CN109321177A - A kind of acrylate solid re-binding adhesive and its preparation and coating method - Google Patents
A kind of acrylate solid re-binding adhesive and its preparation and coating method Download PDFInfo
- Publication number
- CN109321177A CN109321177A CN201811188436.2A CN201811188436A CN109321177A CN 109321177 A CN109321177 A CN 109321177A CN 201811188436 A CN201811188436 A CN 201811188436A CN 109321177 A CN109321177 A CN 109321177A
- Authority
- CN
- China
- Prior art keywords
- acrylate
- solid
- parts
- binding
- monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of acrylate solid re-binding adhesive and its preparation and coating methods, acrylate solid re-binding adhesive, including following raw material: 60-95 parts of acrylate monomers, 0-6 parts of unsaturated acids, 0-6 parts of functional monomers, 1-20 parts of extraordinary monomers, 0.5-3 parts of initiators, 0.1-1 parts of crosslinking agents.The preparation method of acrylate solid re-binding adhesive, comprising the following steps: (1) mix;(2) first segment reacts;(3) second segment reacts;(4) it solidifies.The coating method of acrylate solid re-binding adhesive, comprising the following steps: (1) become fluid state after acrylate solid re-binding adhesive being warmed to 120-350 DEG C by hot melt case;(2) the acrylate solid re-binding adhesive for the fluid state that step (1) obtains is coated on substrate, normal temperature cure.
Description
Technical field
The invention belongs to the fields that high polymer material technology and hot melt adhesive are coated with, and in particular to a kind of acrylate solid can
Adhesive and its preparation and coating method are pasted again.
Background technique
Re-binding can be used to the Notepaper pasted repeatedly, currently, re-binding rises in China.Well known solvent can be again
The shortcomings that rubberizing is it will be apparent that being exactly very not environmentally (solvent is most of harmful).Solvent type glue to the pollution of environment very
Seriously, with the raising of people's environmental consciousness and the foundation of relevant law and perfect, the application of solvent type glue is prohibited and rapid
Decline.Manufacturer's production equipment develops water base glue, has started re-binding Manufacturing Models with Chinese characteristics;Aqueous pressure
Quick high movable adhesive is connect from skill by pressure-sensitive modification, and the strong tack of voltage-dependent characteristic is poor.Re-binding performance is not sent out sufficiently
It waves, it is almost nil repeatedly to paste initial bonding strength.The performance of re-binding can be lost.More important is due to high movable pressure sensitive adhesive
Water-based nature determines that physics creep i.e. modification can be generated by meeting water as the re-binding of substrate using papery, and what it is due to painting is spacing glue,
Re-binding sheet, after gluing is folded originally, whole is bent to glue position, is attached on object, and the place of non-glue position is again to non-glue position
Aspect curling, the reason is that paper water-swellable, dries after-contraction by baking, the place without gluing also retains script
Structure, flatness is constant, thus forms the distinctive elbow phenomenon of re-binding, and need drying time long.It is compacted due to generating
Paper glue position and non-glue position after change not in the same horizontal line, so, after glue position is pasted, another parallel
On line, non-glue position is also rested on original parallel lines, so foring, re-binding is distinctive to stick up tail phenomenon.Due to now can be again
Patch coating machine baking will reach the solidification effect that certain length can be only achieved water accack.So occupied area large volume
Weight, production capacity is low, and cost energy consumption is high, can generate more waste water and sludge;Production run requires tightened up.Re-binding coating machine is logical
Cross what intaglio press transformation came.It is glued using transfer type notch board rod, electric heating bakes, it is common that aqueous pressure is synthesized using lotion
Prepared by the method for quick glue, glue is transferred on paper by anilox roll when in use, through baking oven heating, drying, is wound.Electricity
Energy consumption is high for heating, and stoving temperature is high, and paper creep is big, and ageing resistance is poor.
In view of this, the present invention is specifically proposed.
Summary of the invention
The object of the present invention is to provide a kind of acrylate solid re-binding adhesive and its preparation and coating methods, thoroughly
It solves the problems, such as that the modification of interval dose Paper Coating and viscous force are insufficient, maintains the original smooth performance of paper completely, reach
100% is not bent, and solves the problems, such as that solvent type glue environmental pollution is serious.
