CN109370275A - A kind of cement waterproof paint adding white marble sand - Google Patents
A kind of cement waterproof paint adding white marble sand Download PDFInfo
- Publication number
- CN109370275A CN109370275A CN201811278153.7A CN201811278153A CN109370275A CN 109370275 A CN109370275 A CN 109370275A CN 201811278153 A CN201811278153 A CN 201811278153A CN 109370275 A CN109370275 A CN 109370275A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- agent
- white marble
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cement waterproof paints for adding white marble sand, by liquid material, powder, curing agent is mixed with, the liquid material includes the raw material of following parts by weight: 40-55 parts of polyvinyl acetate, lotion 8-16 parts of plasticising, 1-3 parts of preservative, 1-3 parts of surfactant, 1-3 parts of dispersing agent, 0.5-1.5 parts of galic essential oil, 1-3 parts of defoaming agent, 1-2 parts of coalescing agent, 46-90 parts of deionized water, the powder includes the raw material of following parts by weight: 35-45 parts of portland cement, 23-37 parts of high alumina cement, 7-12 parts of reinforcing fiber, vermiculite 6-10 parts of activation, 4-9 parts of white marble sand, amino modified silica flour 5-9 parts, 3-8 parts of nano-titanium dioxide, the present invention is combined by organic liquid material and inorganic powder and curing agent Three component water-proof anticorrosive paints.The coating had not only had the elasticity of organic coating, but also had many advantages, such as the durability of inorganic coating.
Description
Technical field
The present invention relates to building materials, the cement waterproof paint of specifically a kind of addition white marble sand.
Background technique
White marble main component is calcium carbonate, is mainly made of CaCO3, MgCO3 and SiO2, also comprising a small amount of Al2O3,
The ingredients such as Fe2O3.Belong to the pure white particulate griotte of color, matter is hard, is first-class building and material for carving on it.Substantially it is simultaneously
It is not soluble in water.It may be present in following form: aragonite, calcite, chalk, limestone, marble, calcareous tufa, can be in rock
It finds.The main ingredient of animal dorsal shield and hodmadod.Meanwhile it is also important construction material.White marble quality is hard pure white.
The ornamental column before Tian An-men, Golden Water Bridge, palace pedestal in utero, stone rank, guardrail is made of white marble.The yield of white marble
Account for about the 30% of all marble yield；White marble sand is the multiple tracks such as featured white marble ore, broken, crushing, classification, packaging
Process is process.It is process, is mainly used in by selected: construction and decoration, terrazzo aggregate, terrace, fish jar bed-sit, work
Skill product, sandstone, lacquer, artificial stone, epoxy floor, sand texture coating etc..Natural white marble sand can be used for manufacturing marble,
Floor tile, ceramic tile and decoration sanitary ware etc. have many advantages, such as gloss, smooth, firm wear-resisting.
Building water-proof paint is the incorporation by based on high molecular material, pitch, polymer modified asphalt, inorganic material etc.
The waterproof material of solvent type, water-soluble, emulsion type or powder-type that suitable auxiliary agent, modified material, packing material etc. are processed into
Material.Compared with waterproof roll, water-repellent paint construction is simple is convenient, suitable for the basal plane of any shape, and can be formed fine and close seamless
Film, infiltrate through in gap, good water-proof effect.Therefore, water-repellent paint is widely used in various waterproofing works, and is taken
Obtained rapid development.
But existing rubber asphalt class water-repellent paint mechanical property, waterproof performance and in terms of be not yet
It is very ideal, it especially will appear at high temperature and occur the problems such as embrittlement delamination under creep trickling, low temperature, influenced building
The waterproof performance of object.
Summary of the invention
The purpose of the present invention is to provide a kind of cement waterproof paints for adding white marble sand, to solve above-mentioned background technique
The problem of middle proposition.
To achieve the above object, the invention provides the following technical scheme:
A kind of cement waterproof paint adding white marble sand, is 1:1-3:0.1- by liquid material, powder, curing agent by weight
0.5 is mixed with, and the liquid material includes the raw material of following parts by weight:
40-55 parts of polyvinyl acetate, plasticising lotion 8-16 parts, 1-3 parts of preservative, 1-3 parts of surfactant, dispersing agent
1-3 parts, 0.5-1.5 parts of galic essential oil, 1-3 parts of defoaming agent, 1-2 parts of coalescing agent, 46-90 parts of deionized water,
The powder includes the raw material of following parts by weight: 35-45 parts of portland cement, 23-37 parts of high alumina cement, enhancing are fine
Dimension 7-12 part, activate vermiculite 6-10 parts, 4-9 parts of white marble sand, it is silica flour 5-9 parts amino modified, 3-8 parts of nano-titanium dioxide.
