CN109337539A - Wear-resisting headpiece paint - Google Patents
Wear-resisting headpiece paint Download PDFInfo
- Publication number
- CN109337539A CN109337539A CN201811152745.4A CN201811152745A CN109337539A CN 109337539 A CN109337539 A CN 109337539A CN 201811152745 A CN201811152745 A CN 201811152745A CN 109337539 A CN109337539 A CN 109337539A
- Authority
- CN
- China
- Prior art keywords
- parts
- product
- headpiece
- paint
- wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of wear-resisting headpieces to paint, it is configured by following raw material, 1-2 parts of methyl ethyl ketone peroxide, 0.2-0.3 parts of polysiloxane-polyether copolymer, 5-10 parts of glass powder, 8-10 parts of Neon SiC powder, 10-15 parts of rutile titanium white powder, 0.2-0.4 parts of polymethylphenylsiloxane, 0.5-0.9 parts of glyceryl monostearate, 35-45 parts of dihydric alcohol, aqueous wax liquor 1-3 parts of polyethylene, 15-20 parts of styrene, 0.6-1 parts of cobalt naphthenate, 60-70 parts of butyl acetate, 25-30 parts of hydroxyl alkyd resin, 0.5-0.9 parts of hydroxyethyl cellulose, 5-7 parts of dimethylbenzene.The present invention has the advantages that headpiece can be maintained to have gloss for a long time.
Description
Technical field
The invention belongs to headpieces to paint field, and paint is related to a kind of wear-resisting headpiece paint.
Background technique
Headpiece is called bed mooring, is mounted to a rear portion, supplies the component of human body back-resting.Due to headpiece often by
Human body back friction, the paint on headpiece is easy to be worn, so that headpiece be made to be easy to tarnish.Existing paint is in the head of a bed
The paint layer formed on plate is softer, and paint layer is not wear-resisting, is used for headpiece, generally headpiece can only be maintained in first three used to five
Year has gloss, and headpiece cannot be maintained to have gloss for a long time.Therefore, existing paint, which exists, to maintain headpiece to have for a long time
Glossiness disadvantage.
Summary of the invention
The object of the present invention is to provide a kind of wear-resisting headpieces to paint.The present invention, which has, to maintain headpiece to have for a long time
Glossiness advantage.
Technical solution of the present invention: wear-resisting headpiece paint is configured, methyl ethyl ketone peroxide by following raw material
1-2 parts, 0.2-0.3 parts of polysiloxane-polyether copolymer, 5-10 parts of glass powder, 8-10 parts of Neon SiC powder, rutile titanium
10-15 parts of white powder, 0.2-0.4 parts of polymethylphenylsiloxane, 0.5-0.9 parts of glyceryl monostearate, 35-45 parts of dihydric alcohol,
Aqueous wax liquor 1-3 parts of polyethylene, 15-20 parts of styrene, 0.6-1 parts of cobalt naphthenate, 60-70 parts of butyl acetate, hydroxyl alkyd
25-30 parts of resin, 0.5-0.9 parts of hydroxyethyl cellulose, 5-7 parts of dimethylbenzene.
In wear-resisting headpiece paint above-mentioned, is configured, 1.5 parts of methyl ethyl ketone peroxide, gathered by following raw material
0.25 part of siloxane-polyether copolymer, 7.5 parts of glass powder, 9 parts of Neon SiC powder, 12.5 parts of rutile titanium white powder, poly- first
0.3 part of base phenyl siloxane, 0.7 part of glyceryl monostearate, 40 parts of dihydric alcohol, 2 parts of the aqueous wax liquor of polyethylene, styrene 17.5
Part, 0.8 part of cobalt naphthenate, 65 parts of butyl acetate, 27.5 parts of hydroxyl alkyd resin, 0.7 part of hydroxyethyl cellulose, dimethylbenzene 6
Part.
In wear-resisting headpiece paint above-mentioned, the configuration of paint includes the following steps,
A, by methyl ethyl ketone peroxide, polysiloxane-polyether copolymer, polymethylphenylsiloxane, glyceryl monostearate,
The aqueous wax liquor of dihydric alcohol, polyethylene, styrene, cobalt naphthenate, butyl acetate, hydroxyl alkyd resin, hydroxyethyl cellulose and
Dimethylbenzene is mixed and stirred for uniformly, obtaining A product,
B, A product are heated to 80-90 DEG C, keep the temperature 10-30min, obtains B product,
C, glass powder, Neon SiC powder and rutile titanium white powder are mixed and stirred for uniformly, obtaining C product,
D, C product are mixed with B product, obtain D product,
E, D product are stirred, 1500-2000 revs/min of mixing speed, mixing time 5-10min obtains finished product.
