CN109369940A - Method for processing plastic surface - Google Patents
Method for processing plastic surface Download PDFInfo
- Publication number
- CN109369940A CN109369940A CN201811153403.4A CN201811153403A CN109369940A CN 109369940 A CN109369940 A CN 109369940A CN 201811153403 A CN201811153403 A CN 201811153403A CN 109369940 A CN109369940 A CN 109369940A
- Authority
- CN
- China
- Prior art keywords
- plastics
- plastic surface
- processing plastic
- concentrated sulfuric
- mixed solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is intended to provide method for processing plastic surface, comprising the following steps: A, carry out ungrease treatment to plastics using degreasing solvent;B, oxidizing flame is handled, and is first roughened frosting with emery cloth, then plastics are placed on oxidizing flame and are calcined, is divided into and being calcined three times, calcine 3-5s every time;C, it after impregnating 3-5min with sodium hydroxide solution, then is rinsed with cold water;D, it is activated, impregnates 5-12min in the mixed solution of chromic acid and the concentrated sulfuric acid;E, oxidation processes aoxidize 5-10min in the mixed solution of potassium bichromate and the concentrated sulfuric acid;F, 5-7min is washed in 70-75 DEG C of hot water, is dried under the conditions of 65-75 DEG C after being cleaned with distilled water;G, coating is uniformly coated on the surface of plastics;H, 10-20min is dried under the conditions of 65-75 DEG C.This method overcomes prior art defect, and flexibility is good after having the characteristics that easy to operate, processing.
Description
Technical field
The present invention relates to plastics processing fields, and in particular to a kind of method for processing plastic surface.
Background technique
Plastics can be divided into thermoplastic and thermosetting plastics two major classes.In general, thermosetting plastics wants specific heat
Thermoplastic plastic is easy to be glued.But their surface energy is below the hydrophilic materials such as glass, ceramics, metal, and their tables
Face can often adhere to release agent or evolution plasticizer, therefore be not easy to be infiltrated by adhesive, to influence glue-joint strength.Therefore, one
As be both needed to be surface-treated plastics.Since the kind of plastics is numerous, various performance differences are very big, therefore the side being surface-treated
Method is also just quite different.
Summary of the invention
The present invention is intended to provide a kind of method for processing plastic surface, this method overcome prior art defect, there is operation letter
Just, the good feature of flexibility after handling.
Technical scheme is as follows:
A kind of method for processing plastic surface, the treating method comprises following steps:
A, ungrease treatment is carried out to plastics using degreasing solvent;
B, oxidizing flame handle, be first roughened frosting with emery cloth, then plastics are placed on oxidizing flame and are calcined, be divided into three times into
Row calcining, calcines 3-5s every time;
C, it after impregnating 3-5min with sodium hydroxide solution, then is rinsed with cold water;
D, it is activated, impregnates 5-12min in the mixed solution of chromic acid and the concentrated sulfuric acid;
E, oxidation processes aoxidize 5-10min in the mixed solution of potassium bichromate and the concentrated sulfuric acid;
F, 5-7min is washed in 70-75 DEG C of hot water, is dried under the conditions of 65-75 DEG C after being cleaned with distilled water;
G, coating is uniformly coated on the surface of plastics, its component of coating presses following weight proportion: poly- propylhomoserin acrylic acid 5-
10 parts, 3-8 parts of Sodium Polyacrylate, 1.8-3.5 parts of phenolic resin, 0.8-2.3 parts of acrylate and vinyl acetate emulsion, hexylene glycol butyl ether sodium acetate 0.2-
0.6 part;
H, 10-20min is dried under the conditions of 65-75 DEG C.
Preferably, the degreasing solvent is acetone or butanone.
Preferably, the mass fraction of the sodium hydroxide solution is 30%, and dipping temperature is 60-75 DEG C.
Preferably, the mass ratio of chromic acid, the concentrated sulfuric acid and water is 1:2:4, dipping temperature in the mixed solution in the step D
It is 60-75 DEG C.
Preferably, the mass ratio of potassium bichromate, the concentrated sulfuric acid and water is 1:5:34, oxygen in the mixed solution in the step E
Changing temperature is 65-75 DEG C.
Preferably, the step F is specially to wash 5-7min in 70-75 DEG C of hot water, in 70- after being cleaned with distilled water
It is dried under the conditions of 80 DEG C.
