CN109333710A - A kind of processing method being molded special-shaped bamboo product - Google Patents
A kind of processing method being molded special-shaped bamboo product Download PDFInfo
- Publication number
- CN109333710A CN109333710A CN201811531975.1A CN201811531975A CN109333710A CN 109333710 A CN109333710 A CN 109333710A CN 201811531975 A CN201811531975 A CN 201811531975A CN 109333710 A CN109333710 A CN 109333710A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- mold base
- sliding shoe
- work top
- fixing seat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of processing method for being molded special-shaped bamboo product, including the use of a kind of processing unit (plant) for being molded special-shaped bamboo product, the processing unit (plant) for being molded special-shaped bamboo product includes work top, work top upper surface has mold base, the upper surface middle part of mold base is fixedly connected with fixing seat, each fixing seat side is provided with the multiple sliding shoes being slidably matched with mold base, sliding shoe can be mobile towards fixing seat direction by the driving of sliding block cylinder, adjacent sliding shoe has the forward surface that can be bonded, work top has the cope plate driven by lifting drive, cope plate, there is electric heating tube inside sliding shoe and mold base, processing unit (plant) of the present invention can apply pressure to bamboo, so that bamboo bends in vertical plane, it is simple and crude to compensate for the roasting pattern of existing fire, it is easy to burn black, the defect burnt, solve it is existing mainly with Artificial bending bamboo wood is difficult to control the bending point of bamboo branch, and the one-time formed bamboo product processing quality of energy is good high-efficient.
Description
Technical field
The present invention relates to a kind of processing methods for being molded special-shaped bamboo product.
Background technique
It is widely used with bamboo wood, using bamboo as the household utensils of raw material, box body, cylinder body, shell, curved slab, sketch plate
It is increasing with the abnormity component demand in box-like body, it needs a kind of to be molded the bamboo chip layer acquisition with glue with determining structure shape
The manufacture of the method for the bamboo product of shape or volume.And in order to meet the needs of various shape bamboo product, it needs to carry out mould to bamboo
Pressure heating hot bending processing, existing bamboo wood hot bending treatment process are that fire is roasting.The device is the setation bamboo by root certain length, by bamboo
The both ends of son are fixed on fixed frame, are given after fire roasting bamboo softening and are fixed cooling, however the roasting bamboo softening of existing fire is deposited
In following technical problem: pattern is more simple and crude, bamboo material be easy burn it is black, burn, it is rotten influence it is overall beautiful；Mainly with artificial
It is bent bamboo wood, is difficult to control the bending point of bamboo branch, so that bamboo bending point deviates, or makes bamboo branch curvature not in one plane,
And production efficiency is low.
Summary of the invention
The present invention improves the above problem, i.e., the technical problem to be solved by the present invention is to existing bamboo soften at
Type is using the roasting mode of fire and low by manually bending production efficiency, and quality is irregular.