To achieve the goals above, a kind of acrylate solid re-binding adhesive provided by the invention, including it is following heavy
Amount part raw material: 60-95 parts of acrylate monomers, 0-6 parts of unsaturated acids, 0-6 parts of functional monomers, 1-20 parts of extraordinary monomers,
0.5-3 parts of initiators, 0.1-1 parts of crosslinking agents.
Preferably, including following raw material: 70-90 parts of acrylate monomers, 1-4 parts of unsaturated acids, 1-4 parts of functions
Property monomer, 5-15 parts of extraordinary monomers, 0.5-1.5 parts of initiators, 0.1-0.8 parts of crosslinking agents.
Preferably, the acrylate monomer is acrylic acid C1-8 alkane esters, methacrylic acid C1-8 alkane esters or methyl
One of octadecyl acrylate is a variety of;The functional monomer is the acrylate and/or hydroxyl of hydroxyl
Methacrylate;The special type monomer is maleic acid diester class compound;The initiator is azo or acyl peroxide class
Initiator;The crosslinking agent is polyolefinic monomer.
Preferably, the acrylate monomer is ethyl acrylate, butyl acrylate, Isooctyl acrylate monomer, metering system
One or more of sour methyl esters or octadecyl methacrylate;The unsaturated acids is acrylic acid, methacrylic acid, horse
Carry out sour or fumaric acid;The functional monomer is in hydroxy-ethyl acrylate, hydroxypropyl acrylate or hydroxyethyl methacrylate
It is one or more;The initiator is benzoyl peroxide;The crosslinking agent is dimethyl allene acid diesters.
The present invention also provides a kind of preparation methods of above-mentioned acrylate solid re-binding adhesive, including following step
It is rapid:
(1) it mixes: by the acrylate monomer, unsaturated acids, functional monomer, extraordinary monomer, crosslinking agent and initiation
Agent ratio by weight is uniformly mixed, and obtains mixture;
(2) first segment reacts: the mixture that step (1) obtains being heated and maintains 80~90 DEG C of temperature range
Interior, object to be mixed cools to 50-70 DEG C and keeps the temperature 2 hours when becoming thick;
(3) second segment reacts: carrying out within the temperature range of mixture obtained in step (2) is heated to 150~180 DEG C
Reaction stops reaction, obtains fluid polymer when reaction is to fluid state.
(4) it solidifies: fluid polymer obtained in step (3) is cooled to subzero 70 DEG C hereinafter, fluid polymer
It is frozen into solid state, obtains acrylate solid re-binding adhesive.
The present invention also provides a kind of coating methods of above-mentioned acrylate solid re-binding adhesive, including following step
It is rapid:
(1) the described in any item acrylate solid re-binding adhesives of claim 1-4 are warmed to by hot melt case
Become fluid state after 120-350 DEG C;
(2) the acrylate solid re-binding adhesive for the fluid state that step (1) obtains is coated on substrate, room temperature
Solidification.
Further, the form of coating described in step (2) be comma scraper coating, the coating of extrusion coated, anilox roll or
The reticulate pattern depth of spray head of getting to know coating, the anilox roll of the anilox roll coating is 90-110 microns.
Preferably, the substrate is wood-free paper or BOPP film.
Preferably, the quantification of 75-80g/m of the wood-free paper2。
Preferably, quantification of 5 μm~12 μm of the thickness of the BOPP film.
A kind of acrylate solid re-binding adhesive provided by the invention and its preparation and coating method, have has as follows
Beneficial effect:
1, acrylate solid re-binding adhesive, cement properties are good, and initial bonding strength is strong, can paste repeatedly, do not stay residue glue, no
Hurt adherend surface.Its superpower initial bonding strength and removable power, can also be widely used for removable adhesive material, adhesive tape
Field;It does not need to evaporate solvent, energy-saving and emission-reduction by consuming a large amount of heat when in use;It is non-toxic and tasteless, belong to environment-friendly type
Learn product.Because of its product itself system solid, convenient for packaging, transport and storage, solvent-free, pollution-free, nontoxic type;
2, the preparation method of acrylate solid re-binding adhesive thoroughly solves interval coating technique to Paper Coating
Bring modification problem maintains the original smooth performance of paper completely, reaches 100% and is not bent, improves product quality.
