CN109337159A - A kind of environmentally-friendly EPE pearl wool packaging material - Google Patents
A kind of environmentally-friendly EPE pearl wool packaging material Download PDFInfo
- Publication number
- CN109337159A CN109337159A CN201811025130.5A CN201811025130A CN109337159A CN 109337159 A CN109337159 A CN 109337159A CN 201811025130 A CN201811025130 A CN 201811025130A CN 109337159 A CN109337159 A CN 109337159A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmentally
- packaging material
- pearl wool
- epe pearl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmentally-friendly EPE pearl wool packaging materials, it is formulated by the raw material of following parts by weight: 100-120 parts of ldpe resin, 30-50 parts of foaming agent, 20-40 parts of carboxymethyl cellulose, 4-12 parts of butyl titanate, 2-6 parts of fatty alcohol polyoxyethylene ether, 4-6 parts of dispersing agent, 5-10 parts of antistatic agent.A kind of environmentally-friendly EPE pearl wool packaging material of the present invention has flame retardant property and rustless property, by being added to antistatic agent, packaging material be can be avoided in use and placement process, because friction generates electrostatic, to the difficulty that increases transport and use, it is unlikely to deform, many advantages, such as water absorption rate is low and long service life.
Description
Technical field
The present invention relates to a kind of environmentally-friendly EPE pearl wool packaging materials, belong to field of packaging material.
Background technique
EPE pearl wool foamed material is the novel environmental protection package of one kind, packing material.Its advantageous characteristic, increasingly by
People's understanding, therefore its use constantly will expand and innovate.Especially in terms of packing with other industrial cut stocks, it is than tradition
With material performance it is more preferable, cost is lower, and class is higher, beautiful and generous, better effect.In addition it is in agricultural and sideline product packing timber side
Its more aobvious wide world of face.But EPE pearl wool obtained usually has that antistatic effect is poor, poor fire in the prior art
And the problem that rustless property is poor, demand of the people to pearl cotton product are continuously increased, the required function that it has is also more next
More, traditional EPE pearl wool is unable to satisfy people to the needs of EPE packaging material.
Summary of the invention
The present invention is to solve the above problems, provide a kind of environmentally-friendly EPE pearl wool packaging material.
The purpose of the present invention is what is be achieved through the following technical solutions:
A kind of environmentally-friendly EPE pearl wool packaging material, it is formulated by the raw material of following parts by weight: low-density is poly-
100-120 parts of vinyl, 30-50 parts of foaming agent, 20-40 parts of carboxymethyl cellulose, 4-12 parts of butyl titanate, poly alkyl alcohol
2-6 parts of ethylene oxide ether, 4-6 parts of dispersing agent, 5-10 parts of antistatic agent.
A kind of above-mentioned environmentally-friendly EPE pearl wool packaging material is formulated according to parts by weight by following raw material: low-density
100 parts of polyvinyl resin, 30 parts of foaming agent, 20 parts of carboxymethyl cellulose, 4 parts of butyl titanate, fatty alcohol polyoxyethylene ether 2
Part, 4 parts of dispersing agent, 5 parts of antistatic agent.
A kind of above-mentioned environmentally-friendly EPE pearl wool packaging material is formulated according to parts by weight by following raw material: low-density
120 parts of polyvinyl resin, 50 parts of foaming agent, 40 parts of carboxymethyl cellulose, 12 parts of butyl titanate, fatty alcohol polyoxyethylene ether 6
Part, 6 parts of dispersing agent, 10 parts of antistatic agent.
A kind of above-mentioned environmentally-friendly EPE pearl wool packaging material is formulated according to parts by weight by following raw material: low-density
110 parts of polyvinyl resin, 40 parts of foaming agent, 30 parts of carboxymethyl cellulose, 8 parts of butyl titanate, fatty alcohol polyoxyethylene ether 4
Part, 5 parts of dispersing agent, 8 parts of antistatic agent.
Preferably, the foaming agent is azodicarbonamide.
Further, the dispersing agent is vinyl bis-stearamides.
Further, the antistatic agent is ethylene oxide and polyethylene glycol oxide.
