CN109336518A - A kind of glue for tile and its construction method - Google Patents
A kind of glue for tile and its construction method Download PDFInfo
- Publication number
- CN109336518A CN109336518A CN201811545480.4A CN201811545480A CN109336518A CN 109336518 A CN109336518 A CN 109336518A CN 201811545480 A CN201811545480 A CN 201811545480A CN 109336518 A CN109336518 A CN 109336518A
- Authority
- CN
- China
- Prior art keywords
- parts
- tile
- glue
- waterproof
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of glue for tile and its construction methods, including the following component prepared according to parts by weight: 300-500 parts of cement, 290-630 parts of washed-out sand, 50-100 parts of dicalcium powder, 15-35 parts of metakaolin, 0.2-0.8 parts of cellulose ether, 0.1-0.5 parts of starch ether, 0.3-3 parts of water-reducing agent, 1-3 parts of defoaming agent, 1-4 parts of hydrophober, 1-2 parts of PP fiber, 25-55 parts of pure acrylic acid latex powder.The glue for tile had not only had excellent waterproof performance, but also the performance with outstanding tile bonding, the glue for tile had not only met the current standard of Polymer cement materials but also met the current standard of glue for tile, and the construction of waterproof layer is completed while pasting ceramic tile.The construction method of glue for tile provided by the invention, it is convenient, simple, easily operated, cooperate 2-10 millimeters of glues for tile to apply scratch layers, that is, can reach excellent waterproof effect.
Description
Technical field
The present invention relates to the field of building materials, in particular to a kind of glue for tile and its construction method.
Background technique
For the technical level for improving Indoor Residential Ecological waterproofing work, it is ensured that the function and quality of Indoor Residential Ecological waterproof, house and town and country
The Ministry of Construction is in publication in 2013 " Indoor Residential Ecological waterproofing work technical specification ".Specification points out that Indoor Residential Ecological waterproofing work should be abided by
Follow anti-row combine, temper toughness with gentleness, adaptation to local conditions, economical rationality, safety and environmental protection, comprehensive treatment principle.Indoor Residential Ecological waterproofer
Cheng Yi is according to different positions of setting up defences, and by the sequence of flexible waterproof coating, waterproof roll, rigidity water-proofing material, it is suitable to select
Waterproof material, and should have compatibility between adjacent materials.
Waterproofing industry many years of experience shows that Indoor Residential Ecological water repellent area is small, and structure is complicated, is not suitable for using waterproof roll, by soft
Property the waterproof construction that collectively constitutes of waterproof layer and rigid waterproof layer there is most reliable waterproof effect, this is tempered toughness with gentleness in specification
The source of principle, this was determined by the characteristics of both materials.The advantages of flexible waterproof material, can be covered with retractility
Lid minute crack;The disadvantage is that flexible better, organic component content is higher, and organic component poor corrosion resistance, durable years is short, to base
Layer requires height, and plasticity is poor, is easy to leave weak spot and gap etc. in the construction process.Rigidity water-proofing material and flexible water material
Material has very high complementarity, and rigidity water-proofing material is based on inorganic material, and durability and weather resistance are excellent, corrosion resistant
Erosion, the thicker anti-pressure ability of thickness is strong, and plasticity is high, there is excellent application property in various environment.The disadvantage is that poor ductility, uncomfortable
Conjunction is constructed in unstable base.Present house, especially skyscraper, sound construction are stablized, and design grade is high, to live
The application of rigid waterproofing provides solid foundation in residence room.Rigidity water-proofing material is used for well-set Indoor Residential Ecological waterproof,
It with good waterproof effect, is applied together with flexible water, accomplishes to couple hardness with softness, to ensure that house in technical pattern
Indoor waterproof effect.
