CN109304004A - 一种灭火剂及其制备方法 - Google Patents
一种灭火剂及其制备方法 Download PDFInfo
- Publication number
- CN109304004A CN109304004A CN201710617565.8A CN201710617565A CN109304004A CN 109304004 A CN109304004 A CN 109304004A CN 201710617565 A CN201710617565 A CN 201710617565A CN 109304004 A CN109304004 A CN 109304004A
- Authority
- CN
- China
- Prior art keywords
- silicone oil
- extinguishing chemical
- silica
- carbon black
- sodium chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种灭火剂,其由以下原料制备而成,10‑15wt%氯化钠、10‑20wt%二氧化硅、5‑15wt%可膨胀石墨、5‑10wt%白炭黑、40‑50wt%磷酸氢铵、5‑8wt%硅油。本发明还提供一种灭火剂的制备方法,用于制备上述灭火剂,其包括以下步骤:1)按要求取各原料;2)将二氧化硅、可膨胀石墨、磷酸氢铵分别烘干后混合、搅拌均匀,得到混合料;3)在80‑110℃下,将硅油雾化后喷入混合料中,在喷入硅油时,保持对混合料的搅拌,在硅油加完后继续搅拌混合30‑40分钟;4)然后将白炭黑和氯化钠加入到步骤3)所得到的物料中,保持搅拌、烘干后,即得。上述灭火剂能够提高干粉灭火剂扑灭大面积油池和流淌火的隔热效率和抗复燃性能,有效阻止热辐射主导的火灾蔓延速率和规模。
Description
技术领域
本发明具体涉及一种灭火剂及其制备方法。
背景技术
随着我国经济的不断发展,各地不断有新建的各种型号的油罐,这些油罐一旦发生火灾,极易对周围的建筑和人员形成较大的威胁,如不能及时将其火灾扑灭,仍可能引发灾难性的后果,干粉灭火剂是油类火灾的主要灭火剂,在必要时,辅助以泡沫灭火剂,利用干粉的快速消焰压制火势,再使用泡沫及时覆盖,但是战术配合的难度和干粉消焰后的泡沫降温受火灾规模等因素的影响,除初期的火灾之外,一般难以达到好的效果。
发明内容
本发明的目的在于,提高干粉灭火剂扑灭大面积油池和流淌火的隔热效率和抗复燃性能,有效阻止热辐射主导的火灾蔓延速率和规模,具体的技术方案如下:
一种灭火剂,其由以下原料制备而成,10-15wt%氯化钠、10-20wt%二氧化硅、5-15wt%可膨胀石墨、5-10wt%白炭黑、40-50wt%磷酸氢铵、5-8wt%硅油。
优选地,灭火剂由以下原料制备而成,10wt%氯化钠、20wt%二氧化硅、5wt%可膨胀石墨、10wt%白炭黑、50wt%磷酸氢铵、硅油5wt%。
优选地,灭火剂由以下原料制备而成,15wt%氯化钠、13wt%二氧化硅、15wt%可膨胀石墨、6wt%白炭黑、43wt%磷酸氢铵、硅油8wt%。
本发明还提供一种灭火剂的制备方法,用于制备上述灭火剂,其包括以下步骤:
1)按要求取各原料;
2)将二氧化硅、可膨胀石墨、磷酸氢铵分别烘干后混合、搅拌均匀,得到混合料;
3)在80-110℃下,将硅油雾化后喷入混合料中,在喷入硅油时,保持对混合料的搅拌,在硅油加完后继续搅拌混合30-40分钟;
4)然后将白炭黑和氯化钠加入到步骤3)所得到的物料中,保持搅拌、烘干后,即得。
优选地,在步骤4)中,烘干温度为95-120℃。
本发明中,采用可膨胀石墨、磷酸氢铵、二氧化硅作为干粉灭火剂的主要成分,能够有限地改善现有干粉灭火剂抗复燃性能差的缺陷,其中的可膨胀石墨具有受热膨胀的特性,
具体实施方式
实施例1
1#灭火剂由以下原料制备而成,10wt%氯化钠、20wt%二氧化硅、5wt%可膨胀石墨、10wt%白炭黑、50wt%磷酸氢铵、硅油5wt%。
1#灭火剂采用以下步骤进行制备,
1)按要求取各原料;
2)将二氧化硅、可膨胀石墨、磷酸氢铵分别烘干后混合、搅拌均匀,得到混合料;
3)在80-90℃下,将硅油雾化后喷入混合料中,在喷入硅油时,保持对混合料的搅拌,在硅油加完后继续搅拌混合40分钟;
4)然后将白炭黑和氯化钠加入到步骤3)所得到的物料中,保持搅拌、烘干后,即得。
烘干温度为95-100℃。
实施例2
2#灭火剂由以下原料制备而成,15wt%氯化钠、13wt%二氧化硅、15wt%可膨胀石墨、6wt%白炭黑、43wt%磷酸氢铵、硅油8wt%。
2#灭火剂采用以下步骤进行制备,
1)按要求取各原料;
2)将二氧化硅、可膨胀石墨、磷酸氢铵分别烘干后混合、搅拌均匀,得到混合料;
3)在100-110℃下,将硅油雾化后喷入混合料中,在喷入硅油时,保持对混合料的搅拌,在硅油加完后继续搅拌混合30分钟;
4)然后将白炭黑和氯化钠加入到步骤3)所得到的物料中,保持搅拌、烘干后,即得。
烘干温度为110-120℃。
实施例3
3#灭火剂由以下原料制备而成,13wt%氯化钠、15wt%二氧化硅、10wt%可膨胀石墨、8wt%白炭黑、46wt%磷酸氢铵、硅油8wt%。
3#灭火剂采用以下步骤进行制备,
1)按要求取各原料;
2)将二氧化硅、可膨胀石墨、磷酸氢铵分别烘干后混合、搅拌均匀,得到混合料;
3)在100℃下,将硅油雾化后喷入混合料中,在喷入硅油时,保持对混合料的搅拌,在硅油加完后继续搅拌混合35分钟;
4)然后将白炭黑和氯化钠加入到步骤3)所得到的物料中,保持搅拌、烘干后,即得。
烘干温度为100-110℃。
Claims (5)
1.一种灭火剂,其特征在于,由以下原料制备而成,
10-15wt%氯化钠、10-20wt%二氧化硅、5-15wt%可膨胀石墨、5-10wt%白炭黑、40-50wt%磷酸氢铵、5-8wt%硅油。
2.根据权利要求1所述的灭火剂,其特征在于,由以下原料制备而成,
10wt%氯化钠、20wt%二氧化硅、5wt%可膨胀石墨、10wt%白炭黑、50wt%磷酸氢铵、硅油5wt%。
3.根据权利要求1所述的灭火剂,其特征在于,由以下原料制备而成,
15wt%氯化钠、13wt%二氧化硅、15wt%可膨胀石墨、6wt%白炭黑、43wt%磷酸氢铵、硅油8wt%。
4.一种灭火剂的制备方法,用于制备权利要求1-3任一项所述的灭火剂,其特征在于,包括以下步骤:
1)按要求取各原料;
2)将二氧化硅、可膨胀石墨、磷酸氢铵分别烘干后混合、搅拌均匀,得到混合料;
3)在80-110℃下,将硅油雾化后喷入混合料中,在喷入硅油时,保持对混合料的搅拌,在硅油加完后继续搅拌混合30-40分钟;
4)然后将白炭黑和氯化钠加入到步骤3)所得到的物料中,保持搅拌、烘干后,即得。
5.根据权利要求4所述的制备方法,其特征在于,在步骤4)中,烘干温度为95-120℃。