It entirely produces the no three wastes to generate, is a kind of sustainable environmentally friendly adhesive-preparing technology, simple production process, high added value sticks
Conjunction intensity is big, speed is fast;
3, the coating method of acrylate solid re-binding adhesive had both given full play to the function that can be pasted repeatedly, increased
Strong initial bonding strength, and without scratch, do not hurt substrate, substrate is smooth as before.It is few to can achieve coating weight, meets re-binding or memo
Fine degree as defined in this maintains the original structure of paper, smooth as before.Coating method is simple and effective, and production capacity is high, and production capacity mentions
High by 200%, coating apparatus volume is light and handy, and volume reduces 80%, and structure is simple, and electricity consumption reduces 50%, manufacturing cost at
It reduces again.Since coating method provided by the invention does not need drying equipment, low energy consumption, acrylate solid re-binding glue
Glutinous agent is 100% solid component, is free of solvent, therefore pollution-free, operator will not because more than cleaning glue due to touch it is a large amount of
The toxic solvents such as Formaldehyde and benzene.
Specific embodiment
In order to enable those skilled in the art to better understand the solution of the present invention, With reference to embodiment to this hair
It is bright to be described in further detail.
A kind of acrylate solid re-binding adhesive, including following raw material: 60-95 parts of acrylate monomers,
0-6 parts of unsaturated acids, 0-6 parts of functional monomers, 1-20 parts of extraordinary monomers, 0.5-3 parts of initiators, 0.1-1 parts of crosslinking agents.Wherein
Acrylate monomer is acrylic acid C1-8 alkane esters or methacrylic acid C1-8 alkane esters, as methyl acrylate, acrylic acid second
Ester, propyl acrylate, butyl acrylate, amyl acrylate, Hexyl 2-propenoate, heptylacrylate, Isooctyl acrylate monomer or methyl
Methyl acrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, pentylmethacrylate, methyl-prop
One of the own ester of olefin(e) acid, metering system heptyl heptylate, 2-Propenoic acid, 2-methyl-, octyl ester or octadecyl methacrylate are a variety of;Its
Middle unsaturated acids is acrylic acid, methacrylic acid, maleic acid or fumaric acid etc.;Wherein functional monomer is the acrylic acid of hydroxyl
The methacrylate of ester or hydroxyl, such as one in hydroxy-ethyl acrylate, hydroxypropyl acrylate and hydroxyethyl methacrylate
Kind is a variety of;Wherein extraordinary monomer is maleic acid diester class compound;Wherein initiator is that azo or acyl peroxide class cause
Agent, such as benzoyl peroxide;Wherein crosslinking agent is polyolefinic monomer, such as the dimethacrylate of dimethyl allene acid diesters class
Glycol ester etc..
Acrylate solid re-binding adhesive is a kind of solid colloid that can be pasted repeatedly, is that one kind is not required to solvent, no
Water content, 100% solid fusible polymer, be a kind of adhesive of plasticity, its physics shape in certain temperature range
State changes with temperature and is changed, and chemical characteristic is constant;It is solid at normal temperature, at fluid state, its fusing point after heating
It is 120 degree.
Acrylate solid re-binding adhesive disclosed by the invention, cement properties are good, and initial bonding strength is strong, can paste repeatedly,
Residue glue is not stayed, does not hurt adherend surface.Its superpower initial bonding strength and removable power, can also be widely used for removable adhesive sticker
Material, the field of adhesive tape;It does not need to evaporate solvent, energy-saving and emission-reduction by consuming a large amount of heat when in use;It is non-toxic and tasteless,
Belong to environmental-protecting chemical product.Because of its product itself system solid, convenient for packaging, transport and storage, solvent-free, pollution-free, nontoxic type.
The preparation method of acrylate solid re-binding adhesive, comprising the following steps:
(1) it mixes: acrylate monomer, unsaturated acids, functional monomer, extraordinary monomer, crosslinking agent and initiator is pressed
Weight ratio is uniformly mixed, and obtains mixture;
(2) first segment reacts: the mixture that step (1) obtains being heated and maintains 80~90 DEG C of temperature range
Interior, object to be mixed cools to 50-70 DEG C and keeps the temperature 2 hours when becoming thick;
(3) second segment reacts: carrying out within the temperature range of mixture obtained in step (2) is heated to 150~180 DEG C
Reaction stops reaction when reaction is to fluid state, the reaction time is 40-45 minutes, obtains fluid polymer.
