CN109355897A - A kind of processing method of waterproof fabrics - Google Patents

A kind of processing method of waterproof fabrics Download PDF

Info

Publication number
CN109355897A
CN109355897A CN201811344362.7A CN201811344362A CN109355897A CN 109355897 A CN109355897 A CN 109355897A CN 201811344362 A CN201811344362 A CN 201811344362A CN 109355897 A CN109355897 A CN 109355897A
Authority
CN
China
Prior art keywords
parts
cloth
starching
embryo cloth
processing method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811344362.7A
Other languages
Chinese (zh)
Inventor
葛胜达
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Endurance Textile Technology Co Ltd
Original Assignee
Nantong Endurance Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Endurance Textile Technology Co Ltd filed Critical Nantong Endurance Textile Technology Co Ltd
Priority to CN201811344362.7A priority Critical patent/CN109355897A/en
Publication of CN109355897A publication Critical patent/CN109355897A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of processing methods of waterproof fabrics, comprising the following steps: A, the cloth extension yarn that will need to process first, washing；B, the embryo cloth processed will be needed to be dried, adjusts the humidity of cloth；C, cloth after treatment carries out starching, gluing；D, thermoset forming is carried out to the cloth after starching gluing；E, surface dressing is carried out to the cloth after thermoset forming, when carrying out water-proofing treatment to embryo cloth, whole embryo cloth is handled, remove the end of a thread on embryo cloth surface and the dust of design on fabric surface, then starching, frictioning is carried out using glue scraping plate after gluing, design on fabric surface extra glue is removed while glue surface is struck off, finally carry out thermosetting processing, it is fixed on glue drying on cloth, embryo cloth is processed using this method, not only cloth has good waterproofness, but also the pull resistance of embryo cloth entirety greatly enhances.

