CN109364738A - A kind of formaldehyde in indoor air absorption plant - Google Patents
A kind of formaldehyde in indoor air absorption plant Download PDFInfo
- Publication number
- CN109364738A CN109364738A CN201811325531.2A CN201811325531A CN109364738A CN 109364738 A CN109364738 A CN 109364738A CN 201811325531 A CN201811325531 A CN 201811325531A CN 109364738 A CN109364738 A CN 109364738A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde
- shell
- absorption
- indoor air
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of formaldehyde in indoor air absorption plants, including shell, handle is connected on the right side of the shell, the outer casing bottom is connected with supporting leg, filler is mounted between the partition and outer casing bottom, formaldehyde measurement instrument is mounted in the article putting groove, resettlement groove is provided on the left of the interior of shell, it is connected on the left of the absorption cell with link, the timer surface is provided with display screen, the absorption cell surface is provided with air hole, Storage Box is placed between the carriage, formaldehyde absorption material packet is placed in the Storage Box, catch basin is provided on the right side of the interior of shell, the liner surface is equipped with hinge.The present invention is equipped with timer on absorption cell, when being put into formaldehyde absorption material packet, timing can be started by pressing start button, such user be known that used how long, to guaranteeing to be replaced at the end of formaldehyde absorption material absorption, the case where preventing formaldehyde secondary release generation.
Description
Technical field
The present invention relates to formaldehyde absorption technical field, specially a kind of formaldehyde in indoor air absorption plant.
Background technique
The main harm of formaldehyde is shown as to mucocutaneous stimulation.When formaldehyde reaches a certain concentration indoors, people
Just there is sense of discomfort.Greater than 0.08mg/m3Concentration of formaldehyde can cause to be envious, eye is itched, throat discomfort or pain, hoarseness, spray
It sneezes, is uncomfortable in chest, asthma, dermatitis etc..Newly-decorated room content of formaldehyde is higher, is the main inducing of numerous diseases.Therefore, people adopt
A variety of methods have been taken to absorb indoor formaldehyde.
Present people are to carry out absorption formaldehyde using active carbon or plantation epipremnum aureum mostly, and still, people are in cabinet
Or after room is put into active carbon, can forget to placed how long, activated carbon adsorption formaldehyde is very limited, and is easy to saturation, saturation
Phase only has 20 days or so, just no longer had adsorption capacity more than 20 days, has the danger of the secondary release of formaldehyde instead, in addition, existing
The flowerpot that some plantation epipremnum aureums etc. absorb formaldehyde is inconvenient to add water, and intensive plant is especially grown as epipremnum aureum.
Summary of the invention
The purpose of the present invention is to provide a kind of formaldehyde in indoor air absorption plants, are proposed with solving above-mentioned background technique
Present people are to carry out absorption formaldehyde using active carbon or plantation epipremnum aureum mostly, and still, people are in cabinet or room is put
After entering active carbon, can forget to placed how long, activated carbon adsorption formaldehyde is very limited, and is easy to saturation, and the period of saturation only has 20
It or so just no longer had adsorption capacity more than 20 days, has the danger of the secondary release of formaldehyde instead, in addition, existing plantation
The flowerpot that epipremnum aureum etc. absorbs formaldehyde is inconvenient to the problem of adding water, intensive plant is especially grown as epipremnum aureum.