(4) it solidifies: fluid polymer obtained in step (3) is cooled to subzero 70 DEG C hereinafter, fluid polymer
It is frozen into solid state, obtains acrylate solid re-binding adhesive.
It thoroughly solves the problems, such as the modification that interval coating technique comes to paper coating zone, it is original flat to maintain paper completely
Whole performance reaches 100% and is not bent, improves product quality.It entirely produces no three wastes to generate, is a kind of sustainable environment
Friendly adhesive-preparing technology, simple production process, high added value, bonding strength is big, speed is fast.
The coating method of acrylate solid re-binding adhesive, comprising the following steps:
(1) the acrylate solid re-binding adhesive of solid state is become into fluid state by hot melting process.
By the solid blob of viscose of acrylate solid re-binding adhesive, launches into hot melt case, heat and maintain 120
~350 DEG C, solid blob of viscose is melted, acrylate solid re-binding adhesive becomes fluid state, with the increasing of heating temperature
Add, the viscosity of acrylate solid re-binding adhesive constantly reduces, and the mobility of fluid is also constantly changing.It can basis
Fluid viscosity required for different coated forms determines the temperature value in hot melt case, to reach ideal sizing efficiency, such as
Table 1: the Melt Viscosity table of acrylate solid re-binding adhesive.
Table 1: the Melt Viscosity table of acrylate solid re-binding adhesive
Acrylate solid re-binding adhesive is by the way of conduction-oil warming, and heating melting is to becoming energy after 120 DEG C
The liquid adhesive for flowing and having certain viscosity, has opposite stability.Maximum temperature is arranged at 350 DEG C, at 120 DEG C of fusing point
When, the viscosity of acrylate solid re-binding adhesive is maximum value, as the temperature increases, viscosity also with reduction,
This is that one of key problem in technology point of the invention adjusts viscosity in the process of solid fluid to control temperature, thus root
According to cloth base material matching suitable coating head and coated form is applied, optimal sizing and bond effect are pursued.Freely degree of regulation is big, answers
With extensive, can be adapted for manufacturing re-binding, self-stick notes, the gluings product such as adhesive sticker.
(2) the acrylate solid re-binding adhesive liquid of fluid state is coated on substrate, normal temperature cure.
Start in the unwinding device of coating machine, selection applies cloth base material, and painting cloth base material, which can choose, uses quantification of 75-80g/
m2Wood-free paper or quantification of 5 μm~12 μm of thickness of bidirectional stretching polypropylene film (Biaxially Oriented
Polypropylene, abbreviation BOPP), it selects to be suitble to according to the viscosity for applying cloth base material and acrylate solid re-binding adhesive
Coated form, such as acrylate solid re-binding adhesive viscosity be 2500-3500Pa.s when, can choose use
Anilox roll coating, wherein the reticulate pattern depth of anilox roll is 90-110 microns.
The acrylate solid re-binding adhesive of fluid state heats, by pressure pump, by glue application on substrate,
Wherein according to the viscosity of acrylate solid re-binding adhesive, coated form and substrate setting speed.
According to the above coating method, acrylate re-binding coating paper is obtained.
Above-mentioned coating method had both given full play to the function that can be pasted repeatedly, enhanced initial bonding strength, and without scratch, did not hurt
Substrate, substrate are smooth as before.It is few to can achieve coating weight, meets re-binding or the defined fine degree that loses money in a business of keeping record, maintains
The original structure of paper, it is smooth as before.Coating method is simple and effective, and production capacity is high, and production capacity improves 300%, well known existing painting
The confidential drying tunnel by up to 20m or more of cloth is baked and banked up with earth could be by glue curing, and most fast 100 ms/min of coating speed is hereinafter, and originally
The acrylate solid re-binding adhesive of invention and its coating method can not be baked and banked up with earth and also just should not with normal temperature cure
Drying tunnel, minimum speed can achieve 300 meters or more per minute.
