CN109336466A - A kind of compound quartz stone table top and preparation method thereof - Google Patents
A kind of compound quartz stone table top and preparation method thereof Download PDFInfo
- Publication number
- CN109336466A CN109336466A CN201811166738.XA CN201811166738A CN109336466A CN 109336466 A CN109336466 A CN 109336466A CN 201811166738 A CN201811166738 A CN 201811166738A CN 109336466 A CN109336466 A CN 109336466A
- Authority
- CN
- China
- Prior art keywords
- quartz
- table top
- stone table
- wet feed
- outer mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods of compound quartz stone table top, comprising: production outer mold, the outer mold are equipped with packing area；Quartz wet feed is filled in packing area, a cloth is completed；Lightweight panels are fixed on quartz wet feed；Quartz wet feed is filled in the gap between lightweight panels and outer mold, the lower surface of quartz wet feed and lightweight panels and side is completely attached to, completes secondary material distributing；Quartz wet feed, lightweight panels and outer mold are pressed, baking and curing is then carried out；After completing solidification, outer mold is removed, forms quartzy stone table board first product；Quartzy stone table board first product progress bridge is cut, is polished, compound quartz stone table top finished product is formed.Correspondingly, the invention also discloses a kind of compound quartz stone table tops.Using the present invention, quartzy stone table board is light-weight, convenient transportation, at low cost, in addition, present invention quartz stone table board one-pass molding does not influence the beauty of quartzy stone table board there is no gap is pasted.
Description
Technical field
The present invention relates to quartz technical fields more particularly to a kind of compound quartz stone table top and preparation method thereof.
Background technique
Quartzy stone table board refers to the table top being made into quartz, is mostly made using cullet and quartz sand.Quartzy stone table board
The advantages of be it is wear-resisting be not afraid of scratch, it is heat-resisting well can large area floor file, patch wall, splice it is seamless, it is durable.
The specific production process of quartzy stone table board includes: first to crush the natural siliceous sand of high-quality, next is purified
(process eliminates metal impurities, and avoiding product has radioactivity), mixes using raw material, under vacuum conditions will be quartzy
Large-sized plates material is made by isomerization polymerization technology in the materials such as stone crystal (90%-94%), resin (6%) and micro pigment, so
Rear surface carries out 30 multiple working procedure polishing grindings.
The quartzy stone table board that conventional method is made is a smooth table top, surface smooth and beautiful appearance, but bottom surface is coarse, face
Color is gloomy.In order to save cost, quartzy stone table board polishing grinding surface, bottom surface is green state.In order to save cost, simultaneously
Make quartzy stone table board beautiful again, existing method is to paste blend stop at the edge of table top, and people is avoided to be immediately seen the bottom of table top
Portion.
During existing quartzy stone countertops are made, the quartzy stone table board first product after passing a bridge and cutting polishing will also be again
Bridge cuts out corresponding size, then carries out pasting thickening side, the existing warp for thickening side barbola work and mainly relying on technical staff
It tests to carry out, individual difference is big, is easy to will appear apparent cutter trade, influences the beauty of table top.
In addition, existing 93% or more stone table board of quartz is made of quartz crystals body, quality is hard, close, has it
Characteristics, the coloury combination such as incomparable wear-resisting, the pressure-resistant, high temperature resistant of his ornament materials, anticorrosive, impermeable make its tool
There are the texture and beautiful lustrous surface of lithotome, while also having the weight of lithotome, is not easy to carry.
Summary of the invention
Technical problem to be solved by the present invention lies in, a kind of compound quartz stone table top is provided, light-weight, convenient transportation,
It is at low cost.
Technical problem to be solved by the present invention lies in provide a kind of compound quartz stone table top, hardness is high, toughness is strong, just
In secondary operation.
Technical problem to be solved by the present invention lies in provide a kind of production method of compound quartz stone table top, quartz
Table top one-pass molding does not influence the beauty of quartzy stone table board there is no gap is pasted.
Technical problem to be solved by the present invention lies in provide a kind of production method of compound quartz stone table top, operation letter
It is single, at low cost.