A kind of cement waterproof paint adding white marble sand is mixed by weight for 1:1:0.1 by liquid material, powder, curing agent
Conjunction is prepared, and the liquid material includes the raw material of following parts by weight:
40 parts of polyvinyl acetate, plasticising 8 parts of lotion, 1 part of preservative, 1 part of surfactant, 1 part of dispersing agent, garlic essence
Oily 0.5 part, 1 part of defoaming agent, 1 part of coalescing agent, 46 parts of deionized water,
The powder includes the raw material of following parts by weight: 35 parts of portland cement, 23 parts of high alumina cement, 7 parts of reinforcing fiber,
Activate 6 parts of vermiculite, 4 parts of white marble sand, 5 parts of amino modified silica flour, 3 parts of nano-titanium dioxide.
A kind of cement waterproof paint adding white marble sand is mixed by weight for 1:3:0.5 by liquid material, powder, curing agent
Conjunction is prepared, and the liquid material includes the raw material of following parts by weight:
55 parts of polyvinyl acetate, plasticising 16 parts of lotion, 3 parts of preservative, 3 parts of surfactant, 3 parts of dispersing agent, garlic
1.5 parts of essential oil, 3 parts of defoaming agent, 2 parts of coalescing agent, 90 parts of deionized water,
The powder includes the raw material of following parts by weight: 45 parts of portland cement, 37 parts of high alumina cement, reinforcing fiber 12
Part, activation 10 parts of vermiculite, 9 parts of white marble sand, 9 parts of amino modified silica flour, 8 parts of nano-titanium dioxide.
A kind of cement waterproof paint adding white marble sand is mixed by weight for 1:2:0.3 by liquid material, powder, curing agent
Conjunction is prepared, and the liquid material includes the raw material of following parts by weight:
47 parts of polyvinyl acetate, plasticising 12 parts of lotion, 2 parts of preservative, 2 parts of surfactant, 2 parts of dispersing agent, garlic
1 part of essential oil, 2 parts of defoaming agent, 1.5 parts of coalescing agent, 72 parts of deionized water,
The powder includes the raw material of following parts by weight: 40 parts of portland cement, 30 parts of high alumina cement, 9 parts of reinforcing fiber,
Activate 8 parts of vermiculite, 6 parts of white marble sand, 7 parts of amino modified silica flour, 6 parts of nano-titanium dioxide.
The reinforcing fiber is selected from silicon carbide whisker, carbonization boron whisker, alumina whisker, calcium sulfate crystal whiskers, zirconium dioxide
One of whisker, aluminium nitride whisker, ZnOw, magnesium sulfate crystal whisker and silicon nitride crystal whisker or more than one mixture.
The plasticising lotion includes following raw material: ethyl methacrylate, phenyl triethoxysilane, methacrylic acid,
Propenyl, styrene, polyphosphoric acid amine, neopelex, initiator, water and pH adjusting agent.
The plasticising lotion includes the raw material of following parts by weight: 13-20 parts of ethyl methacrylate, phenyltriethoxy silane
4-7 parts of alkane, 3-6 parts of methacrylic acid, 6-10 parts of propenyl, 5-8 parts of styrene, 2-5 parts of polyphosphoric acid amine, dodecyl benzene sulfonic acid
1-3 parts of sodium, 1-2 parts of initiator, 20-24 parts of water, 1-2 parts of pH adjusting agent.
The partial size of the amino modified silica flour is 50-100nm, and the partial size of the white marble sand is 100-200nm.
The preservative is the mixture that one or both of trbasic zinc phosphate or aluminum phosphate are mixed with arbitrary proportion.
The preparation method of the activation vermiculite: in vermiculite surface spray water, until then vermiculite moistened surface is carried out smelly
Oxygen handles 30min, and the concentration of ozone is 50-75ppm.
Preferably, the defoaming agent is dimethyl silicone polymer.
