CN109333174A - The mirror polishing method for preventing burnishing surface from deforming - Google Patents
The mirror polishing method for preventing burnishing surface from deforming Download PDFInfo
- Publication number
- CN109333174A CN109333174A CN201811501331.8A CN201811501331A CN109333174A CN 109333174 A CN109333174 A CN 109333174A CN 201811501331 A CN201811501331 A CN 201811501331A CN 109333174 A CN109333174 A CN 109333174A
- Authority
- CN
- China
- Prior art keywords
- graphite
- polished face
- polishing
- burnishing surface
- polished
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of mirror polishing methods for preventing burnishing surface from deforming, and described method includes following steps: by the polished face-up of polished part, according to the size in the polished face and the area of shape selection graphite;The graphite is placed in one end of copper particle machine, starts the switch of the copper particle machine, so that the graphite and the polished face contact polishing are to carry out polishing action.By the way that graphite to be fixed on to one end of copper particle machine and carries out sanding and polishing movement with polished face, so that the polishing of polished face is more smooth, so that the material line on polished face, point can eliminate, presentation mirror effect smooth to achieve the effect that;And due to the toughness of graphite itself, fitting mold body shape is more advantageous in its bruting process to achieve the effect that prevent die deformation;And the method for the present invention step is simple, it is easy to operate.
Description
Technical field
The present invention relates to a kind of mirror polishing methods for preventing burnishing surface from deforming.
Background technique
Mold, in industrial production to be molded, be blow molded, squeeze out, die casting or the methods of forging and forming, smelting, punching press obtain
The various moulds and tool of required product.In brief, mold is the tool for making formed article, and this tool is by various
Part is constituted, and different molds is made of different parts.It is mainly realized by the change of physical state of the formed material
The processing of article shape.Mold it is mostly important be mode, therefore the surface smoothness of mode will have a direct impact on product matter
The quality of amount.
In the prior art, general mirror finish technology is unable to satisfy market or producer to the finish on mode surface and puts down
Whole degree also needs processing that mode is further polished and polished.
Summary of the invention
What higher, step that the purpose of the present invention is to provide a kind of polishing precision was simple and convenient to operate prevents burnishing surface from becoming
The mirror polishing method of shape.
In order to achieve the above objectives, the invention provides the following technical scheme: a kind of mirror finish side for preventing burnishing surface from deforming
Method, described method includes following steps:
By the polished face-up of polished part, according to the face of the size in the polished face and shape selection graphite
Product;
The graphite is placed in one end of copper particle machine, starts the switch of the copper particle machine so that the graphite with it is described
Polished face contact polishing is to carry out polishing action.
Further, the area that graphite is selected according to the size and shape in the polished face specifically:
The area for measuring and calculating the polished face is chosen graphite according to the resulting area of calculating and is cut.
Further, described so that the graphite and polished face contact polishing are to carry out polishing action specifically:
During the graphite polishes the polished face, need to smear diamond lap on the polished face
Cream, until polishing program is completed in the polished face.
Further, the particle size range of the diamond paste is W0.5-W14.
Further, the revolving speed of the copper particle machine is 1000-3000 revs/min.
Further, the polishing time range of the graphite is 40-80 seconds.
The beneficial effects of the present invention are: by the way that graphite to be fixed on to one end of copper particle machine and is polished with polished face
Polishing action, so that the polishing of polished face is more smooth, so that the material line, point on polished face can be eliminated to reach
Mirror effect is presented in smooth effect;And due to the toughness of graphite itself, fitting is more advantageous in its bruting process
Mold body shape is to achieve the effect that prevent die deformation;And the method for the present invention step is simple, it is easy to operate.
The above description is only an overview of the technical scheme of the present invention, in order to better understand the technical means of the present invention,
And can be implemented in accordance with the contents of the specification, the following is a detailed description of the preferred embodiments of the present invention and the accompanying drawings.
Detailed description of the invention
Fig. 1 is the flow chart of the mirror polishing method for preventing burnishing surface from deforming of the invention.
Specific embodiment
With reference to the accompanying drawings and examples, specific embodiments of the present invention will be described in further detail.Implement below
Example is not intended to limit the scope of the invention for illustrating the present invention.