Description

A kind of processing method of waterproof fabrics
Technical field
The present invention relates to waterproof fabrics processing technique field, specially a kind of processing method of waterproof fabrics.
Background technique
Fabric final finishing be improved by main method chemically or physically fabric appearance and feel, promote wearability or The technical process for assigning specific function, is the process of textile " making something perfect even more perfect ".The development of present fabric final finishing technology Towards product function, differential, superior, processing technology diversification, depth direction are developed, and emphasize to improve product Wearability increases value-added content of product.
Waterproof fabrics is a kind of novel textile fabric, composition by macromolecule waterproof ventilative material (PTFE film) and cloth Material is combined.According to different product demand make two layers it is compound and three layers compound, it is widely used in outdoor dress ornament, mountain-climbing Clothes, wind coat, raincoat, shoes and hats gloves, cold-proof jacket, sports goods, Medical Devices etc., and gradually it is applied to fashion dress ornament.
Currently, processing technology of the waterproof fabrics used on the market etc., less than guarantee, pull resistance bottom wears no resistance.
Summary of the invention
The purpose of the present invention is to provide a kind of not only clothes to have good waterproofness, but also the pull resistance of embryo cloth entirety The processing method of the waterproof fabrics greatly enhanced, to solve the problems mentioned in the above background technology.
To achieve the above object, the invention provides the following technical scheme: a kind of processing method of waterproof fabrics, feature exist In: the following steps are included:
A, the cloth for needing to process is hung into yarn, washing first；
B, the embryo cloth processed will be needed to be dried, adjusts the humidity of cloth；
C, cloth after treatment carries out starching, gluing；
D, thermoset forming is carried out to the cloth after starching gluing；
E, surface dressing is carried out to the cloth after thermoset forming.
Preferably, described fabric is first passed around Gun Bu mechanism according to step A to carry out blowing, blowing while, passes through embryo cloth Over cleaning pond is cleaned.
Preferably, described to be removed water the embryo cloth after cleaning according to step B, be subsequently placed in temperature be 70-80 DEG C etc. 10min-15min is handled in ion drying box, under oxygen atmosphere, corona treatment obtains pretreated fabric.
Preferably, described according to step C:
A, fabric is subjected to starching by maceration extract under the drive of forming machine；
B, the slurry of extra dipping in embryo cloth is then shut out by roll again, and the embryo cloth after starching is sent into insulating box and is carried out It is dried, completes starching；
C, complete starching after embryo cloth be sent into automatic double surface gluer inside, automatic double surface gluer to the surface of embryo cloth coat it is organic change it is aqueous Glue.
The dipping sizing agent padded in step includes: 3-8 parts of seven water sodium sulfite, 15-20 parts of styrene-acrylic emulsion, containing hydroxyl 2-6 parts of hydrocarbyl polysiloxane, 2-6 parts of epoxychloropropane, 10-20 parts of propylene glycol, 3-6 parts of Tea Saponin, isobutyl palmitate 5-8 Part, 5-8 parts of isothiazolinone, 2-7 parts and deionized water 55-65 parts of 1,2- benzisothiazole-3-ketone, the pick-up are 80-89%；
Organic water-base cement that changes includes: 7-9 parts of antioxidant of 39-41 parts of watersoluble neoprene latex rubber aqueous terpenes tackifying resins 4-6 parts of 45-47 parts of deionized water of 4-6 parts of trimethyl ammonium chlorides of 2-3 parts of alchlor.
Preferably, the described cloth after gluing is sent into dustless insulating box according to step D is dried, dustless insulating box Internal temperature is 60-65 DEG C.
Preferably, 6 parts of seven water sodium sulfite, 15 parts of styrene-acrylic emulsion, the poly- silicon oxygen containing hydroxyl alkyl are contained in the dipping sizing agent 6 parts of alkane, 6 parts of epoxychloropropane, 16 parts of propylene glycol, 6 parts of Tea Saponin, 8 parts of isobutyl palmitate, 8 parts of isothiazolinone, 2- benzo 5 parts and 55 parts of deionized water of isothiazoline -3- ketone.
Preferably, it is described it is organic change in water-base cement be equipped with 41 parts of watersoluble neoprene latex rubber, 9 parts of aqueous terpenes tackifying resin, 6 parts of antioxidant, 3 parts of alchlor, 4 parts of trimethyl ammonium chloride, 47 parts of deionized water.
Preferably, the removal that the edge of embryo cloth after completion gluing is carried out to residue glue according to step E using scraper, and will Embryo cloth that treated carries out clot.
Compared with prior art, the beneficial effects of the present invention are:
The present invention processes embryo cloth using this method, and not only cloth has good waterproofness, but also embryo cloth entirety is anti- Drawing property greatly enhances.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects It encloses.
The invention provides the following technical scheme: a kind of processing method of waterproof fabrics, it is characterised in that: including following step It is rapid:
A, the cloth for needing to process is hung into yarn, washing first；
B, the embryo cloth processed will be needed to be dried, adjusts the humidity of cloth；
C, cloth after treatment carries out starching, gluing；
D, thermoset forming is carried out to the cloth after starching gluing；
E, surface dressing is carried out to the cloth after thermoset forming.
Fabric is first passed around into Gun Bu mechanism and carries out blowing, is cleaned embryo cloth by service sink while blowing, it will Embryo cloth after cleaning is removed water, and is subsequently placed in the plasma drying box that temperature is 70-80 DEG C and is handled 10min-15min, Under oxygen atmosphere, corona treatment obtains pretreated fabric.
Fabric is subjected to starching by maceration extract under the drive of forming machine, it is extra in embryo cloth then to shut out again by roll The slurry of dipping, and the embryo cloth after starching is sent into insulating box and is dried, starching is completed, the embryo cloth after completing starching It is sent into the inside of automatic double surface gluer, automatic double surface gluer, which coats the surface of embryo cloth, organic changes water-base cement.
Padding the dipping sizing agent in step includes: 3-8 parts of seven water sodium sulfite, 15-20 parts of styrene-acrylic emulsion, containing hydroxyl alkyl It is 2-6 parts of polysiloxanes, 2-6 parts of epoxychloropropane, 10-20 parts of propylene glycol, 3-6 parts of Tea Saponin, 5-8 parts of isobutyl palmitate, different 5-8 parts of thiazolinone, 2-7 parts and deionized water 55-65 parts of 1,2- benzisothiazole-3-ketone, the pick-up are 80- 89%；
Organic water-base cement that changes includes: 7-9 parts of antioxidant 4-6 of 39-41 parts of watersoluble neoprene latex rubber aqueous terpenes tackifying resins Part 45-47 parts of deionized water of 4-6 parts of trimethyl ammonium chloride of 2-3 parts of alchlor.
Cloth after gluing to be sent into dustless insulating box and is dried, the temperature inside dustless insulating box is 60-65 DEG C, Contain 6 parts of seven water sodium sulfite, 15 parts of styrene-acrylic emulsion, 6 parts of polysiloxanes containing hydroxyl alkyl, epoxychloropropane 6 in dipping sizing agent Part, 16 parts of propylene glycol, 6 parts of Tea Saponin, 8 parts of isobutyl palmitate, 8 parts of isothiazolinone, 5 parts of 2- benzisothiazole-3-ketone With 55 parts of deionized water, it is organic change in water-base cement be equipped with 41 parts of watersoluble neoprene latex rubber, 9 parts of aqueous terpenes tackifying resin, antioxygen 6 parts of agent, 3 parts of alchlor, 4 parts of trimethyl ammonium chloride, 47 parts of deionized water.
The edge of embryo cloth after completion gluing is carried out to the removal of residue glue using scraper, and embryo cloth is beaten by treated Volume.
In conclusion the present invention processes embryo cloth using this method, not only cloth has good waterproofness, but also The pull resistance of embryo cloth entirety greatly enhances.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding And modification, the scope of the present invention is defined by the appended.