For resident when buying house, the waterproof of Indoor Residential Ecological completes construction according to design via developer.But in ornament
Original waterproof layer is often destroyed to the water power transformation of the positions such as toilet kitchen and balcony when house, therefore, present family
Finishing new house all can do again waterproof after water power transformation.Domestic household when doing indoor waterproof again, by cost (including material
Expect and artificial) factor, time (requiring the regular hour per more procedures) factor, professional knowledge deficiency factor, Gong Renshi
Work habit factor etc. influences, and only does one of waterproof.Selection rigidity water-proofing material or flexible waterproof material have, and predominantly apply
Expect based film waterproof layer.Regardless of selection is flexible or rigidity, all occur much occurring the case where leak after finishing waterproof.Mainly
Reason has, first is that construction reason, coating based film waterproof layer is than relatively thin, and only 1.5 millimeters or so, in addition plasticity is poor, waterproof layer
The thickness of leakage brush or brush is different, weak spot leak, or do not construct in strict accordance with specification, once construct it is too thick cause it is dry and cracked
Etc.;Second is that not doing protective layer after finishing waterproof, thickness is only that the film waterproof material of 1.5 millimeters thicks is destroyed by subsequent construction,
As the ready-made waterproof coating of accomodation ground is destroyed by subsequent patch block working procedure;Third is that material cause, the material of selection is resistance to
Aqueous energy is bad, soaked for a long time in the case where not accomplishing that anti-row combines that waterproof layer is caused to fail;Fourth is that base treatment is not
When.Flexible water is higher to basic level requirement, and moisture content is excessively high to will cause that flexible water film does not form a film or quality of forming film is low or de-
Layer plays drum;Rigid waterproofing coating requires height to the consolidation of base, will cause in the shaky situation such as screed-coat hollowing delamination just
Property waterproof coating by stress deformation cause cracking leak.Basic reason is not accomplish rigid flexible system, and flexible water and rigidity are anti-
The shortcomings that water, is broken.
In view of this, the present invention is specifically proposed.
Summary of the invention
The first object of the present invention is to provide a kind of glue for tile, cannot take into account waterproof performance and ceramic tile to solve existing glue for tile
The problem of bonding, the glue for tile realize that rigid waterproofing and tile paste are two-in-one, had not only saved material cost but also saved
Time cost is environmental protection and energy saving new product.It is a kind of current standard (JC/T984-2011) for both having met waterproof polymer mortar
Meet the new product of the current standard (JC/T547-2005) of glue for tile again.
The second object of the present invention is to provide the construction method of glue for tile described in one kind, which has simple, side
Just, the advantages that easily operated, and can guarantee using relatively thin glue for tile, that is, it can reach good waterproof effect.
In order to realize above-mentioned purpose of the invention, the following technical scheme is adopted:
A kind of glue for tile, including the following component prepared according to parts by weight:
300-500 parts of cement, 290-630 parts of washed-out sand, 50-100 parts of dicalcium powder, 15-35 parts of metakaolin, cellulose ether 0.2-
0.8 part, 0.1-0.5 parts of starch ether, 0.3-3 parts of water-reducing agent, 1-3 parts of defoaming agent, 1-4 parts of hydrophober, 1-2 parts of PP fiber, pure C
25-55 parts of olefin(e) acid latex powder.
Cementitious material of the cement as the glue for tile, relatively low volume advantageously reduce cement shrinkage amount.Washed-out sand can resist water
Mud contractile function is main stuffing, collectively forms mixed mortar, and the adjustable mixed mortar of pure acrylic acid latex powder is added
The main component of flexibility and waterproof, forms a film again in mortar voids, fills up the gap of mortar, reaches impervious effect.Hate
Aqua is a kind of waterproofing agent, reduces the uptake to water, can further enhance the waterproof performance of glue for tile.Higher territory is one
The artificial pozzolanic material of kind high activity, can be with Ca (OH)2(CH) and pozzolanic reaction occurs for water, generates the water similar with cement
Change product, reacts to form compact texture in hardening process.Cellulose ether is a kind of water-retaining agent, can guarantee the aquation of cement
Reaction sufficiently, adjusts the additional amount of cellulose ether, so as to adjust the compactness of mixed mortar, to guarantee the waterproofness of glue for tile
Energy.Defoaming agent is added to adjust the air bubble content in mortar, reduces air bubble content to further increase the compactness of mortar, improves
Waterproof performance.It is raw material that powdered whiting abbreviation coarse whiting, which is with good lime stone, is machined to white powder through lime milling
Body, its main component are CaCO3, calcium carbonate plays an important role in the glue for tile, can not only reduce production cost, may be used also
To increase the toughness and intensity of glue for tile.There is better compatibility between starch ether and other additives, it is common with cellulose ether
In building dry blend, higher thickening property can be assigned, stronger structural, sag resistance and ease for operation, to reinforce porcelain
The waterproof performance and application property of brick glue.Water-reducing agent is a kind of under conditions of maintaining concrete slump constant, can be reduced mix
The concrete admixture of water consumption.PP fiber has cracking resistance effect, can improve the impermeability of glue for tile.