In wear-resisting headpiece paint above-mentioned, the step b is that A product are heated to 85 DEG C, keeps the temperature 20min, obtain B product.
In wear-resisting headpiece paint above-mentioned, the step e is stirring D product, 1750 revs/min of mixing speed, stirs
Time 7.5min, obtains finished product.
Compared with prior art, present invention improves over the techniques of the formula of paint and configuration, with glass powder, nanometer silicon carbide
Three kinds of substances of powder and rutile titanium white powder improve the hardness and wear resistance of paint layer, so that paint layer is not allowed as paint filler
It tarnishes vulnerable to human body back friction, while paint of the invention is easy levelling, paint is not easy bubble when brushing, shape
At paint layer surface gloss it is high.Paint of the invention is acted on headpiece, headpiece can be maintained in the first eight used
Kept glossy by 10 years.Therefore, the present invention has the advantages that headpiece can be maintained to have gloss for a long time.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment 1.Wear-resisting headpiece paint, is configured, 1.5 parts of methyl ethyl ketone peroxide by following raw material, is gathered
0.25 part of siloxane-polyether copolymer, 7.5 parts of glass powder, 9 parts of Neon SiC powder, 12.5 parts of rutile titanium white powder, poly- first
0.3 part of base phenyl siloxane, 0.7 part of glyceryl monostearate, 40 parts of dihydric alcohol, 2 parts of the aqueous wax liquor of polyethylene, styrene 17.5
Part, 0.8 part of cobalt naphthenate, 65 parts of butyl acetate, 27.5 parts of hydroxyl alkyd resin, 0.7 part of hydroxyethyl cellulose, dimethylbenzene 6
Part.
The configuration of paint includes the following steps,
A, by methyl ethyl ketone peroxide, polysiloxane-polyether copolymer, polymethylphenylsiloxane, glyceryl monostearate,
The aqueous wax liquor of dihydric alcohol, polyethylene, styrene, cobalt naphthenate, butyl acetate, hydroxyl alkyd resin, hydroxyethyl cellulose and
Dimethylbenzene is mixed and stirred for uniformly, obtaining A product,
B, A product are heated to 85 DEG C, keep the temperature 20min, obtains B product,
C, glass powder, Neon SiC powder and rutile titanium white powder are mixed and stirred for uniformly, obtaining C product,
D, C product are mixed with B product, obtain D product,
E, D product are stirred, 1750 revs/min of mixing speed, mixing time 7.5min obtains finished product.
Embodiment 2.Wear-resisting headpiece paint, is configured, 1 part of methyl ethyl ketone peroxide, poly- silicon by following raw material
Oxygen alkane -0.2 part of copolyether, 5 parts of glass powder, 8 parts of Neon SiC powder, 10 parts of rutile titanium white powder, polymethyl-benzene base
0.2 part of siloxanes, 0.5 part of glyceryl monostearate, 35 parts of dihydric alcohol, 1 part of the aqueous wax liquor of polyethylene, 15 parts of styrene, cycloalkanes
0.6 part of sour cobalt, 60 parts of butyl acetate, 25 parts of hydroxyl alkyd resin, 0.5 part of hydroxyethyl cellulose, 5 parts of dimethylbenzene.
The configuration of paint includes the following steps,
A, by methyl ethyl ketone peroxide, polysiloxane-polyether copolymer, polymethylphenylsiloxane, glyceryl monostearate,
The aqueous wax liquor of dihydric alcohol, polyethylene, styrene, cobalt naphthenate, butyl acetate, hydroxyl alkyd resin, hydroxyethyl cellulose and
Dimethylbenzene is mixed and stirred for uniformly, obtaining A product,
B, A product are heated to 80 DEG C, keep the temperature 10min, obtains B product,
C, glass powder, Neon SiC powder and rutile titanium white powder are mixed and stirred for uniformly, obtaining C product,
D, C product are mixed with B product, obtain D product,
E, D product are stirred, 1500 revs/min of mixing speed, mixing time 5min obtains finished product.