To achieve the above object, the invention provides the following technical scheme: a kind of formaldehyde in indoor air absorption plant, including
Shell, lanyard, connecting rope, hanging hole, water filling port, water pipe, handle, article putting groove, formaldehyde measurement instrument, filler, partition, supporting leg,
Absorption cell, resettlement groove, catch basin, interlayer, liner, through-hole, hinge, pull ring, water seepage hole, link, air hole, timer, starting
Button, display screen, adhered layer, protective film, pulling buckle, Storage Box and carriage, the shell right side are connected with handle, and handle
Top is connected by water pipe with water filling port, and the outer casing bottom is connected with supporting leg, and partition is welded between supporting leg, institute
It states and is mounted with filler between partition and outer casing bottom, and be provided with article putting groove in the middle part of filler, be mounted in the article putting groove
Formaldehyde measurement instrument, the interior of shell left side is provided with resettlement groove, and absorption cell is mounted in resettlement groove, on the left of the absorption cell
It is connected with link, and is inlaid with timer at the top of absorption cell, the timer surface is provided with display screen, and on the right side of display screen
It is provided with start button, the absorption cell surface is provided with air hole, and two sides are provided with carriage inside absorption cell, institute
It states and is placed with Storage Box between carriage, and store outer box wall and pulling buckle is installed, be provided with water storage on the right side of the interior of shell
Slot, and it is provided with through-hole at the top of catch basin, the catch basin positioned inside has interlayer, and liner is mounted in interlayer, described interior
Gallbladder surface is equipped with hinge, and pull ring is equipped on hinge；
Formaldehyde absorption material packet is placed in the Storage Box (30), the formaldehyde absorption material is wrapped as unit of parts by weight
Include following raw material: 18 parts of nano carbon sol, 7 parts of bentonite particle, 4 parts of mica particle, 3 parts of concave convex rod particle, zinc oxide particles
10 parts, 12 parts of ammonium bromide, 9 parts of carbonyl diamide urea, 6 parts of polyacrylamide, 25 parts of nano-titanium colloidal sol；
The preparation method of the formaldehyde absorption material, comprising the following steps:
(1) after evenly mixing by nano-titanium colloidal sol and nano carbon sol, the bentonite particle, mica particle, recessed is added
Convex stick particle, zinc oxide particles, ammonium bromide, carbonyl diamide urea, polyacrylamide, and stir evenly, obtain raw mixture；
(2) raw mixture ground, be granulated, drying and processing, porous complex microsphere is made, formaldehyde is made and inhales
Receive material.
Preferably, the shell and supporting leg material are disposed as metal material, and shell is set as double-layer structure, described
By being welded to connect between shell and supporting leg, and the shell and handle pass through hot melt glue connection, the front and back two of the shell
Side is provided with hanging hole, and there are four the settings of hanging hole described in side, is connected between the hanging hole by connecting rope, and connecting rope
There is lanyard in upper system.
Preferably, the lanyard and connecting rope material are disposed as twin cable.
Preferably, the material of the water filling port, water pipe and handle is disposed as transparent plastic, and water filling port is set as funnel
Shape structure.
Preferably, it is set as sealing structure at the handle top and cage connection, and at handle bottom and cage connection
It is set as through structure, the handle is set as hollow structure.
Preferably, the filler and interlayer material are disposed as sponge, and filler appearance is provided with protective case, described
Interlayer material is set as hard foam.
Preferably, the absorption cell is set as stand-alone configuration, and absorption cell bottom is provided with adhered layer, the adhered layer
Outside is provided with protective film, and adhered layer setting material is plant acid, rosin and cellulose.
Preferably, the resettlement groove is set as ramp type structure.
Preferably, the liner is set as detachable structure, and liner surface and bottom are provided with water seepage hole.
Preferably, it is connected between the timer, start button and display screen by electric wire, and timer, start button
It is connect with display screen with the battery of timer positioned inside by electric wire.
Compared with prior art, the beneficial effects of the present invention are:
(1) present invention is equipped with timer on absorption cell, when being put into formaldehyde absorption material packet, presses start button i.e.
Can start timing, such user be known that used how long, thus guarantee at the end of formaldehyde absorption material absorption into
Row replacement, the case where preventing formaldehyde secondary release generation；
(2) absorption cell of the present invention is set as stand-alone configuration, and absorption cell bottom is provided with adhered layer, while adhered layer is set
Setting material is plant acid, rosin and cellulose, and such absorption cell may be reused, and reduces the wasting of resources；
(3) present invention will be set as sealing structure at handle top and cage connection, and at handle bottom and cage connection
It is set as being connected by water pipe with water filling port above structure, handle, it may not be necessary to pull out liner, so that it may to plant
Object keeps the skin wet；
(4) material of water filling port of the present invention, water pipe and handle is disposed as transparent plastic, and water filling port is set as funnel-form
Structure, it is convenient to add water in time convenient for surplus water in observation Xushui slot according to the physical principle of the height such as liquid level.
Detailed description of the invention
Fig. 1 is formaldehyde in indoor air absorption plant shell mechanism schematic diagram of the invention；
Fig. 2 is formaldehyde in indoor air absorption plant schematic diagram of internal structure of the invention；
Fig. 3 is formaldehyde in indoor air absorption plant overlooking structure diagram of the invention；
Fig. 4 is formaldehyde in indoor air absorption plant inner-tube structure schematic diagram of the invention；
Fig. 5 is formaldehyde in indoor air absorption plant absorption cell top structure schematic diagram of the invention；
Fig. 6 is formaldehyde in indoor air absorption plant absorption cell right side structural schematic diagram of the invention.