The pure acrylic acid latex powder that the present invention uses, compared with traditional EVA redispersable latex powder, the water resistance of the latex powder
Can be more preferable, therefore the not only flexibility of adjustable mortar, the waterproof performance of glue for tile can also be improved.
Preferably, the glue for tile specifically includes the following component prepared according to parts by weight: 350-450 parts of cement, washing
294.2-622 parts of sand, 70-90 parts of dicalcium powder, 20-30 parts of metakaolin, 0.4-0.6 parts of cellulose ether, starch ether 0.2-0.4
Part, 0.5-1.5 parts of water-reducing agent, 1.5-2.5 parts of defoaming agent, 2-3 parts of hydrophober, 1.2-1.6 parts of PP fiber, pure acrylic acid latex powder
30-50 parts.
It preferably, further include following component in terms of weight fraction: 0.1-1 parts of early strength agent.
Early strength agent is a kind of additive for improving glue for tile early strength, to guarantee the early hardness and intensity of glue for tile, is improved
Construction efficiency.
Preferably, the cement is PO.42.5R cement.
PO.42.5R cement refers to ordinary portland cement, and 28 days intensity is greater than 42.5 megapascal, and it is early that R, which represents this kind of cement,
Strong cement, 7 days 3 days early stage intensity are greater than common P.O42.5 cement and are mentioned with guaranteeing the early hardness and intensity of glue for tile
High construction efficiency.
Preferably, the washed-out sand includes 50-80 mesh and 80-140 mesh gradation washed-out sand.
Using the washed-out sand of gradation, cement shrinkage function can be resisted and accomplish closely knit waterproof, the waterproof of glue for tile can be reinforced
Performance, while improving its anti-contracility energy and flex capability.Low cement mixing content, the proportion of high filler volume, anti-shrink ability are prominent
Out, it is not necessary that swelling agent is added.
The water-reducing agent is polycarboxylate water-reducer.
Polycarboxylic acid series high efficiency water reducing agent overcomes some drawbacks of conventional water reducing agents, with volume is low, function of slump protection is good, concrete is received
Shrinkage is low, adjustability is strong on molecular structure, high performance potentiality are big, outstanding advantages of not using formaldehyde in production process.
Preferably, the viscosity of the cellulose ether is 400-60000Pas.
Cellulose ether under the viscosity, existing good viscosity does not influence the compactness of mortar again, and makes jointly with starch ether
With higher thickening property, stronger structural, sag resistance and ease for operation can be assigned, to ensure that the waterproof of glue for tile
Performance and viscosity.
Preferably, the mesh number of the dicalcium powder is 300-400 mesh.
Dicalcium powder under the mesh number is used in mixed way with mortar, and particle is moderate, is played gradation densification, can be reduced cost, and
Increase the toughness and intensity of glue for tile.
Preferably, the hydrophober is organosilicon moisture repellent.
The waterproof performance of glue for tile can be improved in the use of organosilicon moisture repellent, this agent does not block the direct micropore of mortar, not shadow
Ring distributing for moisture between glue and ceramic tile, i.e., it is moisture-proof and ventilative.Prevent in ceramic tile it is damp and mouldy, the diseases such as black and fall off.
A kind of construction method of glue for tile, comprising the following steps:
First applied in base scrape a layer thickness 2-10 millimeters, the glue for tile in not no gap;Glue for tile is filled into entire porcelain again
The back side of brick, at it is intermediate it is high, around low taper, it is excessive with glue for tile then toward pasting in the base for the glue for tile for having applied one layer
Subject to out.
Currently, there are mainly two types of patch block techniques: one is traditional cement oil to carry on the back patch technique, i.e., toward the ceramic tile back side covered with cement oil
Afterwards toward pasting in base;Another kind is the tooth form scraper plate plaster application newly promoted, and this patch method is first to apply glue for tile toward base, then use
Tooth form scraper plate pulls into up patch block after strip.Both patch methods all have gap with the requirement of waterproof, it is easy to gap is generated, it can not
Guarantee forms continuous waterproof layer.The construction method of glue for tile provided by the invention, i.e. its construction technology are carried on the back in cement oil
It is improved on the basis of patch technique.Glue for tile provided by the invention cooperates this construction technology, protects in terms of material and technique two
Demonstrate,prove outstanding waterproof effect.
