CN109334183A - Electromagnetic shielding composite material - Google Patents
Electromagnetic shielding composite material Download PDFInfo
- Publication number
- CN109334183A CN109334183A CN201811232358.1A CN201811232358A CN109334183A CN 109334183 A CN109334183 A CN 109334183A CN 201811232358 A CN201811232358 A CN 201811232358A CN 109334183 A CN109334183 A CN 109334183A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- electromagnetic shielding
- electromagnetic
- composite material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of electromagnetic shielding composite materials, including electromagnetic absorption layer, ELECTROMAGNETIC REFLECTION layer and separated type material layer, it is characterised in that;The absorbed layer includes 12-15 parts of conductive filler and 40-45 parts of matrix fillers in parts by weight;The ELECTROMAGNETIC REFLECTION layer includes 25-30 parts of fiber bottom and 50-55 points of rubber matrix filler;The separated type material is off-style paper layer or release film layer;The conductive filler includes nickel coated graphite powder, zinc powder and carbon fiber;Described matrix filler includes plasticizer and EVA;The fiber bottom is glass layer;The rubber base material unsaturated polyester resin, glycidyl ester epoxy resin and phenolic resin;It is using metal material as made of raw material that the technical solution that the present invention takes, which solves existing electromagnetic shielding material mostly, and not only expensive but also extension with service life can lead to the problem of effectiveness and gradually subside.
Description
Technical field
The present invention relates to technical field of electromagnetic shielding, and in particular to a kind of electromagnetic shielding composite material.
Background technique
With the improvement of living standards, more and more electric equipment products enter family;These electric appliances more or less can all produce
Raw electromagnetic radiation, will lead to people more than electromagnetic radiation more than 2 milligauss and suffers from the disease, fuel factor, no fuel factor and accumulative effect
The crowd that the compound injury of reply human body causes modern sub-health state is more and more, therefore the radiation pollution of household electrical appliance obtains
More and more pay attention to people;The electromagnetic shielding material used both at home and abroad at present is mostly made of using metal material as raw material
, not only expensive but also extension with service life can lead to the problem of effectiveness and gradually subside.
Summary of the invention
The purpose of the present invention is to provide a kind of electromagnetic shielding composite material, solve existing electromagnetic shielding material mostly and be with
Metal material is made of raw material, and not only expensive but also extension with service life can generate effectiveness gradually
The problem of recession.
In order to solve the above technical problems, the invention adopts the following technical scheme: a kind of electromagnetic shielding composite material, including
Electromagnetic absorption layer, ELECTROMAGNETIC REFLECTION layer and separated type material layer, it is characterised in that;The absorbed layer in parts by weight, includes
The matrix fillers of 12-15 parts of conductive filler and 40-45 part;The ELECTROMAGNETIC REFLECTION layer include 25-30 parts fiber bottom and
50-55 points of rubber matrix filler;The separated type material is off-style paper layer or release film layer;The conductive filler includes nickel packet
Graphite powder, zinc powder and carbon fiber;Described matrix filler includes plasticizer and EVA;The fiber bottom is glass layer;Institute
State rubber base material unsaturated polyester resin, glycidyl ester epoxy resin and phenolic resin;
Further, the plasticizer include para Toluic Acid, methyl benzoate, P-hydroxybenzoic acid, dibutyl ester, ethylenediamine,
Zinc borate, paraffin, glycerol and soda ash;
Further, the EVA is the ethylene-vinyl acetate copolymer that vinyl acetate content is 20%-28%;
Further, the nickel coated graphite powder is 40-45 parts;The zinc powder is 10-18 parts;The carbon fiber is 25-36 parts;
Further, the plasticizer in parts by weight, including 26-28 para Toluic Acid, 35-40 parts of P-hydroxybenzoic acid,
15-20 parts of dibutyl esters, 16-18 parts of ethylenediamines, 3-5 parts of zinc borates, 10-15 parts of paraffin, 12-15 parts of glycerol and 5-7 parts of soda ash;
Further technical solution is that the glass layer is chopped carbon fiber;The chopped carbon fiber length is 10-
13mm;The filament diameter of the chopped carbon fiber is 5um.