Specific embodiments of the present invention are: a kind of processing unit (plant) method being molded special-shaped bamboo product utilizes a kind of molding
The processing unit (plant) of special-shaped bamboo product, the processing unit (plant) for being molded special-shaped bamboo product includes work top, on the work top
Surface has mold base, and the upper surface middle part of the mold base is fixedly connected with fixing seat, each fixing seat side setting
There are the multiple sliding shoes being slidably matched with mold base, the sliding shoe can be moved by the driving of sliding block cylinder towards fixing seat direction
Dynamic, adjacent sliding shoe has the forward surface that can be bonded, the sliding shoe medial surface of multiple enclosings and fixing seat outer surface and mold bottom
Compacting die cavity is formed between seat, has above the work top and the cope plate moved up and down is driven by lifting cylinder；
The work top lower part has mandril cylinder, and the telescopic end of the mandril cylinder, which is fixedly connected with, can run through work top
And the ejector beam of mold base, there is on the work top and mold base the through-hole passed through for ejector beam；
The electric heating tube that the cope plate, sliding shoe and mold base are embedded with, the electric heating tube via line supply heating plate
To improve the temperature of cope plate, sliding shoe and mold base；
Specific step is as follows:
1) bamboo chip is put on mold base and is stuck between fixing seat and sliding shoe around fixing seat, the sliding of fixing seat side
Block is gathered under the driving of cylinder, and sliding shoe closes up after moving to fixing seat direction is enclosed an entirety；
2) in lifting cylinder, the downlink under the driving of lifting cylinder to be located at the intracavitary bamboo and wood of pressing die squeezes shape to cope plate
At die cavity warp architecture, the electric heating tube in cope plate, sliding shoe and mold base is opened, and utilizes electric heating tube cope plate, cunning
Motion block and mold base are preheated；
3) in warm-up phase 3.5~4MPa of pressurization, cope plate, sliding shoe and mold base is made to be heated up to 120 DEG C, and in the pressure
Continue 2 minutes at a temperature of；
4) enter hot pressing holding stage after, in hot pressing holding stage Self-pressurizing agri 5MPa and heat 155~170 DEG C, and at this
Continue 2 minutes under pressure and temperature；
5) release stage Self-pressurizing agri 2MPa heats 120 DEG C and continues 2 minutes at pressure and temperature: after the completion of the release stage
Sliding shoe and upper mold sheet reset, starting are located at the mandril cylinder below work top, and the telescopic rod of mandril cylinder stretches out, using prominent
The ejector beam of mold base is by product ejection die out.
Further, the mold base upper surface has guide rail, and the sliding shoe lower surface, which has, to be cooperated with guide rail
Sliding groove, the guide rail and sliding groove mating surface are dovetail shaped.
Further, the sliding block cylinder is turned shape connector and is fixed on work top.
Further, the work top top is fixed with hanger, and the lifting cylinder is fixed on hanger.
A kind of processing method being molded special-shaped bamboo product according to claim 1, which is characterized in that the bamboo chip packet
Include following making step
(1) bamboo is split into bamboo chip, is split into a thickness of 2.8~3mm, the bamboo chip that width is 16~17 mm, dries bamboo wood humidity
Between 15~18%, bamboo chip cannot be too dry, avoids because bamboo fractures caused by bamboo knee reaction force is excessive；
(2) charing process is carried out to bamboo chip；
(3) one of plywood production adhesive is selected, bamboo chip is dipped in adhesive；
(4) the selected bamboo chip number of plies is required according to products thickness, adjacent bamboo chip is passed through into adhesive bonding and drying 3 minutes.
Compared with prior art, the invention has the following advantages: being heated by processing unit (plant) to bamboo, and it is same
When by mould shape so that bamboo bends in vertical plane, compensate for that the roasting pattern of existing fire is simple and crude, bamboo material holds
Easily burn it is black, burn, rotten influence overall beautiful to be unfavorable for saving；Overall beautiful defect is influenced, is solved existing mainly with people
Work is bent the bending point that bamboo wood is difficult to control bamboo branch, to cause bamboo bending point to deviate or make bamboo branch curvature not in a plane
Upper and low production efficiency technical problem.Bending bamboo wood continues for some time under pressure and temperature, one-time formed bamboo product
Processing quality is good, its indeformable, not degumming of energy in 24 hours in boiling water, and utilizes the forming method work of device progress bamboo
Skill is simple, at low cost, equipment investment is few.Product made from this method has the advantages of bamboo wood and plastic products concurrently, i.e., stiffness it is high,
Impact resistance, light and handy, not mould not aging, and it is cheap.The processing method of molding bamboo product is that bamboo resource opens newly
Approach.
Detailed description of the invention
Fig. 1 is the processing unit (plant) structural schematic diagram that the present invention is molded special-shaped bamboo product.
Fig. 2 is the processing unit (plant) work top superstructure schematic diagram that the present invention is molded special-shaped bamboo product.
Fig. 3 is sliding shoe of the present invention and mold base structural schematic diagram.
Fig. 4 is guide rail of the present invention and guide groove fit structure schematic diagram.
