CN109350349A - A kind of heating pack and its preparation method and application - Google Patents
A kind of heating pack and its preparation method and application Download PDFInfo
- Publication number
- CN109350349A CN109350349A CN201811486241.6A CN201811486241A CN109350349A CN 109350349 A CN109350349 A CN 109350349A CN 201811486241 A CN201811486241 A CN 201811486241A CN 109350349 A CN109350349 A CN 109350349A
- Authority
- CN
- China
- Prior art keywords
- heating pack
- parts
- bag film
- heating
- bag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heating packs, including bag film and the fever material being placed in bag film；Bag film is microporous membrane bag, and oxygen permeability is 0.01-0.02ml (STP)/(m2·h·atm)；Material generate heat by weight, including 6-7 parts of iron powders, 1.5-2 parts of vermiculites, 0.45-1 parts of active carbons, 1-2 portions of salt, 7.5-9 parts of water.Invention additionally discloses the applications of the preparation method and heating pack of a kind of above-mentioned heating pack.Heating pack of the present invention can control fever duration and maximum temperature by the proportion for the material that generates heat and the air permeability of bag film, when it is applied to Moxibustion plaster, moxibustion effect can be improved, prevent from scalding.
Description
Technical field
The present invention relates to field of medical products, more particularly to a kind of heating pack and its preparation method and application.
Background technique
Heating pack due to its can self-heating, can be used for multiple fields, such as food heating, moxibustion product.For moxibustion,
It is the method for reaching treatment illness by thermal stimulus acupuncture point, moxibustion has as one of therapy most ancient inside Chinese medicine
Warming meridian, the regulation of qi and blood, activating microcirculation and removing stasis medicinal, resistance building function.Current moxibustion product is mainly Moxibustion plaster, Moxibustion plaster
In for generate heat part be heating pack, therefore, heating pack is the important component of Moxibustion plaster.
Heating pack in existing Moxibustion plaster, which has the drawback that, is unable to control fever duration, and adstante febre temperature fluctuation is larger,
And it is unable to control maximum temperature, so that moxibustion effect reduces when moxibustion, or even the case where scald.
Provided that a kind of heating pack that can overcome drawbacks described above, is one of current Moxibustion plaster urgent problem to be solved.
Summary of the invention
It is an object of the invention to solve the problems, such as it is above-mentioned at least one, a kind of heating pack and preparation method thereof is provided and is answered
With.
In order to solve the above technical problems, the present invention provides a kind of heating pack, including bag film and the hair being placed in bag film
Thermal material；Bag film is microporous membrane bag, and oxygen permeability is 0.01-0.02ml (STP)/(m2·h·atm)；Heat object
Expect by weight, including 6-7 parts of iron powders, 1.5-2 parts of vermiculites, 0.45-1 parts of active carbons, 1-2 portions of salt, 7.5-9 parts of water.
Wherein, material is generated heat by weight, including 6.3-6.8 parts of iron powders, 1.7-1.9 parts of vermiculites, 0.5-0.9 parts of activity
Charcoal, 1.2-1.8 portion salt, 8-8.9 parts of water.
Wherein, the oxygen permeability of bag film is 0.018ml (STP)/(m2Hatm), material is generated heat by weight
Meter, including 6.5 parts of iron powders, 1.8 parts of vermiculites, 0.6 part of active carbon, 1.5 portions of salt, 8.5 parts of water.
Wherein, the iron-content of iron powder is 98%-98.5%.
Wherein, heating pack is more than or equal to 50 DEG C of a length of 6h or more of adstante febre, and the maximum temperature of heating pack is 52-53
℃。
In order to solve the above technical problems, the present invention provides a kind of preparation method of above-mentioned heating pack, comprising the following steps: press
Proportion weighs vermiculite and active carbon, vermiculite and active carbon be it is powdered, weighed vermiculite and active carbon are put into blender
It stirs evenly, obtains dry powder；Yan Heshui is weighed according to the ratio, is sufficiently mixed, and salt water is obtained；It is intracorporal thin that dry powder is put into case
In film bag, salt water is uniformly sprinkled upon on dry powder, sealed film bag, so that dry powder sufficiently infiltrates, infiltrating time is 12h or more, is obtained
Wet feed；Iron powder is weighed according to the ratio, the wet feed of iron powder and acquisition is put into blender and is stirred evenly, and after mixing evenly, is sent out
Thermal material；Using racking machine and bag film to after mixing evenly iron powder and wet feed be packaged, heating pack is made.