Glue for tile provided by the invention has excellent paste performance, plaster thickness patch.Stickup thickness is thick than relatively thin when plaster
Degree is only 2-10 millimeters.Consider that the position of out-of-flatness base protrusion can tie up stickup thickness when pasting ceramic tile, simultaneously to protect
Waterproof effect is demonstrate,proved, this, which integrates stickup and the glue for tile of rigid waterproofing, there will be excellent waterproof performance.It is provided by the invention
Glue for tile not only conforms with the requirements of Polymer cement materials, also to positions certain during practice of construction adhered layer
Relatively thin situation targetedly improves the thin layer waterproof performance of glue for tile, this glue for tile complies with standard the requirement of floating coat test specimen,
Waterproof performance is excellent, and thin layer waterproof ability is much higher than the product for only meeting mortar specimen, more meets actual use situation, has pole
High practicability.
When construction, the glue for tile overall thickness for guaranteeing that the glue for tile of base's precoating and the ceramic tile back side are coated is not less than 4 millimeters, to reduce
Influence of the construction factor to waterproof effect.
Influence Indoor Residential Ecological waterproof to realize there are three the objective factors coupled hardness with softness: cost factor, time factor, worker, which construct, to practise
Used factor.It allows the glue for tile for only pasting ceramic tile function to have the function of waterproof, without increasing material cost, is not necessarily to multi-processing
Sequence changes current construction habit without worker, realizes that rigid waterproofing and tile paste are two-in-one, viscous without how time-consuming
It has been completed at the same time the construction of rigid waterproof layer during tiling, has killed two birds with one stone.Guide resident's selection when doing coating waterproofing
Flexible waterproof material reuses the ceramic tile adhesive tiling for integrating rigid waterproofing and tile paste, to realize house
Indoor waterproof is coupled hardness with softness, double insurance, will be significantly reduced water leakage situation.
Compared with prior art, the invention has the benefit that
(1) glue for tile provided by the invention not only has waterproof and dampproof function, but also has the function of bonding ceramic tile, and two kinds of functions two are closed
One, it had not only saved cost but also had saved the time.
(2) glue for tile provided by the invention had not only met the current standard (JC/T984-2011) of waterproof polymer mortar but also had met
The current standard (JC/T547-2005) of glue for tile, waterproof performance is excellent, meets the coating specimens standard in 984-2011 standard,
I.e. the coating of 2 millimeters thicks can bear the hydraulic pressure not less than 0.4MPa, and thickness meets practical patch block construction requirement, have high reality
With value.
(3) construction method of glue for tile provided by the invention solves the problems, such as that traditional handicraft can not form continuous waterproof layer,
Construction of waterproof layer is completed while patch block, is saved waterproof material expense, construction cost and construction time, is conducive to reach and temper toughness with gentleness
Waterproof effect, it is convenient, simple, easily operated to have many advantages, such as, and under the construction method, it is only necessary to guarantee effective thickness 2-10
The glue for tile of millimeter can reach excellent waterproof effect.
(4) glue for tile provided by the invention and construction method are solved and following are actually asked from two aspects of material and construction
Topic: (1) common glue for tile is without water-proof function.(2) thinner thickness (2-10 millimeters) are pasted in patch block, water-proof function are taken into account, to porcelain
The waterproof performance requirement of brick glue is high, is only to meet mortar specimen (20 millimeters thick) standard not meeting actual demand, meets coating
Test specimen (2 millimeters thick) standard is able to satisfy actual requirement.(3) traditional handicraft not can guarantee to form continuous waterproof layer.The present invention from
The problem of physical presence, sets out, and proposes the present invention, realizes that stickup and two functions of waterproof are two-in-one, while saving material, people
Work and time, energy conservation and environmental protection have high practicability and practical value.
Specific embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will manage
Solution, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the invention.Specific item is not specified in embodiment
Part person carries out according to conventional conditions or manufacturer's recommended conditions.Reagents or instruments used without specified manufacturer, being can
With the conventional products obtained by commercially available purchase.
