CN109321043A - A kind of seawater pipeline anticorrosive paint and preparation method thereof - Google Patents
A kind of seawater pipeline anticorrosive paint and preparation method thereof Download PDFInfo
- Publication number
- CN109321043A CN109321043A CN201811119803.3A CN201811119803A CN109321043A CN 109321043 A CN109321043 A CN 109321043A CN 201811119803 A CN201811119803 A CN 201811119803A CN 109321043 A CN109321043 A CN 109321043A
- Authority
- CN
- China
- Prior art keywords
- parts
- added
- seawater pipeline
- anticorrosive paint
- piezoluminescence
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of coatings.The object of the present invention is to provide a kind of safe and non-toxic, high-efficient and lasting seawater pipeline anticorrosive paints.The technical solution adopted is that: a kind of seawater pipeline anticorrosive paint is made of the raw material of following parts by weight: 10-15 parts of piezoluminescence material, 6-8 parts of photocatalyst material, 45-50 parts of modified natural glycan super absorbent resin, 20-25 parts of zinc acrylate resin, 0.5-1 parts of emulsified wax, 1-2 parts of PP fiber, 1-3 parts of phosphatide emulsifier, 4-6 parts of organobentonite, 2-3 parts of propylene glycol.Environmental Safety of the present invention, effectiveness persistently, microorganism can be effectively prevent to adhere to.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of seawater pipeline anticorrosive paint and preparation method thereof.
Background technique
Marine corrosion refers to the corrosion that metal component occurs in marine environment.Marine environment is a kind of corrosion ring of complexity
Border.Wherein in addition to the corrosion of seawater, microorganism, mushroom corrosion are also one of important component.Needle in the prior art
It is general using toxic preservative is added in coating to the above problem, although certain anti-corrosion effect is achieved, also to sea
Foreign ecological environment causes biggish broken ring, the especially water environment on seawater pipeline periphery.
Summary of the invention
The object of the present invention is to provide a kind of safe and non-toxic, high-efficient and lasting seawater pipeline anticorrosive paints.
For achieving the above object, the technical scheme adopted by the invention is that: a kind of seawater pipeline anticorrosive paint, by
The raw material of following parts by weight are constituted:
The general formula of the piezoluminescence material are as follows:
The photocatalyst material is Ag doping modified nano-titanium dioxide.
Preferably, it is made of the raw material of following parts by weight:
Preferably, the length of the PP fiber is less than 1mm.
Preferably, the preparation method of the seawater pipeline anticorrosive paint, comprising the following steps:
(1) preparation of piezoluminescence material: bromo tetraphenyl ethylene and 4- aldehyde radical phenyl boric acid are dissolved in toluene, and four fourths are added
Base ammonium bromide and wet chemical;After logical nitrogen 0.5h, tetrakis triphenylphosphine palladium is added, is heated to 90 DEG C of reactions for 24 hours;Reaction
After, the reaction solution for being as cold as room temperature is poured into water, is extracted using ethyl acetate;Organic layer is dry with anhydrous sodium sulfate
Afterwards, solvent is boiled off, is purified using silica gel column chromatography, is drenched and is inhaled as leacheate using n-hexane and methylene chloride mixed solvent, obtained
To white product be piezoluminescence material;
(2) preparation of photocatalyst material: at normal temperature, a certain amount of nano-titanium dioxide being added in silver nitrate solution,
Sodium carbonate liquor is added after reaction after a period of time, mixed solution is made;The mixed solution is straight under the irradiation of ultraviolet radiator
Supernatant liquor is removed after standing to distill water washing to photochemical reaction is completed, lower layer is Ag doping modified nano-silica
Titanium;
(3) modified natural glycan super absorbent resin, zinc acrylate resin and emulsified wax are emulsified 60-80 points together
Clock adds phosphatide emulsifier, and it is stand-by that water-soluble emulsion is made;Again by piezoluminescence material, photocatalyst material, PP fiber,
Organobentonite, propylene glycol are added in water-soluble emulsion, 100 DEG C at a temperature of, stir 15 points with 900 revs/min of speed
Clock is to get finished product.
Beneficial effects of the present invention embody a concentrated reflection of:
(1) safe and non-toxic, effectiveness is lasting using photocatalyst material as antibacterial, sterilizing composition, to inhibiting microorganism attachment tool
There is fabulous effect.
(2) piezoluminescence material is under the fluctuation impact of seawater, and pressure change can generate certain fluorescent effect, with nature
Light matches can provide long-acting trigger condition for photocatalyst.
(3) using Ag doping modified nano-titanium dioxide as photocatalyst material, there is broader Absorber Bandwidth, so that light touches
Catalytic material also has preferable activity under the catalysis of natural light.
(4) addition of PP fiber not only increases the mechanical performance of coating, while improving the roughness of coating surface, makes
Obtaining photocatalyst material and piezoluminescence material has more exposed areas, improves the efficiency of the two.