Wherein, blender is three-dimensional mixer, revolving speed 16-18r/min, mixing time 14-15min.
Wherein, infiltrating time 14h.
In order to solve the above technical problems, the present invention provides a kind of application of heating pack in Moxibustion plaster.
The beneficial effects of the present invention are: being in contrast to the prior art, heating pack of the invention includes bag film and sets
Fever material in bag film, wherein bag film is microporous membrane bag, generates heat material by weight, including 6-7 parts of iron
Powder, 1.5-2 part vermiculite, 0.45-1 parts of active carbons, 1-2 portions of salt, 7.5-9 parts of water.Heating pack of the present invention passes through control bag film
The proportion and unique preparation process of Air permenbility and fever material, so that heating pack is more than or equal to 50 DEG C of a length of 6h of adstante febre
More than, and maximum temperature is 52-53 DEG C, 50 DEG C of temperature changing trends to maximum temperature again to 50 DEG C are flat after heating pack opens temperature
Slow, this temperature profile is applied in moxibustion, and moxibustion effect can be improved, prevent from scalding.
Specific embodiment
Embodiment 1
The present embodiment heating pack includes bag film and fever material, and fever material is placed in bag film, wherein bag film is
Microporous membrane bag.
In the present embodiment, the oxygen permeability of bag film is 0.018ml (STP)/(m2Hatm), fever material is pressed
Parts by weight meter, including 6.5 parts of iron powders, 1.8 parts of vermiculites, 0.6 part of active carbon, 1.5 portions of salt, 8.5 parts of water.Wherein, the iron content of iron powder
Amount is 98%.Wherein, STP (standard temperature and pressure) is normal temperature and normal pressure.
The preparation method of above-mentioned heating pack the following steps are included:
A. weigh vermiculite and active carbon according to the ratio, vermiculite and active carbon be it is powdered, by weighed vermiculite and active carbon
It is put into blender and stirs evenly, obtain dry powder.
Blender used is three-dimensional mixer, revolving speed 17r/min, mixing time 15min when mixing.
B. Yan Heshui is weighed according to the ratio, is sufficiently mixed, and salt water is obtained.
C. dry powder is put into the intracorporal bag film of case, salt water is uniformly sprinkled upon on dry powder, sealed film bag, so that dry powder fills
Sub-dip profit, obtains wet feed.
To save infiltrating time, while reaching effect of impregnation again, preferably infiltrating time is 14h.
D. iron powder is weighed according to the ratio, the wet feed of iron powder and acquisition is put into blender and is stirred evenly, and iron powder and wet feed stir
After mixing uniformly, fever material is obtained.
Blender used is three-dimensional mixer, revolving speed 18r/min, mixing time 15min when mixing.
E. using racking machine and bag film to after mixing evenly iron powder and wet feed be packaged, heating pack is made.
In the present embodiment, for iron powder under the action of salt water, heat can be generated by encountering air, and it is anti-that iron powder can be improved in active carbon
It answers, vermiculite has the function of that heat accumulation, microporous membrane can control Air permenbility.
To make the heating pack of the present embodiment controllable generate heat duration and heating temperature, there is following spy in preparation process
Point: the proportion of each reasonable composition；The Air permenbility of microporous membrane then reduces the ventilative of microporous membrane if thinking that heating pack temperature is low
Amount, heating pack in the preparation, can select the microporous membrane of different Air permenbilities according to the ratio of each ingredient, in other embodiments,
The ratio of each ingredient can also be adjusted according to microporous membrane；Immersion of the salt water to dry powder, impregnate 12 hours or more；The preparation work of innovation
Skill first prepares dry powder, prepares wet-milling again, then mixes wet-milling with iron powder, and the wet-milling that salt water sufficiently infiltrates and iron powder are sufficiently mixed
It closes, iron powder consistent heat generation can be made；Quickly packing prevents fever material to be exposed in air.Based on These characteristics, the present embodiment hair
Heat packet is more than or equal to 50 DEG C of a length of 6h or more of adstante febre, and maximum temperature is 52-53 DEG C, and heating pack opens after temperature 50 DEG C to highest
Temperature changing trend of the temperature again to 50 DEG C is more gentle, substantially rectilinear type, this temperature profile is applied in moxibustion, can be improved
Moxibustion effect prevents from scalding.