In order to solve the above-mentioned technical problems, the present invention provides a kind of production methods of compound quartz stone table top, comprising:
Outer mold is made, the outer mold is equipped with packing area；
Quartz wet feed is filled in packing area, a cloth is completed；
Lightweight panels are fixed on quartz wet feed；
Quartz wet feed is filled in the gap between lightweight panels and outer mold, quartz wet feed and lightweight panels are made
Lower surface and side completely attach to, complete secondary material distributing；
Quartz wet feed, lightweight panels and outer mold are pressed, baking and curing is then carried out；
After completing solidification, outer mold is removed, forms quartzy stone table board first product；
Quartzy stone table board first product progress bridge is cut, is polished, compound quartz stone table top finished product is formed.
As an improvement of the above scheme, the outer mold includes bottom plate plate and the side plate that is arranged on bottom plate, the side plate
The packing area is surrounded with the bottom plate.
As an improvement of the above scheme, the outer mold further includes the baffle for reinforcing side plate, and the baffle plate setting exists
The surrounding of the side plate.
As an improvement of the above scheme, the vibration frequency of the compression moulding is 38-43Hz, time of vibration 80-100s.
As an improvement of the above scheme, the compression moulding carries out vacuumize process, and the time vacuumized is 30-
200s。
As an improvement of the above scheme, the lightweight panels are made of light material.
As an improvement of the above scheme, the light material is PP, PVC, PC or fiber.
As an improvement of the above scheme, the formula of the quartz wet feed by weight percentage is as follows:
Aggregate 85-95%
Resin 5-15%；
The aggregate includes quartz sand and silica flour；
The resin is unsaturated polyester resin.
As an improvement of the above scheme, the quartz wet feed further include:
Curing agent 0.01-1%
Coupling agent 0.01-1%
Colorant 0.1-2%；
The curing agent is intermediate temperature curing agent, and the solidification temperature is 80-95 DEG C；
The coupling agent is organo silane coupling agent.
Correspondingly, the present invention also provides a kind of compound quartz stone table tops, and the compound quartz stone table top is using above-mentioned multiple
The production method for closing quartzy stone table board is made,
Comprising: table-board body and lightweight panels；
The table-board body includes panel and the blend stop that is arranged in face plate edge；
The lightweight panels are arranged on panel, and the blend stop blocks lightweight panels.
The invention has the following beneficial effects:
1, lightweight panels are fixed on quartz wet feed by the production method of a kind of compound quartz stone table top provided by the invention
In, it is then pressed, baking and curing, so that lightweight panels and quartz wet feed are overall structure, using lightweight panels
Increase the integral thickness of table top, mitigate the weight of table top, so that table top transport is more convenient, while reducing quartz wet feed
Dosage, reduce production cost.
2, the production method of a kind of compound quartz stone table top provided by the invention passes through matching for lightweight panels and outer mold
It closes, quartz wet feed is shaped into required shape, so that the panel and blend stop of quartzy stone table board are integrally formed, system of the invention
It is simple, easily operated to make method, the resulting quartzy stone table board one-pass molding of present invention production, do not need by way of bonding come
The edge of table top is thickeied, so that quartzy stone table board is more beautiful, secured.
3, a kind of compound quartz stone table top provided by the invention, including table-board body and lightweight panels, the table-board body
Including panel and the blend stop being arranged in face plate edge, the lightweight panels are arranged on panel, and the blend stop is by lightweight face
Plate blocks.The present invention by by lightweight panels be fixed on panel come and increase the thickness of table top, while will be light by blend stop
Matter panel mask is lived, and not only ensure that the beauty of table top, but also alleviates the weight of table top, is transported convenient for table top, can also be reduced stone
The dosage of diamond stone raw material reduces the cost of table top, achievees the effect that environmental protection and energy saving.