In figure: 1, shell, 2, lanyard, 3, connecting rope, 4, hanging hole, 5, water filling port, 6, water pipe, 7, handle, 8, article putting groove, 9,
Formaldehyde measurement instrument, 10, filler, 11, partition, 12, supporting leg, 13, absorption cell, 14, resettlement groove, 15, catch basin, 16, interlayer,
17, liner, 18, through-hole, 19, hinge, 20, pull ring, 21, water seepage hole, 22, link, 23, air hole, 24, timer, 25, starting
Button, 26, display screen, 27, adhered layer, 28, protective film, 29, pulling buckle, 30, Storage Box, 31, carriage.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Embodiment 1
It is placed with formaldehyde absorption material packet in Storage Box, the formaldehyde absorption material, as unit of parts by weight, including following original
Material: 18 parts of nano carbon sol, 7 parts of bentonite particle, 4 parts of mica particle, 3 parts of concave convex rod particle, 10 parts of zinc oxide particles, bromination
12 parts of ammonium, 9 parts of carbonyl diamide urea, 6 parts of polyacrylamide, 25 parts of nano-titanium colloidal sol.The preparation method of the formaldehyde absorption material,
The following steps are included: (1) by nano-titanium colloidal sol and nano carbon sol after evenly mixing, the bentonite particle, mica grain is added
Son, concave convex rod particle, zinc oxide particles, ammonium bromide, carbonyl diamide urea, polyacrylamide, and stir evenly, obtain raw material mixing
Object；(2) raw mixture ground, be granulated, drying and processing, porous complex microsphere is made, formaldehyde absorption material is made
Material.
The present invention uses nano carbon sol, bentonite particle, mica particle, concave convex rod particle, zinc oxide particles, bromination
Ammonium, carbonyl diamide urea, polyacrylamide cooperate nano-titanium colloidal sol, play the role of collaboration, enhance TiO 2 sol
The performance of intensity, adsorbance and heat resistance etc., and microballoon is made in formaldehyde absorption material by the present invention, is enhanced absorption and is held
Amount and adsorption rate, adsorption effect is good, environmentally protective.Therefore, formaldehyde absorption material PARA FORMALDEHYDE PRILLS(91,95) prepared by the present invention has good
Adsorption effect, PARA FORMALDEHYDE PRILLS(91,95) adsorption rate is fast, and recycling effect is good, and preparation method is simple, strong operability, at low cost, has
Conducive to popularization and application.
The product that the present invention discloses no longer is passively formaldehyde absorption material, but the formaldehyde absorption material of strength, this hair
Ammonium bromide, carbonyl diamide urea, polyacrylamide in bright product are enough chemically reacted with formaldehyde, formaldehyde absorption with higher
Efficiency, it is not only strong but also low in cost to the pernicious gas formaldehyde absorption power in room air, secondary pollution will not be also generated,
For improving the living standard, the health for protecting the mankind, protection environment of the mankind, there are great social and economic implications.
Embodiment 2
500 grams of formaldehyde absorption material of the embodiment of the present invention 1 are taken, it is spare.The use absolute absorption amount of formaldehyde absorption ability
Comparison, test use measurement space of the stainless steel box (0.7m × 0.7m × 0.7m) of sealing as formaldehyde, stainless steel box
Gas outlet be a U-typed pipe, U-typed bottom of the tube can fill up active carbon or formaldehyde absorption material of the invention.This hair
The ability of bright formaldehyde absorption material removal formaldehyde is comparison object of reference with active carbon.The box synchronous contrast tested using two
It carries out, 500 grams of formaldehyde absorption materials of the invention, 500 grams of another filling is put into a U-typed pipe for formaldehyde adsorption
Food grade active charcoal is connected to inspection using formaldehyde measurement instrument (PPM Formaldehydemeter400, resolution ratio 0.01ppm)
Device interface is surveyed, to measure the situation of change of concentration of formaldehyde in box.Then sealing test box is sent constantly into from air inlet into box
The air of the 1.0ppm containing formaldehyde mends the air containing formaldehyde into box as soon as concentration of formaldehyde is reduced in box.Finally, when at 30 points
In clock, when the concentration of formaldehyde no longer reduces in box, record inputs the volume of air total amount in box, calculates absorbed formaldehyde
Total amount, to absorb total amount divided by the quality (active carbon=500 gram, formaldehyde absorption material=500 gram of the invention) of total absorbent,
The ability for calculating separately out active carbon and formaldehyde absorption material removal formaldehyde in air of the invention is as shown in table 1 below.