Referring to Figure 1, the mirror polishing method that an one of preferred embodiment of the invention prevents burnishing surface from deforming, institute
The method of stating includes the following steps:
By the polished face-up of polished part, according to the face of the size in the polished face and shape selection graphite
Product;
The graphite is placed in one end of copper particle machine, starts the switch of the copper particle machine so that the graphite with it is described
Polished face contact polishing is to carry out polishing action.
More specifically, the area that graphite is selected according to the size and shape in the polished face specifically:
The area for measuring and calculating the polished face is chosen graphite according to the resulting area of calculating and is cut.?
In polishing process, due to the toughness of graphite itself, fitting mold body shape is more advantageous in its bruting process to reach anti-
The only effect of die deformation.
More specifically, described so that the graphite and polished face contact polishing are specific to carry out polishing action
Are as follows:
During the graphite polishes the polished face, need to smear diamond lap on the polished face
Cream, until polishing program is completed in the polished face.Diamond paste and the graphite cooperate so that after polishing to
Burnishing surface is brighter and cleaner, smooth, so that it is eliminated spray mottle, to reach the demand of actual production.In the present embodiment, the gold
The particle size range of hard rock abrasive pastes is W0.5-W14.Really, in other embodiments, the granularity of the diamond paste can also
For other, depending on actual production demand.The particle size range of the diamond paste is bigger, then it represents that and grinding is more coarse,
In actual production demand, it can be selected according to different polishing precision.
During the polishing process, the revolving speed of the copper particle machine is 1000-3000 revs/min, can be more preferable in this range of speeds
The polished part of protection so that polished face is not destroyed.Certainly, the range of speeds of the copper particle machine is according to polished part
Depending on material, also depending on actual production demand.
In summary: by the way that graphite to be fixed on to one end of copper particle machine and carries out sanding and polishing movement with polished face, making
It is more smooth to obtain polished face polishing, so that the material line on polished face, point can be eliminated to reach smooth
Mirror effect is presented in effect;And due to the toughness of graphite itself, fitting mold body shape is more advantageous in its bruting process
Shape is to achieve the effect that prevent die deformation;And the method for the present invention step is simple, it is easy to operate.
Each technical characteristic of embodiment described above can be combined arbitrarily, for simplicity of description, not to above-mentioned reality
It applies all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, all should be considered as described in this specification.
The embodiments described above only express several embodiments of the present invention, and the description thereof is more specific and detailed, but simultaneously
It cannot therefore be construed as limiting the scope of the patent.It should be pointed out that coming for those of ordinary skill in the art
It says, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to protection of the invention
Range.Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.
Claims (6)
1. a kind of mirror polishing method for preventing burnishing surface from deforming, which is characterized in that described method includes following steps:
By the polished face-up of polished part, according to the area in the polished face and the area and shape of shape selection graphite
Shape;
The graphite is placed in one end of copper particle machine, starts the switch of the copper particle machine, so that the graphite is with described wait throw
Smooth surface contact polishing is to carry out polishing action.
2. as described in claim 1 prevent burnishing surface deform mirror polishing method, which is characterized in that it is described according to
The area of size and shape the selection graphite of burnishing surface specifically:
The area for measuring and calculating the polished face is chosen graphite according to the resulting area of calculating and is cut.
3. the mirror polishing method for preventing burnishing surface from deforming as described in claim 1, which is characterized in that described so that the stone
It is black to polish with the polished face contact to carry out polishing action specifically:
During the graphite polishes the polished face, need to smear diamond paste on the polished face,
Until polishing program is completed in the polished face.
4. the mirror polishing method for preventing burnishing surface from deforming as claimed in claim 3, which is characterized in that the diamond lap
The particle size range of cream is W0.5-W14.
5. the mirror polishing method for preventing burnishing surface from deforming as described in claim 1, which is characterized in that the copper particle machine turns
Speed is 1000-3000 revs/min.
6. the mirror polishing method for preventing burnishing surface from deforming as described in claim 1, which is characterized in that the polishing of the graphite
Time range is 40-80 seconds.