Preferably, the coating composition further includes 5-7 parts diatomite part.
The invention has the advantages that method for processing plastic surface simple process of the invention, treated plastic cement
It is easy to connect, and glue-joint strength is high;Also, by being coated with one layer of fine and close coating in surface of plastic matrix, it is basic to improve plastics
The toughness of itself extends it using the time, while the color of coating itself can be changed, with different-style of arranging in pairs or groups out, difference taste
Appearance, more cater to the needs in market;And the flexibility for changing coating itself, is allowed to more easily be bonded, is not easy to peel off, prolong
The service life of long plastics is allowed to be hardly damaged, and is more in line with public demand.
Specific embodiment
The present invention is illustrated below with reference to embodiment.
Embodiment 1
A kind of method for processing plastic surface provided in this embodiment, the treating method comprises following steps:
A, ungrease treatment is carried out to plastics using degreasing solvent;
B, oxidizing flame handle, be first roughened frosting with emery cloth, then plastics are placed on oxidizing flame and are calcined, be divided into three times into
Row calcining, calcines 3s every time;
C, it after impregnating 3min with sodium hydroxide solution, then is rinsed with cold water;
D, it is activated, impregnates 5min in the mixed solution of chromic acid and the concentrated sulfuric acid;
E, oxidation processes aoxidize 5min in the mixed solution of potassium bichromate and the concentrated sulfuric acid;
F, 5min is washed in 70 DEG C of hot water, is dried under the conditions of 65 DEG C after being cleaned with distilled water;
G, coating is uniformly coated on the surface of plastics, its component of coating presses following weight proportion: poly- propylhomoserin acrylic acid 5
Part, 3 parts of Sodium Polyacrylate, 1.8 parts of phenolic resin, 0.8 part of acrylate and vinyl acetate emulsion, 0.2 part of hexylene glycol butyl ether sodium acetate;
H, 10min is dried under the conditions of 65 DEG C;
The degreasing solvent is acetone;
The mass fraction of the sodium hydroxide solution is 30%, and dipping temperature is 60 DEG C;
The mass ratio of chromic acid, the concentrated sulfuric acid and water is 1:2:4 in mixed solution in the step D, and dipping temperature is 60 DEG C;
The mass ratio of potassium bichromate, the concentrated sulfuric acid and water is 1:5:34, oxidizing temperature 65 in mixed solution in the step E
℃;
The step F is specially to wash 5-7min in 70 DEG C of hot water, is done under the conditions of 70 DEG C after being cleaned with distilled water
It is dry;The coating composition further includes 5 parts diatomite part.
Embodiment 2
A kind of method for processing plastic surface provided in this embodiment, the treating method comprises following steps:
A, ungrease treatment is carried out to plastics using degreasing solvent;
B, oxidizing flame handle, be first roughened frosting with emery cloth, then plastics are placed on oxidizing flame and are calcined, be divided into three times into
Row calcining, calcines 5s every time;
C, it after impregnating 5min with sodium hydroxide solution, then is rinsed with cold water;
D, it is activated, impregnates 12min in the mixed solution of chromic acid and the concentrated sulfuric acid;
E, oxidation processes aoxidize 10min in the mixed solution of potassium bichromate and the concentrated sulfuric acid;
F, 7min is washed in 75 DEG C of hot water, is dried under the conditions of 65-75 DEG C after being cleaned with distilled water;
G, coating is uniformly coated on the surface of plastics, its component of coating presses following weight proportion: poly- propylhomoserin acrylic acid 10
Part, 8 parts of Sodium Polyacrylate, 3.5 parts of phenolic resin, 2.3 parts of acrylate and vinyl acetate emulsion, 0.6 part of hexylene glycol butyl ether sodium acetate;
H, 20min is dried under the conditions of 75 DEG C;
The degreasing solvent is acetone;
The mass fraction of the sodium hydroxide solution is 30%, and dipping temperature is 75 DEG C;
The mass ratio of chromic acid, the concentrated sulfuric acid and water is 1:2:4 in mixed solution in the step D, and dipping temperature is 75 DEG C;
The mass ratio of potassium bichromate, the concentrated sulfuric acid and water is 1:5:34, oxidizing temperature 75 in mixed solution in the step E
℃;
The step F is specially to wash 7min in 75 DEG C of hot water, is dried under the conditions of 80 DEG C after being cleaned with distilled water;
The coating composition further includes 7 parts diatomite part.