Detailed description of the invention
Fig. 1 is the production flow diagram of compound quartz stone table top of the present invention；
Fig. 2 is the structural schematic diagram of outer mold of the present invention；
Fig. 3 is the schematic diagram that lightweight panels of the present invention are placed on outer mold；
Fig. 4 is the structural schematic diagram of compound quartz stone table top of the present invention；
Fig. 5 is the schematic perspective view of table-board body of the present invention；
Fig. 6 is the schematic perspective view of another embodiment of table-board body of the present invention.
Specific embodiment
To make the object, technical solutions and advantages of the present invention clearer, the present invention is made into one below in conjunction with attached drawing
Step ground detailed description.
It is the production flow diagram of compound quartz stone table top of the present invention, a kind of quartz provided by the invention referring to Fig. 1, Fig. 1
The production method of table top, comprising the following steps:
S101, production outer mold, the outer mold are equipped with packing area.
Referring to fig. 2, the outer mold 1 includes bottom plate 11 and the side plate 12 being arranged on bottom plate 11, the side plate 12 and institute
It states panel 12 and surrounds packing area 13.
Specifically, the bottom plate 11 is made of aluminium sheet, the side plate 12 is made of iron bar, by iron by the way of welding
Item is fixed on bottom plate 11, to form the packing area 13.
Since the stress intensity of bottom plate 11 is lower, in order to mitigate the overall weight of outer mold 1, convenient for subsequent by outer mold 1
Curing oven is put into quartz wet feed, therefore the present invention preferentially selects the aluminium sheet of lighter in weight as bottom plate 11.And side plate 12 needs
Quartz wet feed is fixed in packing area 13, it is subsequent to be also pressed, it can thus be appreciated that the stress intensity of side plate 12
It is larger, therefore iron bar is fixed on bottom plate as side plate 12, and by the way of welding using the biggish iron bar of intensity by the present invention
On 11, thus guarantees the integral strength of outer mold 1, prevent outer mold 1 from deforming, and then guarantee the beauty of quartzy stone table board
It sees.
The side plate 12 includes the first side plate 121 and the second side plate 122, and the length of first side plate 121 is greater than second
The length of side plate 122.Wherein two piece of first side plate 121 is arranged in parallel between two blocks of second parallel side plates 122, to be formed
State packing area 13.
In the other embodiments of the application, the bottom plate 11 can also be by stainless steel plate, iron plate or other sheet metals
It is made.The side plate 12 can also be made of stainless steel plate, aluminium alloy plate or other sheet metals.
Preferably, the outer mold 1 further includes the baffle 13 for reinforcing side plate 12, and the baffle 13 is arranged in the side
The surrounding of plate 12.The baffle 13 is applied not only to reinforce side plate 12, is also used to fill up the gap between side plate 12 and bottom plate 11, prevents
Only quartz wet feed leaks out, and avoids quartz mesa edge rough, influences beauty.
Specifically, the baffle 13 includes first baffle 131 and second baffle 132, the first baffle 131 setting is the
The outside of the second side plate 122 is arranged in the outside of side plate 121, the second baffle 132.Preferably, two pieces parallel second
Baffle 132 is arranged between two pieces of parallel first baffles 121.Since the length of the second side plate 122 is less than the first side plate 121
Length, therefore the stress intensity of the second side plate 122 is greater than the first side plate 121 and avoids to guarantee the integral strength of outer mold 1
1 unbalance stress of outer mold deforms, and the thickness of the second baffle 132 is greater than the thickness of first baffle 121.In addition, this hair
By shifting to install connection between bright the first side plate 121, the second side plate 122, first baffle 131 and second baffle 132, into one
Step ensure that the integral strength of outer mold 1.
S102, quartz wet feed is filled in packing area, completes a cloth.
Specifically, outer mold is moved to below blender, the quartz wet feed being stirred is filled in packing area, and
Quartz wet feed is shakeout, first time cloth is carried out.
In the other embodiments of the application, can also by the way that manually quartz wet feed is paved in packing area, certainly,
The present invention can also carry out cloth by other means, it is needed to achieve the purpose that pave raw material.
The formula of the quartz wet feed is following (by weight percentage):
Aggregate 85-95%
Resin 5-15%；
The aggregate includes quartz sand and silica flour；
The resin is unsaturated polyester resin.