The heating pack of the present embodiment is for illustrating the effectiveness of this heating pack below by specific test in Moxibustion plaster.
Two kinds of Moxibustion plasters are selected, one is the Moxibustion plasters (test group) for using the present embodiment heating pack, and another kind is market
The Moxibustion plaster (control group) of upper purchase, the number of every kind of Moxibustion plaster are 10, detect heating-up time, the duration of Moxibustion plaster
(40 DEG C or more duration), temperature guarantee that the time, (duration of required temperature when treatment opened after temperature 50 DEG C to the highest temperature
Degree is again to 50 DEG C of time), maximum temperature, the numerical value of above-mentioned each detection is average value, meanwhile, guarantee the time in temperature
It is interior, predetermined time measuring temperature is spaced to obtain temperature trend Curve.Testing result is as shown in table 1.
The detection of 1 Moxibustion plaster temperature characterisitic of table
According to test result as can be seen that the heating-up time of test group is shorter than control group, temperature guarantees that the time is longer than control
Group, and temperature guarantees that the accounting of time in duration is higher than control group, maximum temperature is lower than control group, and temperature guarantees the time
Interior temperature trend Curve is substantially rectilinear, and above-mentioned temperature profile makes Moxibustion plaster moxibustion temperature equalization, time long, can fill
Curative effect is waved in distribution, and should not be burned.
Embodiment 2
The present embodiment heating pack includes bag film and fever material, and fever material is placed in bag film, wherein bag film is
Microporous membrane bag.
In the present embodiment, the oxygen permeability of bag film is 0.012ml (STP)/(m2Hatm), fever material is pressed
Parts by weight meter, including 6.3 parts of iron powders, 1.7 parts of vermiculites, 0.7 part of active carbon, 1.5 portions of salt, 8 parts of water.Wherein, the iron-content of iron powder
It is 98%.
The preparation method of above-mentioned heating pack the following steps are included:
A. weigh vermiculite and active carbon according to the ratio, vermiculite and active carbon be it is powdered, by weighed vermiculite and active carbon
It is put into blender and stirs evenly, obtain dry powder.
Blender used is three-dimensional mixer, revolving speed 18r/min, mixing time 14min when mixing.
B. Yan Heshui is weighed according to the ratio, is sufficiently mixed, and salt water is obtained.
C. dry powder is put into the intracorporal bag film of case, salt water is uniformly sprinkled upon on dry powder, sealed film bag, so that dry powder fills
Sub-dip profit, obtains wet feed.
To save infiltrating time, while reaching effect of impregnation again, infiltrating time 12h.
D. iron powder is weighed according to the ratio, and the wet feed of iron powder and acquisition is put into blender and is stirred evenly.
Blender used is three-dimensional mixer, revolving speed 18r/min, mixing time 14min when mixing.
E. using racking machine and bag film to after mixing evenly iron powder and wet feed be packaged, heating pack is made.
In the present embodiment, for iron powder under the action of salt water, heat can be generated by encountering air, and it is anti-that iron powder can be improved in active carbon
It answers, vermiculite has the function of that heat accumulation, microporous membrane can control Air permenbility.
To make the heating pack of the present embodiment controllable generate heat duration and heating temperature, there is following spy in preparation process
Point: the proportion of each reasonable composition；The Air permenbility of microporous membrane then reduces the ventilative of microporous membrane if thinking that heating pack temperature is low
Amount, heating pack in the preparation, can select the microporous membrane of different Air permenbilities according to the ratio of each ingredient, in other embodiments,
The ratio of each ingredient can also be adjusted according to microporous membrane；Immersion of the salt water to dry powder, impregnate 12 hours or more；The preparation work of innovation
Skill first prepares dry powder, prepares wet-milling again, then mixes wet-milling with iron powder, and the wet-milling that salt water sufficiently infiltrates and iron powder are sufficiently mixed
It closes, iron powder consistent heat generation can be made；Quickly packing prevents fever material to be exposed in air.Based on These characteristics, the present embodiment hair
Heat packet is more than or equal to 50 DEG C of a length of 6h or more of adstante febre, and maximum temperature is 52-53 DEG C, and heating pack opens after temperature 50 DEG C to highest
Temperature changing trend of the temperature again to 50 DEG C is more gentle, substantially rectilinear type, this temperature profile is applied in moxibustion, can be improved
Moxibustion effect prevents from scalding.
