CN109306236A - A kind of environment-friendly type macromolecule coating with rapid-curing cutback performance - Google Patents

A kind of environment-friendly type macromolecule coating with rapid-curing cutback performance Download PDF

Info

Publication number
CN109306236A
CN109306236A CN201811155552.4A CN201811155552A CN109306236A CN 109306236 A CN109306236 A CN 109306236A CN 201811155552 A CN201811155552 A CN 201811155552A CN 109306236 A CN109306236 A CN 109306236A
Authority
CN
China
Prior art keywords
environment
rapid
friendly type
coating
curing cutback
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811155552.4A
Other languages
Chinese (zh)
Inventor
冯辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huzhou Junzilan Coatings Co Ltd
Original Assignee
Huzhou Junzilan Coatings Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huzhou Junzilan Coatings Co Ltd filed Critical Huzhou Junzilan Coatings Co Ltd
Priority to CN201811155552.4A priority Critical patent/CN109306236A/en
Publication of CN109306236A publication Critical patent/CN109306236A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance, it is related to high-molecular coating technical field, including following component (by mass percentage): epoxy resin: 10~14%, organic siliconresin: 12~14%, macromolecule polyurethane resin: 15~19%, styrene-acrylic emulsion: 9~11%, asbestos fibre: 6~8%, high molecular emulsion: 14~16%, pigment: 3~5%, cellulose ether: 1.5~4.5%, additive: 0.5~1.5%, quick-drying silicon solution: 1~5%, surplus is pure water.Coating products produced by the present invention, with good antimildew and antibacterial, heat preservation, freeze-thaw resistance, waterproof antiwear, it can reduce under the prolonged and repeated effect of natural environment, phenomena such as coating occurs cracking, dusting, peels off, decentralized medium of the invention is water, and the volatilization of moisture not will cause environmental pollution in work progress, the health of construction personnel will not be endangered, with environmental safety outstanding, better economic benefit, conducive to the popularization in market.