Compared with prior art, the beneficial effects of the present invention are:
The three component water-proof anticorrosive paints that the present invention is combined by organic liquid material and inorganic powder and curing agent.The coating
Not only with the elasticity of organic coating, but also has many advantages, such as the durability of inorganic coating.Coating is tough and tensile high-strength, and waterproof is wear-resistant, impermeable
Gas has good corrosion resistance, and including the corrosion to resistance to, sour, alkali, salt and other solvents etc., coating is not empty by force with basal plane cohesive force
Drum, does not fall off.It is non-toxic and tasteless pollution-free after coating reaction solidification.It is wherein interspersed with reinforcing fiber and amino modified silica flour, is made
Waterproof coating has the mechanical property having had while waterproof performance and weather resistance, improves the service life of waterproof coating.
Form of construction work is the cold motionless open fire of construction, and material is fire-retardant, and construction safety is simple, short time limit, can be in moist or dry a variety of bases
It constructs on material, it can be in plane/elevation construction.Adhesive property is good, and tensile strength is high, and fracture elongation is big, is resistant to subzero 20-30 DEG C
Low temperature.
For the present invention by vermiculite after ozone Oxidation Treatment, the activity on surface can obtain great promotion, can be effective
Stability of the reinforcement vermiculite in coating, and then improve the performance of water based paint.
Specific embodiment
Embodiment 1
A kind of cement waterproof paint adding white marble sand is mixed by weight for 1:1:0.1 by liquid material, powder, curing agent
Conjunction is prepared, and the liquid material includes the raw material of following parts by weight:
40 parts of polyvinyl acetate, plasticising 8 parts of lotion, 1 part of preservative, 1 part of surfactant, 1 part of dispersing agent, garlic essence
Oily 0.5 part, 1 part of defoaming agent, 1 part of coalescing agent, 46 parts of deionized water,
The powder includes the raw material of following parts by weight: 35 parts of portland cement, 23 parts of high alumina cement, 7 parts of reinforcing fiber,
Activate 6 parts of vermiculite, 4 parts of white marble sand, 5 parts of amino modified silica flour, 3 parts of nano-titanium dioxide.
The reinforcing fiber is selected from silicon carbide whisker, carbonization boron whisker, alumina whisker, calcium sulfate crystal whiskers, zirconium dioxide
One of whisker, aluminium nitride whisker, ZnOw, magnesium sulfate crystal whisker and silicon nitride crystal whisker or more than one mixture.
The plasticising lotion includes following raw material: ethyl methacrylate, phenyl triethoxysilane, methacrylic acid,
Propenyl, styrene, polyphosphoric acid amine, neopelex, initiator, water and pH adjusting agent.
The plasticising lotion includes the raw material of following parts by weight: 13-20 parts of ethyl methacrylate, phenyltriethoxy silane
4-7 parts of alkane, 3-6 parts of methacrylic acid, 6-10 parts of propenyl, 5-8 parts of styrene, 2-5 parts of polyphosphoric acid amine, dodecyl benzene sulfonic acid
1-3 parts of sodium, 1-2 parts of initiator, 20-24 parts of water, 1-2 parts of pH adjusting agent.
The partial size of the amino modified silica flour is 50-100nm, and the partial size of the white marble sand is 100-200nm.
The preservative is the mixture that one or both of trbasic zinc phosphate or aluminum phosphate are mixed with arbitrary proportion.
The preparation method of the activation vermiculite: in vermiculite surface spray water, until then vermiculite moistened surface is carried out smelly
Oxygen handles 30min, and the concentration of ozone is 50-75ppm.
Preferably, the defoaming agent is dimethyl silicone polymer.
Embodiment 2
A kind of cement waterproof paint adding white marble sand is mixed by weight for 1:3:0.5 by liquid material, powder, curing agent
Conjunction is prepared, and the liquid material includes the raw material of following parts by weight:
55 parts of polyvinyl acetate, plasticising 16 parts of lotion, 3 parts of preservative, 3 parts of surfactant, 3 parts of dispersing agent, garlic
1.5 parts of essential oil, 3 parts of defoaming agent, 2 parts of coalescing agent, 90 parts of deionized water,
The powder includes the raw material of following parts by weight: 45 parts of portland cement, 37 parts of high alumina cement, reinforcing fiber 12
Part, activation 10 parts of vermiculite, 9 parts of white marble sand, 9 parts of amino modified silica flour, 8 parts of nano-titanium dioxide.
The reinforcing fiber is selected from silicon carbide whisker, carbonization boron whisker, alumina whisker, calcium sulfate crystal whiskers, zirconium dioxide
One of whisker, aluminium nitride whisker, ZnOw, magnesium sulfate crystal whisker and silicon nitride crystal whisker or more than one mixture.