The heating pack of the present embodiment is for illustrating the effectiveness of this heating pack below by specific test in Moxibustion plaster.
Two kinds of Moxibustion plasters are selected, one is the Moxibustion plasters (test group) for using the present embodiment heating pack, and another kind is market
The Moxibustion plasters (control group) different from control group in embodiment 1 of upper purchase, the number of every kind of Moxibustion plaster are 10, detect moxibustion
Heating-up time of patch, duration (40 DEG C or more duration), temperature guarantee the time (when treatment required temperature it is lasting when
Between, that is, open after temperature 50 DEG C to maximum temperature again to 50 DEG C of time), maximum temperature, the numerical value of above-mentioned each detection is average
Value, meanwhile, guarantee in the time in temperature, is spaced predetermined time measuring temperature to obtain temperature trend Curve.Testing result
As shown in table 2.
The detection of 2 Moxibustion plaster temperature characterisitic of table
According to test result as can be seen that the heating-up time of test group is shorter than control group, temperature guarantees that the time is longer than control
Group, and temperature guarantees that the accounting of time in duration is higher than control group, maximum temperature is lower than control group, and temperature guarantees the time
Interior temperature trend Curve is substantially rectilinear, and above-mentioned temperature profile makes Moxibustion plaster moxibustion temperature equalization, time long, can fill
Curative effect is waved in distribution, and should not be burned.
The above, according to the test result of embodiment 1 and embodiment 2, it can be seen that the heating pack of two embodiments is logical
Toning is haircuted the proportion of thermal material and the air permeability of microporous membrane, can control fever duration and maximum temperature well.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (9)
1. a kind of heating pack, which is characterized in that including bag film and the fever material being placed in the bag film；
The bag film is microporous membrane bag, and oxygen permeability is 0.01-0.02ml (STP)/(m2·h·atm)；
The fever material by weight, including 6-7 parts of iron powders, 1.5-2 parts of vermiculites, 0.45-1 parts of active carbons, 1-2 portions of salt,
7.5-9 parts of water.
2. heating pack according to claim 1, which is characterized in that the fever material by weight, including 6.3-6.8
Part iron powder, 1.7-1.9 parts of vermiculites, 0.5-0.9 parts of active carbons, 1.2-1.8 portions of salt, 8-8.9 parts of water.
3. heating pack according to claim 1, which is characterized in that the oxygen permeability of the bag film is 0.018ml
(STP)/(m2Hatm), the fever material by weight, including 6.5 parts of iron powders, 1.8 parts of vermiculites, 0.6 part of activity
Charcoal, 1.5 portions of salt, 8.5 parts of water.
4. according to heating pack described in right 1-3 any one, which is characterized in that the iron-content of the iron powder is 98%-
98.5%.
5. heating pack according to claim 4, which is characterized in that the heating pack is a length of more than or equal to 50 DEG C of adstante febre
6h or more, and the maximum temperature of the heating pack is 52-53 DEG C.
6. the preparation method of heating pack described in claim 1-5 any one, which comprises the following steps:
Weigh vermiculite and active carbon according to the ratio, the vermiculite and active carbon be it is powdered, weighed vermiculite and active carbon are put
Enter in blender and stir evenly, obtains dry powder；
Yan Heshui is weighed according to the ratio, is sufficiently mixed, and salt water is obtained；
Dry powder is put into the intracorporal bag film of case, salt water is uniformly sprinkled upon on dry powder, sealed film bag, so that dry powder sufficiently soaks
Profit, infiltrating time are 12h or more, obtain wet feed；
Iron powder is weighed according to the ratio, and the wet feed of iron powder and acquisition is put into blender and is stirred evenly；
Using racking machine and bag film to after mixing evenly iron powder and wet feed be packaged, heating pack is made.
7. the preparation method of heating pack according to claim 6, which is characterized in that the blender is three-dimensional mixer,
Revolving speed is 16-18r/min, mixing time 14-15min.
8. the preparation method of heating pack according to claim 6, which is characterized in that infiltrating time 14h.
9. application of the heating pack in Moxibustion plaster described in claim 1-5 any one.