CN109355785A - A kind of production technology of crepe jacquard gold and silver fabric - Google Patents
A kind of production technology of crepe jacquard gold and silver fabric Download PDFInfo
- Publication number
- CN109355785A CN109355785A CN201810946827.XA CN201810946827A CN109355785A CN 109355785 A CN109355785 A CN 109355785A CN 201810946827 A CN201810946827 A CN 201810946827A CN 109355785 A CN109355785 A CN 109355785A
- Authority
- CN
- China
- Prior art keywords
- angle
- tension
- yarn
- reeling
- weaving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production technologies of crepe jacquard gold and silver fabric, including warp thread processing and weave, when weaving, the temperature of weaving rooms is 25-26 DEG C, humidity is 65-70%, speed is 520r/min, back beam height is 4cm, angle is 75 °, upper beam of a loom warp tension is 600-670kg*g, lower beam of a loom warp tension 250-300kg*g, single 30# water pump, two 90# sprinkler bodies, 2 40# nozzles, angle of water is 85-90 °, the angle of water to waste selvage yarn is 220-230 °, the angle of yarn to waste selvage yarn is 240-255 °, yarn and reed touching angle are 280-295 °, comprehensive straight angle degree is 345 °.The product is on the basis of the digestion of equipment, absorption, improvement, solve the problems, such as in weaving process it is easily broken through, the metallized thread raw material of use, initial modulus is high, not easily stretchable, by the optimization of weaving process, reduction is resolved through rate, loom efficiency is improved, the fine and smooth soft novel fabric of wash and wear, comfortable feel, quality is developed.
Description
Technical field
The present invention relates to textile fabric production fields, and in particular to a kind of production technology of crepe jacquard gold and silver fabric.
Background technique
Fabric is exactly the material for making clothes, and as one of clothes three elements, fabric can not only annotate clothes
Style and characteristic, and directly control the expression effect of the color of clothes, moulding, with longitude and latitude tissue change shape when face weave
At flower case, yarn count is fine, high to the requirement of raw material cotton, can divide tatting, warp-knitting jacquard and weft jacquard, and weft-knitted fabric is horizontal, longitudinal
There is good elasticity when drawing, warp knit and tatting jacquard weave is horizontal, longitudinal draw is that do not have flexible, traditional fabric there are takings
Bad, the defect that added value is low, of low grade of energy, affects the use of fabric, to reduce the practicability of existing fabric.
Summary of the invention
The purpose of the present invention is to provide a kind of production technology of crepe jacquard gold and silver fabric, it is good to have a wearability, adds
The advantage that value is high, class is high, it is bad to solve traditional fabric wearability, the problem that added value is low, of low grade.
To achieve the above object, the invention provides the following technical scheme: a kind of production technology of crepe jacquard gold and silver fabric, packet
Warp thread processing and weaving are included, when weaving, the temperature of weaving rooms is 25-26 DEG C, humidity 65-70%, speed 520r/min,
Back beam height is 4cm, and angle is 75 °, and upper beam of a loom warp tension is 600-670kg*g, lower beam of a loom warp tension 250-300kg*
G, single 30# water pump, two 90# sprinkler bodies, 2 40# nozzles, angle of water are 85-90 °, and water end of a period angle is 190-200 °, water
Angle to waste selvage yarn is 220-230 °, and the angle of yarn to waste selvage yarn is 240-255 °, and yarn and reed touching angle are 280-
295 °, comprehensive straight angle degree is 345 °；
A kind of production technology of crepe jacquard gold and silver fabric, comprises the technical steps that, reeling-double twisting-section warping-gaits-temperature
Humid control-weaving:
A, reeling: using spooler, sets reeling deal 1.25-1.26kg, reeling duration 250 minutes, crimps tension 29-30CN
Carry out reeling；
B, double twisting: using two-for-one twister, sets ingot speed 12000r/min, adds 0.7*3, tension pearl, 360 ° of progress double twistings of cornerite；?
Cylinder silk shifting rod speed control winds tension control in 8-10CN in 9-10s；
C, section warping: setting swift speed 60m/min, beaming 40m/min match No. three tension caps, and the control of warping tension exists
12g, beaming tension are controlled in 1.8kg, by 288 * 24 progress warpings；
D, gait: comprehensive using 14, style is gaited；
E, Temperature and Humidity Control: temperature is controlled at 25-26 DEG C, and humid control is in 65-70%；
F, weave: speed sets 520r/min, back beam height 4cm, and 75 ° of angle, upper machine tension 260kg is weaved.
Preferably, the spooler model SGD168 type spooler.
Preferably, the two-for-one twister model YB310G type two-for-one twister.
