CN109370184A - A kind of environmental protection aseptic packaging film - Google Patents
A kind of environmental protection aseptic packaging film Download PDFInfo
- Publication number
- CN109370184A CN109370184A CN201811267888.XA CN201811267888A CN109370184A CN 109370184 A CN109370184 A CN 109370184A CN 201811267888 A CN201811267888 A CN 201811267888A CN 109370184 A CN109370184 A CN 109370184A
- Authority
- CN
- China
- Prior art keywords
- parts
- packaging film
- aseptic packaging
- environmentally friendly
- film according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmentally friendly aseptic packaging films, and raw material includes: 70-90 parts of polylactic acid, 50-80 parts of polyvinyl alcohol, 12-25 parts of polyvinyl chloride, 8-12 parts of white carbon blacks, 10-20 parts of modified montmorillonoids, 5-9 parts of titanium dioxide, 3-7 parts of silica, 10-16 parts of glycerol, 2-4 parts of methylcellulose, 1-2 parts of calcium alginates, 80-200 parts of water by weight;Wherein, the raw material of the modified montmorillonoid includes montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate, acetic acid, hydrochloric acid, distilled water.Environmentally friendly aseptic packaging film of the invention has good anti-microbial property, mechanical performance and biological degradability, reduces the pollution to environment.
Description
Technical field
The present invention relates to packaging technical field of membrane, and in particular to a kind of environmental protection aseptic packaging film.
Background technique
Harmful microorganism in nature seriously threatens always the general level of the health of the mankind, and the whole world has millions of every year
People dies of bacterium infection.Therefore, the research of antibacterial agent and antibacterial product is increasingly paid attention in countries in the world.It is ripe to talk about that " disease is from mouth
Enter ", food is the best place of all kinds of microbial reproductions, once packaging is improper, it is easy to and bacterium is bred, therefore is badly in need of exploitation tool
The packaging film of standby anti-microbial property.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of environmentally friendly aseptic packaging films, have good
Anti-microbial property, mechanical performance and biological degradability, it is possible to reduce the pollution to environment.
The invention proposes a kind of environmentally friendly aseptic packaging films, and raw material includes: 60-80 parts of polylactic acid, 50-70 by weight
Part polyvinyl alcohol, 30-50 parts of starch, 12-25 parts of polyvinyl chloride, 10-15 parts of white carbon blacks, 10-20 parts of modified montmorillonoids, 5-9 parts
Titanium dioxide, 3-7 part silica, 10-16 parts of glycerol, 2-4 parts of methylcellulose, 1-2 parts of calcium alginates, 80-200 parts of water;
Wherein, the raw material of the modified montmorillonoid includes montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate, vinegar
Acid, hydrochloric acid, distilled water.
Preferably, the white carbon black, modified montmorillonoid, titanium dioxide, silica weight ratio be 11-14:13-17:
6-8:4-6.
Preferably, the polylactic acid, polyvinyl alcohol, starch, polyvinyl chloride, modified montmorillonoid weight ratio be 65-75:
54-62:35-45:15-22:13-17.
Preferably, the montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate weight ratio be 30-40:2-6:3-
5:2-4.
Preferably, the preparation process of the modified montmorillonoid is as follows:
S1, montmorillonite is added in distilled water, adds dodecyl sodium sulfate, with salt acid for adjusting pH value, stirring is anti-
It answers, stands, filter, wash, it is dry, obtain material A;
S2, chitosan, calcium propionate, acetum are mixed, is stirred at room temperature, material A is added, stir, be centrifuged, does
It is dry, modified montmorillonoid can be obtained.
Preferably, the w/v (g/mL) of the chitosan and acetum is 0.2-0.3:46-55.
Preferably, in S1, montmorillonite is added in distilled water, adds dodecyl sodium sulfate, with salt acid for adjusting pH
Value is stirred to react 3-5h at 55-70 DEG C, stands 1-2h, and filtering washs sediment 3-4 times with distilled water, dry, obtains
Material A.
Preferably, adjusting pH value is 2-3.
Preferably, the temperature of the drying is 60-65 DEG C, drying time 5-10h.