The simple and effective simple volume of coating apparatus structure of coating method is light and handy, if well known existing coating machine speed is most
Fast 100 ms/min, length must reach 40 meters, and use the present invention, and 8 meters of coating machine extreme length, volume reduces 80%.
Production cost and electricity consumption reduce 90%, and the coating machine electricity consumption of well known existing 100 meters of speed is 200,000
Watt/hour or more.Support that electricity is 20 kilowatts/hour or less since coating method provided by the invention does not need drying equipment.
Therefore low energy consumption, and manufacturing cost is greatly lowered.
Acrylate solid re-binding adhesive is 100% solid component, is free of solvent, therefore Zero-discharge non-pollution, together
When operator will not because cleaning more than glue due to touch the toxic solvents such as a large amount of Formaldehyde and benzene.
Embodiment 1
A kind of acrylate solid re-binding adhesive, material composition are as shown in table 1:
The material composition of the acrylate solid re-binding adhesive of 1 embodiment 1 of table
The preparation method of above-mentioned acrylate solid re-binding adhesive the following steps are included:
(1) it mixes: acrylate monomer, unsaturated acids, functional monomer, extraordinary monomer, crosslinking agent and initiator is pressed
Weight ratio is uniformly mixed, and obtains mixture;
(2) first segment reacts: the mixture that step (1) obtains being heated and maintains 80~90 DEG C of temperature range
Interior, object to be mixed cools to 50-70 DEG C and keeps the temperature 2 hours when becoming thick;
(3) second segment reacts: carrying out within the temperature range of mixture obtained in step (2) is heated to 150~180 DEG C
Reaction stops reaction when reaction is to fluid state, the reaction time is 40-45 minutes, obtains fluid polymer.
(4) it solidifies: fluid polymer obtained in step (3) is cooled to subzero 70 DEG C hereinafter, fluid polymer
It is frozen into solid state, obtains acrylate solid re-binding adhesive.
Embodiment 2
A kind of acrylate solid re-binding adhesive, material composition are as shown in table 2:
The material composition of the acrylate solid re-binding adhesive of 2 embodiment 2 of table
The preparation method of above-mentioned acrylate solid re-binding adhesive the following steps are included:
(1) it mixes: acrylate monomer, unsaturated acids, functional monomer, extraordinary monomer, crosslinking agent and initiator is pressed
Weight ratio is uniformly mixed, and obtains mixture;
(2) first segment reacts: the mixture that step (1) obtains being heated and maintains 80~90 DEG C of temperature range
Interior, object to be mixed cools to 50-70 DEG C and keeps the temperature 2 hours when becoming thick;
(3) second segment reacts: carrying out within the temperature range of mixture obtained in step (2) is heated to 150~180 DEG C
Reaction stops reaction when reaction is to fluid state, the reaction time is 40-45 minutes, obtains fluid polymer.
(4) it solidifies: fluid polymer obtained in step (3) is cooled to subzero 70 DEG C hereinafter, fluid polymer
It is frozen into solid state, obtains acrylate solid re-binding adhesive.
Embodiment 3
A kind of acrylate solid re-binding adhesive, material composition are as shown in table 3:
The material composition of the acrylate solid re-binding adhesive of 3 embodiment 3 of table
The preparation method of above-mentioned acrylate solid re-binding adhesive the following steps are included:
(1) it mixes: acrylate monomer, unsaturated acids, functional monomer, extraordinary monomer, crosslinking agent and initiator is pressed
Weight ratio is uniformly mixed, and obtains mixture;
(2) first segment reacts: the mixture that step (1) obtains being heated and maintains 80~90 DEG C of temperature range
Interior, object to be mixed cools to 50-70 DEG C and keeps the temperature 2 hours when becoming thick;
(3) second segment reacts: carrying out within the temperature range of mixture obtained in step (2) is heated to 150~180 DEG C
Reaction stops reaction when reaction is to fluid state, the reaction time is 40-45 minutes, obtains fluid polymer.
(4) it solidifies: fluid polymer obtained in step (3) is cooled to subzero 70 DEG C hereinafter, fluid polymer
It is frozen into solid state, obtains acrylate solid re-binding adhesive.