Description

A kind of environment-friendly type macromolecule coating with rapid-curing cutback performance
Technical field
The present invention relates to high-molecular coating technical field, in particular to a kind of environment-friendly type macromolecule with rapid-curing cutback performance applies Material.
Background technique
The decentralized medium of water paint is water, and after coating application, what is volatilized from film is water and a small amount of auxiliary agent, has ring The performances such as guarantor, safety；The water-based paints for being based primarily upon acrylic emulsions account for the share that Building-coating market is more than 70%, usually The paint for thinking acrylic compounds latex emulsion base is most durable paint for external application.The gas permeability of water paint is relatively good, base Vapor inside layer can be to external diffusion: from the physical and chemical performance of film, certain physical chemistry of water paint It can be not as good as solvent based coating, such as chemical-resistant, weatherability, stain resistance.So the environmental protection of water paint, peace should be retained Congruent feature performance benefit overcomes the shortcomings of its weatherability, stain resistance performance again.Use merely water as carrier dispersion performance not Good, the alcohols object for increasing cosolvency can improve its dispersion performance.Increase surfactant in coating and is also conducive to resin in water work For the emulsion dispersion of carrier.Organic siliconresin is added in acrylic emulsion, is conducive to improve coating weatherability, contaminated resistance. But each component in coating influences each other and interacts, and the accurate each component that matches could obtain the painting of high comprehensive performance Material.
Traditional Architectural Emulsion Paints cause to apply because it needs the organic solvents such as the coalescing agent that more amount is added in coating The content of volatile organic compound of material is higher, furthermore in order to prevent coating storage when becoming morally degenerate and film is mouldy, The organic mould inhibitor being harmful to the human body that more amount is added also is needed in coating, this directly influences the physical and mental health of user. Therefore, it is necessary to solve the above problems to invent a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance, solutions It has determined existing problem.
(2) technical solution
In order to achieve the above object, the present invention is achieved by the following technical programs: a kind of environmental protection with rapid-curing cutback performance Type high-molecular coating, including following component (by mass percentage): epoxy resin: 10~14%, organic siliconresin: 12~ 14%, macromolecule polyurethane resin: 15~19%, styrene-acrylic emulsion: 9~11%, asbestos fibre: 6~8%, high molecular emulsion: 14 ~16%, pigment: 3~5%, cellulose ether: 1.5~4.5%, additive: 0.5~1.5%, quick-drying silicon solution: 1~5%, it is remaining Amount is pure water.
Optionally, the additive following component (by mass percentage): dispersing agent: 0.1~0.4%, fire retardant: 0.2 ~0.5% and mould inhibitor: 0.2~0.6%.
Optionally, the pigment is mixed by calcium carbonate, talcum powder, titanium dioxide and silica, the macromolecule Latex is SBS latex or SBR latex.
Optionally, the calcium carbonate, talcum powder, titanium dioxide and silica are formed by following weight percent: carbonic acid Calcium 35wt%, talcum powder 25wt%, titanium dioxide 10wt% and silica 30wt%.
Optionally, the mould inhibitor is the mixture of copper nanoparticle and nano zine oxide in 1:4 ratio, and the dispersing agent is The more succimide class ashless additives of polyisobutene, the fire retardant are antimony oxide or aluminium hydroxide.
Optionally, including following component (by mass percentage): epoxy resin: 10%, organic siliconresin: 14%, high score Sub- polyurethane resin: 15%, styrene-acrylic emulsion: 11%, asbestos fibre: 6%, high molecular emulsion: 16%, pigment: 3%, cellulose Ether: 4.5%, additive: 0.5%, quick-drying silicon solution: 5%, surplus is pure water.
Optionally, including following component (by mass percentage): epoxy resin: 12%, organic siliconresin: 13%, high score Sub- polyurethane resin: 17%, styrene-acrylic emulsion: 10%, asbestos fibre: 7%, high molecular emulsion: 15%, pigment: 4%, cellulose Ether: 3%, additive: 1%, quick-drying silicon solution: 3%, surplus is pure water.
Optionally, including following component (by mass percentage): epoxy resin: 14%, organic siliconresin: 12%, high score Sub- polyurethane resin: 19%, styrene-acrylic emulsion: 9%, asbestos fibre: 8%, high molecular emulsion: 14%, pigment: 5%, cellulose Ether: 1.5%, additive: 1.5%, quick-drying silicon solution: 1%, surplus is pure water.
(3) beneficial effect
The present invention provides a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance, have it is following the utility model has the advantages that
(1), coating products produced by the present invention have good antimildew and antibacterial, heat preservation, freeze-thaw resistance, waterproof antiwear Property, it can reduce under the prolonged and repeated effect of natural environment, phenomena such as coating occurs cracking, dusting, peels off, it is of the invention to divide Dispersion media is water, and the volatilization of moisture not will cause environmental pollution in work progress, will not endanger the health of construction personnel, With environmental safety outstanding, better economic benefit, conducive to the popularization in market.