Preferably, in S2, the acetum of chitosan, calcium propionate, 1-2% is mixed, 1-2h is stirred at room temperature, be added
Material A, 50-65 DEG C at a temperature of stir 2-4h, be centrifuged, it is dry, modified montmorillonoid can be obtained.
Preferably, the temperature of the drying is 70-75 DEG C, drying time 5-8h.
Environmentally friendly aseptic packaging film of the invention is made using the preparation method of this field routine.
Environmentally friendly aseptic packaging film of the invention, using ingredients such as polylactic acid, polyvinyl alcohol, starch, polyvinyl chloride as base
Material, polylactic acid and starch addition allow environmentally friendly aseptic packaging film biodegradable, reduce the pollution to environment, also addition hard charcoal
The raw materials such as black, modified montmorillonoid, titanium dioxide, silica, glycerol, methylcellulose, calcium alginate can not only promote each
It is dispersed between raw material, also make environmentally friendly aseptic packaging film that there is good anti-microbial property, mechanical performance and water resistance.This hair
The modified montmorillonoid of bright addition is first modified processing to its surface using dodecyl sodium sulfate, is conducive to chitosan, third
The absorption of sour calcium, modified montmorillonoid obtained not only have good compatibility between other raw materials in system, additionally it is possible to
Discharge the antibacterial agents such as chitosan, calcium propionate constantly to inhibit the growth of microorganism;Modified montmorillonoid and titanium dioxide collocation use,
The antibacterial period can be extended, widen antimicrobial spectrum, enhance the antibacterial effect of packaging film;Add calcium alginate, glycerol, methylcellulose
It is used in conjunction with modified montmorillonoid, the compatibility between raw material can be enhanced, wherein the biology of packaging film also can be improved in calcium alginate
Degradability.
Specific embodiment
In the following, technical solution of the present invention is described in detail by specific embodiment.
Embodiment 1
A kind of environmental protection aseptic packaging film, raw material include: 80 parts of polylactic acid, 50 parts of polyvinyl alcohol, 50 parts of shallow lakes by weight
Powder, 12 parts of polyvinyl chloride, 15 parts of white carbon blacks, 10 parts of modified montmorillonoids, 9 parts of titanium dioxide, 3 parts of silica, 16 parts of glycerol, 2
Part methylcellulose, 2 parts of calcium alginates, 80 parts of water;
Wherein, the raw material of the modified montmorillonoid includes montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate, vinegar
Acid, hydrochloric acid, distilled water;The montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate weight ratio be 40:2:5:2;
The preparation process of the modified montmorillonoid is as follows:
S1, montmorillonite is added in distilled water, adds dodecyl sodium sulfate, be 3 with salt acid for adjusting pH value, 55
It is stirred to react 5h at DEG C, stands 1h, filtering washs sediment 4 times with distilled water, is placed at 60 DEG C dry 10h, obtains material
A;
S2, by chitosan, calcium propionate, 1% acetum mix, be stirred at room temperature 2h, material A be added, at 50 DEG C
At a temperature of stir 4h, be centrifuged, dry 8h, can be obtained modified montmorillonoid at 70 DEG C;
The w/v (g/mL) of the chitosan and acetum is 0.2:55.
Embodiment 2
A kind of environmental protection aseptic packaging film, raw material include: 60 parts of polylactic acid, 70 parts of polyvinyl alcohol, 30 parts of shallow lakes by weight
Powder, 25 parts of polyvinyl chloride, 10 parts of white carbon blacks, 20 parts of modified montmorillonoids, 5 parts of titanium dioxide, 7 parts of silica, 10 parts of glycerol, 4
Part methylcellulose, 1 part of calcium alginate, 200 parts of water;
Wherein, the raw material of the modified montmorillonoid includes montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate, vinegar
Acid, hydrochloric acid, distilled water;The montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate weight ratio be 30:6:3:4;
The preparation process of the modified montmorillonoid is as follows:
S1, montmorillonite is added in distilled water, adds dodecyl sodium sulfate, be 2 with salt acid for adjusting pH value, 70
It is stirred to react 3h at DEG C, stands 2h, filtering washs sediment 3 times with distilled water, is placed at 65 DEG C dry 5h, obtains material
A;
S2, by chitosan, calcium propionate, 2% acetum mix, be stirred at room temperature 1h, material A be added, at 65 DEG C
At a temperature of stir 2h, be centrifuged, dry 5h, can be obtained modified montmorillonoid at 75 DEG C;
The w/v (g/mL) of the chitosan and acetum is 0.3:46.
