CN109610170A - A kind of preparation process of vamp sizing lining - Google Patents

A kind of preparation process of vamp sizing lining Download PDF

Info

Publication number
CN109610170A
CN109610170A CN201811293875.XA CN201811293875A CN109610170A CN 109610170 A CN109610170 A CN 109610170A CN 201811293875 A CN201811293875 A CN 201811293875A CN 109610170 A CN109610170 A CN 109610170A
Authority
CN
China
Prior art keywords
base fabric
processing
vamp
drying
drying chamber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811293875.XA
Other languages
Chinese (zh)
Inventor
严华荣
董二莹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG KINGSAFE INTERLINING CO Ltd
Original Assignee
ZHEJIANG KINGSAFE INTERLINING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG KINGSAFE INTERLINING CO Ltd filed Critical ZHEJIANG KINGSAFE INTERLINING CO Ltd
Priority to CN201811293875.XA priority Critical patent/CN109610170A/en
Publication of CN109610170A publication Critical patent/CN109610170A/en
Pending legal-status Critical Current

Abstract

The invention proposes a kind of vamp preparation processes of sizing lining, successively the following steps are included: base fabric is weaved, alkali is rolled to bank up, oxygen bleaching processing, hard finishing, two point dispensing, bake and bank up with earth processing, bake and bank up with earth processing, wind inspection processing, base fabric is weaved into using 58tex × 58tex cotton yarn through broadwise, meet the needs that vamp sizing lining requires good constancy and gas permeability and comfort level, hard finishing is carried out to product using polyacrylate and polyvinyl acetate second dipping and rolling technique, boardness effect after arrangement is good, assign fabric elasticity and the thick and solid feature of feel.

Description

A kind of preparation process of vamp sizing lining
[technical field]
The present invention relates to the field of fabric, the preparation process of especially a kind of vamp sizing lining.
[background technique]
People are also being continuously improved the quality requirement of sock, are especially going out while requiring to be continuously improved to shoes Mouth product, the current domestic universal stiffness of sock is inadequate, guarantor's type is bad, while shrinkage is bigger and solid sense is not also strong, seriously Shoes class and price are affected, therefore proposes a kind of preparation process of vamp sizing lining.
[summary of the invention]
The object of the invention is to solve the problems of the prior art, a kind of preparation process of vamp sizing lining is proposed, The product of this technique production has good stiffness, and dimensionally stable shrinking percentage is low, and shape-retaining ability is splendid, good constancy and thoroughly Gas, environment-friendly tasteless.
To achieve the above object, the invention proposes a kind of vamp preparation processes of sizing lining, comprising the following steps:
A: base fabric weaving: warp thread, weft yarn are weaved into base fabric, warp thread, weft yarn are all made of cotton yarn;
B: it rolls alkali and banks up: pad weak lye processing to base fabric, then bank up 2.5~3 hours to the base for rolling alkali and banking up Cloth carries out desizing washing process, and washing time is 25~30 minutes;
C: oxygen bleaching processing: oxygen bleaching process processing is carried out to base fabric, and adds composite refining enzyme during processing;
D: hard finishing: base fabric is subjected to hard finishing to base fabric using second dipping and rolling technique, base fabric is then fed two Segmentation drying chamber completes drying;
E: two point dispensing: carrying out double-dot coating for silicone oil neutral emulsion and PA glue using cylinder and form hot melt adhesive layer, cooling Base fabric is sent into drying chamber afterwards;
F: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 80~100 DEG C, drying time is 5~7 minutes, and the temperature of the second drying chamber is 100~130 DEG C, and drying time is 4~5 minutes, third drying chamber Temperature be 130~140 DEG C, drying time be 2~3 minutes;
G: winding inspection processing: base fabric being wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding, And it carries out the qualified product of quality, appearance to be packaged as finished product.
Preferably, being passed through in the step a, weft is all made of 58tex × 58tex cotton yarn.
Preferably, second dipping and rolling technique carries out base fabric using polyacrylate and polyvinyl acetate in the step d Hard finishing.
Preferably, the mesh number of cylinder is CP90 in the step e, the aperture of cylinder is 0.26-0.29mm, the thickness of cylinder Degree is 0.16-0.18mm.
Preferably, antibacterial agent is added in the PA glue in the step e in process of production.
Preferably, the two-part drying chamber in the step d includes: prebake section: temperature is 80 DEG C, time 2min, roasting Dry section: temperature is 140 DEG C, time 80s.
Beneficial effects of the present invention: the present invention proposes a kind of preparation process of vamp sizing lining, uses 58tex through broadwise × 58tex cotton yarn is weaved into base fabric, meet vamp sizing lining require good constancy and gas permeability and The needs of comfort level carry out hard finishing to product using polyacrylate and polyvinyl acetate second dipping and rolling technique, after arrangement Boardness effect it is good, assign fabric elasticity and the thick and solid feature of feel.
Feature and advantage of the invention will be described in detail by embodiment.
[specific embodiment]
A kind of preparation process of present invention vamp sizing lining, comprising the following steps:
A: base fabric weaving: warp thread, weft yarn are weaved into base fabric, warp thread, weft yarn are all made of 58tex × 58tex cotton Yarn;
B: it rolls alkali and banks up: pad weak lye processing to base fabric, then bank up 2.5~3 hours to the base for rolling alkali and banking up Cloth carries out desizing washing process, and washing time is 25~30 minutes;
C: oxygen bleaching processing: oxygen bleaching process processing is carried out to base fabric, and adds composite refining enzyme during processing;
D: hard finishing: base fabric endures with all one's will base fabric using polyacrylate and polyvinyl acetate second dipping and rolling technique It arranges, base fabric feeding two-part drying chamber is then completed drying, prebake section: temperature is 80 DEG C, time 2min, bakes section: temperature Degree is 140 DEG C, time 80s;
E: two point dispensing: carrying out double-dot coating for silicone oil neutral emulsion and PA glue using cylinder and form hot melt adhesive layer, cooling Base fabric is sent into drying chamber afterwards;
F: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 80~100 DEG C, drying time is 5~7 minutes, and the temperature of the second drying chamber is 100~130 DEG C, and drying time is 4~5 minutes, third drying chamber Temperature be 130~140 DEG C, drying time be 2~3 minutes;
G: winding inspection processing: base fabric being wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding, And it carries out the qualified product of quality, appearance to be packaged as finished product.
The mesh number of cylinder is CP90 in the step e, and the aperture of cylinder is 0.26-0.29mm, cylinder with a thickness of 0.16- 0.18mm.Antibacterial agent is added in PA glue in process of production.
Technical performance index:
1, peel strength: before washing >=18N/5 × 10cm washing after >=15N/5 × 10cm;
2, xeothermic change in size: through to -1.5~+0.3 broadwise -1.0~+0.4;
3, change in size is washed: through to -1.0~+0.4 broadwise -1.0~+0.4;
4, solid carbon dioxide washes cosmetic variation >=4 grade;
5, free formaldehyde :≤75ppm is discharged.
A kind of preparation process of vamp of present invention sizing lining, this product through broadwise using 58tex × 58tex cotton yarn into Row weaving meets the needs that vamp sizing lining requires good constancy and gas permeability and comfort level, shoes at base fabric The effects of face sizing lining echos the adhesive fabric in fabric, can play reinforcement sizing, waterproof sweat-absorption;
Hard finishing is carried out to product using polyacrylate and polyvinyl acetate second dipping and rolling technique, the fabric after arrangement Stiffness effect is good, assigns fabric elasticity and the thick and solid feature of feel, will not generate traditional hard finishing base fabric place after inhale Moisture can get damp again and reduce hardness and sock be made to soften in receipts air;
Traditional shoes cold adhesive, processing fusing point is lower, can reach sizing aesthetic effect and waterproof effect well, price It is more cheap, but processing pollution is heavier, and have pungent smell in shoes after cooling down, viscous stickiness does not have hot melt adhesive secured, ventilative Property is also poor.This product is formed using PA glue double-dot coating, product environment-friendly tasteless, has suitable hardness and mechanical property, is glued Close good, folding quality is excellent, solve shoes be easy during wearing with lining delamination, the problems such as fracture damage.Sizing is endured It includes, waterproofness better effect, is able to ascend the aesthetic effect of shoes.
Above-described embodiment is the description of the invention, is not limitation of the invention, after any pair of simple transformation of the present invention Scheme all belong to the scope of protection of the present invention.