The plasticising lotion includes following raw material: ethyl methacrylate, phenyl triethoxysilane, methacrylic acid,
Propenyl, styrene, polyphosphoric acid amine, neopelex, initiator, water and pH adjusting agent.
The plasticising lotion includes the raw material of following parts by weight: 13-20 parts of ethyl methacrylate, phenyltriethoxy silane
4-7 parts of alkane, 3-6 parts of methacrylic acid, 6-10 parts of propenyl, 5-8 parts of styrene, 2-5 parts of polyphosphoric acid amine, dodecyl benzene sulfonic acid
1-3 parts of sodium, 1-2 parts of initiator, 20-24 parts of water, 1-2 parts of pH adjusting agent.
The partial size of the amino modified silica flour is 50-100nm, and the partial size of the white marble sand is 100-200nm.
The preservative is the mixture that one or both of trbasic zinc phosphate or aluminum phosphate are mixed with arbitrary proportion.
The preparation method of the activation vermiculite: in vermiculite surface spray water, until then vermiculite moistened surface is carried out smelly
Oxygen handles 30min, and the concentration of ozone is 50-75ppm.
Preferably, the defoaming agent is dimethyl silicone polymer.
Embodiment 3
A kind of cement waterproof paint adding white marble sand is mixed by weight for 1:2:0.3 by liquid material, powder, curing agent
Conjunction is prepared, and the liquid material includes the raw material of following parts by weight:
47 parts of polyvinyl acetate, plasticising 12 parts of lotion, 2 parts of preservative, 2 parts of surfactant, 2 parts of dispersing agent, garlic
1 part of essential oil, 2 parts of defoaming agent, 1.5 parts of coalescing agent, 72 parts of deionized water,
The powder includes the raw material of following parts by weight: 40 parts of portland cement, 30 parts of high alumina cement, 9 parts of reinforcing fiber,
Activate 8 parts of vermiculite, 6 parts of white marble sand, 7 parts of amino modified silica flour, 6 parts of nano-titanium dioxide.
The reinforcing fiber is selected from silicon carbide whisker, carbonization boron whisker, alumina whisker, calcium sulfate crystal whiskers, zirconium dioxide
One of whisker, aluminium nitride whisker, ZnOw, magnesium sulfate crystal whisker and silicon nitride crystal whisker or more than one mixture.
The plasticising lotion includes following raw material: ethyl methacrylate, phenyl triethoxysilane, methacrylic acid,
Propenyl, styrene, polyphosphoric acid amine, neopelex, initiator, water and pH adjusting agent.
The plasticising lotion includes the raw material of following parts by weight: 13-20 parts of ethyl methacrylate, phenyltriethoxy silane
4-7 parts of alkane, 3-6 parts of methacrylic acid, 6-10 parts of propenyl, 5-8 parts of styrene, 2-5 parts of polyphosphoric acid amine, dodecyl benzene sulfonic acid
1-3 parts of sodium, 1-2 parts of initiator, 20-24 parts of water, 1-2 parts of pH adjusting agent.
The partial size of the amino modified silica flour is 50-100nm, and the partial size of the white marble sand is 100-200nm.
The preservative is the mixture that one or both of trbasic zinc phosphate or aluminum phosphate are mixed with arbitrary proportion.
The preparation method of the activation vermiculite: in vermiculite surface spray water, until then vermiculite moistened surface is carried out smelly
Oxygen handles 30min, and the concentration of ozone is 50-75ppm.
Preferably, the defoaming agent is dimethyl silicone polymer.
Claims (9)
1. a kind of cement waterproof paint for adding white marble sand, which is characterized in that be by weight by liquid material, powder, curing agent
1:1-3:0.1-0.5 being mixed with, the liquid material includes the raw material of following parts by weight:
40-55 parts of polyvinyl acetate, plasticising lotion 8-16 parts, 1-3 parts of preservative, 1-3 parts of surfactant, dispersing agent 1-3
Part, 0.5-1.5 parts of galic essential oil, 1-3 parts of defoaming agent, 1-2 parts of coalescing agent, 46-90 parts of deionized water,
The powder includes the raw material of following parts by weight: 35-45 parts of portland cement, 23-37 parts of high alumina cement, reinforcing fiber 7-
12 parts, activation vermiculite 6-10 parts, 4-9 parts of white marble sand, it is silica flour 5-9 parts amino modified, 3-8 parts of nano-titanium dioxide.