Embodiment 3
A kind of environmental protection aseptic packaging film, raw material include: 75 parts of polylactic acid, 54 parts of polyvinyl alcohol, 45 parts of shallow lakes by weight
Powder, 15 parts of polyvinyl chloride, 14 parts of white carbon blacks, 13 parts of modified montmorillonoids, 8 parts of titanium dioxide, 4 parts of silica, 15 parts of glycerol,
2.5 parts of methylcellulose, 1.6 parts of calcium alginates, 100 parts of water;
Wherein, the raw material of the modified montmorillonoid includes montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate, vinegar
Acid, hydrochloric acid, distilled water;The montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate weight ratio be 38:3:5:2;
The preparation process of the modified montmorillonoid is as follows:
S1, montmorillonite is added in distilled water, adds dodecyl sodium sulfate, be 3 with salt acid for adjusting pH value, 66
It is stirred to react 3.5h at DEG C, stands 1h, filtering washs sediment 4 times with distilled water, is placed at 64 DEG C dry 6h, obtains object
Expect A;
S2, by chitosan, calcium propionate, 1% acetum mix, be stirred at room temperature 2h, material A be added, at 62 DEG C
At a temperature of stir 2.5h, be centrifuged, dry 7h, can be obtained modified montmorillonoid at 71 DEG C;
The w/v (g/mL) of the chitosan and acetum is 0.3:49.
Embodiment 4
A kind of environmental protection aseptic packaging film, raw material include: 65 parts of polylactic acid, 62 parts of polyvinyl alcohol, 35 parts of shallow lakes by weight
Powder, 22 parts of polyvinyl chloride, 11 parts of white carbon blacks, 17 parts of modified montmorillonoids, 6 parts of titanium dioxide, 6 parts of silica, 12 parts of glycerol,
3.5 parts of methylcellulose, 1.2 parts of calcium alginates, 160 parts of water;
Wherein, the raw material of the modified montmorillonoid includes montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate, vinegar
Acid, hydrochloric acid, distilled water;The montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate weight ratio be 33:5:3:4;
The preparation process of the modified montmorillonoid is as follows:
S1, montmorillonite is added in distilled water, adds dodecyl sodium sulfate, be 2 with salt acid for adjusting pH value, 60
It is stirred to react 4.5h at DEG C, stands 2h, filtering washs sediment 3 times with distilled water, is placed at 62 DEG C dry 9h, obtains object
Expect A;
S2, by chitosan, calcium propionate, 2% acetum mix, be stirred at room temperature 1h, material A be added, at 55 DEG C
At a temperature of stir 3.5h, be centrifuged, dry 6h, can be obtained modified montmorillonoid at 74 DEG C;
The w/v (g/mL) of the chitosan and acetum is 0.2:53.
Embodiment 5
A kind of environmental protection aseptic packaging film, raw material include: 70 parts of polylactic acid, 58 parts of polyvinyl alcohol, 40 parts of shallow lakes by weight
Powder, 19 parts of polyvinyl chloride, 12 parts of white carbon blacks, 15 parts of modified montmorillonoids, 7 parts of titanium dioxide, 5 parts of silica, 14 parts of glycerol, 3
Part methylcellulose, 1.5 parts of calcium alginates, 130 parts of water;
Wherein, the raw material of the modified montmorillonoid includes montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate, vinegar
Acid, hydrochloric acid, distilled water;The montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate weight ratio be 35:4:5:3;
The preparation process of the modified montmorillonoid is as follows:
S1, montmorillonite is added in distilled water, adds dodecyl sodium sulfate, be 2.5 with salt acid for adjusting pH value,
It is stirred to react 4h at 60 DEG C, stands 1.5h, filtering washs sediment 3 times with distilled water, is placed at 63 DEG C dry 8h, obtains
Material A;
S2, the acetum of chitosan, calcium propionate, 1-2% are mixed, 1.5h is stirred at room temperature, material A is added,
3h is stirred at a temperature of 58 DEG C, is centrifuged, and dry 6h, can be obtained modified montmorillonoid at 72 DEG C;
The w/v (g/mL) of the chitosan and acetum is 0.05:10.
