CN109294065A - A kind of packaging material and preparation method thereof for candy - Google Patents
A kind of packaging material and preparation method thereof for candy Download PDFInfo
- Publication number
- CN109294065A CN109294065A CN201811147776.0A CN201811147776A CN109294065A CN 109294065 A CN109294065 A CN 109294065A CN 201811147776 A CN201811147776 A CN 201811147776A CN 109294065 A CN109294065 A CN 109294065A
- Authority
- CN
- China
- Prior art keywords
- parts
- packaging material
- candy
- preparation
- candy according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of packaging materials for candy, raw material including following parts by weight: 70-78 parts of polypropylene, 30-34 parts of acrylic resin, 60-70 parts of polyvinyl alcohol, 15-20 parts of xanthan gum, 4-10 parts of glutaraldehyde, 13-15 parts of isopropanol, 4-8 parts of pelopon A, 0.5-1 parts of nano silica, 1-1.5 parts of titanium nitride, 3-5 parts of zeolite with carrying silver, 0.5-1 parts of ultraviolet absorbing agent UVP327, 1-3 parts of chitin, 3-6 parts of shale powder, 0.5-1 parts of nano inorganic far-infrared material, 0.1-0.5 parts of vanillic aldehyde, 0.1-0.5 parts of plant polyose, natural 0.1-0.5 parts of beeswax, 0.4-1 parts of calcium fruit fiber.Packaging material materials safety of the invention is reliable, and comprehensive performance is superior, has stable and efficient antibiotic effect, can inhibit bacterial growth, be highly suitable for the packaging of candy.
Description
Technical field
The present invention relates to packaging material fields, and in particular to a kind of packaging material and preparation method thereof for candy.
Background technique
With the fast development of China's packaging industry, packaging production is promoting the development of the national economy, is improving people's object
Position and function in matter culture life increasingly shows.Packaging Industry is arranged as an independent industry system, development
Enter the national economic and social development planning.
Polypropylene (Polypropylene, abbreviation PP) is a kind of hemicrystalline thermoplastic.Impact resistance with higher
Property, engineering properties is tough, resists a variety of organic solvents and acid and alkali corrosion；It is widely used, be usually common high molecular material it
One.
Currently, being badly in need of providing a kind of packaging material for candy.
Summary of the invention
It is an object of the invention to: a kind of packaging material and preparation method thereof for candy is provided.
To achieve the goals above, the invention provides the following technical scheme:
A kind of packaging material for candy, the raw material including following parts by weight:
70-78 parts of polypropylene, 30-34 parts of acrylic resin, 60-70 parts of polyvinyl alcohol, 15-20 parts of xanthan gum, glutaraldehyde
4-10 parts, 13-15 parts of isopropanol, 4-8 parts of pelopon A, 0.5-1 parts of nano silica, titanium nitride 1-1.5
Part, 3-5 parts of zeolite with carrying silver, UVP3270.5-1 parts of ultraviolet absorbing agent, 1-3 parts of chitin, 3-6 parts of shale powder, nano inorganic are remote
0.5-1 parts of infra-red material, 0.1-0.5 parts of vanillic aldehyde, 0.1-0.5 parts of plant polyose, beeswax 0.1-0.5 parts natural, calcium fruit fiber
0.4-1 parts.
Preferably, a kind of packaging material for candy, the raw material including following parts by weight:
72 parts of polypropylene, 32 parts of acrylic resin, 62 parts of polyvinyl alcohol, 17 parts of xanthan gum, 6 parts of glutaraldehyde, isopropanol 14
Part, 5 parts of pelopon A, 0.6 part of nano silica, 1.2 parts of titanium nitride, 4 parts of zeolite with carrying silver, ultraviolet radiation absorption
UVP3270.7 parts of agent, 2 parts of chitin, 4 parts of shale powder, 0.7 part of nano inorganic far-infrared material, 0.2 part of vanillic aldehyde, plant are more
Sugared 0.2 part, 0.2 part of natural beeswax, 0.7 part of calcium fruit fiber.
Preferably, a kind of packaging material for candy, the raw material including following parts by weight:
76 parts of polypropylene, 33 parts of acrylic resin, 68 parts of polyvinyl alcohol, 18 parts of xanthan gum, 8 parts of glutaraldehyde, isopropanol
13.5 parts, it is 7 parts of pelopon A, 0.8 part of nano silica, 1.3 parts of titanium nitride, 3.5 parts of zeolite with carrying silver, ultraviolet
UVP3270.9 parts of light absorbers, 1.5 parts of chitin, 5 parts of shale powder, 0.9 part of nano inorganic far-infrared material, vanillic aldehyde 0.4,
0.4 part of plant polyose, 0.3 part of natural beeswax, 0.8 part of calcium fruit fiber.