The acrylate solid re-binding adhesive that Examples 1 to 3 obtains is detected:
The detection method of peeling force: glue is heated to 150-180 DEG C, is applied on paper, coated glue layer is with a thickness of 2-4um/
m2;It is cut into 25 mm wides patch on the steel plate, 180 ° of pull-ups is pressed with the speed of 300mm/min, detect peeling force.
The detection method of heat resistance: pasting 100 times repeatedly, detects whether to fall glue without remnants, can cohesive force always and just
Viscous force is identical, remains unchanged.
Testing result is as shown in table 4:
The testing result of 4 Examples 1 to 3 of table
Embodiment | Peeling force | It pastes 100 times repeatedly |
1 | 90 grams | Not degumming, no remnants |
2 | 95 grams | Not degumming, no remnants |
3 | 105 grams | Not degumming, no remnants |
From table 4, it can be seen that the acrylate solid re-binding adhesive that the present invention obtains, adhesive force is stablized, durability
It is good, it is used multiple times, pastes repeatedly.
Embodiment 4
The coating method of acrylate solid re-binding adhesive, comprising the following steps:
(1) the acrylate solid re-binding adhesive of solid state is become into fluid state by hot melting process.
By the solid blob of viscose of acrylate solid re-binding adhesive, launches into hot melt case, heat and maintain 120
~350 DEG C, solid blob of viscose is melted into
(2) the acrylate solid re-binding adhesive of the liquid condition of fluid state is coated on substrate, room temperature is solid
Change.The colloid for becoming liquid after fusing is transported to apparatus for coating by pressurizing device, coating is carried out to substrate.
Start in the unwinding device of coating machine, selection uses quantification of 75-80g/m2Wood-free paper as apply cloth base material, choosing
Coated form is selected as anilox roll coating, wherein the reticulate pattern depth of anilox roll is 90-110 microns.
The acrylate solid re-binding adhesive of fluid state is heated up to 180-200 DEG C, at this time the propylene of fluid state
The viscosity of acid esters solid re-binding adhesive is 2500-3500Pa.s, and by pressure pump, glue follows between hot melt case and glue groove
After circulation is dynamic, glue is coated on the substrate of 76-80g wood-free paper by anilox roll, wherein setting speed for 150-180 meters/
Minute.
According to the above coating method, acrylate re-binding coating paper is obtained, quantification of 8-10g/m is glued2, glue is heated
It to 150-180 DEG C, is applied on paper, coated glue layer is with a thickness of -3-5um/m2;It is cut into 25 mm wides patch on the steel plate, with
For the speed of 300mm/min from 180 ° of angle pull-ups, detecting peeling force is 130 grams.
It can paste repeatedly 300 times or more.Adhesive force is stablized, and durability is good, is used multiple times, and pastes repeatedly and does not stay residue glue.
Embodiment 5
The coating method of acrylate solid re-binding adhesive, comprising the following steps:
(1) the acrylate solid re-binding adhesive of solid state is become into fluid state by hot melting process.
By the solid blob of viscose of acrylate solid re-binding adhesive, launches into hot melt case, heat and maintain 120
~350 DEG C, solid blob of viscose is melted into
(2) the acrylate solid re-binding adhesive of the liquid condition of fluid state is coated on substrate, room temperature is solid
Change.The colloid for becoming liquid after fusing is transported to apparatus for coating by pressurizing device, coating is carried out to substrate.
Start in the unwinding device of coating machine, selects to use quantification of 5 μm~12 μm of thickness of BOPP film as coating base
Material selects coated form as spraying of getting to know.
The acrylate solid re-binding adhesive of fluid state is heated up to 260-300 DEG C, at this time the propylene of fluid state
The viscosity of acid esters solid re-binding adhesive be 1500-3000Pa.s, by pressure pump, glue after hot melt case circulates,
The coated die head of glue is painted in BOPP film by hydraulic device, wherein setting speed is 250 ms/min.
According to the above coating method, acrylate re-binding coating paper is obtained, quantification of 15-18g/m is glued2, glue plus
Heat arrives 150-180 DEG C, is applied on paper, coated glue layer is with a thickness of 4-6um/m2;It is cut into 25 mm wides patch on the steel plate, with
For the speed of 300mm/min from 180 angle pull-ups, detecting peeling force is 160 grams.It can paste repeatedly 300 times or more.Adhesive force is steady
Fixed, durability is good, is used multiple times, and pastes repeatedly and does not stay residue glue.