Embodiment 3
A kind of method for processing plastic surface provided in this embodiment, the treating method comprises following steps:
A, ungrease treatment is carried out to plastics using degreasing solvent;
B, oxidizing flame handle, be first roughened frosting with emery cloth, then plastics are placed on oxidizing flame and are calcined, be divided into three times into
Row calcining, calcines 4s every time;
C, it after impregnating 4min with sodium hydroxide solution, then is rinsed with cold water;
D, it is activated, impregnates 8min in the mixed solution of chromic acid and the concentrated sulfuric acid;
E, oxidation processes aoxidize 7min in the mixed solution of potassium bichromate and the concentrated sulfuric acid;
F, 6min is washed in 72 DEG C of hot water, is dried under the conditions of 70 DEG C after being cleaned with distilled water;
G, coating is uniformly coated on the surface of plastics, its component of coating presses following weight proportion: poly- propylhomoserin acrylic acid 8
Part, 6 parts of Sodium Polyacrylate, 2 parts of phenolic resin, 1.5 parts of acrylate and vinyl acetate emulsion, 0.4 part of hexylene glycol butyl ether sodium acetate;
H, 15min is dried under the conditions of 70 DEG C;
The degreasing solvent is acetone;
The mass fraction of the sodium hydroxide solution is 30%, and dipping temperature is 65 DEG C;
The mass ratio of chromic acid, the concentrated sulfuric acid and water is 1:2:4 in mixed solution in the step D, and dipping temperature is 65 DEG C;
The mass ratio of potassium bichromate, the concentrated sulfuric acid and water is 1:5:34, oxidizing temperature 70 in mixed solution in the step E
℃;
The step F is specially to wash 6min in 72 DEG C of hot water, is dried under the conditions of 75 DEG C after being cleaned with distilled water;
The coating composition further includes 6 parts diatomite part.
Claims (7)
1. a kind of method for processing plastic surface, which is characterized in that the treating method comprises following steps:
A, ungrease treatment is carried out to plastics using degreasing solvent;
B, oxidizing flame handle, be first roughened frosting with emery cloth, then plastics are placed on oxidizing flame and are calcined, be divided into three times into
Row calcining, calcines 3-5s every time;
C, it after impregnating 3-5min with sodium hydroxide solution, then is rinsed with cold water;
D, it is activated, impregnates 5-12min in the mixed solution of chromic acid and the concentrated sulfuric acid;
E, oxidation processes aoxidize 5-10min in the mixed solution of potassium bichromate and the concentrated sulfuric acid;
F, 5-7min is washed in 70-75 DEG C of hot water, is dried under the conditions of 65-75 DEG C after being cleaned with distilled water;
G, coating is uniformly coated on the surface of plastics, its component of coating presses following weight proportion: poly- propylhomoserin acrylic acid 5-
10 parts, 3-8 parts of Sodium Polyacrylate, 1.8-3.5 parts of phenolic resin, 0.8-2.3 parts of acrylate and vinyl acetate emulsion, hexylene glycol butyl ether sodium acetate 0.2-
0.6 part;
H, 10-20min is dried under the conditions of 65-75 DEG C.
2. method for processing plastic surface according to claim 1, it is characterised in that: the degreasing solvent is acetone or fourth
Ketone.
3. method for processing plastic surface according to claim 1, it is characterised in that: the step C specifically:
The mass fraction of the sodium hydroxide solution is 30%, and dipping temperature is 60-75 DEG C.
4. method for processing plastic surface according to claim 1, it is characterised in that: in the mixed solution in the step D
The mass ratio of chromic acid, the concentrated sulfuric acid and water is 1:2:4, and dipping temperature is 60-75 DEG C.
5. method for processing plastic surface according to claim 1, it is characterised in that: in the mixed solution in the step E
The mass ratio of potassium bichromate, the concentrated sulfuric acid and water is 1:5:34, and oxidizing temperature is 65-75 DEG C.
6. method for processing plastic surface according to claim 1, it is characterised in that: the step F is specially at 70-75 DEG C
Hot water in wash 5-7min, be dried under the conditions of 70-80 DEG C after being cleaned with distilled water.
7. method for processing plastic surface according to claim 1, it is characterised in that: the coating composition further includes 5-7
Diatomite part of part.