Compared with prior art, beneficial effects of the present invention are as follows:
1, the product solves the problems, such as easily broken through use in weaving process on the basis of the digestion of equipment, absorption, improvement
Metallized thread raw material, initial modulus is high, not easily stretchable, and by the optimization of weaving process, reduction is resolved through rate, improves loom effect
Rate develops the fine and smooth soft novel fabric of wash and wear, comfortable feel, quality.
Detailed description of the invention
A kind of Fig. 1: process flow chart of the production technology of crepe jacquard gold and silver fabric；
A kind of Fig. 2: organization chart of the production technology of crepe jacquard gold and silver fabric；
Fig. 3: a kind of reed draft, the drafting plan of the production technology of crepe jacquard gold and silver fabric；
A kind of Fig. 4: pegging plan of the production technology of crepe jacquard gold and silver fabric.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Please refer to Fig. 1-4, a kind of production technology of crepe jacquard gold and silver fabric, including warp thread processing and weaving when weaving, is knitted
The temperature for making workshop is 25-26 DEG C, humidity 65-70%, speed 520r/min, back beam height 4cm, and angle is 75 °, on
Beam of a loom warp tension is 600-670kg*g, and lower beam of a loom warp tension is 250-300kg*g, single 30# water pump, two 90# sprays
Body, 2 40# nozzles, angle of water are 85-90 °, and water end of a period angle is 190-200 °, and the angle of water to waste selvage yarn is 220-
230 °, the angle of yarn to waste selvage yarn is 240-255 °, and yarn and reed touching angle are 280-295 °, and comprehensive straight angle degree is 345 °；
A kind of production technology of crepe jacquard gold and silver fabric, comprises the technical steps that, reeling-double twisting-section warping-gaits-temperature
Humid control-weaving:
A, reeling: using spooler, sets reeling deal 1.25-1.26kg, reeling duration 250 minutes, crimps tension 29-30CN
Carry out reeling；
B, double twisting: using two-for-one twister, sets ingot speed 12000r/min, adds 0.7*3, tension pearl, 360 ° of progress double twistings of cornerite；?
Cylinder silk shifting rod speed control winds tension control in 8-10CN in 9-10s；
C, section warping: setting swift speed 60m/min, beaming 40m/min match No. three tension caps, and the control of warping tension exists
12g, beaming tension are controlled in 1.8kg, by 288 * 24 progress warpings；
D, gait: comprehensive using 14, style is gaited；
E, Temperature and Humidity Control: temperature is controlled at 25-26 DEG C, and humid control is in 65-70%；
F, weave: speed sets 520r/min, back beam height 4cm, and 75 ° of angle, upper machine tension 260kg is weaved；
The product solves the problems, such as easily broken through the gold of use in weaving process on the basis of the digestion of equipment, absorption, improvement
Filamentary silver raw material, initial modulus is high, not easily stretchable, and by the optimization of weaving process, reduction is resolved through rate, improves loom efficiency,
Develop the fine and smooth soft novel fabric of wash and wear, comfortable feel, quality.
Spooler model SGD168 model employed in the present invention, two-for-one twister model YB310G model.
Embodiment one:
A, reeling: using SGD168 type spooler, sets reeling deal 1.25kg, reeling duration 250 minutes, crimps tension 29CN
Carry out reeling；
B, double twisting: using YB310G type two-for-one twister, sets ingot speed 12000r/min, adds 0.7*3, tension pearl, 360 ° of cornerite progress
Double twisting；Rewinding silk shifting rod speed control winds tension control in 8CN in 9s；
C, section warping: setting swift speed 60m/min, beaming 40m/min match No. three tension caps, and the control of warping tension exists
12g, beaming tension are controlled in 1.8kg, by 288 * 24 progress warpings；
D, gait: the method for gaiting is shown in Fig. 3, and the warp thread in warp beam is comprehensive using 14, and flower, which is worn, gaits；
E, Temperature and Humidity Control: temperature is controlled at 25 DEG C, and humid control is 65%；
F, weave: the temperature of weaving rooms is 25 DEG C, humidity 65%, speed 520r/min, back beam height 4cm, and angle is
75 °, upper beam of a loom warp tension be 605kg*g, lower beam of a loom warp tension be 253kg*g, single 30# water pump, two 90# sprinkler bodies, 2
A 40# nozzle, angle of water are 86 °, and water end of a period angle is 191 °, and water to waste selvage yarn angle is 221 °, yarn to waste selvage yarn angle
241 °, yarn and reed touching angle are 282 °, and comprehensive straight angle degree is 345 °.