Preferably, the formula of the quartz wet feed is following (by weight percentage):
Aggregate 88-92%
Resin 8-12%.
More preferably, the formula of the quartz wet feed is following (by weight percentage):
Aggregate 90%
Resin 10%.
The preparation method of the quartz wet feed, comprising: the aggregate stirring 1-10min is first added, then described in addition
Resin agitating 5-20min.More preferably, the aggregate stirring 1-2min is first added, the resin agitating 3-5min is then added.
It should be noted that the mixing time of the aggregate and resin can be decided according to the actual requirements, such as additional amount
Number, embodiments thereof are not limited to illustrated embodiment of the present invention.
Further, the present invention also needs that curing agent, coupling agent and colorant is added, and is formulated as follows:
Curing agent 0.01-1%
Coupling agent 0.01-1%
Colorant 0.1-2%；
Preferably, the formula of the curing agent, coupling agent and colorant are as follows:
Curing agent 0.01-0.1%
Coupling agent 0.01-0.1%
Colorant 0.1-0.5%；
Wherein, the curing agent is preferably intermediate temperature curing agent, and the solidification temperature is 80-95 DEG C.Specifically, the solidification
Agent can select OT curing agent, but not limited to this.
Using intermediate temperature curing agent, the curing rate of raw material is mitigated compared with normal temperature cure, and solidification is abundant.Also, due to the present invention
Using intermediate temperature setting system, equipment is easy to clean at normal temperature, and in operation if there is unexpected shut-down, it is existing not will cause solidification
As.
In conjunction with raw material and production technology of the invention, the solidification temperature of the curing agent is most preferably set as 90 DEG C, herein
Under the conditions of temperature, the solidification of raw material is the most abundant, and the internal stress inside product is small, and performance can achieve maximum performance.
The coupling agent is preferably organo silane coupling agent, and more preferably, the coupling agent is Silane coupling reagent KH-570.
The chemical name of Silane coupling reagent KH-570: γ-methacryloxypropyl trimethoxy silane, chemistry knot
Structure formula: CH3CCH2COO(CH2)3Si(OCH3)3.Silane coupling reagent KH-570 is a kind of object with two heterogeneity functional groups
Matter, a part of functional group in their molecules can be with the suctions of mineral surfaces with reactive organic molecule, another part functional group
Attached water reaction forms firm bonding.The effect of coupling agent in the composite is that it can be with certain of reinforcing material surface
A little group reactions, and can be reacted with matrix resin, a boundary layer, boundary layer energy are formed between reinforcing material and resin matrix
Stress is transmitted, to enhance adhesive strength between reinforcing material and resin, improves the performance of composite material, while can be with
It prevents from improving interface state to contacting permeation not with other media, being conducive to the ageing-resistant of product, proof stress and electrical insulating property
Energy.
The present invention uses coupling agent kh-570, and adhesive strength between aggregate and resin can be enhanced, improve composite material
Performance, improve interface state, quartz high mechanical strength obtained is unlikely to deform, is non-aging.
S103, lightweight panels are fixed on quartz wet feed.
Referring to Fig. 3, lightweight panels 2 are placed on quartz wet feed, make the axle center of lightweight panels 1 and the axis of packing area 13
The heart is consistent.In order to mitigate the overall weight of table top, the lightweight panels are made of light material.The light material be PP,
PVC, PC or fiber, but not limited to this.Wherein, the size and shape of lightweight panels and the size and shape of table top match.It is described
Lightweight panels include upper surface, lower surface and side, wherein lower surface is the contact surface contacted with quartz wet feed with side.
The present invention can be by the way that the side of lightweight panels to be tightly attached on the side of outer mold, so that quartzy stone table board finished product
Side lack edge, it is possible thereby to which the quartzy stone table board for lacking edge with size with other is spliced, to form area
The more quartzy stone table board of bigger, type.
S104, quartz wet feed is filled in the gap between lightweight panels and outer mold, makes quartz wet feed and connects
Contacting surface completely attaches to, and completes secondary material distributing.