Embodiment 1
Glue for tile provided by the invention, including the following component prepared according to parts by weight:
500 parts of cement, 343.4 parts of washed-out sand, 100 parts of dicalcium powder, 25 parts of metakaolin, 0.2 part of cellulose ether, starch ether 0.1
Part, 0.3 part of water-reducing agent, 1 part of defoaming agent, 1 part of hydrophober, 1 part of PP fiber, 28 parts of pure acrylic acid latex powder.
Embodiment 2
Glue for tile provided by the invention, including the following component prepared according to parts by weight
400 parts of cement, 446.7 parts of washed-out sand, 50 parts of dicalcium powder, 35 parts of metakaolin, viscosity is the cellulose of 40000Pas
0.8 part of ether, 0.5 part of starch ether, 3 parts of water-reducing agent, 3 parts of defoaming agent, 4 parts of hydrophober, 2 parts of PP fiber, pure acrylic acid latex powder 55
Part.
Embodiment 3
Glue for tile provided by the invention, including the following component prepared according to parts by weight: 350 parts of PO.42.5R cement, 50-80
94.2 parts of mesh washed-out sand, 450 parts of 80-140 mesh washed-out sand, 400 50 parts of mesh dicalcium powders, 15 parts of metakaolin, viscosity 400Pa
0.5 part of the cellulose ether of s, 0.2 part of starch ether, 2 parts of defoaming agent, 2 parts of organosilicon moisture repellent, 1 part of PP fiber, pure C
35 parts of olefin(e) acid latex powder, 0.5 part of polycarboxylate water-reducer, 0.1 part of early strength agent.
The construction method of the glue for tile, comprising the following steps:
First applied in base a layer thickness 2 millimeters, the glue for tile in not no gap;Glue for tile is filled to the back of entire ceramic tile again
Face, at it is intermediate it is high, around low taper, then toward pasting in the base for the glue for tile for having applied one layer, glue for tile of being subject to overflows.
Embodiment 4
Glue for tile provided by the invention, including the following component prepared according to parts by weight: 450 parts of PO.42.5R cement, 50-80
172 parts of mesh washed-out sand, 200 parts of 80-140 mesh washed-out sand, 300 90 parts of mesh dicalcium powders, 30 parts of metakaolin, viscosity is
0.6 part of the cellulose ether of 60000Pas, 0.4 part of starch ether, 2.5 parts of defoaming agent, 2.5 parts of organosilicon moisture repellent, pure acrylic acid
50 parts of latex powder, 1.5 parts of polycarboxylate water-reducer, 0.5 part of early strength agent.
The construction method of the glue for tile, comprising the following steps:
First applied in base a layer thickness 10 millimeters, the glue for tile in not no gap;Glue for tile is filled into entire ceramic tile again
The back side, at it is intermediate it is high, around low taper then toward pasting in the base for the glue for tile for having applied one layer be with glue for tile spilling
It is quasi-.
The test of 1 waterproof performance of experimental example
Glue for tile provided by embodiment 1-4 is prevented according to the current standard (JC/T984-2011) of waterproof polymer mortar
Water Performance Evaluation, and compared with traditional glue for tile.Wherein, the current standard (JC/T984- of waterproof polymer mortar
2011) as shown in table 1, experimental result is as shown in table 2.
The current standard (JC/T984-2011- coating specimens-I type) of 1 waterproof polymer mortar of table
2 embodiment 1-4 waterproof performance test result of table
Testing result shows that glue for tile provided by embodiment 1-4 respectively detects individual event and meets the existing of waterproof polymer mortar
Standard (JC/T984-2011), and traditional glue for tile and the performance for not having waterproof, also without the requirement of this respect, it was demonstrated that glue tool
There is good waterproof performance, can be used as waterproof material use.
The current standard of 2 glue for tile of experimental example detects (JC/T547-2005)
(JC/T547-2005) is detected to every gluing of glue for tile provided by embodiment 1-4 according to the current standard of glue for tile
Intensity is assessed, and is compared with traditional glue for tile.Wherein, current standard (JC/T547-2005) such as table of glue for tile
Shown in 3, experimental result is as shown in table 4.
The current standard of 3 glue for tile of table detects C1 type (JC/T547-2005)
Glue for tile provided by 4 embodiment 1-4 of table respectively stretches gluing detected intensities
Testing result shows that glue for tile provided by embodiment 1-4 respectively stretches gluing intensity detection single index and is all larger than 0.5,
Meet current standard (JC/T547-2005) the C1 type requirement of glue for tile, it was demonstrated that there is good stretching in the glue for tile each stage
Gluing intensity is a kind of glue for tile that adhesion strength is fabulous.And the ceramic tile just also has good waterproof performance, is a kind of simultaneous
Care for the glue for tile of waterproof performance and adhesion strength.The glue for tile not only has waterproof and dampproof function, but also has the function of bonding ceramic tile,
Not only it had saved material cost but also had saved time cost, and be environmental protection and energy saving new product.