Embodiment 3.Wear-resisting headpiece paint, is configured, 2 parts of methyl ethyl ketone peroxide, poly- silicon by following raw material
Oxygen alkane -0.3 part of copolyether, 10 parts of glass powder, 10 parts of Neon SiC powder, 15 parts of rutile titanium white powder, polymethyl-benzene
0.4 part of radical siloxane, 0.9 part of glyceryl monostearate, 45 parts of dihydric alcohol, 3 parts of the aqueous wax liquor of polyethylene, 20 parts of styrene, ring
1 part of alkanoic acid cobalt, 70 parts of butyl acetate, 30 parts of hydroxyl alkyd resin, 0.9 part of hydroxyethyl cellulose, 7 parts of dimethylbenzene.
The configuration of paint includes the following steps,
A, by methyl ethyl ketone peroxide, polysiloxane-polyether copolymer, polymethylphenylsiloxane, glyceryl monostearate,
The aqueous wax liquor of dihydric alcohol, polyethylene, styrene, cobalt naphthenate, butyl acetate, hydroxyl alkyd resin, hydroxyethyl cellulose and
Dimethylbenzene is mixed and stirred for uniformly, obtaining A product,
B, A product are heated to 90 DEG C, keep the temperature 30min, obtains B product,
C, glass powder, Neon SiC powder and rutile titanium white powder are mixed and stirred for uniformly, obtaining C product,
D, C product are mixed with B product, obtain D product,
E, D product are stirred, 2000 revs/min of mixing speed, mixing time 10min obtains finished product.
Claims (5)
1. wear-resisting headpiece paint, it is characterised in that: configured, 1-2 parts of methyl ethyl ketone peroxide, gathered by following raw material
0.2-0.3 parts of siloxane-polyether copolymer, 5-10 parts of glass powder, 8-10 parts of Neon SiC powder, rutile titanium white powder 10-
15 parts, 0.2-0.4 parts of polymethylphenylsiloxane, 0.5-0.9 parts of glyceryl monostearate, 35-45 parts of dihydric alcohol, polyethylene water
1-3 parts of wax liquor of property, 15-20 parts of styrene, 0.6-1 parts of cobalt naphthenate, 60-70 parts of butyl acetate, hydroxyl alkyd resin 25-30
Part, 0.5-0.9 parts of hydroxyethyl cellulose, 5-7 parts of dimethylbenzene.
2. wear-resisting headpiece paint according to claim 1, it is characterised in that: it is configured by following raw material,
1.5 parts of methyl ethyl ketone peroxide, 0.25 part of polysiloxane-polyether copolymer, 7.5 parts of glass powder, 9 parts of Neon SiC powder, gold
12.5 parts of red stone titanium dioxide, 0.3 part of polymethylphenylsiloxane, 0.7 part of glyceryl monostearate, 40 parts of dihydric alcohol, polyethylene
2 parts of aqueous wax liquor, 17.5 parts of styrene, 0.8 part of cobalt naphthenate, 65 parts of butyl acetate, 27.5 parts of hydroxyl alkyd resin, hydroxyl second
0.7 part of base cellulose, 6 parts of dimethylbenzene.
3. wear-resisting headpiece paint according to claim 2, it is characterised in that: the configuration of paint includes the following steps,
A, by methyl ethyl ketone peroxide, polysiloxane-polyether copolymer, polymethylphenylsiloxane, glyceryl monostearate, binary
The aqueous wax liquor of alcohol, polyethylene, styrene, cobalt naphthenate, butyl acetate, hydroxyl alkyd resin, hydroxyethyl cellulose and diformazan
Benzene is mixed and stirred for uniformly, obtaining A product,
B, A product are heated to 80-90 DEG C, keep the temperature 10-30min, obtains B product,
C, glass powder, Neon SiC powder and rutile titanium white powder are mixed and stirred for uniformly, obtaining C product,
D, C product are mixed with B product, obtain D product,
E, D product are stirred, 1500-2000 revs/min of mixing speed, mixing time 5-10min obtains finished product.
4. wear-resisting headpiece paint according to claim 3, it is characterised in that: the step b is to be heated to A product
85 DEG C, 20min is kept the temperature, B product are obtained.
5. wear-resisting headpiece paint according to claim 3, it is characterised in that: the step e is stirring D product, stirring
1750 revs/min of speed, mixing time 7.5min obtains finished product.