The cloth process can be paved raw material using material distributing machine, can also be by manually paving raw material in plate
On, certainly, the present invention can also carry out cloth by other means, it is needed to achieve the purpose that pave raw material.
Specifically, the quartz wet feed being filled in the gap between lightweight panels and outer mold is in compression moulding, drying
After solidification, become the blend stop of quartzy stone table board, for blocking lightweight panels, keep table top more beautiful, and is located at lightweight panels
The quartz wet feed of lower section becomes the panel of quartzy stone table board after baking and curing, wherein uses production method system of the invention
Quartz stone table board made of work, blend stop are integrally formed with panel.
S105, quartz wet feed, lightweight panels and outer mold are pressed, then carry out baking and curing.
The present invention suppresses quartz wet feed, lightweight panels and outer mold three together, so that quartz wet feed is flat
It is whole compact, meanwhile, lightweight panels are enclosed in quartz wet feed after compression moulding, it is integrally formed with quartz wet feed,
To ensure that the integral strength of quartzy stone table board.
The compression moulding passes through quartz wet feed, lightweight panels and outer mold the propulsion press that will complete secondary material distributing,
Quartz wet feed vibration moulding in press, wherein the vibration frequency is preferably 38-43Hz, and time of vibration is preferably 80-
100s。
Further, vacuumize process is also carried out in compression moulding, the time vacuumized is 30-200s.Preferably, it takes out
The time of vacuum is 60-120s.
After completing compression moulding, quartz wet feed, lightweight panels and outer mold are put into and carry out baking and curing in curing oven.
The process conditions of the baking and curing can be set to but be not limited to: 90-100 DEG C of drying temperature, drying time 1-1.5h.
S106, after completing solidification, outer mold is removed, forms quartzy stone table board first product.
S107, quartzy stone table board first product progress bridge is cut, is polished, forming compound quartz stone table top finished product.
Lightweight panels are fixed in quartz wet feed by the present invention, are then pressed, baking and curing, so that lightweight
Panel and quartz wet feed are overall structure, increase the integral thickness of table top using lightweight panels, mitigate the weight of table top, make
It is more convenient to obtain table top transport, while reducing the dosage of quartz wet feed, reduces production cost,
In addition, the present invention passes through the cooperation of lightweight panels and outer mold, quartz wet feed is shaped into required shape, is made
The panel and blend stop for obtaining quartzy stone table board are integrally formed, and production method of the invention is simple, easily operated, and the present invention makes gained
Quartzy stone table board one-pass molding, the edge that table top is thickeied by way of bonding is not needed, so that quartzy stone table board is more
It is beautiful, secured.
Below the present invention will be illustrated with specific embodiment
Referring to fig. 4 and Fig. 5, the present invention also provides a kind of compound quartz stone table top, the compound quartz stone table top is used
The production method of above-mentioned compound quartz stone table top is made comprising: table-board body 3 and lightweight panels 2, the table-board body 3 are wrapped
The blend stop 32 for including panel 31 and being arranged on 31 edge of panel, the lightweight panels 2 are arranged on panel 31, the blend stop 32
The lightweight panels 2 are blocked.
The present invention by by lightweight panels 2 be fixed on panel 31 come and increase the integral thickness of table top, while passing through gear
Item 32 shelters from lightweight panels 2, not only ensure that the beauty of table top, but also alleviates the weight of table top, transports convenient for table top, also
The dosage that quartz raw material can be reduced reduces the cost of table top, achievees the effect that environmental protection and energy saving.
It is existing quartz stone table board be directly made of quartz raw material, the thickness of table top depending on the requirement of client,
In order to keep table top beautiful, generally increase blend stop on the edge of table top, in terms of the side of table top, table top due to increasing blend stop,
Its thickness can increased, but the actual (real) thickness of table top does not increase.Since thickness of the client to table top requires, such as
Quartz wet feed is filled in the accommodating chamber that blend stop is enclosed by fruit according to existing method, will necessarily greatly increase table top
Weight, increase table top transport difficulty, and increase table top cost.