(2), present invention addition epoxy resin, good heat resistance, water resistance add macromolecule polyurethane resin, With the characteristics such as high intensity, tear-proof, wear-resisting, add high molecular emulsion and cellulose ether, can be improved coating caking property and Toughness, addition quick-drying silicon solution can play quick solidification, asbestos fibre is added, and play skeleton function, mould inhibitor in the present invention The mixture of 1:4 is pressed for copper nanoparticle and nano zine oxide, metallicity has good killing microorganism, three oxidation two of addition Antimony or aluminium hydroxide can make fire retardant, can not only be fire-retardant, and can prevent smoke, do not generate droppings, do not generate it is toxic Gas.
(3), present invention process is simple, and equipment requirement is low, strong operability, has good society generalization application.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects It encloses.
Embodiment 1:
A kind of environment-friendly type macromolecule coating with rapid-curing cutback performance, comprising the following steps: (press quality hundred including following component Divide ratio): epoxy resin: 10%, organic siliconresin: 14%, macromolecule polyurethane resin: 15%, styrene-acrylic emulsion: 11%, asbestos Fiber: 6%, high molecular emulsion: 16%, pigment: 3%, cellulose ether: 4.5%, additive: 0.5%, quick-drying silicon solution: 5%, Surplus is pure water.
Wherein, additive following component (by mass percentage): dispersing agent: 0.1%, fire retardant: 0.2% and mould inhibitor: 0.2%；The pigment is mixed by calcium carbonate, talcum powder, titanium dioxide and silica, and the high molecular emulsion is SBS Latex or SBR latex；The calcium carbonate, talcum powder, titanium dioxide and silica are formed by following weight percent: calcium carbonate 35wt%, talcum powder 25wt%, titanium dioxide 10wt% and silica 30wt%；The mould inhibitor is copper nanoparticle and nanometer For zinc oxide in the mixture of 1:4 ratio, the dispersing agent is the more succimide class ashless additives of polyisobutene, described fire-retardant Agent is antimony oxide or aluminium hydroxide.
Embodiment 2:
A kind of environment-friendly type macromolecule coating with rapid-curing cutback performance, including following component (by mass percentage): asphalt mixtures modified by epoxy resin Rouge: 12%, organic siliconresin: 13%, macromolecule polyurethane resin: 17%, styrene-acrylic emulsion: 10%, asbestos fibre: 7%, high score Sub- latex: 15%, pigment: 4%, cellulose ether: 3%, additive: 1%, quick-drying silicon solution: 3%, surplus is pure water.
Wherein, additive following component (by mass percentage): dispersing agent: 0.2%, fire retardant: 0.3% and mould inhibitor: 0.4%；The pigment is mixed by calcium carbonate, talcum powder, titanium dioxide and silica, and the high molecular emulsion is SBS Latex or SBR latex；The calcium carbonate, talcum powder, titanium dioxide and silica are formed by following weight percent: calcium carbonate 35wt%, talcum powder 25wt%, titanium dioxide 10wt% and silica 30wt%；The mould inhibitor is copper nanoparticle and nanometer For zinc oxide in the mixture of 1:4 ratio, the dispersing agent is the more succimide class ashless additives of polyisobutene, described fire-retardant Agent is antimony oxide or aluminium hydroxide.
Embodiment 3:
A kind of environment-friendly type macromolecule coating with rapid-curing cutback performance, including following component (by mass percentage): asphalt mixtures modified by epoxy resin Rouge: 14%, organic siliconresin: 12%, macromolecule polyurethane resin: 19%, styrene-acrylic emulsion: 9%, asbestos fibre: 8%, high score Sub- latex: 14%, pigment: 5%, cellulose ether: 1.5%, additive: 1.5%, quick-drying silicon solution: 1%, surplus is pure water.
Wherein, additive following component (by mass percentage): dispersing agent: 0.4%, fire retardant: 0.5% and mould inhibitor: 0.6%；The pigment is mixed by calcium carbonate, talcum powder, titanium dioxide and silica, and the high molecular emulsion is SBS Latex or SBR latex；The calcium carbonate, talcum powder, titanium dioxide and silica are formed by following weight percent: calcium carbonate 35wt%, talcum powder 25wt%, titanium dioxide 10wt% and silica 30wt%；The mould inhibitor is copper nanoparticle and nanometer For zinc oxide in the mixture of 1:4 ratio, the dispersing agent is the more succimide class ashless additives of polyisobutene, described fire-retardant Agent is antimony oxide or aluminium hydroxide.
High-molecular coating can be made by above three groups of embodiments, wherein macromolecule made from second group of embodiment applies Expect that effect is best.Coating products produced by the present invention have good antimildew and antibacterial, heat preservation, freeze-thaw resistance, waterproof antiwear Property, it can reduce under the prolonged and repeated effect of natural environment, phenomena such as coating occurs cracking, dusting, peels off, it is of the invention to divide Dispersion media is water, and the volatilization of moisture not will cause environmental pollution in work progress, will not endanger the health of construction personnel, With environmental safety outstanding, better economic benefit, conducive to the popularization in market.
It should be noted that in the present invention unless specifically defined or limited otherwise, fisrt feature is in second feature It can be that the first and second features directly contact or the first and second features are by intermediary mediate contact "up" or "down". Moreover, fisrt feature can be above the second feature " above ", " above " and " above " fisrt feature right above second feature or tiltedly Top, or first feature horizontal height is merely representative of higher than second feature.Fisrt feature second feature " under ", " lower section " and " following " can be fisrt feature and be directly under or diagonally below the second feature, or be merely representative of first feature horizontal height less than Two features.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention, Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features, All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention Within protection scope.