Table 1 absorbs formaldehyde in air capacity data contrast table
| Test number (TN) | Active carbon (mg/g) | Formaldehyde absorption material (mg/g) of the invention |
| 1 | 0.51 | 264.15 |
| 2 | 1.12 | 320.21 |
| 3 | 0.73 | 234.53 |
As can be seen from Table 1, the absorbability of formaldehyde absorption material of the invention be 285 times of activated carbon adsorptive capacity with
On.
Embodiment 3
10 grams of formaldehyde absorption material prepared using embodiment 1.It is 285 times of active carbon calculating by formaldehyde ability is absorbed, it is living
2.85 kilograms of dosage of charcoal of property.The quantitative variation using concentration of formaldehyde of formaldehyde absorption ability, test are stainless using being fully sealed
Measurement space of the steel box (1.0m × 1.0m × 1.0m) as formaldehyde.The formaldehyde that embodiment 2 is prepared is placed in one box to inhale
10 grams of material are received, another places 2.85 kilograms of active carbon.Initial amount concentration is all 2ppm, controls 25 degree of room temperature, constantly takes
The content of formaldehyde in air in sample monitor box, takes the average value tested three times, and obtained concentration data is as shown in table 2 below.
2 concentration data of table
| Time (hour) | Active carbon | Formaldehyde absorption material of the invention |
| 0 | 2.00 | 2.00 |
| 1 | 1.13 | 0.26 |
| 2 | 1.02 | 0.12 |
| 3 | 0.58 | 0.05 |
| 4 | 0.44 | 0.03 |
| 5 | 0.35 | 0.01 |
| 6 | 0.21 | It is limited lower than detection |
| 7 | 0.19 | It is limited lower than detection |
| 8 | 0.18 | It is limited lower than detection |
| 9 | 0.16 | It is limited lower than detection |
| 10 | 0.11 | It is limited lower than detection |
| 24 | 0.08 | It is limited lower than detection |
| 48 | 0.08 | It is limited lower than detection |
| 72 | 0.08 | It is limited lower than detection |
| Air is heated to 50 DEG C in box | 0.41 | It is limited lower than detection |
It, can be in fully erased air by table 2 the results show that the mechanism of action of formaldehyde absorption material of the invention is to absorb
Formaldehyde, once absorb, heating can not also release formaldehyde.And active carbon only adsorbs, and is a balance, can not thoroughly remove
The formaldehyde of formaldehyde, heat, absorption can reappear release.
Embodiment 4
Fig. 1-6 is please referred to, the present invention provides a kind of technical solution: a kind of formaldehyde in indoor air absorption plant, including it is outer
Shell 1, lanyard 2, connecting rope 3, hanging hole 4, water filling port 5, water pipe 6, handle 7, article putting groove 8, formaldehyde measurement instrument 9, filler 10, partition
11, supporting leg 12, absorption cell 13, resettlement groove 14, catch basin 15, interlayer 16, liner 17, through-hole 18, hinge 19, pull ring 20, infiltration
Water hole 21, link 22, air hole 23, timer 24, start button 25, display screen 26, adhered layer 27, protective film 28, pulling buckle 29,
Storage Box 30 and carriage 31 are connected with handle 7 on the right side of the shell 1, and pass through water pipe 6 and 5 phase of water filling port above handle 7
Connection, 1 bottom of shell is connected with supporting leg 12, and partition 11 is welded between supporting leg 12, the partition 11 and shell 1
It is mounted with filler 10 between bottom, and is provided with article putting groove 8 in the middle part of filler 10, formaldehyde survey is mounted in the article putting groove 8
Instrument 9 is measured, 1 inside left of shell is provided with resettlement groove 14, and absorption cell 13 is mounted in resettlement groove 14, the absorption cell 13
Left side is connected with link 22, and timer 24 is inlaid at the top of absorption cell 13, and 24 surface of timer is provided with display screen
26, and start button 25 is provided on the right side of display screen 26,13 surface of absorption cell is provided with air hole 23, and in absorption cell 13
Portion two sides are provided with carriage 31, Storage Box 30 are placed between the carriage 31, and 30 outer wall of Storage Box is installed
There is pulling buckle 29,1 inner right side of shell is provided with catch basin 15, and through-hole 18 is provided at the top of catch basin 15, the water storage
15 positioned inside of slot has interlayer 16, and liner 17 is mounted in interlayer 16, and 17 surface of liner is equipped with hinge 19, and
Pull ring 20 is installed on hinge 19；
Shell 1 and 12 material of supporting leg are disposed as metal material, and shell 1 is set as double-layer structure, the shell 1 with
By being welded to connect between supporting leg 12, and the shell 1 and handle 7 pass through hot melt glue connection, the front and rear sides of the shell 1
It is provided with hanging hole 4, and there are four the settings of hanging hole 4 described in side, is connected between the hanging hole 4 by connecting rope 3, and connect
It is to have lanyard 2 on rope 3.