The blend stop 32 is perpendicular to the panel 31, and the blend stop 32 is enclosed accommodating chamber 33, the lightweight panels 2
It is arranged in accommodating chamber 33.In the other embodiments of the application, the blend stop 32 can also be inclined on panel 31.
In order to keep table top more beautiful, the panel 31 and the blend stop 32 are integrally formed.In other realities of the invention
It applies in example, the blend stop 32 can also be fixed on the edge of panel 31 by modes such as bondings.
Referring to Fig. 6, the blend stop 12 can be closed type and be enclosed the accommodating chamber 33, be also possible to open-close type enclosing
Form the accommodating chamber 33.
In order to keep table top more beautiful, prevent people from seeing lightweight panels 2, the height of the blend stop 32 from the side of table top
More than or equal to the height of lightweight panels 2.
In other embodiments of the invention, the lightweight panels 2 are fixed in accommodating chamber 33 by glue or fixing piece.
In order to mitigate the overall weight of table top, the lightweight panels 2 are made of light material.The light material be PP,
PVC, PC or fiber, but not limited to this.
In order to guarantee the integral strength of table top, the size of the size and shape of the lightweight panels 2 and the accommodating chamber 33
Match with shape.
Above disclosed is only a preferred embodiment of the present invention, cannot limit the power of the present invention with this certainly
Sharp range, therefore equivalent changes made in accordance with the claims of the present invention, are still within the scope of the present invention.
Claims (10)
1. a kind of production method of compound quartz stone table top characterized by comprising
Outer mold is made, the outer mold is equipped with packing area；
Quartz wet feed is filled in packing area, a cloth is completed；
Lightweight panels are fixed on quartz wet feed；
Quartz wet feed is filled in the gap between lightweight panels and outer mold, is made under quartz wet feed and lightweight panels
Surface and side completely attach to, and complete secondary material distributing；
Quartz wet feed, lightweight panels and outer mold are pressed, baking and curing is then carried out；
After completing solidification, outer mold is removed, forms quartzy stone table board first product；
Quartzy stone table board first product progress bridge is cut, is polished, compound quartz stone table top finished product is formed.
2. the production method of compound quartz stone table top as described in claim 1, which is characterized in that the outer mold includes bottom plate
With the side plate being arranged on bottom plate, the side plate and the bottom plate surround the packing area.
3. the production method of compound quartz stone table top as claimed in claim 2, which is characterized in that the outer mold further includes using
In the baffle for reinforcing side plate, surrounding of the baffle plate setting in the side plate.
4. the production method of compound quartz stone table top as described in claim 1, which is characterized in that the vibration of the compression moulding
Frequency is 38-43Hz, time of vibration 80-100s.
5. the production method of compound quartz stone table top as claimed in claim 4, which is characterized in that the compression moulding carries out
Vacuumize process, the time vacuumized are 30-200s.
6. the production method of compound quartz stone table top as described in claim 1, which is characterized in that the lightweight panels are by lightweight
Material is made.
7. the production method of compound quartz stone table top as claimed in claim 6, which is characterized in that the light material be PP,
PVC, PC or fiber.
8. the production method of compound quartz stone table top as described in claim 1, which is characterized in that institute by weight percentage
The formula for stating quartz wet feed is as follows:
Aggregate 85-95%
Resin 5-15%；
The aggregate includes quartz sand and silica flour；
The resin is unsaturated polyester resin.
9. the production method of compound quartz stone table top as claimed in claim 8, which is characterized in that the quartz wet feed also wraps
It includes:
Curing agent 0.01-1%
Coupling agent 0.01-1%
Colorant 0.1-2%；
The curing agent is intermediate temperature curing agent, and the solidification temperature is 80-95 DEG C；
The coupling agent is organo silane coupling agent.
10. a kind of compound quartz stone table top, which is characterized in that the compound quartz stone table top is used as claim 1-9 is any
The production method of compound quartz stone table top described in is made comprising:
Table-board body and lightweight panels；
The table-board body includes panel and the blend stop that is arranged in face plate edge；
The lightweight panels are arranged on panel, and the blend stop blocks lightweight panels.