Claims (8)

1. a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance, which is characterized in that (press quality percentage including following component Than): epoxy resin: 10~14%, organic siliconresin: 12~14%, macromolecule polyurethane resin: 15~19%, styrene-acrylic emulsion: 9~11%, asbestos fibre: 6~8%, high molecular emulsion: 14~16%, pigment: 3~5%, cellulose ether: 1.5~4.5%, Additive: 0.5~1.5%, quick-drying silicon solution: 1~5%, surplus is pure water.
2. a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance according to claim 1, it is characterised in that: described to add Add agent following component (by mass percentage): dispersing agent: 0.1~0.4%, fire retardant: 0.2~0.5% and mould inhibitor: 0.2~ 0.6%.
3. a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance according to claim 1, it is characterised in that: the face Material is mixed by calcium carbonate, talcum powder, titanium dioxide and silica, and the high molecular emulsion is SBS latex or SBR cream Glue.
4. a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance according to claim 3, it is characterised in that: the carbon Sour calcium, talcum powder, titanium dioxide and silica by following weight percent form: calcium carbonate 35wt%, talcum powder 25wt%, Titanium dioxide 10wt% and silica 30wt%.
5. a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance according to claim 2, it is characterised in that: described anti- Mould dose is copper nanoparticle and nano zine oxide in the mixture of 1:4 ratio, and the dispersing agent is the more succimides of polyisobutene Class ashless additive, the fire retardant are antimony oxide or aluminium hydroxide.
6. a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance according to claim 1, which is characterized in that including with Lower ingredient (by mass percentage): epoxy resin: 10%, organic siliconresin: 14%, macromolecule polyurethane resin: 15%, phenylpropyl alcohol Lotion: 11%, asbestos fibre: 6%, high molecular emulsion: 16%, pigment: 3%, cellulose ether: 4.5%, additive: 0.5%, Quick-drying silicon solution: 5%, surplus is pure water.
7. a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance according to claim 1, which is characterized in that including with Lower ingredient (by mass percentage): epoxy resin: 12%, organic siliconresin: 13%, macromolecule polyurethane resin: 17%, phenylpropyl alcohol Lotion: 10%, asbestos fibre: 7%, high molecular emulsion: 15%, pigment: 4%, cellulose ether: 3%, additive: 1%, quick-drying Silicon solution: 3%, surplus is pure water.
8. a kind of environment-friendly type macromolecule coating with rapid-curing cutback performance according to claim 1, which is characterized in that including with Lower ingredient (by mass percentage): epoxy resin: 14%, organic siliconresin: 12%, macromolecule polyurethane resin: 19%, phenylpropyl alcohol Lotion: 9%, asbestos fibre: 8%, high molecular emulsion: 14%, pigment: 5%, cellulose ether: 1.5%, additive: 1.5%, fast Dry silicon solution: 1%, surplus is pure water.
CN201811155552.4A 2018-09-30 2018-09-30 A kind of environment-friendly type macromolecule coating with rapid-curing cutback performance Pending CN109306236A (en)