Claims (9)

1. a kind of processing method of waterproof fabrics, it is characterised in that: the following steps are included:
A, the cloth for needing to process is hung into yarn, washing first；
B, the embryo cloth processed will be needed to be dried, adjusts the humidity of cloth；
C, cloth after treatment carries out starching, gluing；
D, thermoset forming is carried out to the cloth after starching gluing；
E, surface dressing is carried out to the cloth after thermoset forming.
2. a kind of processing method of waterproof fabrics according to claim 1, it is characterised in that: it is described according to step A by face Material first passes around Gun Bu mechanism and carries out blowing, cleans embryo cloth by service sink while blowing.
3. a kind of processing method of waterproof fabrics according to claim 1, it is characterised in that: it is described will be clear according to step B Embryo cloth after washing is removed water, and is subsequently placed in the plasma drying box that temperature is 70-80 DEG C and is handled 10min-15min, in oxygen Under atmosphere is enclosed, corona treatment obtains pretreated fabric.
4. a kind of processing method of waterproof fabrics according to claim 1, it is characterised in that: described according to step C:
A, fabric is subjected to starching by maceration extract under the drive of forming machine；
B, the slurry of extra dipping in embryo cloth is then shut out by roll again, and the embryo cloth after starching is sent into insulating box and is carried out It is dried, completes starching；
C, complete starching after embryo cloth be sent into automatic double surface gluer inside, automatic double surface gluer to the surface of embryo cloth coat it is organic change it is aqueous Glue.
It includes: 3-8 parts of seven water sodium sulfite, 15-20 parts of styrene-acrylic emulsion, hydrocarbon containing hydroxyl that 5. the dipping sizing agent in step is padded described in 2-6 parts of based polysiloxane, 2-6 parts of epoxychloropropane, 10-20 parts of propylene glycol, 3-6 parts of Tea Saponin, 5-8 parts of isobutyl palmitate, 5-8 parts of isothiazolinone, 2-7 parts and deionized water 55-65 parts of 1,2- benzisothiazole-3-ketone, the pick-up are 80- 89%；
Organic water-base cement that changes includes: 7-9 parts of antioxidant of 39-41 parts of watersoluble neoprene latex rubber aqueous terpenes tackifying resins 4-6 parts of 45-47 parts of deionized water of 4-6 parts of trimethyl ammonium chlorides of 2-3 parts of alchlor.
6. a kind of processing method of waterproof fabrics according to claim 1, it is characterised in that: it is described to be applied according to step D Cloth after glue, which is sent into dustless insulating box, to be dried, and the temperature inside dustless insulating box is 60-65 DEG C.
7. a kind of processing method of waterproof fabrics according to claim 4, it is characterised in that: contain in the dipping sizing agent Seven 6 parts of water sodium sulfites, 15 parts of styrene-acrylic emulsion, 6 parts of polysiloxanes containing hydroxyl alkyl, 6 parts of epoxychloropropane, 16 parts of propylene glycol, tea 6 parts of saponin, 8 parts of isobutyl palmitate, 8 parts of isothiazolinone, 5 parts and 55 parts of deionized water of 2- benzisothiazole-3-ketone.
8. a kind of processing method of waterproof fabrics according to claim 4, it is characterised in that: it is described organic to change in water-base cement Equipped with 41 parts of watersoluble neoprene latex rubber, 9 parts of aqueous terpenes tackifying resin, 6 parts of antioxidant, 3 parts of alchlor, trimethyl ammonia chloride 4 parts of ammonium, 47 parts of deionized water.
9. a kind of processing method of waterproof fabrics according to claim 1, it is characterised in that: it is described will be complete according to step E The removal of residue glue is carried out using scraper at the edge of embryo cloth after gluing, and embryo cloth carries out clot by treated.
CN201811344362.7A 2018-11-13 2018-11-13 A kind of processing method of waterproof fabrics Pending CN109355897A (en)