tested, obtained 50mm multiple tube, density 1.25g/cm3, PP is with glass reinforced plastic interface shear strength
14MPa, axial tensile strength 150MPa, axial compression strength are 165 MPa.
Multiple tube made from above-described embodiment is respectively used to salt mine, insecticide factory, chemical fibre factory and paper mill, it is compound to detect
Durability of the pipe under a variety of corrosion conditions.In salt mine (the hydrochloric acid saturated solution of sodium chloride-containing, sodium sulphate), insecticide factory's (sodium chloride
Saturated solution), chemical fibre factory (metabisulfite solution containing free sulfuric acid) and paper mill (alkaline bleach liquor), multiple tube of the invention be ok
Use 3-5, far superior to carbon steel pipe.
Claims (6)
- It is using composite polypropylene as liner, at tube surfaces coating surface 1. a kind of glass winds composite polypropylene Winding Glass Fiber Reinforcement obtains after reason agent.
- 2. glass according to claim 1 winds composite polypropylene, it is characterised in that: the original of the composite polypropylene Material includes: 80-100 parts of polypropylene in parts by weight, and 10-20 parts of polyurethane, 3-7 parts of bismaleimide, calcium carbonate crystal whisker 1-3 Part, 4-8 parts of anti-impact modifier, 0.6-1.2 parts of antioxidant, 0.5-1.5 parts of nano-ceramic powder, 0.5-1.2 parts of fire retardant.
- 3. glass according to claim 2 winds composite polypropylene, it is characterised in that: the fire retardant is bromo- antimony resistance Fire agent.
- 4. glass according to claim 1 winds composite polypropylene, it is characterised in that: the raw material of the surface treating agent It in parts by weight include: 10-20 parts of acrylic resin, 5-10 parts of phenolic resin, 2-4 parts of tributyl phosphate, 1-2 parts of white carbon black, 1-2 parts of demethylation lignin.
- 5. glass according to claim 1 winds composite polypropylene, it is characterised in that: the Glass Fiber Reinforcement with Parts by weight meter includes: 10 parts of glass fibre, 0.5-1 parts of silicon carbide, 0.1-0.3 parts of coupling agent, 2-3 parts of chopped carbon fiber.
- 6. the preparation method of glass winding composite polypropylene described in claim 1, it is characterised in that: the following steps are included:Step 1, polypropylene, polyurethane, bismaleimide, calcium carbonate crystal whisker, anti-impact modifier, antioxidant, nanometer are made pottery Porcelain powder, fire retardant are placed in 90-120 DEG C of dry 1h, import double screw extruder, and melting extrusion is made through vacuum sizing, molding Composite polypropylene;Step 2, glass fibre, silicon carbide, coupling agent, chopped carbon fiber are mixed, glass fibre belt is made after melting extrusion;Step 3, acrylic resin, phenolic resin, tributyl phosphate, white carbon black, demethylation lignin are mixed, in 100- 120 DEG C of heat preservation 30-40min, grinding, obtain surface treating agent;Step 4, sandblasting polishing is carried out to polypropylene composite materials pipe surface, then by composite polypropylene on wrapping machine, starting Surface treating agent is coated in its surface, dosage 100-200g/m by rotation2, then the glass fibre belt for being soaked with surface treating agent twined Be wound on polypropylene composite materials pipe surface, remove multiple tube after 5-10 layer of winding, progress curing process to get.