Specific embodiment
The preparation method of seawater pipeline anticorrosive paint of the present invention:
(1) preparation of piezoluminescence material: bromo tetraphenyl ethylene and 4- aldehyde radical phenyl boric acid are dissolved in toluene, and four fourths are added
Base ammonium bromide and wet chemical;After logical nitrogen 0.5h, tetrakis triphenylphosphine palladium is added, is heated to 90 DEG C of reactions for 24 hours;Reaction
After, the reaction solution for being as cold as room temperature is poured into water, is extracted using ethyl acetate;Organic layer is dry with anhydrous sodium sulfate
Afterwards, solvent is boiled off, is purified using silica gel column chromatography, is drenched and is inhaled as leacheate using n-hexane and methylene chloride mixed solvent, obtained
To white product be piezoluminescence material, output capacity 88%;Since coating of the present invention is typically employed in seawater
On pipe element, natural light is relatively poor.For this purpose, the activity in order to guarantee photocatalyst material, the present invention is added with piezoluminescence
Material, the piezoluminescence material namely can be issued light by after external pressure stimulation, urge to provide for photocatalyst material
Change source.The general structure of the piezoluminescence material are as follows:
(2) preparation of photocatalyst material: the extinction bandwidth in order to improve photocatalyst material plays visible light and fluorescence more
Good catalytic action, better way are that photocatalyst material of the present invention uses Ag doping modified nano-titanium dioxide,
It exactly utilizes and adulterates silver particles in nano-titanium dioxide, to improve the extinction bandwidth of nano-titanium dioxide, make it non-ultraviolet
Also there is preferable activity under environment.The present invention controls the PH numerical value of solution, by one at normal temperature using photochemical precipitation method
Quantitative nano-titanium dioxide is added in silver nitrate solution, strong stirring, and it is molten that sodium carbonate is added after reaction after a period of time
Mixed solution is made in liquid;The mixed solution under the irradiation of ultraviolet radiator until complete photochemical reaction, it is quiet to distill water washing
Removing supernatant liquor is postponed, lower layer is Ag doping modified nano-titanium dioxide.Ag doping modified Nano two of the present invention
Titanium oxide still has high activity under visible light environment, reduces the catalysis difficulty of photocatalyst material.
(3) modified natural glycan super absorbent resin, zinc acrylate resin and emulsified wax are emulsified 60-80 points together
Clock adds phosphatide emulsifier, and it is stand-by that water-soluble emulsion is made;Again by piezoluminescence material, photocatalyst material, PP fiber,
Organobentonite, propylene glycol are added in water-soluble emulsion, 100 DEG C at a temperature of, stir 15 points with 900 revs/min of speed
Clock is to get finished product.
The present invention is illustrated in more detail below with reference to embodiment.
Embodiment 1
10 parts of piezoluminescence material, 8 parts of photocatalyst material, 45 parts of modified natural glycan super absorbent resin, acrylic acid
25 parts of zinc resin, 0.5 part of emulsified wax, 2 parts of PP fiber, 1 part of phosphatide emulsifier, 6 parts of organobentonite, 2 parts of propylene glycol.
Embodiment 2
15 parts of piezoluminescence material, 6 parts of photocatalyst material, 50 parts of modified natural glycan super absorbent resin, acrylic acid
20 parts of zinc resin, 1 part of emulsified wax, 1 part of PP fiber, 3 parts of phosphatide emulsifier, 4 parts of organobentonite, 3 parts of propylene glycol.
Embodiment 3
13 parts of piezoluminescence material, 7 parts of photocatalyst material, 48 parts of modified natural glycan super absorbent resin, acrylic acid
23 parts of zinc resin, 0.7 part of emulsified wax, 1.5 parts of PP fiber, 2 parts of phosphatide emulsifier, 5 parts of organobentonite, propylene glycol 2.5
Part.
Through detecting, the coating antibacterial circle diameter of three embodiments of the present invention respectively reaches 63mm, 65mm and 74mm,
The fungistatic effect of middle embodiment 3 is especially apparent.The present invention is for the first time applying photocatalyst technology and piezoluminescence technology connected applications
Material field, Environmental Safety, effectiveness are lasting, effectively can prevent microorganism from adhering to.
Claims (4)
1. a kind of seawater pipeline anticorrosive paint, which is characterized in that be made of the raw material of following parts by weight:
The general formula of the piezoluminescence material are as follows:
The photocatalyst material is Ag doping modified nano-titanium dioxide.
2. seawater pipeline anticorrosive paint according to claim 1, it is characterised in that: by the raw material structure of following parts by weight
At:
3. seawater pipeline anticorrosive paint according to claim 2, it is characterised in that: the length of the PP fiber is less than
1mm。
4. the preparation method of seawater pipeline anticorrosive paint according to claim 1 to 3, which is characterized in that including following step
It is rapid:
(1) preparation of piezoluminescence material: bromo tetraphenyl ethylene and 4- aldehyde radical phenyl boric acid are dissolved in toluene, and tetrabutyl bromine is added
Change ammonium and wet chemical;After logical nitrogen 0.5h, tetrakis triphenylphosphine palladium is added, is heated to 90 DEG C of reactions for 24 hours;Reaction terminates
Afterwards, the reaction solution for being as cold as room temperature is poured into water, is extracted using ethyl acetate;After organic layer anhydrous sodium sulfate drying,
Solvent is boiled off, is purified using silica gel column chromatography, is drenched and is inhaled as leacheate using n-hexane and methylene chloride mixed solvent, obtained
White product is piezoluminescence material;
(2) preparation of photocatalyst material: at normal temperature, a certain amount of nano-titanium dioxide is added in silver nitrate solution, is passed through
Sodium carbonate liquor is added after the reaction of a period of time, mixed solution is made;The mixed solution is under the irradiation of ultraviolet radiator until complete
At photochemical reaction, to distill water washing, supernatant liquor is removed after standing, lower layer is Ag doping modified nano-titanium dioxide;
(3) modified natural glycan super absorbent resin, zinc acrylate resin and emulsified wax are emulsified 60-80 minutes together,
Phosphatide emulsifier is added, it is stand-by that water-soluble emulsion is made;Again by piezoluminescence material, photocatalyst material, PP fiber, organic
Bentonite, propylene glycol are added in water-soluble emulsion, 100 DEG C at a temperature of, stir 15 minutes with 900 revs/min of speed, i.e.,
Obtain finished product.