Fig. 5 is cope plate structural schematic diagram of the present invention.
Fig. 6 is Fig. 1 partial structurtes enlarged diagram of the present invention.
Specific embodiment
The present invention will be further described in detail with reference to the accompanying drawings and detailed description.
As shown in figs. 1 to 6, a kind of processing unit (plant) of the molding abnormity bamboo product utilized for processing method of the present invention, packet
Work top 10 is included, 10 upper surface of work top has mold base 20, and the upper surface middle part of the mold base 20 is solid
Surely it is connected with fixing seat 210, each 210 side of fixing seat is provided with the multiple sliding shoes 30 being slidably matched with mold base 20,
The sliding shoe can be mobile towards fixing seat direction by slide-driving device driving, and adjacent sliding shoe 30 is opposite with that can be bonded
Face.
When multiple sliding shoes contact with each other forward surface be bonded to each other be enclosed an entirety when, be located at the inside of sliding shoe 30
Compacting die cavity 100 is formed between face and 210 outer surface of fixing seat and mold base, the work top has by lifting driving dress
The cope plate 40 of driving is set, there is heating device inside the cope plate 40, sliding shoe 30 and mold base 20.
In the present embodiment, the work top top is fixed with hanger 410, and the lifting drive is lifting cylinder
420, the lifting cylinder is fixed on hanger, and the telescopic end that cope plate 40 is fixed on lifting cylinder drives upper mold by lifting cylinder
About 40 plate is run.
In the present embodiment, 20 upper surface of mold base has guide rail 220, and 30 surfaces have and match with guide rail under the sliding shoe
The sliding groove 330 of conjunction, in this implementation, the guide rail 220 and sliding groove mating surface are dovetail shaped, utilize guide rail and sliding groove 330
Cooperation be able to achieve being slidably matched for sliding shoe and mold base, and guarantee operation rail of the sliding block when being pushed by sliding cylinder
Mark (mobile toward or away from fixing seat 210).
In the present embodiment there are four the tools of sliding shoe 30, it is located at the surrounding of fixing seat 210.
In the present embodiment, the slide-driving device is sliding block cylinder 310, and the sliding block cylinder is turned shape connector 320
It is fixed on work top 10.
In order to facilitate the material ejection being located in compacting die cavity 100, the work top lower part has mandril gas
Cylinder 50, the telescopic end of the mandril cylinder is fixedly connected with can be through work top and the ejector beam 510 of mold base, the work
Make that there is the through-hole passed through for ejector beam on table top 10 and mold base 20.
In the present embodiment, the heating device can also be added using the electricity in cope plate, sliding shoe and mold base
Heat pipe, the electric heating tube are connect to supply electric heating tube heating with electric wire 60 to improve cope plate, sliding shoe and mould
Have the temperature of pedestal, heat-shaping can be carried out to the intracavitary bamboo and wood of press type is placed in molding in this way.
There is supporting leg below the work top, be used to support work top.
In addition, the mode of heating can also have heating to close using in the cope plate, sliding shoe and mold base
Heating chamber, the heating device include with heating chamber connection can be passed through to heating chamber heating after oil liquid oil liquid pipe, utilize
The high oil liquid of heat is passed through inside to cope plate, sliding shoe and mold base to promote cope plate, sliding shoe and mold base
Heating.
Embodiment one: it when work, is carried out according to the following steps
1) according to by product, the built-in power-up heating sheet of mold, sliding shoe is under the promotion of sliding cylinder to the movement of fixing seat direction
Close up and is enclosed an entirety；
2) sliding shoe 30 of 210 side of fixing seat is gathered under the driving of cylinder, and cope plate is in lifting cylinder in lifting cylinder
Lower downlink is driven to squeeze to form die cavity warp architecture to which the intracavitary bamboo and wood of pressing die will be located at, in heating using on electric heating tube
Template, sliding shoe and mold base are preheated；
3) in warm-up phase 3.5~4MPa of pressurization, cope plate, sliding shoe and mold base is made to be heated up to 120 DEG C, and in the pressure
Continue 2 minutes at a temperature of:
4) enter hot pressing holding stage after, in hot pressing holding stage Self-pressurizing agri 5MPa and heat 155~170 DEG C, and at this
Continue 2 minutes under pressure and temperature:
5) release stage Self-pressurizing agri 2MPa heats 120 DEG C and continues 2 minutes at pressure and temperature: after the completion of the release stage
Sliding shoe and upper mold sheet reset, starting are located at the mandril cylinder of 10 lower section of work top, and the telescopic rod of mandril cylinder is stretched out, utilized
The ejector beam of prominent mold base is by product ejection die.