Lanyard 2 and 3 material of connecting rope are disposed as twin cable, improve toughness, avoid disconnecting in suspension and lead
Plant is caused to fall.
The material of water filling port 5, water pipe 6 and handle 7 is disposed as transparent plastic, and water filling port 5 is set as funnel-shaped structure,
The handle 7 is set as hollow structure.
7 top of handle is set as sealing structure with 1 junction of shell, and 7 bottom of handle is set as passing through with 1 junction of shell
Wear structure.
Filler 10 and 16 material of interlayer are disposed as sponge, and 10 appearance of filler is provided with protective case, the interlayer
16 materials are set as hard foam.
Absorption cell 13 is set as stand-alone configuration, and 13 bottom of absorption cell is provided with adhered layer 27, outside the adhered layer 27
Side is provided with protective film 28, and it is plant acid, rosin and cellulose that material, which is arranged, in adhered layer 27.
Resettlement groove 14 is set as ramp type structure, conveniently takes, and is replaced, to ensure the effect for absorbing formaldehyde.
16 material of interlayer is set as hard foam, can flow into catch basin 15 to avoid the soil in liner 17, to keep away
Exempt from nutrient loss.
Liner 17 is set as detachable structure, and 17 surface of liner and bottom are provided with water seepage hole 21.
It is connected between timer 24, start button 25 and display screen 26 by electric wire, and timer 24,25 and of start button
Display screen 26 is connect with the battery of 24 positioned inside of timer by electric wire.
The working principle of the present embodiment: when using the formaldehyde in indoor air absorption plant, pull ring can be held first
20, the liner 17 that kind is implanted with epipremnum aureum is put into 15 middle part of catch basin of shell 1, is then slowly infused by water filling port 5 into water pipe 6
Water tap water and nutrient solution observe the liquid level of 7 internal water of handle, after water enters catch basin 15, interlayer 16 while adding water
It is filled moisture, the water seepage hole 21 through 17 surface of liner is phytoremediation, meanwhile, user can hold pulling buckle 29, will store
Box 30 takes out out of absorption cell 13 under the action of carriage 31, and is put into formaldehyde absorption material packet, protective film of then tearing
28, the adhered layer 27 of absorption cell 13 is hung in wardrobe, the start button 25 of timer 24 is then pressed, observes display screen 26,
When the time, by 5700 days, (adsorption capacity of formaldehyde absorption material of the present invention was 285 times or more of active carbon, activated carbon adsorption formaldehyde
It is very limited, and it is easy to saturation, the period of saturation only has 20 days, it is therefore assumed that the formaldehyde absorption material period of saturation of the present invention is 5700
It, replaces in time when timer is out of power.) when can be replaced with PARA FORMALDEHYDE PRILLS(91,95) absorbing material packet, when user needs to test family
It, can be by formaldehyde measurement instrument (PPM Formaldehydemeter400, resolution ratio 0.01ppm) 9 from filling when content of formaldehyde
It takes out and uses in object 10, so that user places article.
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art,
It is still possible to modify the technical solutions described in the foregoing embodiments, or part of technical characteristic is carried out etc.
With replacement, all within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in this
Within the protection scope of invention.