Comparative example 1
Substantially the same manner as Example 5, difference is only in that: not being used modified montmorillonoid, is obtained the packaging film of comparative example 1.
Test example 1
Mechanical performance and antibiotic property are carried out to the environmentally friendly aseptic packaging film and comparative example 1 of 1-5 of the embodiment of the present invention respectively
Detection, the examination criteria of mechanical performance are GB/T 13022-1991, and the examination criteria of anti-microbial property is QB/T 2591-2003,
Test result is as shown in table 1.
Table 1
As can be seen from Table 1, the environmentally friendly aseptic packaging film that the present invention obtains has preferable mechanical performance and antibacterial effect.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (10)
1. a kind of environmental protection aseptic packaging film, which is characterized in that its raw material includes: 60-80 parts of polylactic acid, 50-70 parts by weight
Polyvinyl alcohol, 30-50 part starch, 12-25 parts of polyvinyl chloride, 10-15 parts of white carbon blacks, 10-20 parts of modified montmorillonoids, 5-9 part two
Titanium oxide, 3-7 part silica, 10-16 parts of glycerol, 2-4 parts of methylcellulose, 1-2 parts of calcium alginates, 80-200 parts of water;
Wherein, the raw material of the modified montmorillonoid includes montmorillonite, dodecyl sodium sulfate, chitosan, calcium propionate, acetic acid, salt
Acid, distilled water.
2. environmentally friendly aseptic packaging film according to claim 1, which is characterized in that the white carbon black, modified montmorillonoid, titanium dioxide
Titanium, silica weight ratio be 11-14:13-17:6-8:4-6.
3. environmentally friendly aseptic packaging film according to claim 1, which is characterized in that the polylactic acid, starch, is gathered polyvinyl alcohol
Vinyl chloride, modified montmorillonoid weight ratio be 65-75:54-62:35-45:15-22:13-17.
4. environmentally friendly aseptic packaging film according to claim 1, which is characterized in that the montmorillonite, dodecyl sodium sulfate, shell
Glycan, calcium propionate weight ratio be 30-40:2-6:3-5:2-4.
5. environmentally friendly aseptic packaging film according to claim 1, which is characterized in that the preparation process of the modified montmorillonoid is such as
Under:
S1, montmorillonite is added in distilled water, adds dodecyl sodium sulfate, with salt acid for adjusting pH value, be stirred to react, it is quiet
It sets, filters, wash, it is dry, obtain material A;
S2, chitosan, calcium propionate, acetum are mixed, is stirred at room temperature, material A is added, stir, is centrifuged, it is dry, i.e.,
Modified montmorillonoid can be obtained.
6. environmentally friendly aseptic packaging film according to claim 5, which is characterized in that the weighing body of the chitosan and acetum
Product is 0.2-0.3:46-55 than (g/mL).
7. environmentally friendly aseptic packaging film according to claim 5, which is characterized in that in S1, montmorillonite is added in distilled water,
Dodecyl sodium sulfate is added, with salt acid for adjusting pH value, 3-5h is stirred to react at 55-70 DEG C, stands 1-2h, is filtered, is used
Distilled water washs sediment 3-4 times, dry, obtains material A.
8. environmentally friendly aseptic packaging film according to claim 7, which is characterized in that adjusting pH value is 2-3;Preferably, described dry
Dry temperature is 60-65 DEG C, drying time 5-10h.
9. environmentally friendly aseptic packaging film according to claim 5, which is characterized in that in S2, by chitosan, calcium propionate, 1-2%
Acetum mixing, is stirred at room temperature 1-2h, and material A is added, 50-65 DEG C at a temperature of stir 2-4h, be centrifuged, it is dry,
Modified montmorillonoid can be obtained.
10. environmentally friendly aseptic packaging film according to claim 9, which is characterized in that the temperature of the drying is 70-75 DEG C, is done
The dry time is 5-8h.