Embodiment two:
A, reeling: using SGD168 type spooler, sets reeling deal 1.26kg, reeling duration 250 minutes, crimps tension
29.5CN carrying out reeling；
B, double twisting: using YB310G type two-for-one twister, sets ingot speed 12000r/min, adds 0.7*3, tension pearl, 360 ° of cornerite progress
Double twisting；Rewinding silk shifting rod speed control winds tension control in 9CN in 9.5s；
C, section warping: setting swift speed 60m/min, beaming 40m/min match No. three tension caps, and the control of warping tension exists
12g, beaming tension are controlled in 1.8kg, by 288 * 24 progress warpings；
D, gait: the method for gaiting is shown in Fig. 3, and the warp thread in warp beam is comprehensive using 14, and flower, which is worn, gaits；
E, Temperature and Humidity Control: temperature is controlled at 25.5 DEG C, and humid control is 68%；
F, weave: the temperature of weaving rooms is 25.5 DEG C, humidity 68%, speed 520r/min, back beam height 4cm, angle
It is 75 °, upper beam of a loom warp tension is 636kg*g, and lower beam of a loom warp tension is 273kg*g, single 30# water pump, two 90# sprays
Body, 2 40# nozzles, angle of water are 88 °, and water end of a period angle is 194 °, and water to waste selvage yarn angle is 224 °, yarn to waste selvage yarn
249 ° of angle, yarn and reed touching angle are 289 °, and comprehensive straight angle degree is 345 °.
Embodiment three:
A, reeling: using SGD168 type spooler, sets reeling deal 1.26kg, reeling duration 250 minutes, crimps tension 30CN
Carry out reeling；
B, double twisting: using YB310G type two-for-one twister, sets ingot speed 12000r/min, adds 0.7*3, tension pearl, 360 ° of cornerite progress
Double twisting；Rewinding silk shifting rod speed control winds tension control in 10CN in 10s；
C, section warping: setting swift speed 60m/min, beaming 40m/min match No. three tension caps, and the control of warping tension exists
12g, beaming tension are controlled in 1.8kg, by 288 * 24 progress warpings；
D, gait: the method for gaiting is shown in Fig. 3, and the warp thread in warp beam is comprehensive using 14, and flower, which is worn, gaits；
E, Temperature and Humidity Control: temperature is controlled at 26 DEG C, and humid control is 70%；
F, weave: the temperature of weaving rooms is 26 DEG C, humidity 70%, speed 520r/min, back beam height 4cm, and angle is
75 °, upper beam of a loom warp tension be 668kg*g, lower beam of a loom warp tension be 297kg*g, single 30# water pump, two 90# sprinkler bodies, 2
A 40# nozzle, angle of water are 89 °, and water end of a period angle is 199 °, and water to waste selvage yarn angle is 228 °, yarn to waste selvage yarn angle
253 °, yarn and reed touching angle are 294 °, and comprehensive straight angle degree is 345 °.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
1. a kind of production technology of crepe jacquard gold and silver fabric, including warp thread processing and weaving, when weaving, the temperature of weaving rooms is
25-26 DEG C, humidity 65-70%, speed 520r/min, back beam height 4cm, angle is 75 °, and upper beam of a loom warp tension is
600-670kg*g, lower beam of a loom warp tension 250-300kg*g, single 30# water pump, two 90# sprinkler bodies, 2 40# nozzles, water outlet
Angle is 85-90 °, and water end of a period angle is 190-200 °, and the angle of water to waste selvage yarn is 220-230 °, the angle of yarn to waste selvage yarn
It is 240-255 °, yarn and reed touching angle are 280-295 °, and comprehensive straight angle degree is 345 °；
A kind of production technology of crepe jacquard gold and silver fabric, comprises the technical steps that, reeling-double twisting-section warping-gaits-temperature
Humid control-weaving, it is characterised in that:
A, reeling: using spooler, sets reeling deal 1.25-1.26kg, reeling duration 250 minutes, crimps tension 29-30CN
Carry out reeling；
B, double twisting: using two-for-one twister, sets ingot speed 12000r/min, adds 0.7*3, tension pearl, 360 ° of progress double twistings of cornerite；?
Cylinder silk shifting rod speed control winds tension control in 8-10CN in 9-10s；
C, section warping: setting swift speed 60m/min, beaming 40m/min match No. three tension caps, and the control of warping tension exists
12g, beaming tension are controlled in 1.8kg, by 288 * 24 progress warpings；
D, gait: comprehensive using 14, style is gaited；
E, Temperature and Humidity Control: temperature is controlled at 25-26 DEG C, and humid control is in 65-70%；
F, weave: speed sets 520r/min, back beam height 4cm, and 75 ° of angle, upper machine tension 260kg is weaved.
2. a kind of production technology of crepe jacquard gold and silver fabric according to claim 1, it is characterised in that: the reeling type
Number be SGD168 type spooler.
3. a kind of production technology of crepe jacquard gold and silver fabric according to claim 1, it is characterised in that: the double twisting type
Number be YB310G type two-for-one twister.