In conclusion glue for tile provided by the invention, traditional EVA latex powder is substituted using pure acrylic acid latex powder, and tie
Other adding ingredients are closed, waterproof performance and gluing performance are taken into account, are a kind of current standard (JC/ for meeting waterproof polymer mortar
T984-2011 water-proof building material) has certain waterproof ability;And meet the current standard (JC/ of glue for tile again
T547-2005 gluing product) is a kind of glue for tile that adhesion strength is fabulous,.The glue for tile be one kind take into account waterproof performance and
The glue for tile of adhesive property.The glue for tile not only has waterproof and dampproof function, but also has the function of bonding ceramic tile, both saves material
Cost saves time cost again, is the new product of environmental protection and energy saving.The construction method of glue for tile provided by the invention, the construction party
Method have many advantages, such as it is simple, conveniently, it is easily operated, solve the problems, such as that traditional handicraft can not form continuous waterproof layer, in patch block
While complete construction of waterproof layer, save waterproof material expense, construction cost and construction time, be conducive to reach temper toughness with gentleness it is anti-
Water effect, it is convenient, simple, easily operated to have many advantages, such as, and under the construction method, it is only necessary to guarantee 2-10 millimeters of effective thickness
Glue for tile can reach excellent waterproof effect.
Although illustrate and describing the present invention with specific embodiment, it will be appreciated that without departing substantially from spirit of the invention
With many other change and modification can be made in the case where range.It is, therefore, intended that including in the following claims
Belong to all such changes and modifications in the scope of the invention.
Claims (10)
1. a kind of glue for tile, which is characterized in that including the following component prepared according to parts by weight: 300-500 parts of cement, washing
290-630 parts of sand, 50-100 parts of dicalcium powder, 15-35 parts of metakaolin, 0.2-0.8 parts of cellulose ether, 0.1-0.5 parts of starch ether,
0.3-3 parts of water-reducing agent, 1-3 parts of defoaming agent, 1-4 parts of hydrophober, 1-2 parts of PP fiber, 25-55 parts of pure acrylic acid latex powder.
2. glue for tile according to claim 1, which is characterized in that specifically include prepare according to parts by weight such as the following group
Point: 350-450 parts of cement, 294.2-622 parts of washed-out sand, 70-90 parts of dicalcium powder, 20-30 parts of metakaolin, cellulose ether 0.4-
0.6 part, 0.2-0.4 parts of starch ether, 0.5-1.5 parts of water-reducing agent, 1.5-2.5 parts of defoaming agent, 2-3 parts of hydrophober, PP fiber 1.2-
1.6 parts, 30-50 parts of pure acrylic acid latex powder.
3. glue for tile according to claim 1 or 2, which is characterized in that further include following component in terms of weight fraction: early
Strong 0.1-1 parts of agent.
4. glue for tile according to claim 1 or 2, which is characterized in that the cement is PO.42.5R cement.
5. glue for tile according to claim 1, which is characterized in that the washed-out sand includes 50-80 mesh and 80-140 mesh grade
With washed-out sand.
6. glue for tile according to claim 1 or 2, which is characterized in that the water-reducing agent is polycarboxylate water-reducer.
7. glue for tile according to claim 1 or 2, which is characterized in that the viscosity of the cellulose ether is 400-
60000Pa·s。
8. glue for tile according to claim 1 or 2, which is characterized in that the mesh number of the dicalcium powder is 300-400 mesh.
9. glue for tile according to claim 1 or 2, which is characterized in that the hydrophober is organosilicon moisture repellent.
10. a kind of construction method of -9 described in any item glues for tile according to claim 1, which is characterized in that including following step
It is rapid: first applied in base scrape a layer thickness 2-10 millimeters, the glue for tile in not no gap;Glue for tile is filled into entire ceramic tile again
The back side, at it is intermediate it is high, around low taper overflowed with glue for tile then toward pasting in the base for the glue for tile for having applied one layer
Subject to.