Embodiment two: using above-mentioned molding abnormity bamboo product processing unit (plant) molding bamboo product specifically includes the following steps:
(1) bamboo is split into bamboo chip, is split into a thickness of 2.8~3mm, the bamboo chip that width is 16~17 mm, dries bamboo wood humidity
Between 15~18%, bamboo chip cannot be too dry, avoids because bamboo fractures caused by bamboo knee reaction force is excessive；
(2) charing process is carried out to bamboo chip；
(3) one of plywood production adhesive is selected, bamboo chip is dipped in adhesive；
(4) the selected bamboo chip number of plies is required according to products thickness, it, will by adjacent bamboo chip by adhesive bonding and after drying 3 minutes
Bamboo chip layer, which is stacked, to be put on mold base and is stuck between fixing seat and sliding shoe around fixing seat, and the sliding shoe of fixing seat side exists
Bamboo chip pushing shape is shaped to required shape under the action of sliding cylinder, cope plate descending guarantee suppresses cavity closed；
(5) preheat pre-pressing stage: to the bamboo chip layer in mold press 3.5~4MPa, be heated up to 120 DEG C, and in the pressure and temperature
Continue 2 minutes under degree；The effect in this stage is to solidify bamboo wood adhesive under lower reaction speed；Heating rate
Cannot be too fast, it otherwise can cause to gather cruelly, concentrate curing reaction heat release excessively, lead to material interlaminar delamination；
Heating rate is 40 DEG C/min in the present embodiment.
(6) hot pressing holding stage: to the bamboo chip layer pressure 5MPa in mold, 155-170 DEG C of heating, and in the pressure and temperature
Continue 2 minutes under degree, it is therefore intended that material and adhesive is enable sufficiently to solidify；
(7) the release stage: to the bamboo chip layer in mold press 2 MPa, be cooled to 120 DEG C, and continue 2 at pressure and temperature
Minute, it is therefore intended that at a slow speed in molding, gradually to cool down in the case where guaranteeing pressure after heat preservation, when mold temperature is down to 120 DEG C
When following, stripping operation can be carried out.
Cooling method takes natural cooling.
(8) after wait keep the temperature, starting is located at the mandril cylinder of 10 lower section of work top, and the telescopic rod of mandril cylinder is stretched
Out, using the ejector beam of prominent mold base by product ejection die.
If the present invention is open or relates to the components or structural member of connection fastened to each other, unless otherwise stated,
It is fixedly connected it is to be understood that connection (such as connecting using bolt or screw) can be removedly fixed, it is understood that are as follows:
It is non-removable to be fixedly connected with (such as riveting, welding), certainly, connection fastened to each other or integral structure (such as make
Manufactured with casting technique is integrally formed) replaced (obviously can not be using except integrally formed technique).
In addition, for indicating the art of positional relationship or shape applied in any technical solution disclosed in aforementioned present invention
Its meaning includes approximate with its, similar or close state or shape to language unless otherwise stated.
Either component provided by the invention by multiple individual component parts either assembled, or one
The separate part that forming technology manufactures.
Finally it should be noted that: the above embodiments are merely illustrative of the technical scheme of the present invention and are not intended to be limiting thereof；To the greatest extent
The present invention is described in detail with reference to preferred embodiments for pipe, it should be understood by those ordinary skilled in the art that: still
It can modify to a specific embodiment of the invention or some technical features can be equivalently replaced；Without departing from this hair
The spirit of bright technical solution should all cover within the scope of the technical scheme claimed by the invention.