The beneficial effects of the present invention are: a kind of environmentally-friendly EPE pearl wool packaging material of the present invention have flame retardant property and
Rustless property can be avoided packaging material in use and placement process, because friction generation is quiet by being added to antistatic agent
Electricity is unlikely to deform, many advantages, such as water absorption rate is low and long service life thus the difficulty for increasing transport and using.
Specific embodiment
Embodiment one
A kind of environmentally-friendly EPE pearl wool packaging material of the present invention is formulated according to parts by weight by following raw material:
100 parts of ldpe resin, 30 parts of foaming agent, 20 parts of carboxymethyl cellulose, 4 parts of butyl titanate, fatty alcohol polyoxy second
2 parts of alkene ether, 4 parts of dispersing agent, 5 parts of antistatic agent.
Preferably, the foaming agent is azodicarbonamide.
Further, the dispersing agent is vinyl bis-stearamides.
Further, the antistatic agent is ethylene oxide and polyethylene glycol oxide.
Embodiment 2
A kind of environmentally-friendly EPE pearl wool packaging material of the present invention is formulated according to parts by weight by following raw material:
120 parts of ldpe resin, 50 parts of foaming agent, 40 parts of carboxymethyl cellulose, 12 parts of butyl titanate, fatty alcohol polyoxy second
6 parts of alkene ether, 6 parts of dispersing agent, 10 parts of antistatic agent.
Preferably, the foaming agent is azodicarbonamide.
Further, the dispersing agent is vinyl bis-stearamides.
Further, the antistatic agent is ethylene oxide and polyethylene glycol oxide.
Embodiment 3
A kind of environmentally-friendly EPE pearl wool packaging material of the present invention is formulated according to parts by weight by following raw material:
110 parts of ldpe resin, 40 parts of foaming agent, 30 parts of carboxymethyl cellulose, 8 parts of butyl titanate, fatty alcohol polyoxy second
4 parts of alkene ether, 5 parts of dispersing agent, 8 parts of antistatic agent.
Preferably, the foaming agent is azodicarbonamide.
Further, the dispersing agent is vinyl bis-stearamides.
Further, the antistatic agent is ethylene oxide and polyethylene glycol oxide.
Claims (7)
1. a kind of environmentally-friendly EPE pearl wool packaging material, which is characterized in that it is formulated by the raw material of following parts by weight
: 100-120 parts of ldpe resin, 30-50 parts of foaming agent, 20-40 parts of carboxymethyl cellulose, butyl titanate 4-12
Part, 2-6 parts of fatty alcohol polyoxyethylene ether, 4-6 parts of dispersing agent, 5-10 parts of antistatic agent.
2. a kind of environmentally-friendly EPE pearl wool packaging material according to claim 1, which is characterized in that it is by following heavy
What the raw material of amount part was formulated: 100 parts of ldpe resin, 30 parts of foaming agent, 20 parts of carboxymethyl cellulose, metatitanic acid four
4 parts of butyl ester, 2 parts of fatty alcohol polyoxyethylene ether, 4 parts of dispersing agent, 5 parts of antistatic agent.
3. a kind of environmentally-friendly EPE pearl wool packaging material according to claim 1, which is characterized in that it is by following heavy
What the raw material of amount part was formulated: 120 parts of ldpe resin, 50 parts of foaming agent, 40 parts of carboxymethyl cellulose, metatitanic acid four
12 parts of butyl ester, 6 parts of fatty alcohol polyoxyethylene ether, 6 parts of dispersing agent, 10 parts of antistatic agent.
4. a kind of environmentally-friendly EPE pearl wool packaging material according to claim 1, which is characterized in that it is by following heavy
What the raw material of amount part was formulated: 110 parts of ldpe resin, 40 parts of foaming agent, 30 parts of carboxymethyl cellulose, metatitanic acid four
8 parts of butyl ester, 4 parts of fatty alcohol polyoxyethylene ether, 5 parts of dispersing agent, 8 parts of antistatic agent.
5. a kind of environmentally-friendly EPE pearl wool packaging material according to claim 1, which is characterized in that the foaming agent is
Azodicarbonamide.
6. a kind of environmentally-friendly EPE pearl wool packaging material according to claim 1, which is characterized in that the dispersing agent is
Vinyl bis-stearamides.
7. a kind of environmentally-friendly EPE pearl wool packaging material according to claim 1, which is characterized in that the antistatic agent
For ethylene oxide and polyethylene glycol oxide.