Specific case used herein elaborates inventive concept, the explanation of above example is only intended to
Help understands core of the invention thought.It should be pointed out that for those skilled in the art, not departing from this
Under the premise of inventive concept, any obvious modification, equivalent replacement or the other improvements made should be included in the present invention
Protection scope within.
Claims (10)
1. a kind of acrylate solid re-binding adhesive, which is characterized in that including following raw material: 60-95 parts of propylene
Acid ester monomer, 0-6 parts of unsaturated acids, 0-6 parts of functional monomers, 1-20 parts of extraordinary monomers, 0.5-3 parts of initiators, 0.1-1 parts of friendships
Join agent.
2. acrylate solid re-binding adhesive according to claim 1, which is characterized in that former including following parts by weight
Material: 70-90 parts of acrylate monomers, 1-4 parts of unsaturated acids, 1-4 parts of functional monomers, 5-15 parts of extraordinary monomers, 0.5-1.5 parts
Initiator, 0.1-0.8 parts of crosslinking agents.
3. acrylate solid re-binding adhesive according to claim 1 or 2, which is characterized in that the acrylate
Monomer is one of acrylic acid C1-8 alkane esters, methacrylic acid C1-8 alkane esters or octadecyl methacrylate or more
Kind;The functional monomer is the acrylate of hydroxyl and/or the methacrylate of hydroxyl;The special type monomer is horse
Carry out acid diesters class compound;The initiator is azo or acyl peroxide class initiator;The crosslinking agent is polyolefinic monomer.
4. acrylate solid re-binding adhesive according to claim 3, which is characterized in that the acrylate monomer
For in ethyl acrylate, butyl acrylate, Isooctyl acrylate monomer, methyl methacrylate or octadecyl methacrylate
It is one or more of;The unsaturated acids is acrylic acid, methacrylic acid, maleic acid or fumaric acid;The functional monomer is third
One of olefin(e) acid hydroxyl ethyl ester, hydroxypropyl acrylate or hydroxyethyl methacrylate are a variety of;The initiator is benzoyl peroxide
Formyl;The crosslinking agent is dimethyl allene acid diesters.
5. a kind of preparation method of the described in any item acrylate solid re-binding adhesives of claim 1-4, feature exist
In, comprising the following steps:
(1) it mixes: the acrylate monomer, unsaturated acids, functional monomer, extraordinary monomer, crosslinking agent and initiator is pressed
Weight ratio is uniformly mixed, and obtains mixture;
(2) first segment reacts: within the temperature range of heating by the mixture that step (1) obtains and maintain 80~90 DEG C, to
50-70 DEG C is cooled to when mixture becomes thick keeps the temperature 2 hours;
(3) second segment reacts: carrying out within the temperature range of mixture obtained in step (2) is heated to 150~180 DEG C anti-
It answers, stops reaction when reaction is to fluid state, obtain fluid polymer.
(4) it solidifies: fluid polymer obtained in step (3) is cooled to subzero 70 DEG C hereinafter, fluid polymer solidifies
At solid state, acrylate solid re-binding adhesive is obtained.
6. a kind of coating method of the described in any item acrylate solid re-binding adhesives of claim 1-4, feature exist
In, comprising the following steps:
(1) the described in any item acrylate solid re-binding adhesives of claim 1-4 are warmed to 120- by hot melt case
Become fluid state after 350 DEG C;
(2) the acrylate solid re-binding adhesive for the fluid state that step (1) obtains is coated on substrate, room temperature is solid
Change.
7. coating method according to claim 6, which is characterized in that the form of coating described in step (2) is scraped for comma
Cutter painting cloth, extrusion coated, anilox roll coating or spray head coating of getting to know, the reticulate pattern depth of the anilox roll of the anilox roll coating are
90-110 microns.
8. coating method according to claim 6, which is characterized in that the substrate is wood-free paper or BOPP film.
9. coating method according to claim 8, which is characterized in that the quantification of 75-80g/m of the wood-free paper2。
10. coating method according to claim 8, which is characterized in that quantification of 5 μm~12 μ of the thickness of the BOPP film
m。