Compared with prior art, the beneficial effects of the present invention are:
1, electromagnetic absorption layer and reflecting layer are combined, can either electromagnetic wave absorption again can reflection electromagnetic wave, enhance pair
The shield effectiveness of electromagnetism;
2, nickel coated graphite powder is selected in conductive filler, while further increasing electric conductivity, can reduce cost;
3, the raw material used is reusable, improves sustainability.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment 1: a kind of electromagnetic shielding composite material, including electromagnetic absorption layer, ELECTROMAGNETIC REFLECTION layer and separated type material layer,
It is characterized in that;The absorbed layer includes 12-15 parts of conductive filler and 40-45 parts of matrix fillers in parts by weight;
The ELECTROMAGNETIC REFLECTION layer includes 25-30 parts of fiber bottom and 50-55 points of rubber matrix filler;The separated type material be from
Type paper layer or release film layer;The conductive filler includes nickel coated graphite powder, zinc powder and carbon fiber;Described matrix filler includes
Plasticizer and EVA;The fiber bottom is glass layer;The rubber base material unsaturated polyester resin, glycidol
Esters epoxy resin and phenolic resin;Electromagnetic absorption layer and reflecting layer are combined, can either electromagnetic wave absorption again can be anti-
Radio magnetic wave enhances the shield effectiveness to electromagnetism;Nickel coated graphite powder is selected in conductive filler, is further increasing electric conductivity
While energy, cost can reduce;The raw material of use is reusable, improves sustainability.
Embodiment 2: a kind of electromagnetic shielding composite material, including electromagnetic absorption layer, ELECTROMAGNETIC REFLECTION layer and separated type material layer,
It is characterized in that;The absorbed layer includes 12-15 parts of conductive filler and 40-45 parts of matrix fillers in parts by weight;
The ELECTROMAGNETIC REFLECTION layer includes 25-30 parts of fiber bottom and 50-55 points of rubber matrix filler;The separated type material be from
Type paper layer or release film layer;The conductive filler includes nickel coated graphite powder, zinc powder and carbon fiber;Described matrix filler includes
Plasticizer and EVA;The fiber bottom is glass layer;The rubber base material unsaturated polyester resin, glycidol
Esters epoxy resin and phenolic resin;The plasticizer includes para Toluic Acid, methyl benzoate, P-hydroxybenzoic acid, two fourths
Ester, ethylenediamine, zinc borate, paraffin, glycerol and soda ash;The raw material acquisition of plasticizer is simple and convenient, and without carcinogen and has
Malicious composition can reduce the harm to human body with being widely applied with the equipment such as household electrical appliances.
Embodiment 3: a kind of electromagnetic shielding composite material, including electromagnetic absorption layer, ELECTROMAGNETIC REFLECTION layer and separated type material layer,
It is characterized in that;The absorbed layer includes 12-15 parts of conductive filler and 40-45 parts of matrix fillers in parts by weight;
The ELECTROMAGNETIC REFLECTION layer includes 25-30 parts of fiber bottom and 50-55 points of rubber matrix filler;The separated type material be from
Type paper layer or release film layer;The conductive filler includes nickel coated graphite powder, zinc powder and carbon fiber;Described matrix filler includes
Plasticizer and EVA;The fiber bottom is glass layer;The rubber base material unsaturated polyester resin, glycidol
Esters epoxy resin and phenolic resin;The EVA is the ethylene-vinyl acetate copolymer that vinyl acetate content is 20%-28%;Second
Sour ethylene contents are that the EVA of 20%-28% can play optimal adhesive force in matrix fillers.
Embodiment 4: a kind of electromagnetic shielding composite material, including electromagnetic absorption layer, ELECTROMAGNETIC REFLECTION layer and separated type material layer,
It is characterized in that;The absorbed layer includes 12-15 parts of conductive filler and 40-45 parts of matrix fillers in parts by weight;
The ELECTROMAGNETIC REFLECTION layer includes 25-30 parts of fiber bottom and 50-55 points of rubber matrix filler;The separated type material be from
Type paper layer or release film layer;The conductive filler includes nickel coated graphite powder, zinc powder and carbon fiber;Described matrix filler includes
Plasticizer and EVA;The fiber bottom is glass layer;The rubber base material unsaturated polyester resin, glycidol
Esters epoxy resin and phenolic resin;The nickel coated graphite powder is 40-45 parts;The zinc powder is 10-18 parts;The carbon fiber is
25-36 parts;
Embodiment 5: a kind of electromagnetic shielding composite material, including electromagnetic absorption layer, ELECTROMAGNETIC REFLECTION layer and separated type material layer, feature
It is;The absorbed layer includes 12-15 parts of conductive filler and 40-45 parts of matrix fillers in parts by weight;It is described
ELECTROMAGNETIC REFLECTION layer includes 25-30 parts of fiber bottom and 50-55 points of rubber matrix filler;The separated type material is release paper
Layer or release film layer;The conductive filler includes nickel coated graphite powder, zinc powder and carbon fiber;Described matrix filler includes plasticising
Agent and EVA;The fiber bottom is glass layer;The rubber base material unsaturated polyester resin, glycidol esters
Epoxy resin and phenolic resin;The plasticizer in parts by weight, including 26-28 para Toluic Acid, 35-40 parts of para hydroxybenzenes
Formic acid, 15-20 part dibutyl ester, 16-18 parts of ethylenediamines, 3-5 parts of zinc borates, 10-15 parts of paraffin, 12-15 parts of glycerol and 5-7 parts are pure
Alkali.