A kind of preparation method of the packaging material for candy, weighs each raw material according to the ratio, mixing, melting mixing, extrusion
Granulation.
Preferably, the temperature of melting mixing is 150~210 DEG C.
Preferably, the temperature of melting mixing is 180 DEG C.
Preferably, the temperature of extruding pelletization is 150~220 DEG C.
Preferably, the temperature of extruding pelletization is 175 DEG C.
The beneficial effects of the present invention are:
Packaging material materials safety of the invention is reliable, and comprehensive performance is superior, has stable and efficient antibiotic effect, can
To inhibit bacterial growth, it is highly suitable for the packaging of candy.
Specific embodiment
Embodiment 1
A kind of packaging material for candy, the raw material including following parts by weight:
70 parts of polypropylene, 30 parts of acrylic resin, 60 parts of polyvinyl alcohol, 15 parts of xanthan gum, 4 parts of glutaraldehyde, isopropanol 13
Part, 4 parts of pelopon A, 0.5 part of nano silica, 1 part of titanium nitride, 3 parts of zeolite with carrying silver, ultraviolet absorbing agent
UVP3270.5 parts, 1 part of chitin, 3 parts of shale powder, 0.5 part of nano inorganic far-infrared material, 0.1 part of vanillic aldehyde, plant polyose
0.1 part, 0.1 part of natural beeswax, 0.4 part of calcium fruit fiber.
The preparation method of the above-mentioned packaging material for candy weighs each raw material according to the ratio, mixing, melting mixing, extrusion
Granulation, wherein the temperature of melting mixing is 150 DEG C, and the temperature of extruding pelletization is 150 DEG C.
Embodiment 2
A kind of packaging material for candy, the raw material including following parts by weight:
72 parts of polypropylene, 32 parts of acrylic resin, 62 parts of polyvinyl alcohol, 17 parts of xanthan gum, 6 parts of glutaraldehyde, isopropanol 14
Part, 5 parts of pelopon A, 0.6 part of nano silica, 1.2 parts of titanium nitride, 4 parts of zeolite with carrying silver, ultraviolet radiation absorption
UVP3270.7 parts of agent, 2 parts of chitin, 4 parts of shale powder, 0.7 part of nano inorganic far-infrared material, 0.2 part of vanillic aldehyde, plant are more
Sugared 0.2 part, 0.2 part of natural beeswax, 0.7 part of calcium fruit fiber.
The preparation method of the above-mentioned packaging material for candy weighs each raw material according to the ratio, mixing, melting mixing, extrusion
Granulation, wherein the temperature of melting mixing is 180 DEG C, and the temperature of extruding pelletization is 175 DEG C.
Embodiment 3
A kind of packaging material for candy, the raw material including following parts by weight:
76 parts of polypropylene, 33 parts of acrylic resin, 68 parts of polyvinyl alcohol, 18 parts of xanthan gum, 8 parts of glutaraldehyde, isopropanol
13.5 parts, it is 7 parts of pelopon A, 0.8 part of nano silica, 1.3 parts of titanium nitride, 3.5 parts of zeolite with carrying silver, ultraviolet
UVP3270.9 parts of light absorbers, 1.5 parts of chitin, 5 parts of shale powder, 0.9 part of nano inorganic far-infrared material, vanillic aldehyde 0.4,
0.4 part of plant polyose, 0.3 part of natural beeswax, 0.8 part of calcium fruit fiber.
The preparation method of the above-mentioned packaging material for candy weighs each raw material according to the ratio, mixing, melting mixing, extrusion
Granulation, wherein the temperature of melting mixing is 200 DEG C, and the temperature of extruding pelletization is 200 DEG C.
Embodiment 4
A kind of packaging material for candy, the raw material including following parts by weight:
78 parts of polypropylene, 34 parts of acrylic resin, 70 parts of polyvinyl alcohol, 20 parts of xanthan gum, 10 parts of glutaraldehyde, isopropanol 15
Part, 8 parts of pelopon A, 1 part of nano silica, 1.5 parts of titanium nitride, 5 parts of zeolite with carrying silver, ultraviolet absorbing agent
UVP3271 parts, 3 parts of chitin, 6 parts of shale powder, 1 part of nano inorganic far-infrared material, 0.5 part of vanillic aldehyde, plant polyose 0.5
Part, 0.5 part of natural beeswax, 1 part of calcium fruit fiber.