Claims (6)

1. a kind of vamp preparation process of sizing lining, it is characterised in that: the following steps are included:
A: base fabric weaving: warp thread, weft yarn are weaved into base fabric, warp thread, weft yarn are all made of cotton yarn;
B: roll alkali and bank up: pad weak lye processing to base fabric, then bank up 2.5~3 hours to roll base fabric that alkali is banked up into Row desizing washing process, washing time are 25~30 minutes;
C: oxygen bleaching processing: oxygen bleaching process processing is carried out to base fabric, and adds composite refining enzyme during processing;
D: hard finishing: base fabric is subjected to hard finishing to base fabric using second dipping and rolling technique, base fabric is then fed into two-part Drying chamber completes drying;
E: two point dispensing: carrying out double-dot coating for silicone oil neutral emulsion and PA glue using cylinder and form hot melt adhesive layer, will after cooling Base fabric is sent into drying chamber;
F: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 80~100 DEG C, is dried The dry time is 5~7 minutes, and the temperature of the second drying chamber is 100~130 DEG C, and drying time is 4~5 minutes, the temperature of third drying chamber It is 130~140 DEG C, drying time is 2~3 minutes;
G: winding inspection processing: base fabric is wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding, and will The qualified product of quality, appearance carries out being packaged as finished product.
2. a kind of preparation process of vamp sizing lining as described in claim 1, it is characterised in that: passed through in the step a, latitude Line is all made of 58tex × 58tex cotton yarn.
3. a kind of preparation process of vamp sizing lining as described in claim 1, it is characterised in that: two leaching in the step d Two roll process carry out hard finishing to base fabric using polyacrylate and polyvinyl acetate.
4. a kind of preparation process of vamp sizing lining as described in claim 1, it is characterised in that: cylinder in the step e Mesh number be CP90, the aperture of cylinder is 0.26-0.29mm, cylinder with a thickness of 0.16-0.18mm.
5. a kind of preparation process of vamp sizing lining as described in claim 1, it is characterised in that: the PA in the step e Antibacterial agent is added in glue in process of production.
6. a kind of preparation process of vamp sizing lining as described in claim 1, it is characterised in that: two in the step d Segmentation drying chamber includes: prebake section: temperature is 80 DEG C, and time 2min bakes section: temperature is 140 DEG C, time 80s.
CN201811293875.XA 2018-11-01 2018-11-01 A kind of preparation process of vamp sizing lining Pending CN109610170A (en)