Claims (10)
1. a kind of formaldehyde in indoor air absorption plant, including shell (1), lanyard (2), connecting rope (3), hanging hole (4), water filling port
(5), water pipe (6), handle (7), article putting groove (8), formaldehyde measurement instrument (9), filler (10), partition (11), supporting leg (12), suction
Receive box (13), resettlement groove (14), catch basin (15), interlayer (16), liner (17), through-hole (18), hinge (19), pull ring (20),
Water seepage hole (21), link (22), air hole (23), timer (24), start button (25), display screen (26), adhered layer (27),
Protective film (28), pulling buckle (29), Storage Box (30) and carriage (31), it is characterised in that: be connected on the right side of the shell (1)
Handle (7), and be connected by water pipe (6) with water filling port (5) above handle (7), shell (1) bottom is connected with supporting leg
(12), it and between supporting leg (12) is welded with partition (11), is mounted with filler between the partition (11) and shell (1) bottom
(10), it and in the middle part of filler (10) is provided with article putting groove (8), is mounted with formaldehyde measurement instrument (9) in the article putting groove (8), it is described
Shell (1) inside left is provided with resettlement groove (14), and is mounted with absorption cell (13) in resettlement groove (14), the absorption cell (13)
Left side is connected with link (22), and is inlaid with timer (24) at the top of absorption cell (13), timer (24) the surface setting
Have display screen (26), and be provided with start button (25) on the right side of display screen (26), absorption cell (13) surface is provided with ventilative
Hole (23), and the internal two sides of absorption cell (13) are provided with carriage (31), are placed with storage between the carriage (31)
It deposits box (30), and Storage Box (30) outer wall is equipped with pulling buckle (29), shell (1) inner right side is provided with catch basin (15),
And be provided with through-hole (18) at the top of catch basin (15), catch basin (15) positioned inside has interlayer (16), and in interlayer (16)
It is mounted with liner (17), liner (17) surface is equipped with hinge (19), and pull ring (20) are equipped on hinge (19)；
It is placed with formaldehyde absorption material packet in the Storage Box (30), the formaldehyde absorption material, as unit of parts by weight, including with
Lower raw material: 18 parts of nano carbon sol, 7 parts of bentonite particle, 4 parts of mica particle, 3 parts of concave convex rod particle, 10 parts of zinc oxide particles,
12 parts of ammonium bromide, 9 parts of carbonyl diamide urea, 6 parts of polyacrylamide, 25 parts of nano-titanium colloidal sol；
The preparation method of the formaldehyde absorption material, comprising the following steps:
(1) after evenly mixing by nano-titanium colloidal sol and nano carbon sol, the bentonite particle, mica particle, concave convex rod is added
Particle, zinc oxide particles, ammonium bromide, carbonyl diamide urea, polyacrylamide, and stir evenly, obtain raw mixture；
(2) raw mixture ground, be granulated, drying and processing, porous complex microsphere is made, formaldehyde absorption material is made
Material.
2. formaldehyde in indoor air absorption plant according to claim 1, it is characterised in that: the shell (1) and support
Leg (12) material is disposed as metal material, and shell (1) is set as double-layer structure, the shell (1) and supporting leg (12) it
Between by being welded to connect, and the shell (1) and handle (7), by hot melt glue connection, the front and rear sides of the shell (1) are all provided with
It is equipped with hanging hole (4), and there are four hanging hole described in side (4) settings, is connected between the hanging hole (4) by connecting rope (3), and
It is to have lanyard (2) in connecting rope (3).
3. formaldehyde in indoor air absorption plant according to claim 1, it is characterised in that: the lanyard (2) and connection
Rope (3) material is disposed as twin cable.
4. formaldehyde in indoor air absorption plant according to claim 1, it is characterised in that: the water filling port (5), water pipe
(6) and the material of handle (7) is disposed as transparent plastic, and water filling port (5) is set as funnel-shaped structure.
5. formaldehyde in indoor air absorption plant according to claim 1, it is characterised in that: at the top of the handle (7) with
Shell (1) junction is set as sealing structure, and handle (7) bottom and shell (1) junction are set as through structure, and described
Hand (7) is set as hollow structure.
6. formaldehyde in indoor air absorption plant according to claim 1, it is characterised in that: the filler (10) and every
Layer (16) material is disposed as sponge, and filler (10) appearance is provided with protective case, and interlayer (16) material is set as hard
Matter sponge.
7. formaldehyde in indoor air absorption plant according to claim 1, it is characterised in that: absorption cell (13) setting
For stand-alone configuration, and absorption cell (13) bottom is provided with adhered layer (27), is provided with protective film on the outside of the adhered layer (27)
(28), and adhered layer (27) setting material is plant acid, rosin and cellulose.
8. formaldehyde in indoor air absorption plant according to claim 1, it is characterised in that: resettlement groove (14) setting
For ramp type structure.
9. formaldehyde in indoor air absorption plant according to claim 1, it is characterised in that: the liner (17) is set as
Detachable structure, and liner (17) surface and bottom are provided with water seepage hole (21).
10. formaldehyde in indoor air absorption plant according to claim 1, it is characterised in that: the timer (24) is opened
It is connected between dynamic button (25) and display screen (26) by electric wire, and timer (24), start button (25) and display screen (26)
It is connect with the battery of timer (24) positioned inside by electric wire.