The preparation method of the above-mentioned packaging material for candy weighs each raw material according to the ratio, mixing, melting mixing, extrusion
Granulation, wherein the temperature of melting mixing is 210 DEG C, and the temperature of extruding pelletization is 210 DEG C.
Embodiment 5
Antibacterial test is carried out to embodiment 1-4 resulting materials, as a result as shown in the table:
| Staphylococcus aureus | Escherichia coli | |
| Embodiment 1 | 99.6% | 99.3% |
| Embodiment 2 | 99.7% | 99.8% |
| Embodiment 3 | 99.4% | 99.4% |
| Embodiment 4 | 99.4% | 99.3% |
As can be seen from the table: the anti-microbial property of the plastics of the embodiment of the present invention is apparently higher than comparative example, has good
Good anti-microbial property, meets the requirement of long acting antibiotic.
Claims (8)
1. a kind of packaging material for candy, it is characterised in that: the raw material including following parts by weight:
70-78 parts of polypropylene, 30-34 parts of acrylic resin, 60-70 parts of polyvinyl alcohol, 15-20 parts of xanthan gum, glutaraldehyde 4-10
Part, carries 13-15 parts of isopropanol, 4-8 parts of pelopon A, 0.5-1 parts of nano silica, 1-1.5 parts of titanium nitride
3-5 parts of silver zeolite, UVP3270.5-1 parts of ultraviolet absorbing agent, 1-3 parts of chitin, 3-6 parts of shale powder, nano inorganic far infrared
0.5-1 parts of material, 0.1-0.5 parts of vanillic aldehyde, 0.1-0.5 parts of plant polyose, beeswax 0.1-0.5 parts natural, calcium fruit fiber 0.4-1
Part.
2. a kind of packaging material for candy according to claim 1, is characterized in that: the original including following parts by weight
Material:
72 parts of polypropylene, 32 parts of acrylic resin, 62 parts of polyvinyl alcohol, 17 parts of xanthan gum, 6 parts of glutaraldehyde, 14 parts of isopropanol, ten
5 parts of dialkyl benzene sulfonic acids sodium salt, 0.6 part of nano silica, 1.2 parts of titanium nitride, 4 parts of zeolite with carrying silver, ultraviolet absorbing agent
UVP3270.7 parts, 2 parts of chitin, 4 parts of shale powder, 0.7 part of nano inorganic far-infrared material, 0.2 part of vanillic aldehyde, plant polyose
0.2 part, 0.2 part of natural beeswax, 0.7 part of calcium fruit fiber.
3. a kind of packaging material for candy according to claim 1, is characterized in that: the original including following parts by weight
Material:
76 parts of polypropylene, 33 parts of acrylic resin, 68 parts of polyvinyl alcohol, 18 parts of xanthan gum, 8 parts of glutaraldehyde, 13.5 parts of isopropanol,
7 parts of pelopon A, 0.8 part of nano silica, 1.3 parts of titanium nitride, 3.5 parts of zeolite with carrying silver, ultraviolet radiation absorption
UVP3270.9 parts of agent, 1.5 parts of chitin, 5 parts of shale powder, 0.9 part of nano inorganic far-infrared material, vanillic aldehyde 0.4, plant are more
Sugared 0.4 part, 0.3 part of natural beeswax, 0.8 part of calcium fruit fiber.
4. a kind of preparation method of packaging material for candy according to claim 1 to 3, feature exist
In: each raw material is weighed according to the ratio, is mixed, melting mixing, extruding pelletization.
5. a kind of preparation method of packaging material for candy according to claim 4, it is characterised in that: melting mixing
Temperature be 150~210 DEG C.
6. a kind of preparation method of packaging material for candy according to claim 5, it is characterised in that: melting mixing
Temperature be 180 DEG C.
7. a kind of preparation method of packaging material for candy according to claim 4, it is characterised in that: extruding pelletization
Temperature be 150~220 DEG C.
8. a kind of preparation method of packaging material for candy according to claim 7, it is characterised in that: extruding pelletization
Temperature be 175 DEG C.