Embodiment 6: a kind of electromagnetic shielding composite material, including electromagnetic absorption layer, ELECTROMAGNETIC REFLECTION layer and separated type material layer,
It is characterized in that;The absorbed layer includes that 12-15 parts of conductive filler and 40-45 parts of matrix are filled out in parts by weight
Material;The ELECTROMAGNETIC REFLECTION layer includes 25-30 parts of fiber bottom and 50-55 points of rubber matrix filler;The separated type material
For off-style paper layer or release film layer;The conductive filler includes nickel coated graphite powder, zinc powder and carbon fiber;Described matrix filler packet
Plasticizer and EVA are included;The fiber bottom is glass layer;The rubber base material unsaturated polyester resin shrinks
Glyceride type epoxy resin and phenolic resin;The glass layer is chopped carbon fiber;The chopped carbon fiber length is 10-
13mm;The filament diameter of the chopped carbon fiber is 5um.
Although reference be made herein to invention has been described for multiple explanatory embodiments of the invention, however, it is to be understood that
Those skilled in the art can be designed that a lot of other modification and implementations, these modifications and implementations will fall in this Shen
It please be within disclosed scope and spirit.It more specifically, within the scope of the present disclosure and claims, can be to master
The building block and/or layout for inscribing composite configuration carry out a variety of variations and modifications.In addition to what is carried out to building block and/or layout
Outside modification and improvement, to those skilled in the art, other purposes also be will be apparent.
Claims (6)
1. a kind of electromagnetic shielding composite material, including electromagnetic absorption layer, ELECTROMAGNETIC REFLECTION layer and separated type material layer, it is characterised in that;
The absorbed layer includes 12-15 parts of conductive filler and 40-45 parts of matrix fillers in parts by weight;The electromagnetism
Reflecting layer includes 25-30 parts of fiber bottom and 50-55 points of rubber matrix filler;The separated type material be off-style paper layer or
Release film layer;The conductive filler includes nickel coated graphite powder, zinc powder and carbon fiber;Described matrix filler include plasticizer and
EVA;The fiber bottom is glass layer;The rubber base material unsaturated polyester resin, glycidol esters epoxy
Resin and phenolic resin.
2. electromagnetic shielding composite material according to claim 1, it is characterised in that: the plasticizer includes to benzene first
Acid, methyl benzoate, P-hydroxybenzoic acid, dibutyl ester, ethylenediamine, zinc borate, paraffin, glycerol and soda ash.
3. electromagnetic shielding composite material according to claim 1, it is characterised in that: the EVA is that vinyl acetate content is
The ethylene-vinyl acetate copolymer of 20%-28%.
4. electromagnetic shielding composite material according to claim 1, it is characterised in that: the nickel coated graphite powder is 40-45 parts;
The zinc powder is 10-18 parts;The carbon fiber is 25-36 parts.
5. electromagnetic shielding composite material according to claim 2, it is characterised in that: the plasticizer is according to parts by weight
It calculates, including 26-28 para Toluic Acid, 35-40 parts of P-hydroxybenzoic acid, 15-20 parts of dibutyl esters, 16-18 parts of ethylenediamines, 3-5 parts of boron
Sour zinc, 10-15 part paraffin, 12-15 parts of glycerol and 5-7 parts of soda ash.
6. electromagnetic shielding composite material according to claim 1, it is characterised in that: the glass layer is the carbon fiber that is chopped
Dimension;The chopped carbon fiber length is 10-13mm;The filament diameter of the chopped carbon fiber is 5um.