Claims (5)
1. a kind of processing unit (plant) method of the special-shaped bamboo product of molding, which is characterized in that be molded adding for special-shaped bamboo product using a kind of
Tooling is set, and the processing unit (plant) for being molded special-shaped bamboo product includes work top, and the work top upper surface has mold bottom
Seat, the upper surface middle part of the mold base are fixedly connected with fixing seat, and each fixing seat side is provided with sliding with mold base
Multiple sliding shoes of dynamic cooperation, the sliding shoe can be mobile towards fixing seat direction by the driving of sliding block cylinder, adjacent sliding shoe tool
There is the forward surface that can be bonded, forms pressing die between the sliding shoe medial surface and fixing seat outer surface and mold base of multiple enclosings
Chamber, the work top top, which has, drives the cope plate moved up and down by lifting cylinder；
The work top lower part has mandril cylinder, and the telescopic end of the mandril cylinder, which is fixedly connected with, can run through work top
And the ejector beam of mold base, there is on the work top and mold base the through-hole passed through for ejector beam；
The electric heating tube that the cope plate, sliding shoe and mold base are embedded with, the electric heating tube via line supply heating plate
To improve the temperature of cope plate, sliding shoe and mold base；
Specific step is as follows:
1) bamboo chip is put on mold base and is stuck between fixing seat and sliding shoe around fixing seat, the sliding of fixing seat side
Block is gathered under the driving of cylinder, and sliding shoe closes up after moving to fixing seat direction is enclosed an entirety；
2) in lifting cylinder, the downlink under the driving of lifting cylinder to be located at the intracavitary bamboo and wood of pressing die squeezes shape to cope plate
At die cavity warp architecture, the electric heating tube in cope plate, sliding shoe and mold base is opened, and utilizes electric heating tube cope plate, cunning
Motion block and mold base are preheated；
3) in warm-up phase 3.5~4MPa of pressurization, cope plate, sliding shoe and mold base is made to be heated up to 120 DEG C, and in the pressure
Continue 2 minutes at a temperature of；
4) enter hot pressing holding stage after, in hot pressing holding stage Self-pressurizing agri 5MPa and heat 155~170 DEG C, and at this
Continue 2 minutes under pressure and temperature；
5) release stage Self-pressurizing agri 2MPa heats 120 DEG C and continues 2 minutes at pressure and temperature: after the completion of the release stage
Sliding shoe and upper mold sheet reset, starting are located at the mandril cylinder below work top, and the telescopic rod of mandril cylinder stretches out, using prominent
The ejector beam of mold base is by product ejection die out.
2. a kind of processing method for being molded special-shaped bamboo product according to claim 1, which is characterized in that the mold base
Upper surface has guide rail, and the sliding shoe lower surface has the sliding groove cooperated with guide rail, the guide rail and sliding groove mating surface
Section is dovetail shaped.
3. a kind of processing method for being molded special-shaped bamboo product according to claim 1, which is characterized in that the sliding block cylinder
Shape connector is turned to be fixed on work top.
4. a kind of processing method for being molded special-shaped bamboo product according to claim 1, which is characterized in that the work top
Top is fixed with hanger, and the lifting cylinder is fixed on hanger.
5. a kind of processing method for being molded special-shaped bamboo product according to claim 1, which is characterized in that the bamboo chip includes
Following making step
(1) bamboo is split into bamboo chip, is split into a thickness of 2.8~3mm, the bamboo chip that width is 16~17 mm, dries bamboo wood humidity
Between 15~18%, bamboo chip cannot be too dry, avoids because bamboo fractures caused by bamboo knee reaction force is excessive；
(2) charing process is carried out to bamboo chip；
(3) one of plywood production adhesive is selected, bamboo chip is dipped in adhesive；
(4) the selected bamboo chip number of plies is required according to products thickness, adjacent bamboo chip is passed through into adhesive bonding and drying 3 minutes.