2. the cement waterproof paint of addition white marble sand according to claim 1, which is characterized in that by liquid material, powder, consolidate
Agent is that 1:1:0.1 is mixed with by weight, and the liquid material includes the raw material of following parts by weight:
40 parts of polyvinyl acetate, plasticising 8 parts of lotion, 1 part of preservative, 1 part of surfactant, 1 part of dispersing agent, galic essential oil
0.5 part, 1 part of defoaming agent, 1 part of coalescing agent, 46 parts of deionized water,
The powder includes the raw material of following parts by weight: 35 parts of portland cement, 23 parts of high alumina cement, 7 parts of reinforcing fiber, activation
6 parts of vermiculite, 4 parts of white marble sand, 5 parts of amino modified silica flour, 3 parts of nano-titanium dioxide.
3. the cement waterproof paint of addition white marble sand according to claim 1, which is characterized in that by liquid material, powder, consolidate
Agent is that 1:3:0.5 is mixed with by weight, and the liquid material includes the raw material of following parts by weight:
55 parts of polyvinyl acetate, plasticising 16 parts of lotion, 3 parts of preservative, 3 parts of surfactant, 3 parts of dispersing agent, galic essential oil
1.5 parts, 3 parts of defoaming agent, 2 parts of coalescing agent, 90 parts of deionized water,
The powder includes the raw material of following parts by weight: 45 parts of portland cement, 12 parts of reinforcing fiber, is lived at 37 parts of high alumina cement
Change 10 parts of vermiculite, 9 parts of white marble sand, 9 parts of amino modified silica flour, 8 parts of nano-titanium dioxide.
4. the cement waterproof paint of addition white marble sand according to claim 1, which is characterized in that by liquid material, powder, consolidate
Agent is that 1:2:0.3 is mixed with by weight, and the liquid material includes the raw material of following parts by weight:
47 parts of polyvinyl acetate, plasticising 12 parts of lotion, 2 parts of preservative, 2 parts of surfactant, 2 parts of dispersing agent, galic essential oil 1
Part, 2 parts of defoaming agent, 1.5 parts of coalescing agent, 72 parts of deionized water,
The powder includes the raw material of following parts by weight: 40 parts of portland cement, 30 parts of high alumina cement, 9 parts of reinforcing fiber, activation
8 parts of vermiculite, 6 parts of white marble sand, 7 parts of amino modified silica flour, 6 parts of nano-titanium dioxide.
5. the cement waterproof paint of addition white marble sand according to claim 1, which is characterized in that the reinforcing fiber choosing
From silicon carbide whisker, carbonization boron whisker, alumina whisker, calcium sulfate crystal whiskers, zirconium dioxide whisker, aluminium nitride whisker, zinc oxide
One of whisker, magnesium sulfate crystal whisker and silicon nitride crystal whisker or more than one mixture.
6. the cement waterproof paint of addition white marble sand according to claim 1, which is characterized in that the plasticising lotion packet
Include following raw material: ethyl methacrylate, phenyl triethoxysilane, methacrylic acid, propenyl, styrene, polyphosphoric acid amine,
Neopelex, initiator, water and pH adjusting agent.
7. the cement waterproof paint of addition white marble sand according to claim 6, which is characterized in that the plasticising lotion packet
Include the raw material of following parts by weight: 13-20 parts of ethyl methacrylate, 4-7 parts of phenyl triethoxysilane, methacrylic acid 3-6
Part, 6-10 parts of propenyl, 5-8 parts of styrene, 2-5 parts of polyphosphoric acid amine, 1-3 parts of neopelex, 1-2 parts of initiator,
20-24 parts of water, 1-2 parts of pH adjusting agent.
8. the cement waterproof paint of addition white marble sand according to claim 1, which is characterized in that the amino modified stone
The partial size of English powder is 50-100nm, and the partial size of the white marble sand is 100-200nm；
The preservative is the mixture that one or both of trbasic zinc phosphate or aluminum phosphate are mixed with arbitrary proportion.
9. the cement waterproof paint of addition white marble sand according to claim 1, which is characterized in that the activation vermiculite
Preparation method: in vermiculite surface spray water, until then vermiculite moistened surface is carried out ozone treatment 30min, the concentration of ozone
For 50-75ppm.